《ASTM C1656-2013 Standard Guide for Measuring the Reactivity of Hydraulic Refractory Castables using Exothermic Profile《利用放热曲线图测量液压耐熔铸块活性的标准指南》.pdf》由会员分享，可在线阅读，更多相关《ASTM C1656-2013 Standard Guide for Measuring the Reactivity of Hydraulic Refractory Castables using Exothermic Profile《利用放热曲线图测量液压耐熔铸块活性的标准指南》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1656 13Standard Guide forMeasuring the Reactivity of Hydraulic Refractory Castablesusing Exothermic Profile1This standard is issued under the fixed designation C1656; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, th

2、e year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This guide applies to all castables with a reactive bindersystem that produces a measurable heat profile dur

3、ing thesetting and hardening process. The majority of these systemswill have calcium aluminate cement as one component of thebinder system.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to

4、 establish appro-priate safety and health practices and to determine theapplicability of regulatory limitations prior to use .2. Referenced Documents2.1 ASTM Standards:2C401 Classification of Alumina and Alumina-SilicateCastable RefractoriesC71 Terminology Relating to RefractoriesC862 Practice for P

5、reparing Refractory Concrete Specimensby Casting3. Terminology3.1 Definitions:3.1.1 EP exothermic profile, n the curve generated byplotting temperature of the embedded thermocouple versustime.3.1.2 LCC, nLow cement castable4. Significance and Use4.1 The heat of hydration of a calcium aluminate based

6、castable is liberated over a short period of time (as comparedto Portland cement). This makes it easy to measure the heatprofile using off-the-shelf thermocouple equipment.4.2 The heat profile can be used to make inferences aboutthe setting and strength gain behavior of a castable andsometimes the w

7、orking time of a castable.4.3 Factors that should be controlled when comparing twocastables include: size, shape and mass of cast object, starttemperature of the mix, temperature of environment, and thethermal conductivity of the environment. If these factors areheld constant, then the two castables

8、 heat profiles can becompared.4.4 The temperature increase created by the castable exo-thermic reaction shall be at least 2.0C more than the normalfluctuation of the laboratory temperature so that the time of thisincrease is easily discernible to the user.4.5 Varying the amount of cement in the cast

9、able, theamount of water, the type and quantity of admixtures, and soforth, will change the shape, maximum temperature and time tomaximum temperature of the curve.4.6 Following is an example of a curve generated for anLCC (see Fig. 1) that does exhibit two peaks, the first onemarking the end of work

10、ing time. In this curve one could alsoinfer that the start temperature of the mix was 24C and alsothat the hydraulic strength gain reaction was significantlystarted, but not completed by 6 h.5. Apparatus5.1 Mixing equipment as prescribed in C862.5.2 Type T thermocouple (Type J, E, or K are also acce

11、pt-able but not preferred due to range of sensitivity. Other typescannot be used.) Wire ends should be joined by solder orwelding. Simple twisting is not recommended due to thepotential for inaccurate readings.5.3 Thermocouple sheathing (optional)5.4 Voltmeter, data acquisition card or some other in

12、stru-ment to read the thermocouple mV value.5.5 Container for storage of castable during heat profilegeneration and constant temperature environment in which tostore the container.5.6 Personal computer loaded with above card will makecurve generation easier.1This guide is under the jurisdiction of A

13、STM Committee C08 on Refractoriesand is the direct responsibility of Subcommittee C08.09 on Monolithics.Current edition approved April 1, 2013. Published June 2013. Originallyapproved in 2007. Last previous edition approved in 2007 as C1656-07. DOI:10.1520/C1656-13.2For referenced ASTM standards, vi

14、sit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2

15、959. United States16. Hazards6.1 There are no known hazards associated with the method.Safe practice should be used when mixing the castable.Castable MSDS should be consulted to determine if anyhazards exist with the castable.7. Procedure7.1 Prepare the castable according to the manufacturersmixing

16、instructions noting the time of water addition. Forcomparison testing, the water addition should produce acomparable consistency of the castables.7.2 If the entire sample will not be used for the EPgeneration, grab select a representative sample of required sizefrom the mixing bowl by successive qua

17、rtering when the mixeris turned off.7.3 Place castable in a container. Place container in anenvironment with constant temperature.7.4 Place thermocouple in the center of the castable in thecontainer. Use of a sheath is not required but will allow foreasier removal of the thermocouple later. Use of a

18、n insulatingcontainer will drive the final peak temperature to a higherpoint.7.5 Begin taking readings within 5 minutes of placing thecastable in the container. Readings can be taken either manu-ally at desired time intervals (note the mV (or temperature)reading readjusting your time 0 from the wate

19、r addition pointor automatically with a PC) by using a strip recorder orautomatically gathering the information with a PC outfittedwith the correct hardware to read thermocouple values.7.6 Plot temperature versus time to view the EP. This can beautomated through the use of a personal computer and a

20、dataacquisition card or a strip or chart recorder.8. Report8.1 Record the type of castable, mixing time, and wateradded and consistency after mixing.8.2 Record the temperature of the immediate surroundings.8.3 Record the amount of castable and the type of containerused during the EP generation.8.4 R

21、ecord the type and presence of any insulation used asthe container or around the container.8.5 Record the start temperature.8.6 Generate the EP curve.9. Keywords9.1 castable; refractory; exothermic profile; EP; workingtimeFIG. 1 Example of LCC Exo ProfileC1656 132ASTM International takes no position

22、 respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.T

23、his standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM In

24、ternational Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address show

25、n below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C1656 133