ASTM C1419-2014 Standard Test Method for Sonic Velocity in Refractory Materials at Room Temperature and Its Use in Obtaining an Approximate Young&rsquo s Modulus《室温下耐火材料中的声速和其在获得近似.pdf

《ASTM C1419-2014 Standard Test Method for Sonic Velocity in Refractory Materials at Room Temperature and Its Use in Obtaining an Approximate Young&rsquo s Modulus《室温下耐火材料中的声速和其在获得近似.pdf》由会员分享，可在线阅读，更多相关《ASTM C1419-2014 Standard Test Method for Sonic Velocity in Refractory Materials at Room Temperature and Its Use in Obtaining an Approximate Young&rsquo s Modulus《室温下耐火材料中的声速和其在获得近似.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1419 14Standard Test Method forSonic Velocity in Refractory Materials at Room Temperatureand Its Use in Obtaining an Approximate Youngs Modulus1This standard is issued under the fixed designation C1419; the number immediately following the designation indicates the year oforiginal adop

2、tion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method describes a procedure for measuringthe sonic velocity i

3、n refractory materials at room temperature.The sonic velocity can be used to obtain an approximate valuefor Youngs modulus.1.2 The sonic velocity may be measured through the length,thickness, and width of the specimen.1.3 The values stated in SI units are to be regarded asstandard. No other units of

4、 measurement are included in thisstandard.1.4 This standard does not purport to address the safetyconcerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety andhealth practices and determine the applicability of regulatorylimitatio

5、ns prior to use.2. Referenced Documents2.1 ASTM Standards:2C134 Test Methods for Size, Dimensional Measurements,and Bulk Density of Refractory Brick and InsulatingFirebrickC179 Test Method for Drying and Firing Linear Change ofRefractory Plastic and Ramming Mix SpecimensC769 Test Method for Sonic Ve

6、locity in ManufacturedCarbon and Graphite Materials for Use in ObtainingYoungs ModulusC885 Test Method for Youngs Modulus of RefractoryShapes by Sonic ResonanceE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE691 Practice for Conducting an Interlaboratory Study toDetermine t

7、he Precision of a Test MethodIEEE/ASTM SI10 American National Standard for Use ofthe International System of Units (SI): The Modern MetricSystem3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 longitudinal sonic pulse, na sonic pulse in which thedisplacements are in the directi

8、on of propagation of the pulse.3.1.2 pulse travel time, (Tt), nthe total time, measured inmicroseconds, required for the sonic pulse to traverse thespecimen being tested, and for the associated electronic signalsto traverse the circuits of the pulse propagation circuitry.3.1.3 zero time, (To), nthe

9、travel time (correction factor),measured in microseconds, associated with the electroniccircuits in the pulse-propagation system.4. Summary of Test Method4.1 The velocity of sound waves passing through the testspecimen is determined by measuring the distance through thespecimen and dividing by the t

10、ime lapse between the transmit-ted pulse and the received pulse.3,4An approximate value forYoungs modulus can be obtained as follows:E 5 v2(1)where:E = Youngs modulus of elasticity, Pa, = density, kg/m3, andv = signal velocity, m/s.4.2 Strictly speaking, the elastic constant given by thismeasurement

11、 is not E but C33, provided the sonic pulse islongitudinal and the direction of propagation is along the axisof symmetry.3,45. Significance and Use5.1 This test method is used to determine the sonic velocityand approximate Youngs modulus of refractory shapes at1This test method is under the jurisdic

12、tion of ASTM Committee C08 onRefractories and is the direct responsibility of Subcommittee C08.01 on Strength.Current edition approved Sept. 1, 2014. Published October 2014. Originallyapproved in 1999. Last previous edition approved in 2009 as C1419 99a (2009).DOI: 10.1520/C1419-14.2For referenced A

13、STM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Schreiber, Anderson, and Soga, Elastic Constants and Their Measurement,McGraw

14、-Hill Book Co., 1221Avenue of theAmericas, NewYork, NY10020, 1973.4American Institute of Physics Handbook, 3rd ed., McGraw-Hill Book Co., 1221Avenue of the Americas, New York, NY 10020, 1972, pp. 398ff.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959

15、. United States1room temperature. Since this test is nondestructive, specimensmay be used for other tests as desired.5.2 This test method is useful for research and development,engineering application and design, manufacturing quality andprocess control, and for developing purchasing specifications.

16、6. Apparatus6.1 Driving Circuit, which consists of an ultra sonic pulsegenerator capable of producing pulses in a frequency rangefrom 0.5 to 2.5 MHz.6.2 Transducer, input.6.3 Transducer, output.6.4 Oscilloscope, dual trace with a preamplifier and timedelay circuity.6.5 See Fig. 1 for a typical set-u

17、p.7. Test Specimen7.1 Specimens may be prisms of any desired length withparallel smooth surfaces. Opposite surfaces across the length,width, and thickness shall be parallel. The smallest dimensionshall be greater than 5 times the diameter of the largestaggregate in the refractory. The surface on whi

18、ch the transduc-ers will be located must have a width of at least 1.5 times thediameter of the transducer being used.7.2 Dry the specimens in an oven at 110C for a minimumof 5 h. Cool to room temperature. Test for sonic velocity within5 h of drying.7.3 Measurement of Density and DimensionsCalculate

19、thedensity of the specimens by Test Methods C134 and determinethe specimen lengths by either Test Methods C134 or C179.8. Procedure8.1 Assemble and connect the apparatus as shown in Fig. 1and refer to the equipment manufacturers instructions for hookup precautions. If using commercially available eq

20、uipmentdesigned to measure sonic velocity, refer to the manufacturersset-up and operating instructions. Allow adequate time for thetest apparatus to warm up and stabilize.8.2 Provide a suitable coupling medium on the transducerfaces.NOTE 1Petroleum jelly or grease couple well but may be difficult to

21、remove for subsequent tests on the same specimen.8.3 Bring the transducer faces into intimate contact, but donot exceed the manufacturers recommended contact pressure.8.4 Determine To, the zero time (zero correction) measuredin microseconds, associated with the electronic circuits in thepulse propag

22、ation instrument and coupling. Alternately, if acommercially available apparatus is used, which utilizes a zerooffset and a supplied calibration standard, the instrument canbe zeroed using the standard and Todoes not have to bedetermined or used in the final calculation.8.5 Measure and weigh and cal

23、culate the density of the testspecimen as in 7.3.8.6 Lightly coat the faces of the test specimen that will be incontact with the transducers with the coupling medium. Posi-tion the transducers on opposite surfaces so that they provide amirror image and that the distance between the input transducera

24、nd the output transducer is equal to the dimension throughwhich the measurement is performed. Place the transducersagainst the test specimen. Apply firm pressure until the pulsetravel time stabilizes.8.7 Determine Tt, the pulse travel time from the oscilloscopetraces as illustrated in Fig. 2, or, if

25、 the instrument used has azero correction, Tc, the corrected travel time.9. Calculation9.1 Velocity of Signal:v 5LTt2 To(2)orv 5LTc(3)FIG. 1 Equipment Set-upC1419 142where:v = velocity of signal, m/s,L = distance between the two transducers, the dimensionthrough which the measurement is performed, m

26、,Tt= pulse travel time, s,To= zero times, s, andTc= corrected travel time (TtTo), s.9.2 An appropriate value for Youngs modulus of thespecimen can be obtained using the following equation:E 5 v2(4)where:E = Youngs modulus of elasticity, Pa (approximate), = density, kg/m3, andv = signal velocity, m/s

27、.9.3 Conversion FactorsSee IEEE/ASTM SI10.10. Report10.1 Report the following information:10.1.1 Specimen dimensions and weight.10.1.2 Sonic velocity for each specimen.10.1.3 Density for each specimen, if calculated.10.1.4 Youngs modulus for each specimen, if calculated.10.1.5 It is recommended that

28、 the average and standarddeviation values be included for each group of specimens.10.1.6 Frequency of the transducers used and sonic velocityequipment identification.10.1.7 Method of coupling the transducers to the specimen.10.1.8 As available a complete identification of the materialbeing tested in

29、cluding manufacturer, brand, lot number, firinghistory, and specimen sampling plan.11. Precision and Bias11.1 Interlaboratory Test DataAn interlaboratory studywas completed among nine laboratories in 1996.Astandard setof samples consisting of five different refractory materials anda Plexiglas prism

30、were circulated and tested by each labora-tory.5The samples tested were Plexiglas, two high aluminabrick (SR-90 and SR-99), an alumina insulating brick (B-301),an isopressed alumina shape (A-1148), and a zircon brick(ZRX). The dimensions of all samples were approximately 228mm 114 mm 75 mm. Each lab

31、oratory measured andweighed each sample and tested each for signal travel time.Each time was the average of three test determinations.11.2 PrecisionTables 1 and 2 contain the precision statis-tics for the sonic velocity and approximate Youngs modulusresults, respectively. The terms repeatability lim

32、it and repro-ducibility limit are used as specified in Practice E177.11.3 BiasNo justifiable statement can be made on the biasof the test method for measuring the sonic velocity andapproximate Youngs modulus of refractories because thevalue of the sonic velocity and approximate Youngs moduluscan be

33、defined only in terms of the test method.12. Keywords12.1 modulus of elasticity; refractories; sonic velocity;Youngs modulus5Since these samples were not destroyed in testing, they are being retained incustody by C08.01 for future reference and test development.FIG. 2 Typical Oscilloscope DisplayTAB

34、LE 1 Precision Statistics for Sonic VelocityMaterialAverage(m/s)Std. Dev.WithinLabs, SrStd. Dev.BetweenLabs, SRRepeatabilityLimit, rReproducibilityLimit, RPlexiglas 2731.3 1.19 28.97 3.37 81.93A-1148 9223.3 18.29 182.59 51.73 516.36B-301 2511.6 6.96 43.49 19.68 122.98SR-90 3911 19.5 81.26 55.15 229.

35、8SR-99 4697.5 9.35 81.12 26.45 229.44ZRX 5789.8 39.99 126.94 113.09 358.99TABLE 2 Precision Statistics for Approximate Youngs ModulusMaterialAverage(MPa)Std. Dev.WithinLabs, SrStd. Dev.BetweenLabs, SRRepeatabilityLimit, rReproducibilityLimit, RPlexiglas 8970 8.42 191 23.8 541A-1148 293000 1190 11500

36、 3370 32600B-301 9380 52 317 147 896SR-90 43400 434 1590 1230 4500SR-99 67900 829 2180 2340 6170ZRX 90400 1270 4370 3590 12300C1419 143ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this stand

37、ard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andi

38、f not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, wh

39、ich you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,

40、United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 144