《ASTM B653 B653M-2011 Standard Specification for Seamless and Welded Zirconium and Zirconium Alloy Welding Fittings《无缝和焊接锆及锆合金锻造配件标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B653 B653M-2011 Standard Specification for Seamless and Welded Zirconium and Zirconium Alloy Welding Fittings《无缝和焊接锆及锆合金锻造配件标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation:B653/B653M06 Designation: B653/B653M 11Standard Specification forSeamless and Welded Zirconium and Zirconium AlloyWelding Fittings1This standard is issued under the fixed designation B653/B653M; the number immediately following the designation indicates the yearof original adoption or, i

2、n the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers fittings, factory made from three grades of zirconium an

3、d zirconium alloys. The term weldingfittings applies to butt-welding parts such as 45 and 90 elbows, 180 returns, caps, tees, reducers, lap-joint stub ends, and othertypes.1.2 The values stated in either inch-pound units or SI units are to be regarded separately as the standard. Within the text, the

4、SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be usedindependently of the other. Combining values from the two systems may result in nonconformance with the specification.1.3 This standard does not purport to address all of th

5、e safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B493 Specification for Zircon

6、ium and Zirconium Alloy ForgingsB523/B523M Specification for Seamless and Welded Zirconium and Zirconium Alloy TubesB550/B550M Specification for Zirconium and Zirconium Alloy Bar and WireB551/B551M Specification for Zirconium and Zirconium Alloy Strip, Sheet, and PlateB614 Practice for Descaling and

7、 Cleaning Zirconium and Zirconium Alloy SurfacesB658/B658M Specification for Seamless and Welded Zirconium and Zirconium Alloy Pipe2.2 ANSI Standards:B16.9 Wrought Steel Butt-Welding Fittings3B36.19 Stainless Steel Pipe32.3 Manufacturers Standardization Society of the Valve and Fittings Industry Sta

8、ndards:SP-25 Standard Marking System for Valves, Fittings, Flanges, and Unions4SP-43 Standard Practice for Light Weight Stainless Steel Fittings42.4 American Society of Mechanical Engineers:ASME Boiler and Pressure Vessel Code, Sections VIII and IX53. Terminology3.1 Lot Definitions:3.1.1 weld fittin

9、gs, ndefinition is to be mutually agreed upon between manufacturer and the purchaser.4. Classification4.1 The fittings are furnished in three grades as follows:4.1.1 Grade R60702 (PZ 2)Unalloyed zirconium.1This specification is under the jurisdiction of ASTM Committee B10 on Reactive and Refractory

10、Metals and Alloys and is the direct responsibility of SubcommitteeB10.02 on Zirconium and Hafnium.Current edition approved Sept.April 1, 2006.2011. Published September 2006.April 2011. Originally approved in 1979. Last previous edition approved in 20022006 asB653/B653M 026. DOI: 10.1520/B0653_B0653M

11、-0611.2For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3Available from American National Standards Institute

12、 (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.4Available from Manufacturers Standardization Society of the Valve and Fittings Industry (MSS), 127 Park St., NE, Vienna, VA 22180-4602, http:/www.mss-.5Available from American Society of Mechanical Engineers (ASME), ASME Int

13、ernational Headquarters, Three Park Ave., New York, NY 10016-5990, http:/www.asme.org.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to

14、 adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Cons

15、hohocken, PA 19428-2959, United States.4.1.2 Grade R60704 (PZ 4)Zirconium-tin.4.1.3 Grade R60705 (PZ 5)Zirconium-niobium.5. Ordering Information5.1 Orders for materials under this specification shall include the following information:5.1.1 Quantity,5.1.2 Name of material (zirconium fittings),5.1.3 G

16、rade number (see 4.1),5.1.4 ASTM designation and year of issue,5.1.5 Hydrostatic test requirements (see 10.2),5.1.6 Inspection requirements (see 11.1),5.1.7 Finish (see Section 9), and5.1.8 Additions to the specification and supplementary requirements, if required.NOTE 1A typical ordering descriptio

17、n is as follows: 15 pieces, zirconium, 4-in. 100 mm, Schedule 40, 90 long radius elbows, descaled, ASTMB653 - 01, Grade R60702. Supplementary Requirement S3, Stress Relief Heat Treatment.6. Materials and Manufacture6.1 Forging, forming, or shaping operations may be performed by hammering, pressing,

18、piercing, extruding, upsetting, rolling,bending, fusion welding, machining, or by a combination of these operations. The forming procedure shall be so applied that itwill not produce injurious defects in the fittings.6.2 Fittings containing welded seams or other joints made by welding shall comply w

19、ith the following provisions:6.2.1 Welded by welders, welding operators, and welding procedures qualified under the provisions of Section IX of the ASMEBoiler and Pressure Vessel Code.6.2.2 Filler metal, when used, shall be the same grade as the base metal.6.2.3 All welds on grade R60705 shall be st

20、ress relief annealed within 14 days after welding to prevent delayed hydridecracking, in accordance with Supplementary Requirements Section S3, Stress Relief Heat Treatment.7. Chemical Composition7.1 The material shall conform to the requirements as to chemical composition prescribed in Table 1.8. T

21、ensile Requirements8.1 The material shall conform to the requirements as to the tensile properties prescribed in Table 1.9. Workmanship, Finish, and Appearance9.1 For fittings covered by ANSI B16.9 or MSS SP-43, or for fittings to be used with pipe ordered to ANSI B36.19, the sizes,shapes, and dimen

22、sions of the fittings shall be as specified in those standards.9.2 The fittings shall be free of injurious external and internal imperfections of a nature that will interfere with the purpose forwhich the fittings are intended. Minor defects may be removed by grinding, providing the wall thickness i

23、s not decreased to lessthan the minimum thickness, and further provided that the ground-out area shall be faired out.10. Hydrostatic Tests10.1 All fittings shall be capable of withstanding without failure, leakage, or impairment of their serviceability, a test pressureprescribed in the applicable st

24、andards in Table 1 for the pipe or tubing with which the fitting is planned to be used.10.2 Hydrostatic tests shall be performed when required by the purchase order.11. Inspection11.1 The manufacturer shall inspect the material covered by this specification prior to shipment. If so specified in the

25、purchaseorder, the purchaser or his representative may witness the testing and inspection of the material at the place of manufacture. In suchcases the purchaser shall state in his purchase order which tests he desires to witness. The manufacturer shall give ample noticeTABLE 1 Permissible Raw Mater

26、ialsGradeAProduct and ASTM DesignationPipe Tube Plate Bar ForgingPZ 2(R60702)B658/B658MGrade R60702B523/B523MGrade R60702B551/B551MGrade R60702B550/B550MGrade R60702B493Grade R60702PZ 4(R60704)B658/B658MGrade R60704B523/B523MGrade R60704B551/B551MGrade R60704B550/B550MGrade R60704B493Grade R60704PZ

27、5(R60705)B658/B658MGrade R60705B523/B523MGrade R60705B551/B551MGrade R60705B550/B550MGrade R60705B493Grade R60705AWhen fittings are of welded construction, the symbol shown shall be supplemented by the letter “W.”B653/B653M 112to the purchaser as to the time and place of the designated tests. If the

28、 purchasers representative does not present himself at thetime agreed upon for the testing, the manufacturer shall consider the requirement for the purchasers inspection at the place ofmanufacture to be waived.11.2 The manufacturer shall afford the inspector representing the purchaser, without charg

29、e, all reasonable facilities to satisfyhim that the material is being furnished in accordance with this specification. This inspection shall be so conducted as not tointerfere unnecessarily with the operation of the works.12. Rejection12.1 Rejection for failure of the material to meet the requiremen

30、ts of this specification shall be reported to the manufacturer.Unless otherwise specified, rejected material may be returned to the manufacturer at the manufacturers expense, unless thepurchaser receives, within three weeks of the notice of rejection, other instructions for disposition.13. Certifica

31、tion13.1 A producer or supplier shall furnish the purchaser with a certificate that the material was manufactured, sampled, tested,and inspected in accordance with this specification and has been found to meet the requirements. The certificate shall include areport of the test results.13.2 All mater

32、ial incorporated within the fitting shall be identified and shall be in accordance with the applicable standards inTable 1.14. Referee14.1 In the event of disagreement between the manufacturer and the purchaser on the conformance of the material to therequirements of this specification or any specia

33、l test specified by the purchaser, a mutually acceptable referee shall perform the testsin question. The results of the referees testing shall be used in determining conformance of the material to this specification.15. Product Marking15.1 Unless otherwise specified, the manufacturers name or tradem

34、ark, the schedule number, material, and size shall bestamped (see Note 2), stenciled, electroetched, or otherwise suitably marked on each fitting. In addition, each fitting shall bemarked with the identification grade symbol and suffix for the respective specification listed in Table 1. On wall thic

35、knesses thinnerthan Schedule 40S, no stamps or other indented markings shall be used. When the size does not permit complete marking,identification marks may be omitted in the sequence shown in MSS SP-25.NOTE 2When steel stamps are used, they should be applied prior to heat treatment and care should

36、 be taken so that the marking is not deep enoughto cause cracks or to reduce the wall thickness of the fitting below the minimum allowed.16. Packaging and Package Marking16.1 The fittings shall be packaged suitably in such a manner as to assure safe delivery to its destination when properlytransport

37、ed by common carrier.17. Keywords17.1 fitting; pipe; zirconium; zirconium alloySUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not be considered unless specified in the order, in which event thetest shall be made by the manufacturer at the purchasers expense.S1. Surface InspectionS1.1 Liq

38、uid penetrant inspection may be performed on all outside-diameter surfaces of the fittings and inside-diameter surfaceswhere practicable.Acceptance shall be in accordance withAppendix 8, Section VIII of theASME Boiler and Pressure Vessel Code.S2. Radiographic Inspections of WeldsS2.1 Radiographic in

39、spection may be performed on all weldments of the fittings in accordance with paragraph UW-51, SectionVIII, of the ASME Boiler and Pressure Vessel Code.S3. Stress-Relief Heat TreatmentS3.1 The stress-relieving treatment shall consist of holding the fitting at a minimum temperature of 1100F 600C for

40、not lessthan h/in.30 min per inch 25 mm of the maximum thickness in a nonreducing atmosphere.S3.2 The minimum time at this temperature is 15 min. All stress-relieved parts shall be cleaned subsequently and shall be freeof oxide scale contamination (see Practice B614).B653/B653M 113ASTM International

41、 takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their ow

42、n responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be ad

43、dressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, a

44、t the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).B653/B653M 114