ASTM B564-2015 Standard Specification for Nickel Alloy Forgings《镍合金锻件的标准规格》.pdf
《ASTM B564-2015 Standard Specification for Nickel Alloy Forgings《镍合金锻件的标准规格》.pdf》由会员分享,可在线阅读,更多相关《ASTM B564-2015 Standard Specification for Nickel Alloy Forgings《镍合金锻件的标准规格》.pdf(9页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B564 15Standard Specification forNickel Alloy Forgings1This standard is issued under the fixed designation B564; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indica
2、tes the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification2covers forgings of:Alloy Type UNS Number(s)Fe-Ni-Cr-Mo-N
3、N08367Low-carbon Cr-Ni-Fe-N R20033Low-carbon Ni-Cr-Mo N06035, N06058, N06059Low-carbon Ni-Cr-Mo-Cu N06200Low-carbon Ni-Cr-Mo-W N06686Low-carbon Ni-Fe-Cr-Mo-Cu N08031Low-carbon Ni-Mo-Cr N10276, N06022, N10362Low-carbon Ni-Mo-Cr-Ta N06210Ni N02200Ni-Co-Cr-Si N12160Ni-Cr-Co-Mo N06617Ni-Cr-Fe N06600, N0
4、6603, N06690Ni-Cr-Fe-Al N06025Ni-Cr-Fe-Si N06045Ni-Cr-Mo-Nb N06625Ni-Cr-Mo-Si N06219Ni-Cr-Mo-W N06110Ni-Cr-W-Mo N06230Ni-Cu N04400Ni-Fe-Cr N08120, N08800, N08810, N08811Ni-Fe-Cr-Mo-Cu N08825Ni-Fe-Cr-W N06674Ni-Mo N10665, N10675, N10629Ni-Mo-Cr-Fe N10242, N106241.1.1 The nickel-iron-chromium alloys a
5、re UNS N08120,UNS N08800, UNS N08810, and UNS N08811. Alloy UNSN08800 is normally employed in service temperatures up toand including 1100F (593C). Alloys UNS N08810, N08120,and UNS N08811 are normally employed in service tempera-tures above 1100F (593C) where resistance to creep andrupture is requi
6、red, and are annealed to develop controlledgrain size for optimum properties in this temperature range.1.1.2 Nickel-iron-chromium-tungsten alloy UNS N06674 isnormally employed in service temperatures above 1100F(593C) where resistance to creep and rupture is required, andis annealed to develop optim
7、um properties in this temperaturerange.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address
8、all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateSafety Data Sheet (SDS) for this product/material as providedby the manufacturer, to establish appropriate
9、safety and healthpractices, and determine the applicability of regulatory limi-tations prior to use.2. Referenced Documents2.1 ASTM Standards:3B880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys andCobalt AlloysE8 Test Methods for Tension Testing o
10、f Metallic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE76 Test Methods for Chemical Analysis of Nickel-CopperAlloys (Withdrawn 2003)4E112 Test Methods for Determining Average Grain SizeE350 Test Methods for Chemical Analysis of Carbon S
11、teel,Low-Alloy Steel, Silicon Electrical Steel, Ingot Iron, andWrought Iron1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved
12、Oct. 1, 2015. Published October 2015. Originallyapproved in 1972. Last previous edition approved in 2011 as B564 111. DOI:10.1520/B0564-15.2For ASME Boiler and Pressure Vessel Code applications see related Specifi-cation SB-564 in Section II of that Code.* New designations established in accordance
13、withASTM E527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe
14、 ASTM website.4The last approved version of this historical standard is referenced onwww.astm.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1E1473 Test Methods for
15、Chemical Analysis of Nickel,Cobalt, and High-Temperature Alloys2.2 Military Standards:5MIL-STD-129 Marking for Shipment and StorageMIL-STD-271 Nondestructive Testing Requirements forMetals3. Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessa
16、ry for material ordered under thisspecification. Examples of such requirements include, but arenot limited to, the following:3.1.1 Alloy (Table 1).3.1.2 Condition (Table 2).3.1.3 Quantity (mass or number of pieces).3.1.4 Forging, sketch or drawing.3.1.5 CertificationState if certification or a repor
17、t of testresults is required (14.1).3.1.6 Samples for Product (Check) AnalysisWhethersamples for product (check) analysis should be furnished (see4.2).3.1.7 Purchaser InspectionIf the purchaser wishes towitness tests or inspection of material at the place ofmanufacture, the purchase order must so st
18、ate indicating whichtests or inspections are to be witnessed (12.1).4. Chemical Composition4.1 The material shall conform to the composition limitsspecified in Table 1.4.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations
19、 in accordance with Specification B880.5. Mechanical Properties and Other Requirements5.1 Mechanical PropertiesThe material shall conform tothe mechanical properties specified in Table 2.5.2 Grain SizeAnnealed alloys UNS N08810, N08120,and UNS N08811 shall conform to an average grain size ofASTM No.
20、 5 or coarser. Annealed alloy UNS N06674 shallconform to an average grain size of ASTM No. 7 or coarser.5Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.TABLE 1 Chemical RequirementsAComposition,
21、 %ElementNickelAlloyNickel-CopperAlloyLow-CarbonNickel-Molybdenum-ChromiumAlloyNickel-Chromium-Iron-AluminumAlloyLow-CarbonNickel-Chromium-MolybdenumAlloyNickel-Chromium-Iron-SiliconAlloyLow-CarbonNickel-Chromium-MolybdenumAlloyLow-CarbonNickel-Chromium-MolybdenumAlloyNickel-Chromium-Molybdenum-Tung
22、stenAlloyUNSN02200UNSN04400UNSN06022UNSN06025UNSN06035UNSN06045UNSN06058UNSN06059UNSN06110Nickel 99.0Bmin 63.0Bmin balanceBbalance balanceB45 min balance balanceB51.0BminCopper 0.25 28.034.0 . 0.10 0.30 0.3 0.50 0.50 0.50Iron 0.40 2.5 2.06.0 8.011.0 2.00 21.025.0 1.5 1.5 1.0Manganese 0.35 2.0 0.50 0
23、.15 0.50 1.0 0.50 0.5 1.0Carbon 0.15 0.3 0.015 0.150.25 0.050 0.050.12 0.010 0.010 0.15Silicon 0.35 0.5 0.08 0.5 0.60 2.53.0 0.10 0.10 1.0Sulfur 0.01 0.024 0.02 0.01 0.015 0.010 0.010 0.010 0.015Chromium . . 20.022.5 24.026.0 32.2534.25 26.029.0 20.023.0 22.024.0 28.033.0Aluminum . . . 1.82.4 0.40 .
24、 0.40 0.10.4 1.0Titanium . . . 0.10.2 . . . . 1.0Columbium(Nb) +Tantalum. . . . . . . . 1.0Molybdenum . . 12.514.5 . 7.609.00 . 18.521.0 15.016.5 9.012.0Phosphorus . . 0.02 0.02 0.030 0.02 0.015 0.015 0.50Tungsten . . 2.53.5 . 0.60 . 0.3 . 1.0-4.0Cobalt . . 2.5 . 1.00 . 0.3 0.3 .Vanadium . . 0.35 .
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB5642015STANDARDSPECIFICATIONFORNICKELALLOYFORGINGS 镍合金 锻件 标准 规格 PDF
链接地址:http://www.mydoc123.com/p-461577.html