《ASTM B475-2007(2013) Standard Specification for UNS N08020 UNS N08024 and UNS N08026 Nickel Alloy Round Weaving Wire《UNS N08020 UNS N08024和UNS N08026镍合金圆形编织线标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B475-2007(2013) Standard Specification for UNS N08020 UNS N08024 and UNS N08026 Nickel Alloy Round Weaving Wire《UNS N08020 UNS N08024和UNS N08026镍合金圆形编织线标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B475 07 (Reapproved 2013)Standard Specification forUNS N08020, UNS N08024, and UNS N08026 Nickel AlloyRound Weaving Wire1This standard is issued under the fixed designation B475; the number immediately following the designation indicates the year oforiginal adoption or, in the case of r

2、evision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers UNS N08020, UNS N08026,and UNS N08024 round weaving wire.NOTE 1Weaving

3、wire is customarily not welded. For applicationsinvolving welding in which the wire should be stabilized against loss ofcorrosion resistance, the purchaser should refer to Specification B473.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are

4、mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards

5、including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standard

6、s:2B473 Specification for UNS N08020, UNS N08024, andUNS N08026 Nickel Alloy Bar and WireB880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys andCobalt AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE1473 Test Methods for Chemical An

7、alysis of Nickel,Cobalt, and High-Temperature Alloys3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 weaving wire, nterm weaving wire as used in thisspecification shall be understood to cover round wire intendedespecially for weaving.4. Ordering Information4.1 It is the respons

8、ibility of the purchaser to specify allrequirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include, but are not limited to,the following:4.1.1 Quantity (weight),4.1.2 Name of material or UNS number,4.1.3

9、Dimensions,4.1.4 Condition (9.2),4.1.5 Finish (9.2),4.1.6 Inspection (14.1),4.1.7 CertificationState if certification or a report of testresults is required (Section 16),4.1.8 ASTM designation and year of issue, and4.1.9 If possible, the intended end use.NOTE 2A typical ordering description is as fo

10、llows: 200 lb (90.7 kg),UNS N08020, 0.020 in. (0.508 mm), annealed and pickled, ASTMSpecification B475.5. Materials and Manufacture5.1 The last heat treatment shall be a solution-annealingheat treatment.NOTE 3The recommended annealing temperatures are 1900 to 2100F(1038 to 1149C) for UNS N08020 and

11、2050 to 2200F (1121 to 1204C)for UNS N08026 and UNS N08024, all followed by quenching in wateror rapidly cooling by other means.5.2 Wire shall be annealed or cold drawn as a final operationto produce the specified mechanical properties.6. Chemical Composition6.1 The material shall conform to the req

12、uirements as tochemical composition prescribed in Table 1.6.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations prescribed in Specification B880.1This specification is under the jurisdiction of ASTM Committee B02 onNonfer

13、rous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Oct. 1, 2013. Published October 2013. Originallyapproved in 1968. Last previous edition approved in 2007 as B475 07. DOI:10.1520/B0475-07R13.2For refer

14、enced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West

15、Conshohocken, PA 19428-2959. United States17. Mechanical Properties7.1 The material shall conform to the requirements as tomechanical properties prescribed in Table 2 at room tempera-ture.8. Dimensions and Permissible Variations8.1 The diameter of the wire shall not vary from thatspecified by more t

16、han the permissible variations prescribed inTable 3.9. Workmanship, Finish, and Appearance9.1 The wire shall be uniform in diameter and free ofinjurious seams, laps, pits, die marks, or defects tending toimpair the use of the wire.9.2 The wire shall be supplied as annealed or cold-drawnhaving a fini

17、sh as pickled, bright-annealed, or cold-drawn.10. Sampling10.1 Lot:10.1.1 A lot for chemical analysis shall consist of one heat.10.1.2 A lot for mechanical properties shall consist of thesame gage of each heat in each heat treatment charge.10.2 Test Material Selection:10.2.1 Chemical AnalysisReprese

18、ntative samples shall betaken during pouring or subsequent processing.10.2.1.1 Check analysis shall be wholly the responsibility ofthe purchaser.10.2.2 Mechanical PropertiesSamples of the material toprovide test specimens shall be taken from such locations ineach lot as to be representative of that

19、lot.11. Number of Tests11.1 Chemical AnalysisOne test per lot.11.2 Mechanical PropertiesOne test per lot.12. Specimen Preparation12.1 Tension test specimens shall be taken from materialafter final heat treatment and cold drawing. The tension testspecimens shall conform to the appropriate sections of

20、 TestMethods E8.13. Test Methods13.1 The chemical composition and mechanical propertiesof the material as enumerated in this specification shall, in caseof disagreement, be determined in accordance with the follow-ing methods:Test ASTM DesignationsChemical analysis E1473ATension E8AIron shall be det

21、ermined arithmetically by difference.14. Inspection14.1 If specified, source inspection of the material by thepurchaser at the manufacturers plant shall be made as agreedupon between the purchaser and the manufacturer as part of thepurchase contract.15. Rejection and Rehearing15.1 Material that fail

22、s to conform to the requirements ofthis specification may be rejected. Rejection should be reportedto the producer or supplier promptly and in writing. In case ofTABLE 1 Chemical RequirementsElementComposition, %UNS N08026 UNS N08020 UNS N08024Carbon, max 0.03 0.07 0.03Manganese, max 1.00 2.00 1.00P

23、hosphorus, max 0.03 0.045 0.035Sulfur, max 0.03 0.035 0.035Silicon, max 0.50 1.00 0.50Nickel 33.00 to 37.20 32.00 to 38.00 35.00 to 40.00Chromium 22.00 to 26.00 19.00 to 21.00 22.50 to 25.00Molybdenum 5.00 to 6.70 2.00 to 3.00 3.50 to 5.00Copper 2.00 to 4.00 3.00 to 4.00 0.50 to 1.50Columbium (Nb)+

24、tantalum. 8 carbon-1.00 0.15 to 0.35Nitrogen 0.10 to 0.16 . .Iron remainderAremainderAremainderAABy difference.TABLE 2 Mechanical PropertiesCondition Diameter, in. (mm)Tensile Strength, psi(MPa)Annealed Over 0.006 to 0.019 115 000 (790) max(0.152 to 0.483), inclOver 0.019 to 0.049 110 000 (760) max(

25、0.483 to 1.245), inclOver 0.049 to 0.099 105 000 (720) max(1.245 to 2.515), inclOver 0.099 (2.515) 100 000 (690) maxCold-drawnAOver 0.030 to 0.125(0.762 to 3.175), incl120 000 to 150 000(830 to 1030)Over 0.125 (3.175) 110 000 to 140 000(760 to 970)AWire ordered in the cold-drawn condition can be sup

26、plied to higher tensilestrength levels as specified by the purchaser.TABLE 3 Permissible Variations in DiameterDiameter, in.Permissible Variations in Diameter, in.ACold-DrawnConditionAnnealedCondition0.312 to 0.044 incl 0.001 0.002Under 0.044 to 0.033, incl 0.0008 0.0013Under 0.033 to 0.024, incl 0.

27、0005 0.0008Under 0.024 to 0.012, incl 0.0004 .Under 0.012 to 0.008, incl 0.0003 .Under 0.008 to 0.006, incl 0.0002 .Diameter, mmPermissible Variations in Diameter, mmACold-DrawnConditionAnnealedCondition7.925 to 1.118, incl 0.0254 0.0508Under 1.118 to 0.838, incl 0.0203 0.0330Under 0.838 to 0.610, i

28、ncl 0.0127 0.0203Under 0.610 to 0.305, incl 0.0102 .Under 0.305 to 0.203, incl 0.0076 .Under 0.203 to 0.152, incl 0.0051 .AThe wire shall not be out-of-round more than one half the total permissiblevariation specified above.B475 07 (2013)2dissatisfaction with the results of the test, the producer or

29、supplier may make claim for a rehearing.16. Certification16.1 When specified in the purchase order or contract, amanufacturers certification shall be furnished to the purchaserstating that material has been manufactured, tested, and in-spected in accordance with this specification, and that the test

30、results on representative samples meet specification require-ments. When specified in the purchase order or contract, areport of the test results shall be furnished.17. Product Marking17.1 The size of the wire, ASTM specification number,grade or UNS number, heat number, and name or trademark ofthe m

31、anufacturer shall be marked on a tag securely attached toeach coil or spool.18. Packaging and Package Marking18.1 Each coil or spool shall be one continuous length ofwire, properly coiled or spooled, and firmly tied. Unlessotherwise specified, coils shall be placed in drums or shall bepaper-wrapped,

32、 and spools shall be packaged in such a manneras to assure safe delivery to their destination when properlytransported by any common carrier.19. Keywords19.1 UNS N08020; UNS N08024; UNS N08026; wireASTM International takes no position respecting the validity of any patent rights asserted in connecti

33、on with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible

34、 technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consi

35、deration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Ba

36、rr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).B475 07 (2013)3