ASTM B435-2006(2011) Standard Specification for UNS N06002 UNS N06230 UNS N12160 and UNS R30556 Plate Sheet and Strip《UNS N06002 UNS N06230 UNS N12160和UNS R30556板 薄板和带材标准规范》.pdf

《ASTM B435-2006(2011) Standard Specification for UNS N06002 UNS N06230 UNS N12160 and UNS R30556 Plate Sheet and Strip《UNS N06002 UNS N06230 UNS N12160和UNS R30556板 薄板和带材标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B435-2006(2011) Standard Specification for UNS N06002 UNS N06230 UNS N12160 and UNS R30556 Plate Sheet and Strip《UNS N06002 UNS N06230 UNS N12160和UNS R30556板 薄板和带材标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B435 06 (Reapproved 2011)Standard Specification forUNS N06002, UNS N06230, UNS N12160, and UNS R30556Plate, Sheet, and Strip1This standard is issued under the fixed designation B435; the number immediately following the designation indicates the year oforiginal adoption or, in the case

2、of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers alloys UNS N06002, UNSN06230, UNS N12160, and UNS R30556* in the fo

3、rm ofrolled plate, sheet, and strip for heat-resisting and generalcorrosive service.1.2 The following products are covered under this specifi-cation:1.2.1 Sheet and StripHot- or cold-rolled, annealed, anddescaled unless solution annealing is performed in an atmo-sphere yielding a bright finish.1.2.2

4、 PlateHot-rolled, solution-annealed, and descaled.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.4 This standard does not purport

5、to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to e

6、stablish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B906 Specification for General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and StripE527 Practice for Numbering Me

7、tals and Alloys in theUnified Numbering System (UNS)3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 plate, nmaterial316 in. (4.76 mm) and over inthickness.3.1.2 sheet and strip, nmaterial under316 in. (4.76 mm) inthickness.4. General Requirements4.1 Material furnished under th

8、is specification shall con-form to the applicable requirements of Specification B906unless otherwise provided herein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Examples of such requi

9、rements include, but arenot limited to the following:5.1.1 Alloy,5.1.2 DimensionsThickness (in decimals of an inch),width, and length (inch or fraction of an inch),5.1.3 CertificationState if certification or a report of testresults is required (Specification B906, section on Material TestReport an

10、Certification),5.1.4 Optional RequirementPlate; state how plate is to becut (Specification B906, Table titled Permissible Variations inwidth and Length of Sheared, Torch-Cut, or Abrasive-CutRectangular Plate),5.1.5 Purchase InspectionState which tests or inspectionsare to be witnessed (Specification

11、 B906, section on Inspection),and5.1.6 Samples for Product (Check) AnalysisState whethersamples should be furnished (Specification B906, section onSampling).1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of Subcommi

12、tteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved June 1, 2011. Published June 2011. Originallyapproved in 1966. Last previous edition approved in 2006 as B435 - 06. DOI:10.1520/B0435-06R11.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-ca

13、tion SB-435 in Section II of that Code.* New designation established in accordance with Practice E527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book

14、 of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Chemical Composition6.1 The material shall conform to the requirements as tochem

15、ical composition prescribed in Table 1.6.2 If a product (check) analysis is made by the purchaser,the material shall conform to the requirements specified inTable 1 and Specification B906.7. Mechanical Properties and Other Requirements7.1 Tensile PropertiesThe material shall conform to theroom tempe

16、rature tensile properties prescribed in Table 2.7.2 Grain Size for Sheet and Strip:7.2.1 Annealed alloys UNS N06002, UNS N06230, andUNS R30556 sheet and strip shall conform to the grain sizerequirements given in Table 3.7.2.2 Annealed alloy UNS N12160 shall conform to anaverage grain size of ASTM No

17、. 5 or coarser.8. Dimensions, Mass, and Permissible Variations8.1 WeightFor calculations of mass or weight, the follow-ing densities shall be used:Alloy Densitylb/in.3(g/cm3)N06002 0.297 (8.23)N06230 0.324 (8.97)R30556 0.297 (8.23)N12160 0.292 (8.08)8.2 Thickness:8.2.1 Sheet and StripThe thickness s

18、hall be measuredwith the micrometer spindle38 in. (9.525 mm) or more fromany edge for material 1 in. (25.4 mm) or over in width and atany place on material under 1 in. in width.8.3 Length:8.3.1 Sheet and StripSheet and strip may be ordered to cutlengths, in which case a variation of18 in. (3.175 mm)

19、 over thespecified length shall be permitted, with a 0 minus tolerance.8.4 Straightness:8.4.1 The edgewise curvature (depth of chord) of flat sheet,strip, and plate shall not exceed the product of 0.05 in.multiplied by the length in feet (0.04 mm multiplied by thelength in centimetres).8.4.2 Straigh

20、tness for coiled strip is subject to agreementbetween the manufacturer and the purchaser.8.5 Squareness (Sheet)For sheets of all thicknesses andwidths of 6 in. (152.4 mm) or more, the angle between adjacentsides shall be 90 6 0.15 (116 in. in 24 in. or 2.6 mm/m).8.6 FlatnessPlate, sheet, and strip s

21、hall be commerciallyflat.8.7 Edges:8.7.1 Plates shall have sheared, abrasive-cut or plasma-torch-cut edges as specified.8.7.2 Sheet and strip shall have sheared or slit edges.9. Product Marking9.1 Each plate, sheet, or strip shall be marked on one facewith the specification number, alloy, heat numbe

22、r, manufactur-ers identification, and size. The markings shall have nodeleterious effect on the material or its performance and shallbe sufficiently stable to withstand normal handling.9.2 Each bundle or shipping container shall be marked withthe name of the material; this specification number; allo

23、y; theTABLE 1 Chemical RequirementsElementComposition Limits, %UNS N06002 UNS N06230 UNS R30556 UNS N12160Nickel remainder remainder 19.022.5 remainderIron 17.020.0 3.0 max remainder 3.5 maxChromium 20.523.0 20.024.0 21.023.0 26.030.0Cobalt 0.52.5 5.0 max 16.021.0 27.033.0Molybdenum 8.010.0 1.03.00

24、2.54.0 1.0 maxTungsten 0.21.0 13.015.0 2.03.5 1.0 maxCarbon 0.050.15 0.050.15 0.050.15 0.15 maxSilicon 1.00 max 0.250.75 0.200.80 2.43.0Manganese 1.00 max 0.301.00 0.502.00 1.5 maxPhosphorus 0.04 max 0.030 max 0.04 max 0.030 maxSulfur 0.03 max 0.015 max 0.015 max 0.015 maxColumbium (N6) . . 0.30 max

25、 1.0 maxTantalum . . 0.301.25 .Aluminum . 0.50 max 0.100.50 .Zirconium . . 0.0010.10 .Lanthanum . 0.0050.050 0.0050.10 .Nitrogen . . 0.100.30 .Boron . 0.015 max 0.02 max .Titanium . . . 0.200.80TABLE 2 Mechanical Property RequirementsUNSTensile Strength,min, ksi (MPa)Yield Strength(0.2 % Offset),min

26、, ksi (MPa)Elongation in 2 in.(50.8 mm) or 4D,Amin, %N06002 95 (655) 35 (240) 35N06230B110 (760) 45 (310) 40R30556C100 (690) 45 (310) 40N12160D90 (670) 35 (240) 40AD refers to the diameter of the tension specimen.BSolution annealed at a temperature between 2200 and 2275F (1204 and1246C) followed by

27、a water quench or rapidly cooled by other means.CSolution annealed at 2100F (1150C) minimum.DSolution annealed at 1950F (1065C) minimum.TABLE 3 Grain Size for Annealed SheetThickness, in. (mm)ASTM Micrograin SizeNumber, maxAverage Grain,Diameter, max, in.(mm)0.125 (3.175) and under 3.0 0.0050 (0.127

28、)Over 0.125 (3.175) 1.5 0.0084 (0.214)B435 06 (2011)2size; gross, tare, and net weight; consignor and consigneeaddress; contract or order number; and such other informationas may be defined in the contract or order.10. Keywords10.1 plate; sheet; strip; UNS N06002; UNS N06230; UNSN12160; UNS R30556AP

29、PENDIX(Nonmandatory Information)X1. HEAT TREATMENTX1.1 Proper heat treatment during or subsequent to fabri-cation is necessary for optimum performance, and the manu-facturer shall be consulted for details.ASTM International takes no position respecting the validity of any patent rights asserted in c

30、onnection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the resp

31、onsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive carefu

32、l consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International,

33、 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).B435 06 (2011)3