ASTM B411 B411M-2008 Standard Specification for Copper-Nickel-Silicon Alloy Rod and Bar《铜镍硅合金杆材和棒材的标准规格》.pdf

《ASTM B411 B411M-2008 Standard Specification for Copper-Nickel-Silicon Alloy Rod and Bar《铜镍硅合金杆材和棒材的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B411 B411M-2008 Standard Specification for Copper-Nickel-Silicon Alloy Rod and Bar《铜镍硅合金杆材和棒材的标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 411/B 411M 08Standard Specification forCopper-Nickel-Silicon Alloy Rod and Bar1This standard is issued under the fixed designation B 411/B 411M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revisi

2、on. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification establishes the requirements

3、 forcopper-nickel-silicon alloy rod and bar produced from CopperAlloy UNS No. C64700 in straight lengths.1.2 UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standard. Thevalues stated in each system may not be exact equivalents;therefore, each system sh

4、all be used independently of the other.Combining values from the two systems may result in non-conformance with the standard.2. Referenced Documents2.1 ASTM Standards:2B 193 Test Method for Resistivity of Electrical ConductorMaterialsB 249/B 249M Specification for General Requirements forWrought Cop

5、per and Copper-Alloy Rod, Bar, Shapes andForgingsB 601 Classification for Temper Designations for Copperand Copper AlloysWrought and CastB 846 Terminology for Copper and Copper AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE8M Test Methods for Tension Testing of Metallic Mate-rials

6、Metric3E54 Test Methods for Chemical Analysis of SpecialBrasses and Bronzes3E 478 Test Methods for Chemical Analysis of CopperAlloys3. General Requirements3.1 The following sections of Specification B 249/B 249Mconstitute a part of this specification:3.1.1 Terminology,3.1.2 Workmanship, Finish, and

7、Appearance,3.1.3 Sampling,3.1.4 Number of Tests and Retests,3.1.5 Specimen Preparation,3.1.6 Test Methods,3.1.7 Significance of Numerical Limits,3.1.8 Inspection,3.1.9 Rejection and Rehearing,3.1.10 Certification,3.1.11 Mill Test Report,3.1.12 Packaging and Package Marking, and3.1.13 Supplementary R

8、equirements.3.2 In addition, when a section with a title identical to thatreferenced in 3.1 appears in this specification, it containsadditional requirements which supplement those appearing inSpecification B 249/B 249M.4. Terminology4.1 For the definition of terms related to copper and copperalloys

9、, refer to Terminology B 846.5. Ordering Information5.1 Include the following information when placing ordersfor product under this specification, as applicable:5.1.1 ASTM designation and year of issue (for example,B 411/B 411M 06),5.1.2 Copper alloy UNS No. designation,5.1.3 Temper,5.1.4 Product fo

10、rm (cross section such as round, hexagonal,square, and so forth),5.1.5 Dimensions (diameter or distance between parallelsurfaces, width, thickness),5.1.6 Edge contours,5.1.7 Length, nominal,5.1.8 Quantity; total weight, length, or number of pieces foreach form and size, and5.1.9 When product is purc

11、hased for agencies of the U.S.government.5.2 The following options are available and should bespecified at the time of placing the order, when required:5.2.1 Certification (Specification B 249/B 249M), and1This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys a

12、nd is the direct responsibility of Subcommittee B05.02 on Rod,Bar, Wire, Shapes and Forgings.Current edition approved Oct. 1, 2008. Published November 2008. Originallyapproved in 1965. Last previous edition approved in 2006 as B 411/B 411M 06.2For referenced ASTM standards, visit the ASTM website, w

13、ww.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.astm.org.1*A Summary of Changes

14、section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2.2 Mill test report (Specification B 249/B 249M).6. Material and Manufacture6.1 MaterialThe material of manufacture shall be castbillets or

15、 ingots of Copper Alloy UNS No. C64700 of suchsoundness and structure that they are suitable for processinginto the products prescribed herein.6.2 ManufactureThe product shall be manufactured byhot extrusion or rolling and finished by such cold working,annealing, cooling, straightening, and heat tre

16、atment as may benecessary to achieve the required properties.7. Chemical Composition7.1 The material shall conform to the chemical compositionrequirements specified in Table 1.7.1.1 These composition limits do not preclude the presenceof other elements. By agreement between the manufacturer andthe p

17、urchaser, limits may be established and analysis requiredfor the unnamed elements.7.2 Copper, given as the remainder, is the difference be-tween the sum of results of all elements determined and 100 %.7.3 When all elements specified in Table 1 are determined,the sum of results shall be 99.5 % minimu

18、m.8. Temper8.1 The standard temper for product described in thisspecification is given in Table 2.8.2 Tempers are as defined in Classification B 601.8.3 Other tempers available when specified are:8.3.1 TB00 (solution heat-treated).8.3.2 TD00 (solution heat-treated and cold-worked18 hard).8.3.3 TD01

19、(solution heat-treated and cold-worked14 hard).8.3.4 TD02 (solution heat-treated and cold-worked12 hard).8.3.5 TD03 (solution heat-treated and cold-worked34 hard).8.3.6 TD04 (solution heat-treated and cold-worked hard).9. Physical Property Requirements9.1 Electrical Resistivity RequirementThe precip

20、itationheat-treated product furnished shall conform to the electricalmass resistivity of 0.348 36 to 0.589 54 Vg/m2or conductivityof 44.0 to 26.0 % IACS at 68F (20C) when tested inaccordance with Test Method B 193.10. Mechanical Property Requirements10.1 Tensile Strength Requirements:10.1.1 Product

21、furnished in the precipitation-hardened TF00temper, as normally supplied, shall conform to the tensilerequirements prescribed in Table 2, when tested in accordancewith Test Methods E8or E8M.10.1.2 Product furnished in TB00 (solution heat-treated)temper or TD00 through TD02 (solution heat-treated and

22、cold-worked) inclusive, shall be capable of meeting the re-quirements specified in Table 2 for each size and form afterbeing given a suitable precipitation heat treatment and whentested in accordance with Test Methods E8or E8M.NOTE 1The purchaser should consult with the manufacturer forrecommended p

23、recipitation heat treatment procedures.10.1.3 The tensile requirements for as supplied rod and barin sizes and tempers other than the standard, shall be as agreedbetween the supplier or manufacturer and the purchaser.11. Performance Requirements11.1 Heat TreatmentFor purchasers product acceptanceonl

24、y, the information shown in Table 3 shall be consideredsuitable for precipitation heat treatment.12. Other Requirements12.1 Purchases for the U.S. GovernmentProduct pur-chased for agencies of the U.S. government shall conform tothe additional requirements prescribed in the SupplementaryRequirements

25、section of Specification B 249/B 249M.13. Dimensions and Permissible Variations13.1 The dimensions and tolerances for product describedby this specification shall be as specified in SpecificationB 249/B 249M with particular reference to the following tablesand related paragraphs:13.1.1 Diameter or D

26、istance Between Parallel Surfaces:13.1.1.1 Rod: Round, Hexagonal, OctagonalRefer toTable 2, Tolerances for Diameter of Cold-Drawn Rod.13.1.1.2 Bar: Rectangular and SquareRefer to Table 9,Thickness Tolerances for Rectangular and Square Bar forthickness and Table 11, Width Tolerances for Rectangular B

27、arfor width.13.1.2 LengthRefer to Table 13, Length Tolerances forRod, Bar, and Shapes for length tolerance and Table 15,Schedule of Lengths for schedule of lengths with ends.13.1.3 StraightnessRefer to Table 16, Straightness Toler-ances for Rod, Bar, and Shapes.13.1.4 Edge ContoursRefer to the secti

28、on entitled, “EdgeContours” and Fig. 1, Fig. 2, and Fig. 3.14. Test Methods14.1 Chemical Analysis:14.1.1 In cases of disagreement, determine the composition,using the following methods:Element ASTM Test MethodCopper E 478Iron E 478Lead E 478 (AA)Nickel E 478 (photometric)Silicon E54(perchloric acid)

29、Zinc E 478 (AA)TABLE 1 Chemical RequirementsElement Composition, %Nickel, incl cobalt 1.62.2Silicon 0.400.8Lead, max 0.09Iron, max 0.10Zinc, max 0.50Copper, incl silver remainderB 411/B 411M 08215. Keywords15.1 copper-nickel-silicon alloy bar; copper-nickel-siliconalloy rod; UNS C64700 bar; UNS C647

30、00 rodSUMMARY OF CHANGESCommittee B05 has identified the location of selected changes to this standard since the last issue(B 411/B 411M 06) that may impact the use of this standard. (Approved Oct. 1, 2008.)(1) Table 1, Chemical Requirements, change the C64700 leadentry from .10 % max to .09 % max.A

31、STM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are

32、entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standard

33、sand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committe

34、e on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress o

35、r at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).TABLE 2 Required Mechanical Properties for Material in the TF00 (Precipitation-Hardened (AT) ConditionFormDiameter or Distance Between Parallel Surfaces,ATensile Strength,minYield St

36、rength at0.5 % ExtensionUnder Load, minElongation,Bin4D,min,%in. mm ksi MPa ksi MPaRod:Round332 to 112 , inclOver 112 to 2, incl2.4 to 38, inclOver 38 to 50, incl9080620550757051548588Hexagonal andOctagonal18 to 112 , inclOver 112 to 2, incl3 to 38, inclOver 38 to 50, incl9080620550757051548588Bar:S

37、quare Over 0.188 to 1, incl 5 to 25, incl 90 620 75 515 8Over 1 to 112 , incl Over 25 to 38, incl 80 550 70 485 8Rectangular Over 0.188 to 112 thick andup to 212 wide, inclOver 5 to 38 thick andup to 65 wide, incl80 550 70 485 8AFor rectangular bar the thickness dimension applies.BElongation in 43 d

38、iameter or thickness, but in any case, a minimum gage length of 1 in. (25 mm) shall be used.TABLE 3 Precipitation-Hardening Heat TreatmentFormsDiameter or DistanceBetween ParallelSurfaces,ATemperatureTime atTemperature,minin. mm F CUnder 0.050 Under 1.3 800 427 90All 0.050 to 1.000, incl 1.3 to 25, incl 850 454 90Over 1.000 Over 25 850 454 120AFor rectangular bar, the thickness dimension applies.B 411/B 411M 083