《ASTM B361-2008 Standard Specification for Factory-Made Wrought Aluminum and Aluminum-Alloy Welding Fittings《工厂加工的锻制铝及铝合金焊接件的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B361-2008 Standard Specification for Factory-Made Wrought Aluminum and Aluminum-Alloy Welding Fittings《工厂加工的锻制铝及铝合金焊接件的标准规范》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 361 08Standard Specification forFactory-Made Wrought Aluminum and Aluminum-AlloyWelding Fittings1This standard is issued under the fixed designation B 361; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of

2、last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers only factory-made wroughtaluminum and aluminum-alloy welding fittings in contrast tofield-m

3、ade fittings. The term “welding fittings” applies tobutt-welding or socket-end parts, such as 45 elbows, 180return bends, 90 short radius elbows, and other types made tothe dimensional standards specified by ASME B16.9 andB16.11.NOTE 1Throughout this specification use of the term alloy in thegeneral

4、 sense includes aluminum as well as aluminum-alloy.1.2 For acceptance criteria for inclusion of new aluminumand aluminum alloys in this specification, see Annex A1.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to

5、SI units that are provided for information onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and heal practices and determ

6、ine the applicabilityof regulatory limitations prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on dateof material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:2B 209 Specification for Aluminum and Aluminum-AlloySh

7、eet and PlateB 210 Specification for Aluminum and Aluminum-AlloyDrawn Seamless TubesB211 Specification for Aluminum and Aluminum-AlloyBar, Rod, and WireB 221 Specification for Aluminum and Aluminum-AlloyExtruded Bars, Rods, Wire, Profiles, and TubesB 234 Specification for Aluminum and Aluminum-Alloy

8、Drawn Seamless Tubes for Condensers and Heat Exchang-ersB 241/B 241M Specification forAluminum andAluminum-Alloy Seamless Pipe and Seamless Extruded TubeB 247 Specification for Aluminum and Aluminum-AlloyDie Forgings, Hand Forgings, and Rolled Ring ForgingsB 660 Practices for Packaging/Packing of Al

9、uminum andMagnesium ProductsB 881 Terminology Relating to Aluminum- andMagnesium-Alloy ProductsD 3951 Practice for Commercial Packaging2.3 ANSI Standards:H35.1/H35.1(M) Alloy and Temper Designation Systemsfor Aluminum32.4 ASME Standards:B16.9 Factory-Made Wrought Butt-Welding Fittings4B16.11 Forged

10、Fittings, Socket-Welding and Threaded4Section VIII Boiler and Pressure Vessel Code4Section IX Boiler and Pressure Vessel Code42.5 AWS Standards:AWS D10.7M/D10.7 Recommended Practices for GasShielded-Arc Welding ofAluminum andAluminum-AlloyPipe52.6 Manufacturers Standardization Society of the Valvean

11、d Fittings Industry:MSS SP 25 Standard Marking System for Valves, Fittings,Flanges and Unions61This specification is under the jurisdiction of ASTM Committee B07 on LightMetals and Alloys and is the direct responsibility of Subcommittee B07.03 onAluminum Alloy Wrought Products.Current edition approv

12、ed Nov. 1, 2008. Published December 2008. Originallyapproved in 1960. Last previous edition approved in 2002 as B 361 02.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refe

13、r to the standards Document Summary page onthe ASTM website.3Available from Aluminum Association, Inc., 1525 Wilson Blvd., Suite 600,Arlington, VA 22209, http:/www.aluminum.org.4Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York,

14、 NY 10016-5990, http:/www.asme.org.5Available from American Welding Society (AWS), 550 NW LeJeune Rd.,Miami, FL 33126, http:/www.aws.org.6Available from Manufacturers Standardization Society of the Valve and FittingsIndustry (MSS), 127 Park St., NE, Vienna, VA 22180-4602, http:/www.mss-1*A Summary o

15、f Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.2.7 Federal Standards:Fed. Std. No. 123 Marking for Shipment (Civil Agencies)72.8 American Society for Nondestructive Testing Standa

16、rd:ASNT Recommended Practice No. SNT-TC-1A PersonnelQualification and Certification in Nondestructive Test-ing83. Terminology3.1 Definitions: Refer to ASTM Terminology B 881 fordefinitions of product terms used in this specification.3.2 Definitions of Terms Specific to This Standard:3.2.1 capable of

17、The term capable of as used in thisspecification means that the test need not be performed by theproducer of the material. However, should testing by thepurchaser establish that the material does not meet theserequirements, the material shall be subject to rejection.4. Ordering Information4.1 Orders

18、 for material to this specification shall include thefollowing information:4.1.1 This specification designation (which includes thenumber, the year, and the revision letter, if applicable),4.1.2 Size, shape, and dimensions (8.1),4.1.3 Quantity in number of pieces,4.1.4 Alloy (Section 5),4.1.5 Temper

19、 (Section 5),4.1.6 Class WP*S and WP*W (seamless or welded)shall be specified.4.2 Additionally, orders for material to this specificationshall include the following information when required by thepurchaser:4.2.1 Whether tension tests of finished fittings are required(9.1),4.2.2 Whether hydrostatic

20、tests are required (10.2),4.2.3 Whether inspection or witness of inspection and testsby the purchasers representative is required prior to materialshipment (Section 11),4.2.4 Whether Practices B 660 applies and, if so, the levelsof preservation, packaging, and packing required (14.3), and4.2.5 Wheth

21、er certification is required (Section 15).4.2.6 For civil agencies, whether marking for shipment shallbe in accordance with Fed. Std. No. 123 or ASTM PracticeD 3951.5. Material5.1 The aluminum or aluminum-alloy material used in themanufacture of the fittings shall be in accordance with the alloyand

22、temper specified in the order. The material shall be in theform of rod, bar, forgings, sheet, plate, seamless pipe orseamless tube, each of which conforms to all requirements ofthe applicable ASTM specifications for the particular form andalloy involved. The applicable ASTM specifications and alloyd

23、esignations are listed in Table 1.6. Manufacture6.1 Forging or shaping operations may be performed byhammering, pressing, piercing, rolling, extruding, upsetting,bending, fusion welding, machining, or by a combination oftwo or more of these operations. The forming procedure shallbe so applied that i

24、t will not produce injurious defects in thefittings.6.2 Fittings ordered as Class WP*S shall be of seamlessconstruction and meet all requirements of ASME B16.9.6.3 Fittings ordered as Class WP*W shall meet therequirements of ASME B16.9 and shall have full penetrationfusion welds radiographically exa

25、mined throughout their entirelength in accordance with Paragraph UW-51 of Section VIII,Division 1, of the ASME Boiler and Pressure Vessel Code. Theradiography of this class of fittings may be done either prior toor after forming at the option of the manufacturer.6.3.1 All welds shall be made in acco

26、rdance with proce-dures by welders or welding operators qualified under therequirements of the ASME Boiler and Pressure Vessel Code,Section IX.6.3.2 Personnel performing NDE examinations shall bequalified in accordance with SNT-TC-1A.6.4 For welds made in accordance with the ASME Boilerand Pressure

27、Vessel Code, Section IX, the joint shall bereinforced at the center of the weld by at least116 in. (1.6 mm)but not more than18 in. (3.2 mm). Unless otherwise agreedupon between the producer and the purchaser, this reinforce-ment may be removed at the producers option. The contour ofthe reinforcement

28、 shall be smooth, with no valley or groovealong the edge or in the center of the weld, and the depositedmetal shall be fused smoothly and uniformly into the surface ofthe original material. The finish of the welded joint shall bereasonably smooth and free of irregularities, grooves, ordepressions.7.

29、 Responsibility for Quality Assurance7.1 Responsibility for Inspection and TestsUnless other-wise specified in the contract or purchase order, the producer isresponsible for the performance of all inspection and testrequirements specified herein. Except as otherwise specified inthe contract or order

30、, the producer may use his own or anyother suitable facilities for the performance of the inspectionand test requirements specified herein, unless disapproved bythe purchaser. The purchaser shall have the right to performany of the inspections and tests set forth in this specificationwhere such insp

31、ections are deemed necessary to assure thatmaterial conforms to prescribed requirements.7.2 Lot DefinitionAn inspection lot shall consist of allfittings of the same alloy, size, shape, and dimensions subjectedto inspection at one time.8. General Quality8.1 The sizes, shapes, and dimensions, and, unl

32、ess other-wise specified, the end preparation (Note 2), shall be asspecified for fittings covered by ASME B16.9 and B16.11.NOTE 2Other types of end preparations have been developed such asthe “V” groove of ASME B16.9 and B16.11, which appear to be superiorto the straight bevel under many circumstanc

33、es. They may be specified7Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.8Available fromAmerican Society for Nondestructive Testing (ASNT), P.O. Box28518, 1711 Arlingate Ln., Columbus, OH 43228-

34、0518, http:/www.asnt.org.B361082when desired. The so-called “modified vee” end preparation described inAWS D10.7 is one example.8.2 Unless otherwise specified, the material shall be sup-plied in the mill finish and shall be uniform as defined by therequirements of this specification and shall be com

35、merciallysound. Any requirement not so covered is subject to negotia-tion between producer and purchaser.9. Tension Tests9.1 Tension tests of the finished fittings are not required,unless otherwise agreed upon between the producer and thepurchaser and so specified in the order. When tension tests ar

36、emade, methods of test, test specimens, and sampling frequencyshall be agreed upon between the producer and the purchaser.10. Hydrostatic Tests10.1 Welding fittings shall be capable of withstanding aninternal hydrostatic pressure, calculated according to the fol-lowing equation, without developing l

37、eaks:P 5 2St/D (1)where:P = maximum hydrostatic test pressure (gage), psi (MPa)(Note 3),S = 0.50 times the minimum specified yield strength of thedesignated material, psi (MPa),t = nominal wall thickness, in. (mm) of designated sched-ule number (Note 4), andD = outside diameter at bevel, in. (mm).10

38、.2 Hydrostatic acceptance tests shall be made only whenagreed upon between the producer and the purchaser and sospecified in the order.NOTE 3See Appendix X1.NOTE 4For nominal wall thicknesses corresponding to schedulenumbers, see Specification B 241/B 241M.11. Source Inspection11.1 If the purchaser

39、desires that his representative inspector witness the inspection and testing of the material prior toshipment, such agreement shall be made by the purchaser andproducer as part of the purchase contract.TABLE 1 Requirements for Aluminum and Aluminum-Alloy Materials Used in the Manufacture of Fittings

40、Applicable ASTM SpecificationsAlloy DesignationA,BType of MaterialPipe or Tube Plate Bar ForgingWP1060C99.6 % pure aluminum B 210B 221B 234B 241/B 241M B 209B211B 221 .WP1100Ccommercially pure low-strength aluminum B 210B 221B 241/B 241M B 209B211B 221 B 247WP3003Caluminum-base manganese alloy B 210

41、B 221B 234B 241/B 241M B 209B211B 221 B 247WP AlcladC3003 aluminum-base manganese alloy core, clad on oneside (inside only) in case of pipeB 210B 221B 234B 241/B 241M B 209WP5083Daluminum-base magnesium-manganese alloy B 210B 221B 241/B 241M B 209 B 221 B 247WP5086Daluminum-base magnesium-manganese

42、alloy B 210B 221B 241/B 241M B 209 B 221WP5154Caluminum-base magnesium alloy B 210B 221 B 209B211B 221WP6061 aluminum-base magnesium-silicon heat-treatable alloy B 210B 221B 234B 241/B 241M B 209B211B 221 B 247WP6063 aluminum-base magnesium-silicon heat-treatable alloy B 210B 221B 241/B 241M . B 221

43、 .AWhen fittings are of welded construction, designation shall be supplemented by the suffix “W.BThese alloy designations were established in accordance with ANS1 H35.1/H35.1(M), except for the letter symbols “WP, which denote wrought product.CFittings in nonheat-treatable alloys 1060, 1100, 3003, A

44、lclad 3003, and 5154 are available only in the F or H112 tempers as covered by the applicable raw materialspecification.DFittings in nonheat-treatable alloys 5083 and 5086 are available in the O, F, or H112 tempers as covered by the applicable raw material specification.B36108311.2 When such inspect

45、ion or witness of inspection andtesting is agreed upon, the seller shall afford the purchasersrepresentative all reasonable facilities to satisfy him that thematerial meets the requirements of this specification. Inspec-tion and tests shall be conducted so there is no unnecessaryinterference with th

46、e producers operations.12. Retest and Rejection12.1 If any material fails to conform to all of the applicablerequirements of this specification, it shall be cause for rejectionof the inspection lot.12.2 When there is evidence that a failed specimen was notrepresentative of the inspection lot and whe

47、n no other samplingplan is provided or approved by the purchaser through thecontract or purchase order, at least two additional specimensshall be selected to replace each test specimen that failed. Allspecimens so selected for retest shall meet the requirements ofthe specification or the lot shall b

48、e subject to rejection.12.3 Material in which defects are discovered subsequent toinspection may be rejected.12.4 If material is rejected by the purchaser, the producer orsupplier is responsible only for replacement of material to thepurchaser.As much as possible of the rejected material shall beret

49、urned to the producer or supplier.13. Identification Marking of Product13.1 The producers name or trademark, the size andschedule number, and the material shall be stamped (Note 5),stenciled, or otherwise suitably marked on each fitting. Whenthe size does not permit complete marking, identificationmarks may be omitted in the sequence specified in SP25, of theManufacturers Standardization Society of the Valve and Fit-tings Industry. Each fitting shall be marked with the alloydesignation listed in Table 1. On wall thicknesses thinner thanSche