ASTM B352 B352M-2017 Standard Specification for Zirconium and Zirconium Alloy Sheet Strip and Plate for Nuclear Application《核应用锆和锆合金薄板材 带材和厚板材的标准规格》.pdf
《ASTM B352 B352M-2017 Standard Specification for Zirconium and Zirconium Alloy Sheet Strip and Plate for Nuclear Application《核应用锆和锆合金薄板材 带材和厚板材的标准规格》.pdf》由会员分享,可在线阅读,更多相关《ASTM B352 B352M-2017 Standard Specification for Zirconium and Zirconium Alloy Sheet Strip and Plate for Nuclear Application《核应用锆和锆合金薄板材 带材和厚板材的标准规格》.pdf(8页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B352/B352M 11 (Reapproved 2016)B352/B352M 17Standard Specification forZirconium and Zirconium Alloy Sheet, Strip, and Plate forNuclear Application1This standard is issued under the fixed designation B352/B352M; the number immediately following the designation indicates the yearof origin
2、al adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers hot- and cold-rolled zirconium and zirc
3、onium alloy sheet, strip, and plate.1.2 One unalloyed and three alloys for use in nuclear applications are described.1.3 The products covered in this specification include the following forms and sizes:1.3.1 Sheet, 24 in. 600 mm or more in width; under 0.187 in. 4.8 mm) in thickness,1.3.2 Strip, les
4、s than 24 in. 600 mm in width; under 0.187 in. 4.8 mm in thickness, and1.3.3 Plate, over 10 in. 250 mm in width; 0.187 in. 4.8 mm and over in thickness.NOTE 1Material over 0.187 in. 4.8 mm in thickness and less than 10 in. 250 mm wide is covered as bar in Specification B351/B351M.1.4 Unless a single
5、 unit is used, for example corrosion mass gain in mg/dm2, the values stated in either inch-pound or SI unitsare to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore each system mustbe used independently of the other. SI values cannot be mixed w
6、ith inch-pound values.1.5 The following precautionary caveat pertains only to the test method portions of this specification. This standard does notpurport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard toestablish approp
7、riate safety and health practices and determine the applicability of regulatory limitations prior to use.1.6 This international standard was developed in accordance with internationally recognized principles on standardizationestablished in the Decision on Principles for the Development of Internati
8、onal Standards, Guides and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2B350/B350M Specification for Zirconium and Zirconium Alloy Ingots for Nuclear ApplicationB351/B351M Specification for Hot-Rolled and
9、 Cold-Finished Zirconium and ZirconiumAlloy Bars, Rod, and Wire for NuclearApplicationE8/E8M Test Methods for Tension Testing of Metallic MaterialsE21 Test Methods for Elevated Temperature Tension Tests of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data to Determine Conforma
10、nce with SpecificationsE114 Practice for Ultrasonic Pulse-Echo Straight-Beam Contact TestingE1001 Practice for Detection and Evaluation of Discontinuities by the Immersed Pulse-Echo Ultrasonic Method UsingLongitudinal WavesG2/G2M Test Method for Corrosion Testing of Products of Zirconium, Hafnium, a
11、nd Their Alloys in Water at 680F (360C)or in Steam at 750F (400C)3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 annealed, ndenotes material that exhibits a recrystallized grain structure.1 This specification is under the jurisdiction of ASTM B10 on Reactive and Refractory Met
12、als and Alloys and is the direct responsibility of B10.02 on Zirconium andHafnium.Current edition approved Oct. 1, 2016May 1, 2017. Published October 2016May 2017. Originally approved in 1960. Last previous edition approved in 20112016 asB352/B352M 11.B352/B352M 11 (2016). DOI: 10.1520/B0352_B0352M-
13、11R16.10.1520/B0352_B0352M-17.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM st
14、andard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all ca
15、ses only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.2 Lot Definition:3.2.1 Sheet, strip, and plate products (single definition, c
16、ommon to nuclear and non-nuclear standards), na lot shall consistof a material of the same size, shape, condition, and finish produced from the same ingot or powder blend by the same reductionschedule and the same heat treatment parameters. Unless otherwise agreed between manufacturer and purchaser,
17、 a lot shall belimited to the product of an 8 h period for final continuous anneal, or to a single furnace load for final batch anneal.4. Ordering Information4.1 Purchase orders for material under this specification should include the following information as required to adequatelydescribe the desir
18、ed material:4.1.1 Quantity (weight or number of pieces),4.1.2 Name of material,4.1.3 Condition (Section 6),4.1.4 Finish (Section 14),4.1.5 Form (Sheet, strip, plate),4.1.6 Edge (Section 15),4.1.7 Dimensions (size, thickness, width and length),4.1.8 Grade designation (Table 1), and4.1.9 ASTM designat
19、ion and year of issue.4.1.10 Transverse test requirements, if any (Section 8),4.1.11 Ultrasonic test requirements (Section 12),4.1.12 Standards of acceptability for cracks, seams, slivers, blisters, and other imperfections (Section 13), and4.1.13 Special packaging and shipping requirements (Section
20、21).NOTE 2A typical ordering description is as follows: _ 5000 lb reactor grade zirconium alloy, cold-rolled, vacuum annealed strip, 4.750 by 0.065 by72 in., ASTM Specification B352/B352M - 11, Grade R60804.4.2 In addition to the data specified in 4.1, the following options and points of agreement b
21、etween the manufacturer and thepurchaser should be specified on the purchase order as required:4.2.1 Temperature and direction of mechanical testing (see Section 8 and Table 2),TABLE 1 Chemical RequirementsElement Composition, Weight %UNS R60001 UNS R60802 UNS R60804 UNS R60901Tin . . . 1.201.70 1.2
22、01.70 . . .Iron . . . 0.070.20 0.180.24 . . .Chromium . . . 0.050.15 0.070.13 . . .Nickel . . . 0.030.08 . . . . . .Niobium (columbium) . . . . . . . . . 2.402.80Oxygen A A A 0.090.15Iron + chromium + nickel . . . 0.180.38 . . . . . .Iron + chromium . . . . . . 0.280.37 . . .Maximum Impurities, Weig
23、ht %Aluminum 0.0075 0.0075 0.0075 0.0075Boron 0.00005 0.00005 0.00005 0.00005Cadmium 0.00005 0.00005 0.00005 0.00005Calcium . 0.0030 0.0030 .Carbon 0.027 0.027 0.027 0.027Chromium 0.020 . . . . . . 0.020Cobalt 0.0020 0.0020 0.0020 0.0020Copper 0.0050 0.0050 0.0050 0.0050Hafnium 0.010 0.010 0.010 0.0
24、10Hydrogen 0.0025 0.0025 0.0025 0.0025Iron 0.150 . . . . . . 0.150Magnesium 0.0020 0.0020 0.0020 0.0020Manganese 0.0050 0.0050 0.0050 0.0050Molybdenum 0.0050 0.0050 0.0050 0.0050Nickel 0.0070 . . . 0.0070 0.0070Niobium . 0.0100 0.0100 .Nitrogen 0.0080 0.0080 0.0080 0.0080Phosphorus . . . . . . . . .
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB352B352M2017STANDARDSPECIFICATIONFORZIRCONIUMANDZIRCONIUMALLOYSHEETSTRIPANDPLATEFORNUCLEARAPPLICATION

链接地址:http://www.mydoc123.com/p-461011.html