ASTM B240-2007 Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloys in Ingot Form for Foundry and Die Castings《铸造和压模铸件用铸锭结构中锌和锌铝(ZA)合金的标准规范》.pdf

《ASTM B240-2007 Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloys in Ingot Form for Foundry and Die Castings《铸造和压模铸件用铸锭结构中锌和锌铝(ZA)合金的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B240-2007 Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloys in Ingot Form for Foundry and Die Castings《铸造和压模铸件用铸锭结构中锌和锌铝(ZA)合金的标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 240 07Standard Specification forZinc and Zinc-Aluminum (ZA) Alloys in Ingot Form forFoundry and Die Castings1This standard is issued under the fixed designation B 240; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision,

2、the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers commercial zinc and zinc-aluminum (ZA) alloys in ingot form for remelting for

3、themanufacture of pressure die castings, foundry castings andcontinuous cast bar stock as designated and specified in Table1. Seven alloy compositions are specified, designated asfollows:Common Traditional ASTMAUNSAAlloy 3 Zamak 3 AG 40A Z33521Alloy 7 Zamak 7 AG 40B Z33522Alloy 5 Zamak 5 AC 41A Z355

4、30Alloy 2 Zamak 2 AC 43A Z35540ZA-8 ZA-8 . Z35635ZA-12 ZA-12 . Z35630ZA-27 ZA-27 . Z35840_ASee Table 1, footnote B.1.2 Zinc alloys Z33521, Z33522, Z35530, and Z35540 areused primarily for remelting in the manufacture of pressure diecastings. Zinc-aluminum alloys Z35635, Z35630, and Z35840are used fo

5、r remelting in the manufacture of both foundry andpressure die castings. Castings made from these ingots arespecified in Specification B86, Standard Specification for Zincand Zinc-Aluminum Alloys for Foundry and Die Castings.1.3 The values stated in inch-pound units are to be regardedas standard.1.4

6、 Systems of nomenclature used to designate zinc andzinc-aluminum (ZA) alloys used for casting are described inAppendix X1.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarw

7、ith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2

8、.1 The following documents of the issue in effect on dataof order acceptance form a part of this specification to theextent referenced herein:2.2 ASTM Standards:2B86 Specification for Zinc and Zinc-Aluminum (ZA)AlloyFoundry and Die CastingsB 275 Practice for Codification of Certain Nonferrous Met-al

9、s and Alloys, Cast and WroughtB 897 Specification for the Configuration of Zinc and ZincAlloy Jumbo and Block IngotB 899 Terminology Relating to Non-ferrous Metals andAlloysB 908 Practice for the Use of Color Codes for Zinc CastingAlloy IngotE29 Practice for Using Significant Digits in Test Data toD

10、etermine Conformance with SpecificationsE47 Test Methods for Chemical Analysis of Zinc Die-Casting Alloys3E88 Practice for Sampling Nonferrous Metals and Alloysin Cast Form for Determination of Chemical CompositionE 527 Practice for Numbering Metals and Alloys (UNS)E 536 Test Methods for ChemicalAna

11、lysis of Zinc and ZincAlloysE 634 Practice for Sampling of Zinc and Zinc Alloys forOptical Emission Spectrometric Analysis2.3 Other ASTM Document:Methods for Emission Spectrochemical Analysis42.4 ISO Standard5ISO 301 Zinc Alloy Ingots Intended for CastingISO 38151 Zinc and zinc alloys Part 1:Analysi

12、s of solidsamples by optical emission spectrometry.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.04 on Zinc and Cadmium.Current edition approved July 1, 2007. Published August 2007. Originallyapp

13、roved in 1949. Last previous edition approved in 2006 as B 240 - 06.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM w

14、ebsite.3Withdrawn.4Methods for Emission Spectrochemical Analysis: General Practices, Nomen-clature, Standard Methods, Proposed Methods, Suggested Methods, ASTM Inter-national, 1982.5Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.a

15、nsi.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.ISO 38152 Zinc and zinc alloys Part 2: Analysis byinductively coupled plasma optical emission spectrometry.3. T

16、erminology3.1 Terms shall be defined in accordance with TerminologyB 899.3.2 Definitions of Terms Specific to This Standard:3.2.1 continuous casting, na casting technique in which acast is continuously withdrawn through the bottom of the moldas it solidifies, so that its length is not determined by

17、molddimensions; used chiefly to produce semifinished mill productssuch as billets, blooms, ingots, slabs and tubes; also known asconcast.3.2.2 die casting, na casting process in which moltenmetal is injected under high velocity and pressure into a metaldie and solidified, also a product produced by

18、such a process.Alternately known as pressure die casting.4. Ordering Information4.1 Orders for ingot under this specification shall includethe following information:4.1.1 Quantity in pounds,4.1.2 Alloy (Table 1),4.1.3 Size, if not manufacturers standard (see Section 7),4.1.4 Specification number and

19、 date,4.1.5 Source inspection (Section 10),4.1.6 Marking (Section 12), and4.1.7 Whether certification is required (Section 13).5. Materials and Manufacturer5.1 The material covered by this specification shall be ofuniform quality and reasonably free from dross, adheringforeign matter, and surface ox

20、ide.6. Chemical Requirements6.1 The ingots shall conform to the requirements as tochemical composition prescribed in Table 1. Conformanceshall be determined by the manufacturer by analyzing samplestaken at the time the ingots are poured or samples taken fromthe ingots. Unless otherwise agreed in the

21、 contact or purchaseorder, sampling procedure will be the manufacturers choice.7. Ingot Sizes and Shapes7.1 Zinc casting alloy ingots are typically supplied in ingotbundles weighing 1700 to 2400 lb.7.2 Ingots and bundles vary in size and weight depending onthe alloy and supplier.7.2.1 Standard ingot

22、s have a nominal weight in the range of17 to 24 lb. and are generally 24 to 26 in. long.7.2.2 Margash bars or ingots come in two sizes with anominal weight in the range of either 12 to 14 lb. or 20 to 24lb.7.3 Zinc casting alloy ingot may be ordered in jumbos orblocks, as specified in Specification

23、B 897.7.4 Zinc casting alloy ingot may also be ordered in othershapes.8. Sampling for Determination of Chemical Composition8.1 In the event of a dispute, if the ingots are shipped incarload lots of the same alloy, not less than five ingots shall betaken at random from the carload for sampling. If th

24、e shipmentis less than a carload lot, one sample ingot shall be taken foreach 10,000 lb. (4500 kg) or fraction thereof. Either party mayrequest that a sample be taken from each melt of 1000 lb. (450kg) or more.8.2 The samples for chemical analysis shall be taken bysawing, milling, or drilling in suc

25、h a manner as to beTABLE 1 Chemical and North American Color Code RequirementsAlloy 3A,B,C,DAlloy 7A,B,C,DAlloy 5A,B,C,DAlloy 2A,B,C,DZA-8B,C,EZA-12B,C,EZA-27B,C,EZamak 3 Zamak 7 Zamak 5 Zamak 2 ZA-8 ZA-12 ZA-27(AG40A) (AG40B) (AC41A) (AC43A)Z33521 Z33522 Z35530 Z35540 Z35635 Z35630 Z35840Color Code

26、FNone Brown Black Green Blue Orange PurpleElementAluminum 3.9-4.3 3.9-4.3 3.9-4.3 3.9-4.3 8.2-8.8 10.8-11.5 25.5-28.0Magnesium 0.03-0.06 0.010-0.020 0.03-0.06 0.025-0.05 0.02-0.03 0.02-0.03 0.012-0.020Copper 0.10 max 0.10 max 0.7-1.1 2.7-3.3 0.9-1.3 0.5-1.2 2.0-2.5Iron, Max 0.035 0.075 0.035 0.035 0

27、.035 0.05 0.07Lead, Max 0.0040 0.0030 0.0040 0.0040 0.005 0.005 0.005Cadmium, Max 0.0030 0.0020 0.0030 0.0030 0.005 0.005 0.005Tin, Max 0.0015 0.0010 0.0015 0.0015 0.002 0.002 0.002Nickel - - - 0.005-0.020 - - - - - - - - - - - - - - -ZincGRemainder Remainder Remainder Remainder Remainder Remainder

28、RemainderAZinc alloy ingot for die casting may contain nickel, chromium, silicon, and manganese in amounts of up to 0.02, 0.02, 0.035 and 0.05 %, respectively. No harmful effectshave ever been noted due to the presence of these elements in up to these concentrations and, therefore, analyses are not

29、required for these elements, except that nickelanalysis is required for Z33522.BASTM alloy designations were established in accordance with Practice B 275. UNS assignations were established in accordance with Practice E 527. The last digitof a UNS number differentiates between alloys of similar comp

30、osition. UNS designations for ingot and casting versions of an alloy were not assigned in the same sequencefor all alloys.CFor purposes of acceptance and rejection, the observed value or calculated value obtained from analysis should be rounded to the nearest unit in the last right-handplace of figu

31、res, used in expressing the specified limit, in accordance with the rounding procedure prescribed in Practice E 29.DWhen this material is required to conform to ISO Standard 301, the chemical limits for thallium and indium each shall not exceed 0.001 %.EZinc-aluminum ingot for foundry and pressure d

32、ie casting may contain nickel, chromium, and manganese in amounts of up to 0.01 % each or 0.03 % total. No harmfuleffects have ever been noted due to the presence of these elements in up to these concentrations and, therefore, analyses are not required for these elements.FRefer to Practice B 908. (N

33、ote: Colors indicated are for North American applications.)GDetermined arithmetically by difference.B240072representative of the average cross section of the ingot. Theweight of a prepared sample shall be not less than 75 g inaccordance with Practice E 88.8.3 The saw drill, or cutter used for taking

34、 the sample shallbe thoroughly cleaned. No lubricant shall be used in theoperation, and the sawings or metal chips shall be carefullytreated with a magnet to remove any particles or iron intro-duced in taking the sample by the method prescribed in 8.2.8.4 An optional method of sampling for analysis

35、may be bymelting together representative portions of each ingot selectedand then sampling the liquid composite by casting suitablespecimens for either spectrographic or chemical analysis.8.5 Samples for Spectrochemical and Other Methods ofAnalysis4Samples for spectrochemical and other methods ofanal

36、ysis shall be suitable for the form of material beinganalyzed and the type of analytical method used (for example,see Practice E 634).9. Methods for Chemical Analysis9.1 The determination of chemical composition shall bemade in accordance with suitable analytical methods. In caseof dispute, the resu

37、lts secured by an approved method (orcombination of approved methods), or by a method agreedupon by both parties, shall be the basis of acceptance.9.1.1 Approved method include: Test Methods E 536, TestMethod E47(for tin), ISO 38151,orISO 38152.9.2 For purposes of determining compliance with specifi

38、edcomposition limits as given in Table 1, an observed orcalculated value shall be rounded to the nearest unit in the lastright-hand place of figures shown in Table 1, in accordancewith the rounding method of Practice E 29.10. Source Inspection10.1 If the purchaser desires that his representative ins

39、pector witness the inspections and testing of the product prior toshipment, such agreement shall be made by the purchaser andproducer or supplier as part of the contract or purchase order.10.2 When such inspection or witness of inspection andtesting is agreed upon, the producer or supplier shall aff

40、ord thepurchasers representative all reasonable facilities to satisfyhim that the product meets the requirements of this specifica-tion. Inspection and tests shall be conducted so there is nounnecessary interference with the producers operations.11. Rejection and Rehearing11.1 Material that fails to

41、 conform to the requirements ofthis specification may be rejected. Rejection should be reportedto the producer or supplier promptly and in writing. In case ofdissatisfaction with the results of the test, the producer orsupplier may make claim for a rehearing. If the rehearingestablishes that the mat

42、erial does not conform to the require-ments of this specification, as much of the rejected originalmaterial as possible shall be returned to the producer orsupplier.12. Identification Marking12.1 All ingots shall be properly marked for identificationwith the producers name or brand.12.2 Each bundle

43、or skid shall be identified with theproducers heat, lot, or other identification mark.12.3 Each ingot, bundle or skid shall be marked with theappropriate Color Code for the alloy as per North Americanrequirements in Practice B 908.13. Certification13.1 When specified in the purchase order or contrac

44、t, aproducers or suppliers certification shall be furnished to thepurchaser that the material was manufactured, sampled testedand inspected in accordance with this specification and hasbeen found to meet the requirements. When specified in thepurchase order or contract, a report of the test result s

45、hall befurnished.14. Preparation for Delivery14.1 PackagingUnless otherwise specified, the ingot shallbe packaged to provide adequate protection during normalhandling and transportation. Each package shall contain onlyone alloy unless otherwise agreed upon.15. Keywords15.1 bar stock; castings; conca

46、st; continuous cast bar stock;die castings; foundry castings; permanent mold castings; pres-sure die castings; prototyping; sand castings; ZA alloys;Zamak; zinc; zinc-aluminum alloys; zinc metalAPPENDIX(Nonmandatory Information)X1. NOMENCLATURE SYSTEMS FOR ZINC AND ZINC-ALUMINUM (ZA) ALLOYSX1.1 The

47、information in this appendix does not constitutea part of this specification but is provided for informationalpurposes only. The nomenclature covers commercial zinc andzinc-aluminum (ZA) alloys in ingot form for remelting for themanufacture of pressure die castings and foundry castings, asdesignated

48、 and specified in Table 1.X1.2 Several different systems of nomenclature haveevolved over the years to designate the zinc alloys used forcasting, as listed in Table X1.1.X1.2.1 Common names refer to the long established zinccasting alloys by number based their sequential developmentpreceded by the w

49、ord Alloy. Zinc-aluminum alloys (with ahigher aluminum content that the conventional zinc die castingB240073alloys) use the prefix ZA followed by their approximatealuminum content. These terms are in common usage.X1.2.2 Traditional names for the long established zinccasting alloys use the prefix ZAMAK which was devised basedon the major elements present: zinc, aluminum, magnesiumand kopper (copper). Zinc-aluminum alloys use the prefix ZAfollowed by their approximate aluminum content. These termsare in common usage.X1.2.3 ASTM designations are established i