《ASTM A965 A965M-2006a Standard Specification for Steel Forgings Austenitic for Pressure and High Temperature Parts《压力和高温零件用奥氏体钢锻件的标准技术规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A965 A965M-2006a Standard Specification for Steel Forgings Austenitic for Pressure and High Temperature Parts《压力和高温零件用奥氏体钢锻件的标准技术规范》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 965/A 965M 06aStandard Specification forSteel Forgings, Austenitic, for Pressure and HighTemperature Parts1This standard is issued under the fixed designationA 965/A 965M; the number immediately following the designation indicates the yearof original adoption or, in the case of revisi

2、on, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers austenitic stainless steel forg-ings for boilers, pressure vessels, high t

3、emperature parts, andassociated equipment.1.2 Supplementary requirements are provided for use whenadditional testing, inspection, or processing is required. Inaddition, supplementary requirements from SpecificationA 788/A 788M may be specified when appropriate.1.3 This specification includes the aus

4、tenitic steel forgingsthat were a part of Specification A 336/A 336M.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Co

5、mbiningvalues from the two systems may result in non-conformancewith the standard.1.5 Unless the order specifies the applicable “M” specifica-tion designation, the material shall be furnished to the inch-pound units.1.6 This standard does not purport to address all of thesafety concerns, if any, ass

6、ociated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A 336/A 336M Specification for Alloy Steel Forgings forP

7、ressure and High-Temperature PartsA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 788/A 788M Specification for Steel Forgings, GeneralRequirementsE112 Test Methods for Determining Average Grain Size2.2 Other Standards:ASME Boiler and Pressure Vessel Code, including Sectio

8、nVIII Pressure Vessels and Section IX Welding Qualifica-tions33. Ordering Information and General Requirements3.1 In addition to the ordering information required bySpecification A 788/A 788M, the intended use should be statedif 5.1 is to be applicable.3.2 Material supplied to this specification sha

9、ll conform tothe requirements of Specification A 788/A 788M, which out-lines additional ordering information, manufacturing require-ments, testing and retesting methods and procedures, marking,certification, product analysis variations, and additional supple-mentary requirements.3.3 If the requireme

10、nts of this specification are in conflictwith the requirements of Specification A 788/A 788M, therequirements of this specification shall prevail.3.4 If the forgings are intended for use under the ASMEBoiler and Pressure Vessel Code at temperatures exceeding1000F 540C, then use Supplementary Require

11、ment S7.Grain size requirements for service exceeding 1000F 540Cshould be specified unless the required grade has the suffix“H.”4. Melting and Forging4.1 In addition to the melting and forging requirements ofSpecification A 788/A 788M, which may include Supplemen-tary Requirement S8, the following c

12、ondition applies:4.1.1 A sufficient discard shall be made to secure freedomfrom injurious pipe and undue segregation.5. Machining5.1 Forged pressure vessels for steam power service shallhave the inner surface machined or ground. Unfired pressurevessels shall have the inner surfaces sufficiently free

13、 of scale topermit inspection.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.06 on Steel Forgings and Billets.Current edition approved Sept. 1, 2006. Published September 2006. Origina

14、llyapproved in 1996. Last previous edition approved in 2006 as A 965/A 965M 06.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page o

15、nthe ASTM website.3Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York, NY 10016-5990.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Consho

16、hocken, PA 19428-2959, United States.5.2 When rough machining is performed, it may be doneeither before or after heat treatment.6. Heat Treatment6.1 Forgings shall be furnished in the solution treatedcondition. On completion of forging operations, the forgingsshall be solution annealed and quenched

17、in water, oil, or apolymer water solution. Direct quenching after completion offorging without subsequent reheating to the temperaturesprescribed in 6.2-6.5 is not permissible.6.2 For Grades F304H, F309H, F310H, F316H, F321H,F347H, and F 348H, the minimum solution annealing tempera-ture shall be 192

18、5F 1050C.6.3 Grades FXM-11 and FXM-19 shall be solution annealedat 1950F 1065C.6.4 Grade F46 shall be solution annealed in the temperaturerange of 20102140F 11001170C.6.5 The remaining grades in Table 1 shall be solutionannealed at a minimum temperature of 1900F 1040C.7. Chemical Composition7.1 Heat

19、 AnalysisThe heat analysis obtained from sam-pling in accordance with Specification A 788/A 788M shallcomply with Table 1.7.2 Product AnalysisThe manufacturer shall use the prod-uct analysis provision of SpecificationA 788/A 788M to obtaina product analysis from a forging representing each heat ormu

20、ltiple heat. The product analysis tolerances for carbon shallnot apply, and the carbon requirements shall conform to Table1.7.3 Types (common names) and UNS designations follow:Grade Type UNS DesignationF304 304 S30400F304H 304H S30409F304L 304L S30403F304N 304N S30451F304LN 304LN S30453F309H 309H S

21、30909F310 310 S31000F310H 310H S31009F316 316 S31600F316H 316H S31609F316L 316L S31603F316N 316N S31651F316LN 316LN S31653F321 321 S32100F321H 321H S32109F347 347 S34700F347H 347H S34709F348 348 S34800F348H 348H S34809FXM-19 XM19 S20910FXM-11 XM11 S21904F46 S306008. Mechanical Properties8.1 Requirem

22、entsThe material shall conform to the re-quirements for mechanical properties prescribed in Table 2 or,if applicable, Supplementary Requirement S2. The largestobtainable tension test specimen as specified in Test Methodsand Definitions A 370 shall be used.8.2 Number of TestsThe number and location o

23、f tests arebased on the heat-treated weight of the forging(s) from thesame heat, solution annealed in the same furnace charge.8.2.1 For forgings weighing less than 5000 lb 2250 kg asheat treated, one tension test shall be required on the basis ofone test per heat in each heat treatment load. This te

24、st shall betaken from a prolongation of one of the forgings. Use of aseparately forged test bar for the mechanical test specimens,instead of an integral prolongation, is acceptable for forgingsweighing less than 5000 lb 2250 kg, provided that theheat-treated cross section of the test bar is not less

25、 than themaximum heat-treated cross section of the forgings it repre-sents. The separately forged test bar shall be from the sameheat as the forgings it represents and shall accompany theforgings during heat treatment.8.2.2 When heat treatment is performed in continuous typefurnaces equipped with re

26、cording pyrometers, such that com-plete heating records are available, a solution annealing chargemay be considered as any continuous run not exceeding an 8 hperiod.8.2.3 For forgings weighing over 5000 lb 2250 kg, as heattreated, one tension test shall be taken from a prolongation oneach forging.8.

27、3 The longitudinal axis of the tension test specimen shallbe parallel to the direction of major working of the forging,except when Supplementary Requirement S2 is specified. Forupset disk forgings the longitudinal axis of the specimen shallbe in either the tangential or radial direction.8.3.1 The lo

28、cation of the longitudinal axis of the tension testspecimen shall be located midway between the parallel sur-faces of the test extension, if added to the periphery of disks,or midway between the center and surface of solid forgings.For hollow forgings, or those heat treated after boring, thespecimen

29、 shall be located at midwall. For the special case offorgings that are heat treated solid, but are subsequently bored,the tension test specimen may be taken at the location of theminimum inside diameter after boring instead of the mid-radiusposition.9. Grain Size9.1 For Grades F304H, F316H, F309H, F

30、310H, F321H,F347H, and F348H, the grain size of the forgings shall beascertained according to Test Methods E112, after solutiontreatment. One sample shall be examined for each tensilespecimen required in 8.2 and shall be taken from the tensiontest location. The grain size shall be number 6, or coars

31、er, overat least 75 % of the surveyed area.10. Repair Welding10.1 Repair welding of forgings may be permitted but onlyat the option of the purchaser. Such repair welds shall be madein accordance with Section IX of the ASME Boiler andPressure Vessel Code.11. Marking11.1 The marking requirements of Sp

32、ecification A 788/A 788M apply.A 965/A 965M 06a2TABLE1ChemicalRequirementsAusteniticSteelsGradeElementF304F304HF304LF304NF304LNF309HF310F310HF316F316HF316LF316NF316LNF321F321HF347F347HF348F348HFXM-19FXM-11F46ACarbon0.08 max0.04 0.100.030 max0.08 max0.030 max0.04 0.100.15max0.04 0.100.08 max0.04 0.10

33、0.035 max0.08 max0.0300.08 max0.04 0.100.08max0.04 0.100.08 max0.04 0.100.06 max0.04 max0.018maxManganese2.00 max2.00 max2.00max2.00 max2.00max2.00max2.00max2.00max2.00 max2.00 max2.00 max2.00 max2.00 max2.00 max2.00 max2.00max2.00max2.00 max2.00 max4.0 6.08.0 10.02.00maxPhosphorus,max0.0450.0450.04

34、50.0450.0450.0450.0450.0450.0450.0450.0400.0450.0450.0450.0450.0450.0450.0450.0450.0450.0450.020Sulfur,max0.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.0300.020Silicon1.00 max1.00 max1.001.00 max1.00max1.00max1.00max1.00max1.00 max1.00 max1.00

35、max1.00 max1.00 max1.00 max1.00 max1.00max1.001.001.001.001.00 max3.7 4.3Nickel8.0 11.08.0 11.08.0 12.08.0 11.08.0 11.012.0 15.019.0 22.019.0 22.010.0 14.010.0 14.010.0 15.010.0 13.010.0 13.09.0-12.09.012.09.0 12.09.0 12.09.0 12.09.0 12.011.513.55.5 7.514.0 15.5Chromium18.0 20.018.0 20.018.0 20.018.

36、0 20.018.0 20.022.0 24.024.0 26.024.0 26.016.0 18.016.0 18.016.0 18.016.0 18.016.0 18.017.0- 19.017.0 19.017.0 19.017.0 19.017.0 19.017.0 19.020.5 23.519.0 21.517.0 18.5Molybdenum.2.00 3.002.00 3.002.00 3.002.00 3.002.00 3.00.1.50 3.00.0.20maxNitrogen.0.10 0.160.10 0.16.0.10 0.160.10 0.160.10 max.0.

37、20 0.400.15 0.40.Columbiumandtan-talum.B83Cminto1.10max103Cminto1.10 max83Cminto1.10 max0.10 0.30.Titanium.CD.Tantalum.0.10 max0.10 max.Vanadium.0.10 0.30.Cobalt,max.0.0200.020.UNS DesignationS30400S30409S30403S30451S30453S30909S31000S31009S31600S31609S31603S31651S31653S32100S32109S34700S34709S34800

38、S34809S20910S21904S30600AF46shallhaveamaximumcoppercontentof0.50.BF347shallhaveacolumbiumcontentofnotlessthantentimesthecarboncontentandnotmorethan1.10%.(Alternatively,tantalummaybesubstitutedforpartofthecolumbiumasapprovedbythepurchaser.)CF321shallhaveatitaniumcontentofnotlessthan5x(C+N)andnotmoret

39、han0.70%.DF321Hshallhaveatitaniumcontentofnotlessthan4x(C+N)andnotmorethan0.70%.A 965/A 965M 06a3TABLE2TensileRequirementsAusteniticSteelsGradeF304F304HF304LF304NF304LNF309HF310F310HF316F316HF316LF316NF316LNF321F321HF347F347HF348F348HFXM-19FXM-11F46Tensilestrengthmin,ksiMPa70485704856545080550704857

40、0485755157048570485704856545080550704857048570485704857048570485704851006909062078100540690Yieldstrength(0.2%offset),min,ksiMPa30205302052517035240302053020530205302053020530205251703524030205302053020530205302053020530205553805034532220Elongationin2in.or50mm,min,%30303025303030303030302530303030303

41、030304040Reductionofarea,min,%45454545454535454545454545454545454545505050A 965/A 965M 06a412. Test Reports12.1 The certification requirements of Specification A 788/A 788M shall apply.13. Keywords13.1 austenitic stainless steel forgings; high temperatureservice; pressure containing parts; pressure

42、vessel serviceSUPPLEMENTARY REQUIREMENTSOne or more of the following supplementary requirements shall apply only when specified by thepurchaser in the inquiry, contract, and order. Details of these supplementary requirements shall beagreed upon between the manufacturer and the purchaser.S1. Rough Tu

43、rning and BoringS1.1 The position of the rough turning and boring in thesequence of manufacturing operations shall be specified.S2. Transverse Tension TestS2.1 Instead of the test specimen orientation requirementsin 8.3, the longitudinal axis of the test specimens shall betransverse to the direction

44、 of major working of the forging. Theresults shall conform with requirements of Table 2, with theexception of the ductility limits which shall be as prescribed inTable S2.1.S3. Hydrostatic TestS3.1 Ahydrostatic pressure test shall be applied. The detailsof the test, including its position in the seq

45、uence of manufac-turing operations, shall be specified.S4. Stabilization Heat TreatmentS4.1 When specified, Grades F347 and F321 shall receivestabilization treatment, which shall consist of holding theforging at 1500 to 1600F 815 to 870C, for not less than2 h/in. of thickness and then cooling in the

46、 furnace or in stillair.S5. MarkingS5.1 Forgings shall be marked at a location indicated by thepurchaser in the purchase order or drawing.S6. Individual ForgingS6.1 Forgings, whether identical or not identical, shall beproduced individually. They shall not be forged in multiple andseparated prior to

47、 or after heat treatment.S6.2 The shape and size of individual forgings shall beagreed between the manufacturer and the purchaser by meansof a forging drawing or the purchase order.S7. Grain Size Requirements for Service Exceeding1000F 540CS7.1 For design metal temperatures above 1000F 540C,the forg

48、ings shall have a grain size of 7 or coarser asdetermined in accordance with Test Methods E112. The actualgrain size shall be reported on the certificate of test.A 965/A 965M 06a5TABLES2.1DuctilityLimitsGradeF304F304HF304LF304NF304LNF309HF310F310HF316F316HF316LF316NF316LNF321F321HF347F347HF348F348HFXM19FXM11F46Elongationin2in.or50mm,min,%30303025303030303030302530303030303030304040Reductionofarea,min,%35353535353535353535353535353537353535354040A 965/A 965M 06a6SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard