1、Designation: A941 16Standard Terminology Relating toSteel, Stainless Steel, Related Alloys, and Ferroalloys1This standard is issued under the fixed designation A941; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last
2、revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This standard is a compilation of definitions of termsrelated to steel, stainless steel, related alloys, and ferroalloys.1.
3、2 When a term is used in an ASTM document for whichCommittee A01 is responsible, it is included herein only whenjudged, after review by Subcommittee A01.92, to be a gener-ally usable term.1.3 Some definitions include a discussion section, which isa mandatory part of the definition and contains addit
4、ionalinformation that is relevant to the meaning of the defined term.1.4 Definitions of terms specific to a particular standard willappear in that standard and will supersede any definitions ofidentical terms in this standard.2. Referenced Documents2.1 ASTM Standards:2E112 Test Methods for Determini
5、ng Average Grain Size3. Terminology3.1 Definitions of Terms Specific to This Standard:Accm, Ac1, Ac3, Ac4See transformation temperature.Aecm, Ae1, Ae3, Ae4See transformation temperature.age hardening, nhardening by aging, usually after rapidcooling or cold working.age hardening, nsee precipitation h
6、ardening.aging, na change in the properties of certain steels thatoccurs at ambient or moderately elevated temperatures afterhot working or a heat treatment (quench aging, naturalaging, or artificial aging) or after a cold-working operation(strain aging).DISCUSSIONThe change in properties is often,
7、but not always, due toprecipitation hardening, but never involves a change in the chemicalcomposition of the steel.alloy steel, na steel, other than a stainless steel, thatconforms to a specification that requires one or more of thefollowing elements, by mass percent, to have a minimumcontent equal
8、to or greater than: 0.30 for aluminum; 0.0008for boron; 0.30 for chromium; 0.30 for cobalt; 0.40 forcopper; 0.40 for lead; 1.65 for manganese; 0.08 for molyb-denum; 0.30 for nickel; 0.06 for niobium (columbium); 0.60for silicon; 0.05 for titanium; 0.30 for tungsten (wolfram);0.10 for vanadium; 0.05
9、for zirconium; or 0.10 for any otheralloying element, except sulphur, phosphorus, carbon, andnitrogen.annealing, na generic term covering any of several heattreatments.DISCUSSIONThis treatment is used for purposes such as reducinghardness, improving machinability, facilitating cold working, produc-i
10、ng a desired microstructure, or obtaining desired mechanical, physical,or other properties. Where applicable, it is preferred that the followingmore specific terms be used: box annealing, bright annealing, fullannealing, intermediate annealing, isothermal annealing, processannealing, spheroidizing,
11、and subcritical annealing. The term“annealing,” without qualification, implies full annealing. Any pro-cess of annealing will usually reduce stresses; however, if thetreatment is applied for the sole purpose of stress reduction, it should bedesignated stress relieving.Arcm, Ar1, Ar3, Ar4See transfor
12、mation temperature.artificial aging, naging above room temperature.atmospheric corrosion resistance, nthe ability to resistdegradation or alteration of material through chemical reac-tion with the surrounding atmosphere.DISCUSSIONThis term generally pertains to carbon steel, low alloysteel, or micro
13、-alloyed steel.austempering, nheat treatment involving quenching asteel object from a temperature above the transformationrange in a medium maintained at a temperature above themartensite range sufficiently fast to avoid the formation ofhigh temperature transformation products, and then holdingit at
14、 that temperature until transformation is complete.austenitizing, nforming austenite by heating a steel objectabove the transformation range.1This terminology is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA
15、01.92 on Terminology.Current edition approved Nov. 15, 2016. Published January 2017. Originallyapproved in 1995. Last previous edition approved in 2015 as A941 15. DOI:10.1520/A0941-16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceast
16、m.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with in
17、ternationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1baking, nheating to a low temperature in orde
18、r to removegases.batch furnace, na heating device within which steel objectsare held stationary or oscillated during the thermal process-ing cycle.blank carburizing, nsimulating the carburizing operationwithout introducing carbon.DISCUSSIONThis is usually accomplished by using an inert materialin pl
19、ace of the carburizing agent, or by applying a suitable protectivecoating on the object being heat treated.blank nitriding, nsimulating the nitriding operation withoutintroducing nitrogen.DISCUSSIONThis is usually accomplished by using an inert materialin place of the nitriding agent, or by applying
20、 a suitable protectivecoating on the object being heat treated.bluing, nsubjecting the scale-free surface of a steel object tothe action of air, steam, or other agents at a suitabletemperature, thereby forming a thin blue film of oxide andimproving the objects appearance and corrosion resistance.DIS
21、CUSSIONThis term is ordinarily applied to sheet, strip, orfinished parts. It is used also to denote the heating of springs afterfabrication in order to improve their properties.box annealing, nannealing in a sealed container underconditions that minimize oxidation.DISCUSSIONThe charge is usually hea
22、ted slowly to a temperaturebelow the transformation range, but sometimes above or within it,and is then cooled slowly.bright annealing, nannealing in a protective medium toprevent discoloration of the bright surface.capped steel, na rimmed steel in which, during ingotsolidification, the rimming acti
23、on was limited by mechanicalor chemical means.carbon potential, nthe carbon content at the surface of aspecimen of pure iron in equilibrium with the carburizingmedium considered, and under the conditions specified.carbon restoration, nreplacing the carbon lost from thesurface layer in previous proce
24、ssing by carburizing this layerto substantially the original carbon level.carbon steel, na steel that conforms to a specification thatprescribes a maximum limit, by heat analysis in masspercent, of not more than: 2.00 for carbon and 1.65 formanganese, but does not prescribe a minimum limit forchromi
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMA9412016STANDARDTERMINOLOGYRELATINGTOSTEELSTAINLESSSTEELRELATEDALLOYSANDFERROALLOYS 有关 不锈钢 相关 合金

链接地址:http://www.mydoc123.com/p-460045.html