ASTM A543 A543M-2009 Standard Specification for Pressure Vessel Plates Alloy Steel Quenched and Tempered Nickel-Chromium-Molybdenum《淬火回火的镍铬钼合金压力容器钢板用标准规范》.pdf

《ASTM A543 A543M-2009 Standard Specification for Pressure Vessel Plates Alloy Steel Quenched and Tempered Nickel-Chromium-Molybdenum《淬火回火的镍铬钼合金压力容器钢板用标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A543 A543M-2009 Standard Specification for Pressure Vessel Plates Alloy Steel Quenched and Tempered Nickel-Chromium-Molybdenum《淬火回火的镍铬钼合金压力容器钢板用标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A543/A543M 09Standard Specification forPressure Vessel Plates, Alloy Steel, Quenched andTempered Nickel-Chromium-Molybdenum1This standard is issued under the fixed designation A543/A543M; the number immediately following the designation indicates the yearof original adoption or, in the

2、case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification2covers nickel-chromium-molybdenum alloy steel plates for use in the

3、quenched andtempered condition, intended for the fabrication of weldedpressure vessels and other pressure equipment. These alloycompositions are normally considered for construction involv-ing plate thicknesses of 2 in. 50 mm or greater.1.2 Material under this specification is available in twotypes,

4、 B and C. The material is also available in three classesas follows:Class Minimum Tensile Strength, ksi MPa1 105 7252 115 7953 90 6201.3 The maximum thickness of plates is limited only by thecapacity of the chemical composition to meet the specifiedmechanical property requirements.1.4 The minimum pl

5、ate thickness is316 in. 5 mm.1.5 These alloy steel plates in the as-rolled condition aresensitive to cracking during flame cutting, transit, and han-dling. They should be shipped in the as-rolled condition onlywith the mutual agreement of the manufacturer and thepurchaser or fabricator.1.6 The value

6、s stated in either inch-pound units or SI unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently of the other. Combining values from thetwo systems

7、 may result in nonconformance with the specifi-cation.2. Referenced Documents2.1 ASTM Standards:3A20/A20M Specification for General Requirements forSteel Plates for Pressure VesselsA435/A435M Specification for Straight-Beam UltrasonicExamination of Steel PlatesA577/A577M Specification for Ultrasonic

8、 Angle-Beam Ex-amination of Steel PlatesA578/A578M Specification for Straight-Beam UltrasonicExamination of Rolled Steel Plates for Special Applica-tions3. General Requirements and Ordering Information3.1 Material supplied to this material specification shallconform to Specification A20/A20M. These

9、requirements out-line the testing and retesting methods and procedures, permit-ted variations in dimensions, and mass, quality and repair ofdefects, marking, loading, and ordering information.3.2 In addition to the basic requirements of this specifica-tion, certain supplementary requirements are ava

10、ilable whenadditional control, testing, or examination is required to meetend use requirements. The purchaser is referred to the listedsupplementary requirements in this specification and to thedetailed requirements in Specification A20/A20M.3.3 If the requirements of this specification are in confl

11、ictwith the requirements of Specification A20/A20M, the require-ments of this specification shall prevail.4. Manufacture4.1 Steelmaking PracticeThe steel shall be killed andshall conform to the fine austenitic grain size requirement ofSpecification A20/A20M.1This specification is under the jurisdict

12、ion of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.11 on Steel Plates for Boilers and Pressure Vessels.Current edition approved Oct. 1, 2009. Published October 2009. Originallyapproved in 1965. Last previous edition approved in 2

13、004 as A543/A543M 93 (2004)1. DOI: 10.1520/A0543_A0543M-09.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SA-543 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. Fo

14、r Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5. H

15、eat Treatment5.1 All plates shall be heat treated by heating to a suitableaustenitizing temperature, holding for a sufficient time periodto attain uniform temperature through the thickness andquenching in a suitable liquid medium by spraying or immer-sion. The plates shall then be tempered to produc

16、e the requiredproperties by heating to a suitable temperature not lower than1100F 595C with a holding time of not less than12 h/in.1.2 min/mm of thickness but not less than12 h.5.2 Plates over 4 in. 100 mm in thickness shall receive aprior treatment of normalizing at, or water quenching from atemper

17、ature within the range from 1650 to 1850F 900 to1010C before the heat treatment specified in 5.1.5.3 When the fabricator elects to perform the heat treatmentin 5.1 and 5.2, the manufacturer shall normalize the plates at anappropriate temperature prior to shipment unless otherwiseagreed to.6. Chemica

18、l Requirements6.1 The steel shall conform to the chemical requirementsshown in Table 1 unless otherwise modified in accordance withSupplementary Requirement S17, Vacuum Carbon-DeoxidizedSteel, in Specification A20/A20M.7. Mechanical Requirements7.1 Tension Test Requirements:7.1.1 The material as rep

19、resented by the tension-test speci-mens shall conform to the requirements shown in Table 2.7.1.2 For nominal plate thicknesses of34 in. 20 mm andunder, the 112-in. 40-mm wide rectangular specimen may beused for the tension test and the elongation may be determinedin a 2-in. 50-mm gage length that in

20、cludes the fracture andshows the greatest elongation.8. Keywords8.1 alloy steel; alloy steel plate; pressure containing parts;pressure vessel steels; steel plates; steel plates for pressurevesselsSUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the order.Alist

21、 of standardized supplementary requirements for use at the option of the purchaser are includedin Specification A20/A20M. Several of those considered suitable for use with this specification arelisted below by title. Other tests may be performed by agreement between the supplier and thepurchaser.S1.

22、 Vacuum Treatment,S2. Product Analysis,S3. Simulated Post-Weld Heat Treatment of MechanicalTest Coupons,S4.2 Additional Tension Test,S5. Charpy V-Notch Impact Test,S6. Drop Weight Test (for Material 0.625 in. 16 mm andover in Thickness),S7. High-Temperature Tension Test,S8. Ultrasonic Examination in

23、 accordance with Specifica-tion A435/A435M,S9. Magnetic Particle Examination,S11. Ultrasonic Examination in accordance with Specifica-tion A577/A577M,S12. Ultrasonic Examination in accordance with Specifica-tion A578/A578M, andS17. Vacuum Carbon-Deoxidized Steel.TABLE 1 Chemical RequirementsElementC

24、omposition, %Type B Type CCarbon, maxA0.20 0.18Manganese, maxA0.40 0.40Phosphorus, maxA0.020 0.020Sulfur, maxA0.020 0.020Silicon:Heat analysis 0.150.40 0.150.40Product analysis 0.130.45 0.130.45Nickel:Heat analysis 2.254.00 2.003.50Product analysis 2.184.07 1.933.57Chromium:Heat analysis 1.001.90 1.

25、001.90Product analysis 0.941.96 0.941.96Molybdenum:Heat analysis 0.200.65 0.200.65Product analysis 0.160.69 0.160.69AApplies to both heat and product analyses.TABLE 2 Tensile RequirementsClass 1 Class 2 Class 3Tensile strength, ksi MPa 10512572586011513579593090115620795Yield strength, min, ksi MPa

26、85 585 100 690 70 485Elongation, 2 in. 50 mm,min, %A,B14 14 16ASee 7.1.2.BSee Specification A20/A20M for elongation adjustment.A543/A543M 092SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A543/A543M 93 (2004)1) that may impact th

27、e use of this standard. (Approved Oct. 1, 2009.)(1) 1.5 added.(2) Section 3 editorially revised.(3) 5.3 revised to acknowledge the crack sensitivity of thissteel in the unheat treated condition.(4) Table 1 revised to delete maximum vanadium requirementsince this is covered by Specification A20/A20M.

28、(5) Section 8 added.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement

29、 of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or fo

30、r additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known

31、 to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A543/A543M 093