ASTM A416 A416M-2016 Standard Specification for Low-Relaxation Seven-Wire Steel Strand for Prestressed Concrete《预应力混凝土用低松弛七股钢绞线的标准规格》.pdf

《ASTM A416 A416M-2016 Standard Specification for Low-Relaxation Seven-Wire Steel Strand for Prestressed Concrete《预应力混凝土用低松弛七股钢绞线的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A416 A416M-2016 Standard Specification for Low-Relaxation Seven-Wire Steel Strand for Prestressed Concrete《预应力混凝土用低松弛七股钢绞线的标准规格》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A416/A416M 15A416/A416M 16Standard Specification forLow-Relaxation, Seven-Wire Steel Strand for PrestressedConcrete1This standard is issued under the fixed designation A416/A416M; the number immediately following the designation indicates the yearof original adoption or, in the case of

2、revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This spec

3、ification covers two grades of low-relaxation, seven-wire steel strand for use in prestressed concrete construction.Grade 250 1725 and Grade 270 1860 have minimum tensile strengths of 250 ksi 1725 MPa and 270 ksi 1860 MPa,respectively, based on the nominal area of the strand.1.2 Asupplementary requi

4、rement (S1) is provided for use where bond strength testing of 0.600-in. 15.24-mm diameter Grade270 1860 strand for applications in prestressed ground anchors is required by the purchaser. The supplementary requirementapplies only when specified in the purchase order.1.3 The text of this specificati

5、on contains notes or footnotes, or both, that provide explanatory material. Such notes andfootnotes do not contain any mandatory information.1.4 This specification is applicable for orders in either inch-pound units (as Specification A416) or in SI units (as SpecificationA416M).1.5 The values stated

6、 in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI unitsare shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be usedindependently of the other. Combining values from the two systems

7、may result in non-conformance with the specification.2. Referenced Documents2.1 ASTM Standards:2A981/A981M Test Method for Evaluating Bond Strength for 0.600-in. 15.24-mm Diameter Steel Prestressing Strand, Grade270 1860, Uncoated, Used in Prestressed Ground AnchorsA1061/A1061M Test Methods for Test

8、ing Multi-Wire Steel Strand2.2 U.S. Military Standard:3MIL-STD-129 Marking for Shipment and Storage2.3 U.S. Federal Standard:3Fed. Std. No. 123 Marking for Shipments (Civil Agencies)3. Terminology3.1 Definition of Term Specific to This Specification:=Specification:3.1.1 strand, na group of wires hav

9、ing a center wire enclosed tightly by six helically placed outer wires with uniform pitchof not less than 12 and not more than 16 times the nominal diameter of the strand.3.1.1.1 DiscussionThe direction of lay may be either right- or left-hand; however, strands of different lays should not be splice

10、d together.left-hand.1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.05on Steel Reinforcement.Current edition approved May 1, 2015March 1, 2016. Published June 2015March 2016. Origina

11、lly approved in 1957. Last previous edition approved in 20122015 asA416/A416M 12a.A416/A416M 15. DOI: 10.1520/A0416_A0416M-15.10.1520/A0416_A0416M-16.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Stand

12、ardsvolume information, refer to the standards Document Summary page on the ASTM website.3 Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/dodssp.daps.dla.mil.This document is not an ASTM standard and is intended o

13、nly to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current ver

14、sionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States14. Ordering Information4.1 It shall be

15、 the responsibility of the purchaser to specify all requirements that are necessary for material ordered under thisspecification. Such requirements to be considered include, but are not limited to, the following:4.1.1 Quantity (feet metres),4.1.2 Nominal diameter of strand,4.1.3 Grade of strand,4.1.

16、4 Specially dimensioned strand (7.4), if desired,4.1.5 Weldless, if desired (8.1),4.1.6 Outside inspection, if required (11.1),4.1.7 Load-elongation curve, if desired (13.2),4.1.8 Packaging (14.1),4.1.9 Supplementary Requirement S1, if desired, and4.1.10 ASTM designation A416 A416M and year of issue

17、.5. Materials and Manufacture5.1 Base MetalThe base metal shall be carbon steel of such quality that when drawn to wire, fabricated into strand, and thenthermally treated, shall have the properties and characteristics prescribed in this specification.5.2 WireThe wire from which the strand is to be f

18、abricated shall be round and have a dry-drawn finish.NOTE 1This product is a composite of seven wires and is produced only to meet the prescribed mechanical properties. The chemical compositionof all wires or any individual wire is not pertinent to this application, and heat identity is not necessar

19、ily maintained. It is possible that wire from morethan one heat may be used in the manufacture of a reel or reelless pack. Traceability is based on identity of reels or reelless packs as maintained andreported by the manufacturer.5.3 TreatmentAfter stranding, strand shall be subjected to a continuou

20、s thermal-mechanical treatment to produce theprescribed mechanical properties. Temper colors which result from the thermal-mechanical treatment are considered normal for thefinished appearance of this strand.6. Mechanical Property Requirements6.1 Tests for mechanical properties shall be conducted in

21、 accordance with Test Methods A1061/A1061M.6.2 Breaking StrengthThe breaking strength of the finished strand shall conform to the requirements prescribed in Table 1.6.3 Yield StrengthYield strength in pounds kN shall be measured at 1 % 1.0 % extension under load. The minimum yieldstrength shall be 9

22、0 % of the breaking strength listed in Table 1. Initial loads for the test and minimum yield strengths are listedin Table 2.6.3.1 The extension under load shall be measured by an extensometer calibrated with the smallest division not larger than0.0001 in./in. 0.0001 mm/mm of gage length.6.4 Elongati

23、onThe total elongation under load shall not be less than 3.5 % using a gage length of not less than 24 in. 600mm. It shall be permissible to determine the total elongation value by adding, to the 1.0 % yield extension, the percent extensionor movement between the jaws gripping the strand after yield

24、 determination. The percent is calculated on the new base length ofjaw-to-jaw distance.TABLE 1 Breaking Strength RequirementsNominal Diameterof Strand, in. mmMinimum BreakingStrength ofStrand, lbf kNSteel Area ofStrand, in.2 mm2Weight Mass ofStrand lb/1000 ftkg/1000 mGrade 250 17250.250 6.4 9 000 40

25、.0 0.036 23 122 1820.313 7.9 14 500 64.5 0.058 37 197 2940.375 9.5 20 000 89.0 0.080 52 272 4050.438 11.1 27 000 120 0.108 69.7 367 5480.500 12.7 36 000 160 0.144 92.9 490 7300.600 15.2 54 000 240 0.216 139 737 1090Grade 270 18600.375 9.53 23 000 102 0.085 55 290 4300.438 11.1 31 000 138 0.115 74.2

26、390 5800.500 12.7 41 300 184 0.153 98.7 520 7800.520 13.2 45 000 200 0.167 108 570 8400.563 14.3 51 700 230 0.192 124 650 9700.600 15.2 58 600 261 0.217 140 740 11000.620 15.7 62 800 279 0.231 150 780 12000.700 17.8 79 400 353 0.294 190 1000 1500A416/A416M 1626.5 Relaxation PropertiesStrand shall ha

27、ve relaxation losses of not more than 2.5 % when initially loaded to 70 % of specifiedminimum breaking strength or not more than 3.5 % when loaded to 80 % of specified minimum breaking strength of the strandafter 1000 hours of testing.6.5.1 If required, relaxation evidence shall be provided from the

28、 manufacturers records of tests on similarly dimensioned strandof the same grade.7. Dimensions and Permissible Variations7.1 The size of the finished strand shall be expressed as the nominal diameter of the strand in inches millimetres.7.2 The diameter of the center wire of any strand shall be large

29、r than the diameter of any outer wire in accordance with Table3.7.3 Permissible Variations in Diameter:7.3.1 All Grade 250 1725 strand shall conform to a size tolerance of 60.016 in. 60.40 mm from the nominal diametermeasured across the crowns of the wires.7.3.2 All Grade 270 1860 strand shall confo

30、rm to a size tolerance of +0.026, 0.006 in. +0.65, 0.15 mm from the nominaldiameter measured across the crowns of the wires.7.3.3 Variation in cross-sectional area and in unit stress resulting therefrom shall not be cause for rejection provided that thediameter differences of the individual wires an

31、d the diameters of the strand are within the tolerances specified.7.4 It shall be permitted to furnish specially dimensioned strands with nominal diameters up to 0.750 in. 19 mm. The breakingstrength shall be defined, and the yield strength, as defined in 6.3, shall not be less than 90 % of the spec

32、ified minimum breakingstrength. All other requirements shall apply.8. Workmanship, Finish, and Appearance8.1 Joints:TABLE 2 Yield Strength RequirementsNominal Diameter ofStrand in. mm Initial Load, lbf kNMinimum Load at1 %1.0 % Extension, lbfkNGrade 250 17250.250 6.4 900 4.0 8 100 36.00.313 7.9 1 45

33、0 6.5 13 050 58.10.375 9.5 2 000 8.9 18 000 80.10.438 11.1 2 700 12.0 24 300 108.10.500 12.7 3 600 16.0 32 400 144.10.600 15.2 5 400 24.0 48 600 216.2Grade 270 18600.375 9.53 2 300 10.2 20 700 92.10.438 11.1 3 100 13.8 27 900 124.10.500 12.7 4 130 18.4 37 170 165.30.520 13.2 4 500 20.0 40 500 180.10

34、.563 14.3 5 170 23.0 46 530 207.00.600 15.2 5 860 26.1 52 740 234.60.620 15.7 6 280 27.9 56 520 251.40.700 17.8 7 940 35.3 71 500 318.0TABLE 3 Diameter Relation Between Center and Outer WiresNominal Diameter of Strand, in.mmMinimum Difference Between CenterWire Diameter and Diameter of AnyOuter Wire

35、, in. mmGrade 250 17250.250 6.4 0.001 0.0250.313 7.9 0.0015 0.0380.375 9.5 0.002 0.0510.438 11.1 0.0025 0.0640.500 12.7 0.003 0.0760.600 15.2 0.004 0.102Grade 270 18600.375 9.53 0.002 0.0510.438 11.1 0.0025 0.0640.500 12.7 0.003 0.0760.520 13.2 0.003 0.0760.563 14.3 0.0035 0.0890.600 15.2 0.004 0.10

36、20.620 15.7 0.004 0.1020.700 17.8 0.0045 0.114A416/A416M 1638.1.1 There shall be no strand joints or strand splices in any length of the finished strand unless specifically permitted by thepurchaser.8.1.2 During the process of manufacture of individual wires for stranding, welding shall be permitted

37、 only prior to or at the sizeof the last thermal treatment, for example, patenting or controlled cooling. There shall be no welds in the wire after it has beendrawn through the first die in the wire drawing except as provided in 8.1.3.8.1.3 During fabrication of the strand, butt-welded joints are pe

38、rmitted in the individual wires, provided there shall not be morethan one such joint in any 150-ft 45-m section of the finished strand.8.1.4 When specifically ordered as “Weldless,” a product free of welds shall be furnished. When “Weldless” is specified, thestrand is produced as one continuous leng

39、th with no welds as allowed by 8.1.3.8.2 The finished strand shall be uniform in diameter and shall be free of imperfections.8.3 When the strand is cut without seizings, the wire shall not fly out of position. If any wire flies out of position and can bereplaced by hand, the strand shall be consider

40、ed satisfactory.8.4 The strand shall not be oiled or greased. Slight rusting, provided it is not sufficient to cause pits visible to a person withnormal or corrected vision, shall not be cause for rejection.NOTE 2Guidance for evaluating the degree of rusting on prestressed concrete strand is present

41、ed in Sason.49. Sampling9.1 Test specimens cut from either end of the reel or reelless pack are permitted. Any specimen found to contain a wire jointshall be discarded and a new specimen obtained.10. Number of Tests10.1 One test specimen shall be taken from each 30-ton 27-tonne production lot of fin

42、ished strand, and tested for breakingstrength, yield strength, and elongation.11. Inspection11.1 If outside inspection is required, the manufacturer shall afford the inspector representing the purchaser reasonable accessto the facilities, which concern the manufacture of the material ordered, to sat

43、isfy the inspector that the material is being furnishedin accordance with this specification. All tests and inspections shall be made at the place of manufacture prior to shipment, unlessotherwise agreed upon at the time of purchase, and shall be so conducted as not to interfere unnecessarily with t

44、he manufacturersoperations.12. Rejection12.1 Failure of any test specimen to comply with the requirements of the specification shall constitute grounds for rejection ofthe production lot represented by the specimen.12.2 The production lot shall be resubmitted for inspection by testing a specimen fro

45、m each reel or reelless pack and sortingout non-conforming material.12.3 If there is a reasonable doubt in the initial testing as to the ability of the strand to meet any requirement of this specification,two additional tests shall be made on specimens of strand from the same reel or reelless pack,

46、and if failure occurs in either ofthese tests, the strand shall be rejected.13. Certification13.1 If outside inspection is not required, a manufacturers certification that the material has been tested in accordance with andmeets the requirements of this specification shall be the basis of acceptance

47、 of the material. The certification shall include thespecification number, year of issue, and revision letter, if any.13.2 When requested in the purchase order or contract, the manufacturer shall furnish a representative load-elongation curvefor each size and grade of strand shipped.13.3 When the mo

48、dulus of elasticity of a seven-wire strand is provided, the cross-sectional area used to calculate that modulusalso shall be provided. The area provided in the certification shall be the area used to calculate the modulus of elasticity.13.4 A material test report, certificate of inspection, or similar document printed from or used in electronic form from anelectronic data interchange (EDI) transmission shall be regarded as having the same validity as a counterpart printed in thecertifiers facility. The content of the EDI transmitted