ASTM A285 A285M-2012 Standard Specification for Pressure Vessel Plates Carbon Steel Low- and Intermediate-Tensile Strength 《压力容器用低和中等抗拉强度的碳素钢板的标准规格》.pdf

《ASTM A285 A285M-2012 Standard Specification for Pressure Vessel Plates Carbon Steel Low- and Intermediate-Tensile Strength 《压力容器用低和中等抗拉强度的碳素钢板的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A285 A285M-2012 Standard Specification for Pressure Vessel Plates Carbon Steel Low- and Intermediate-Tensile Strength 《压力容器用低和中等抗拉强度的碳素钢板的标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation:A285/A285M03(Reapproved2007) Designation: A285/A285M 12Standard Specification forPressure Vessel Plates, Carbon Steel, Low- andIntermediate-Tensile Strength1This standard is issued under the fixed designation A285/A285M; the number immediately following the designation indicates the year

2、of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Departmen

3、t of Defense.1. Scope*1.1 This specification2covers carbon steel plates of low- and intermediate-tensile strengths which may be made by killed,semi-killed, capped, or rimmed steel practices at the producers option. These plates are intended for fusion-welded pressurevessels.1.2 Plates under this spe

4、cification are available in three grades having different strength levels as follows:Grade Tensile Strength, ksi MPaA 4565 310450B 5070 345485C 5575 3805151.3 The maximum thickness of plates under this specification, for reasons of internal soundness, is limited to a maximumthickness of 2 in. 50 mm

5、for all grades.NOTE 1For killed carbon steels only refer to the following ASTM specifications:3A 299/A 299M Pressure Vessel Plates, Carbon Steel, Manganese-Silicon.A 515/A 515M Pressure Vessel Plates, Carbon Steel, forIntermediate- and Higher-Temperature ServiceA 516/A 516M Pressure Vessel Plates, C

6、arbon Steel, for Moderate-and Lower-Temperature Service.1.4For1.4 For plates produced from coil and furnished without heat treatment or with stress relieving only, the additionalrequirements, including additional testing requirements and the reporting of additional test results, of Specification A20

7、/A20Mapply.1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI unitsare shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be usedindependently of the other. Combining

8、values from the two systems may result in nonconformance with the specification.2. Referenced Documents2.1 ASTM Standards:3A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels3. General Requirements and Ordering Information3.1Plates3.1 Material supplied to this produ

9、ctmaterial specification shall conform to Specification A20/A20M, which outlinesthe testing and retesting methods and procedures, permissible variations in dimensions and mass, quality and repair of defects,marking, loading, etc.3.2Specification . These requirements outline the testing and retesting

10、 methods and procedures, permitted variations indimensions, and mass, quality and repair of defects, marking, loading, and ordering information.3.2 In addition to the basic requirements of this specification, certain supplementary requirements are available when additionalcontrol, testing, or examin

11、ation is required to meet end use requirements. The purchaser is referred to the listed Supplementary1This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.11on Steel Plates for Boilers and

12、 Pressure Vessels.Current edition approved Nov.May 1, 2007.2012. Published March 2008.June 2012. Originally approved in 1946. Last previous edition approved in 20032007 asA285/A285M 03 (2007). DOI: 10.1520/A0285_A0285M-03R07.10.1520/A0285_A0285M-12.2For ASME Boiler and Pressure Vessel Code applicati

13、ons, see related Specification SA-285/SA-285M in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the

14、 ASTM website.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users co

15、nsult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohock

16、en, PA 19428-2959, United States.requirements in this specification and to the detailed requirements in SpecificationA20/A20Malso establishes the rules for orderinginformation that should be complied with when purchasing plates to this specification.3.3In addition to the basic requirements of this s

17、pecification, certain supplementary requirements are available where additionalcontrol, testing, or examination is required to meet end use requirements.3.4The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements inSpecification A20/A2

18、0M.3.5Coils3.3 Coils are excluded from qualification to this specification until they are processed into finished plate. Platesproduced from coil means plates that have been cut to individual lengths from coil. The processor directly controls, or isresponsible for, the operations involved in the pro

19、cessing of coils into finished plates. Such operations include decoiling, leveling,cutting to length, testing, inspection, conditioning, heat treatment (if applicable), packaging, marking, loading for shipment, andcertification.NOTE 2For plates produced from coil and furnished without heat treatment

20、 or with stress relieving only, three test results are reported for eachqualifying coil. Additional requirements regarding plate produced from coil are described in Specification A20/A20M.3.6If3.4 If the requirements of this specification are in conflict with the requirements of Specification A20/A2

21、0M, therequirements of this specification shall prevail.4. Heat Treatment4.1 Plates are normally supplied in the as-rolled condition. The plates may be ordered normalized or stress relieved, or both.5. Chemical Composition5.1 The steel shall conform to the requirements as to chemical composition as

22、given in Table 1.6. Mechanical Properties6.1 Tension TestThe plates, as represented by the tension test specimens, shall conform to the requirements given in Table 2.7. Keywords7.1 carbon steel plate; low-and-intermediate strength steel plate for pressure vessels; steel plate for pressure vesselsSUP

23、PLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the purchase order.A list of standardized supplementary requirements for use at the option of the purchaser is includedin SpecificationA20/A20M. Those that are considered suitable for use with this specification ar

24、e listedbelow by title.S3. Simulated Post-Weld Heat Treatment of Mechanical Test Coupons, andTABLE 1 Chemical RequirementsElementsComposition, %Grade A Grade B Grade CCarbon, maxA0.17 0.22 0.28Manganese, max:Heat analysis 0.90 0.90 0.90Product analysis 0.98 0.98 0.98Phosphorus, maxA0.035 0.035 0.035

25、Phosphorus, maxA0.025 0.025 0.025Sulfur, maxA0.035 0.035 0.035Sulfur, maxA0.025 0.025 0.025AApplies to both heat and product analyses.TABLE 2 Tensile RequirementsGrade A Grade B Grade Cksi MPa ksi MPa ksi MPaTensile strength 4565 310450 5070 345485 5575 380515Yield strength, minA24 165 27 185 30 205

26、Elongation in 8 in. or 200 mm, min, %B27 25 23Elongation in 2 in. or 50 mm, min, %B30 28 27ADetermined by either the 0.2 % offset method or the 0.5 % extension-under-load method.BSee pecification A20/A20M for elongation adjustment.A285/A285M 122S4. Additional Tension Test.ADDITIONAL SUPPLEMENTARY RE

27、QUIREMENTSAlso listed below are additional optional supplementary requirements suitable for this specification:S57. Copper-BearingS57.1 The copper content, by heat analysis shall be 0.200.35 % and by product analysis 0.180.37 %.S58. Restricted CopperS58.1 The maximum incidental copper content by hea

28、t analysis shall not exceed 0.25 %.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A285/A285M01) that may impact the use of this standard.(1) 1.4, 3.5, and Note 2 were revised to be consistent with the terminology and requirements

29、 of Specification A20/A20M.Committee A01 has identified the location of selected changes to this standard since the last issue(A285/A285M 03 (2007) that may impact the use of this standard. (Approved May 1, 2012.)(1) Table 1 was revised.(2) Section 3 was editorially revised.(3) Section 7 was added.A

30、STM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are

31、entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standard

32、sand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committe

33、e on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A285/A285M 123