ASTM A146-2004(2014) Standard Specification for Molybdenum Oxide Products《氧化钼制品的标准规格》.pdf

《ASTM A146-2004(2014) Standard Specification for Molybdenum Oxide Products《氧化钼制品的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A146-2004(2014) Standard Specification for Molybdenum Oxide Products《氧化钼制品的标准规格》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A146 04 (Reapproved 2014)Standard Specification forMolybdenum Oxide Products1This standard is issued under the fixed designation A146; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number

2、 in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers four grades of molybdenumoxide, designated as A, B1, B2, and molybdic oxide briquets.1.2 The values stated in inch-

3、pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.2. Referenced Documents2.1 ASTM Standards:2A1025 Specification for Ferroalloys and Other AlloyingMaterials, General

4、 Requirements3. General Conditions for Delivery3.1 Materials furnished to this specification shall conform tothe requirements of Specification A1025, including any supple-mentary requirements that are indicated in the purchase order.Failure to comply with the general requirements of Specifica-tion A

5、1025 constitutes nonconformance with this specification.In case of conflict between the requirements of this specifica-tion and Specification A1025, this specification shall prevail.4. Chemical Requirements4.1 The various grades shall conform to the requirements asto chemical composition specified i

6、n Table 1.4.2 The manufacturer shall furnish an analysis of eachshipment showing the percentage of each element specified.5. Sampling5.1 Sampling Small BagsWhen packed in the standard-ized small packages, each holding contained molybdenum, thematerial shall be sampled by selecting at random one twen

7、tiethof the bags that may bear the same manufacturing lot number,and the combined content of these bags shall be reduced andanalyzed as a separate sample. When a shipment cannot bedivided by lot numbers, one twentieth of the total number ofbags constituting the shipment shall be selected and treated

8、 asone sample. The material forming a sample shall be crushed ifnecessary, and in any event passed through a No. 10 (2.00-mm)sieve. The sample after sieving shall be thoroughly mixed byconing and then reduced to about 2 lb (0.9 kg) by quartering orby means of a riffle sampler. The reduced sample sha

9、ll then becrushed and passed through a No. 60 (250-m) sieve. Thesample after sieving shall again be mixed by coning and thendivided through a riffle, preferably a Jones divider, into therequired number of analytical samples.5.2 Sampling Large ContainersWhen packed in drums orlarge bags or cartons, t

10、he material shall be sampled by selectingabout one twentieth of the content of each package that maybear the same manufacturing lot number, and the combinedmaterial selected shall be reduced and analyzed as a separatesample. When a shipment cannot be divided by lot numbers,about one twentieth of the

11、 content of each package in theshipment shall be selected, and the combined material selectedshall be treated as one sample. The material comprising asample shall be thoroughly mixed by coning and reduced byhalf-shoveling, alternating the operations until the residualweight reaches about 40 lb (18.1

12、 kg). Segregation of sizes shallbe carefully avoided. The sample thus reduced shall becrushed, if necessary, to pass through a No. 10 (2.00-mm)sieve, and the subsequent sampling procedure shall be asprescribed in 5.1 .5.3 Correcting Sample to Dry Net WeightAbsorption ofmoisture by the material would

13、 depress the analytical percent-ages with respect to the dry basis, on which the product wasanalyzed when packaged. Accordingly, any analytical sampleshall be dried at 110C, before analysis, and the samplersmoist net weight of the shipment, of a manufacturing lot, or ofany constituent package shall

14、be appropriately corrected to thecorresponding dry weight, thus leading to the proper weight ofcontained molybdenum.6. Keywords6.1 molybdenum; molybdenum oxide1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibil

15、ity of SubcommitteeA01.18 on Castings.Current edition approved Oct. 1, 2014. Published October 2014. Originallyapproved in 1932. Last previous edition approved in 2009 as A146 04(2009).Replaces A146 63 T. DOI: 10.1520/A0146-04R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org,

16、orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1SUPPLEMENTARY REQ

17、UIREMENTSS1. The composition shall be further limited by the requirements of Table S1.1 in addition to thosein Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressl

18、y advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, e

19、ither reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may atte

20、nd. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. I

21、ndividual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secur

22、ed from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Chemical RequirementsMolybdenum OxideMolybdicOxideBriquetsGrade A Grade B1 Grade B2Molybdenum, min 55.0 57.0 57.0 51.6Sulfur, max 0.25 0.10 0.10 0.15Copper, max 1.0 1.0 0.15 0.15TABLE S1.1 Sup

23、plementary Chemical RequirementsComposition, %AMolybdenum OxideMolybdic OxideBriquetsGrade AGrade B1 andB2CarbonPhosphorus, maxtrace0.050trace0.05012.0 (approx)0.050AThe values shown are maxima. Upon request of the purchaser, the manufacturershall furnish an analysis for any of these elements on a cumulative basis over aperiod mutually agreed upon by the manufacturer and the purchaser. An analysisof each lot is not required.A146 04 (2014)2