1、Designation: A1069/A1069M 11Standard Specification forLaser-Fused Stainless Steel Bars, Plates, and Shapes1This standard is issued under the fixed designation A1069/A1069M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year o

2、f last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers laser-fused stainless steel bars,plates, and shapes of structural quality for use in bolte

3、d orwelded structural applications.1.2 Shapes covered in this specification include those clas-sified in Article 3.1.2 of Specification A6/A6M and those thatare made from two or more shapes or plates.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standar

4、d. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associ

5、ated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A6/A6M Specification for General Requirements for RolledStr

6、uctural Steel Bars, Plates, Shapes, and Sheet PilingA240/A240M Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for PressureVessels and for General ApplicationsA262 Practices for Detecting Susceptibility to IntergranularAttack in Austenitic Stainless SteelsA276

7、Specification for Stainless Steel Bars and ShapesA370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA479/A479M Specification for Stainless Steel Bars andShapes for Use in Boilers and Other Pressure VesselsA484/A484M Specification for General Requirements forStainless Steel Bars

8、, Billets, and ForgingsA673/A673M Specification for Sampling Procedure forImpact Testing of Structural SteelA700 Practices for Packaging, Marking, and Loading Meth-ods for Steel Products for ShipmentA751 Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel ProductsA923 Test Metho

9、ds for Detecting Detrimental IntermetallicPhase in Duplex Austenitic/Ferritic Stainless SteelsA941 Terminology Relating to Steel, Stainless Steel, Re-lated Alloys, and FerroalloysE190 Test Method for Guided Bend Test for Ductility ofWeldsE208 Test Method for Conducting Drop-Weight Test toDetermine N

10、il-Ductility Transition Temperature of FerriticSteelsE290 Test Methods for Bend Testing of Material for Duc-tility2.2 ISO Standards:ISO 13919-1 Welding and laser-beam welded joints-Guidance on quality levels for imperfections- Part 1:Steel.ISO 15609-4 Specification and qualification of weldingproced

11、ures for metallic materials. Welding procedurespecification.ISO 15614-11 Specification and qualification of weldingprocedures for metallic materials- Welding proceduretest-Part 11: Electron and laser beam welding.2.3 U.S. Military Standards:MIL-STD-129 Marking for shipment and storage.2.4 Federal St

12、andards:Federal Standard No. 123 Marking for Shipment (CivilAgencies).3. Terminology3.1 Definitions:3.1.1 Definitions of terms pertaining to this specificationshall be those of Terminology A941, “Standard TerminologyRelating to Steel, Stainless Steel, Related Alloys, and Ferroal-loys.”3.2 Definition

13、s of Terms Specific to This Standard:1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled and Wrought Stainless Steel.Current edition approved Jan. 15, 2011. Published Jan

14、uary 2011. DOI: 10.1520/A1069_A1069M11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM Intern

15、ational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.3.3 laser fusion, na joining process that produces coales-cence of material with the heat obtained from the application ofa concentrated coherent light beam impinging on the surface ofa weld joint.4. Orderin

16、g Information4.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Such requirements may include but are notlimited to the following:4.1.1 Name of structural product (plate, shape, bar, or sheetpiling).4.1.2 Shape de

17、signation and applicable dimensions includ-ing size, thickness, width, diameter, and length.4.1.3 Type or UNS designation as specified in Table 1 ofSpecification A240/A240M.4.1.4 Quantity (weight or number of pieces).4.1.5 Special packaging, marking, and loading for shipmentrequirements, if any.4.1.

18、6 ASTM specification designation and edition year ifother than the latest edition.4.1.7 Condition, whether stress-relieved, heat treated, or aswelded.4.1.8 Finish.4.1.9 Supplementary Requirements, when invoked.4.1.10 Preparation for delivery.4.1.11 Marking requirements.4.1.12 Special requirements.NO

19、TE 1A typical ordering description is as follows: 5000 lb (2300kg), Angle, L4 3 4 312 in. (L100 3 100 3 13mm), laser fused, 20 ft (6m) in length, Type 304L, ASTM Specification AXXXX dated _.5. Materials and Manufacture5.1 Condition:5.1.1 Parent materials shall be in accordance to the require-ments o

20、f Specifications A240/A240M.5.1.2 Laser-fused section materials shall conform to therequirements of Specifications A276 or A479/A479M.5.1.3 Bars and shapes shall be in the as-fused condition.5.1.4 Fusion weld process shall comply with ISO 15614-11and ISO 15609-4 standards.5.1.5 The quality levels of

21、 welded joints shall be in accor-dance with ISO 13919-1 standard. If not otherwise specified,quality level B of ISO 13919-1 standard shall be met.5.1.6 The tensile strength of the fusion weldment conductedon coupons excised from the laser fused stainless steel plates,as shown in Fig. 1, shall meet o

22、r exceed those specified inSpecificationsA240/A240M,A276,orA479/A479M when anyof those materials are specified in the purchase order. Tensiletesting and specimen dimensions shall be in accordance withTest Methods A370.5.1.7 Bend tests in accordance with Article 14 of TestMethods A370 shall be conduc

23、ted for evaluating the ductilityof the fusion weldment. Test coupons shall be excised from thelaser fused stainless steel plates in accordance with Fig. 1. Theinside diameter for root bend test specimens shall meet thevalue(s) stipulated in the application specification, or thespecific requirements

24、of the purchase order. Root bend testsshall be conducted, removing any flash or melt-through at theroots of the weld, and shall be in accordance with either TestMethods E190 or E290, depending on the thickness of thematerial and the purchasers application. Lack of penetration orthe presence of crack

25、s, visible to persons with normal orcorrected vision, shall be cause for rejection of the weldments.6. Chemical Composition6.1 The steel shall conform to the requirements for chemicalcomposition specified in Table 1 of Specifications A240/A240M, A276 and A479/A479M.6.2 Methods and practices relating

26、 to chemical analysisrequired by this specification shall be in accordance with TestMethods, Practices, and Terminology A751.FIG. 1 Butt-Welded Test Pieces Are Laser-Fusion Welded and Then Subsequently Machined Into Tensile Test Bars and Root-Bend TestSpecimens (Not to Scale)A1069/A1069M 1127. Mecha

27、nical Properties7.1 The product shall conform to the mechanical test re-quirements specified in Table 2 of Specifications A240/A240M, A276,orA479/A479M.8. Dimensions, Mass, and Permissible Variations8.1 The permitted variations in dimensions shall conform tothe requirements of Section 9 of Specifica

28、tion A484/A484M.9. Quality, Finish, and Appearance of the Laser-FusedProduct9.1 The product shall be of uniform quality consistent withgood manufacturing and inspection practices. Imperfections inthe product shall be of such a nature or degree for the type andquality ordered that they shall not adve

29、rsely affect the forming,machining, or fabrication of finished parts.10. Packaging, Marking, and Loading for Shipment10.1 Packaging, marking, and loading for shipment shall bein accordance with Practices A700.10.2 When specified in the contract or order and for directprocurement by or direct shipmen

30、t to the U.S. Government,marking for shipment, in addition to requirements specified inthe contract or order, shall be in accordance with MIL-STD-129 for military agencies and with Federal Standard No. 123for civil agencies.11. Keywords11.1 joining; laser-fusion; laser-weld; plates; shapes;stainless

31、SUPPLEMENTARY REQUIREMENTSThe following standardized supplementary requirements are for use when desired by the purchaser.Those that are considered suitable for use with each material specification are listed in thespecification. Other tests may be performed by agreement between the supplier and the

32、 purchaser.These additional requirements shall apply only when specified in the order, in which event thespecified tests shall be made by the manufacturer or processor before shipment of the material.Charpy V-Notch Impact Test for Structural ShapesS1.1 Charpy V-notch impact tests shall be conducted

33、inaccordance with Specifications A673/A673M and Test Meth-ods A370.S1.2 The frequency of testing, the test temperature to beused, and the absorbed energy requirements shall be asspecified on the order. Unless otherwise specified in thepurchase order, the minimum average absorbed energy for eachtest

34、shall be 20 ft 3 lbf 27 J and the test temperature shall be70F 20C.Drop-Weight Test (for Material 0.625 in. 16 mm andOver in Thickness)S2.1 Drop-weight tests shall be made in accordance withTest Method E208. The specimens shall represent the materialin the final condition of heat treatment. Agreemen

35、t shall bereached between the purchaser and the manufacturer or pro-cessor as to the number of pieces to be tested and whether amaximum nil-ductility transition (NDT) temperature is man-datory or if the test results are for information only.Intergranular Corrosion TestS3.1 For shapes fabricated from

36、 austenitic stainless steels,tests for the presence of undesirable precipitate phases orsusceptibility of the weld joint to intergranular corrosion shallbe made by cutting and fabricating coupons obtained from thewelded test pieces, and exposing them to one or more of thepractice reagents described

37、in Practices A262. The purchasershall prescribe which particular practice(s) shall be followed inthe purchase order.S3.2 For shapes fabricated from duplex austenitic/ferriticstainless steels, tests for the presence of undesirable phases inthe weld joint shall be made by cutting and fabricating coupo

38、nsobtained from the welded test pieces, and testing them per therequirements of Test Methods A923. The purchaser shallprescribe which particular test method(s) shall be followed inthe purchase order.S3.3 The producer shall provide a report of the test resultsfor certification and acceptance of the w

39、eld joints to thepurchaser prior to shipment of the product.A1069/A1069M 113ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validit

40、y of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comment

41、s are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not

42、 received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copi

43、es) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A1069/A1069M 114