ASTM A1030 A1030M-2011 Standard Practice for Measuring Flatness Characteristics of Steel Sheet Products《薄钢板制品的的平整度特征测量标准实施规范》.pdf

《ASTM A1030 A1030M-2011 Standard Practice for Measuring Flatness Characteristics of Steel Sheet Products《薄钢板制品的的平整度特征测量标准实施规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A1030 A1030M-2011 Standard Practice for Measuring Flatness Characteristics of Steel Sheet Products《薄钢板制品的的平整度特征测量标准实施规范》.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A1030/A1030M 11Standard Practice forMeasuring Flatness Characteristics of Steel Sheet Products1This standard is issued under the fixed designation A1030/A1030M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year

2、of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 Flatness is a significant quality characteristic of steelsheet products. Sheet flatness is affected by mill proces

3、s factorsplus the grade, thickness and width of the material supplied. Itis the purpose of this practice to define the different flatnesscharacteristics and to describe the method(s) most commonlyused to measure particular characteristics. The methods de-scribed are designed and intended to be used

4、in mill situationsand environments.1.2 The substrate shall conform to all the requirements ofthe appropriate specifications as follows: Specifications A568/A568M or A924/A924M.1.3 Quantitative limits are not addressed and are establishedin the general requirements, or individual product specifica-ti

5、ons, or both; or when applicable, as agreed to betweensupplier and user.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other.

6、 Combiningvalues from the two systems may result in non-conformancewith the standard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices an

7、d determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A568/A568M Specification for Steel, Sheet, Carbon, Struc-tural, and High-Strength, Low-Alloy, Hot-Rolled andCold-Rolled, General Requirements forA924/A924M Specification for General Requi

8、rements forSteel Sheet, Metallic-Coated by the Hot-Dip Process3. Significance and Use3.1 The definitions and procedures for measuring flatnesscharacteristics of steel sheet products are provided so thatpurchasers and suppliers have common definitions and mea-suring procedures for flatness characteri

9、stics. The intention ofthese definitions and measuring methods is not to provide adimensional specification for flatness characteristics, but rathercommon procedure(s) for quantifying flatness anomalies. Fordetermining compliance with flatness specifications, referencesare provided to appropriate AS

10、TM standards.4. Interferences4.1 Measurement of flatness often has been subjective, atbest. Successful measurement of various flatness anomalies onquantitative terms requires recognition of several factors thatcan interfere with accurate measurements.4.1.1 Flat surfaces are required. Measurement of

11、severalanomalies requires laying of the sample, or a coil area, on arecognized flat surface. In most cases, laying the sample, or acoil area, on a floor will produce satisfactory results, as long asthe floor is recognized as being flat. The flatness of coil areas1This practice is under the jurisdict

12、ion of ASTM Committee A05 on Metallic-Coated Iron and Steel Products and is the direct responsibility of SubcommitteeA05.07 on Methods of Testing.Current edition approved May 1, 2011. Published May 2011. Originallyapproved in 2003. Last previous edition approved in 2005 as A1030/A1030M - 05.DOI: 10.

13、1520/A1030_A1030M-11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears a

14、t the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.is also measured on the flat tables of coil processing lines, withthe strip tension released. If the measuring surface is notrecognized as being flat, a machin

15、ed flat surface is recom-mended.4.1.2 Stepblock gauges or tapered gauges should bechecked regularly with a calibrated hand micrometer. Wear ordirt build up will affect accuracy.4.1.3 The flat tables of shape gauges capable of measuringflatness characteristics must be clean and the sensors must bein

16、good condition.4.1.4 The sheet sample must be damage free.5. Apparatus5.1 Appropriate tools to measure flatness anomalies aredescribed along with drawings as indicated.5.1.1 Flat SurfacesAccurate measurements of flatnessanomalies require a flat surface, machined flat preferred.5.1.2 Machined Stepblo

17、ck GaugeSee Fig. 1. Typicallysteps are in116 in. 1 mm increments.5.1.3 Tapered GaugeSee Fig. 2.5.1.4 Standard Ruler or Tape Measure.5.1.5 Hand Micrometer.5.1.6 Lightweight StraightedgeRigid, but light enoughnot to affect the test result.6. Procedure6.1 Wavy Edge (see Fig. 3):6.1.1 DefinitionA series

18、 of rolling direction edge devia-tions or undulations of the sheet from a recognized flat surface,having a height (H) and a measurable cycle length (L).6.1.2 Measuring Methods:6.1.2.1 With a sheet sample, or coil area, of at least 4 ft 1.2m in length by coil width on a recognized flat surface, measu

19、rethe height (H) at the peak point of each wave from therecognized flat surface with a ruler, tape measure, taperedgauge, or stepblock gauge. Also measure the cycle length (L)from peak to peak of each wave with a ruler or tape measure.6.1.3 Permissible Variations6.1.3.1 The height (H) of the highest

20、 peak measured inaccordance with 6.1.2.1 shall comply with applicable limits,such as found in the tables on flatness tolerances of Specifica-tions A568/A568M or A924/A924M. Note that the referencedtables apply to cut sheet that has received adequate flattening.While the wavy edge height result from

21、a coil area stillattached to a coil is a reasonable indication of flatness, it is notbound by the limits of the referenced tables.6.1.3.2 As stated in the section on flatness tolerances ofSpecifications A568/A568M or A924/A924M, I-Unit and %Steepness rejection limits are subject to agreement between

22、producer and purchaser. Using the procedures ofAppendix X1,and the readings from 6.1.2.1, determine the I-Unit and %Steepness values, first using the distance between the twohighest peaks, and second using the distance between twoadjacent peaks. The highest I-Unit and % Steepness valuesobtained from

23、 these two situations shall be used to determineif the specification has been met.6.1.3.3 If the I-Unit and % Steepness values are supplieddirectly using a shape gauge; determine if the results are withinthe maximum specified values.6.2 Ridge Buckle, Quarter Buckle, Center Buckle (see Fig.4):6.2.1 D

24、efinitionBuckles are continuous deviations from arecognized flat surface, having a height (H) and a measurablecycle (L), and usually occur in narrow width areas parallel tothe rolling direction other than at the sheet edges.6.2.2 Measuring Methods:6.2.2.1 With a sheet sample, or coil area, of at lea

25、st 4 ft 1.2m by coil width resting on a recognized flat surface, place alightweight straightedge on the highest portion of a buckle andon the highest portion of the next repeating buckle. Measurethe height (H) between the straightedge and a strip using aruler, tape measure, tapered gauge, or stepblo

26、ck gauge. Mea-sure the cycle length (L) from peak to peak of each buckle witha ruler or tape measure.6.2.2.2 In the case of a sheet sample, it is permissible toshear through the centerline of the flatness anomaly andmeasure as an edge wave (see 6.1.2.1) using a ruler, tapemeasure, tapered gauge, or

27、stepblock gauge.6.2.3 Permissible Variations6.2.3.1 The height (H) of the highest peak measured inaccordance with 6.2.2.1 or 6.2.2.2 shall comply with applicablelimits, such as found in the tables on flatness tolerances ofSpecifications A568/A568M or A924/A924M. Note that thereferenced tables apply

28、to cut sheet that has received adequateflattening. While the buckle height result from a coil area stillNOTE 1Stepblock gauge for all thicknesses and sizes of cut sheets.NOTE 2Dimensions given are approximate overall dimensions.FIG. 1 Flatness Stepblock GaugeA1030/A1030M 112attached to a coil is a r

29、easonable indication of flatness, it is notbound by the limits of the referenced tables.6.2.3.2 As stated in the section on flatness tolerances ofSpecifications A568/A568M or A924/A924M, I-Unit and %Steepness rejection limits are subject to agreement betweenproducer and purchaser. Using the procedur

30、es ofAppendix X1,and the readings from 6.2.2.1 or 6.2.2.2, determine the I-Unitand % Steepness values, first using the distance between thetwo highest peaks, and second using the distance between twoadjacent peaks. The highest I-Unit and % Steepness valuesobtained from these two situations shall be

31、used to determineif the specification has been met.6.2.3.3 If the I-Unit and % Steepness values are supplieddirectly using a shape gauge; determine if the results are withinthe maximum specified values.6.3 Full Center (see Fig. 5):6.3.1 DefinitionAny overall deviation of a sheet from arecognized fla

32、t surface, having a height (H) and a measurablecycle (L), and occurring over a major portion of the sheet widthparallel to the rolling direction other than at the sheet edges.6.3.2 Measuring Methods:6.3.2.1 With a sheet sample, or a coil area, of at least 4 ft1.2 m by coil width resting on a recogni

33、zed flat surface, placea lightweight straightedge on the highest portion of a full centerregion and on the highest portion of the next repeating regionof full center. Measure the height (H) between the straightedgeand the strip using a ruler, tape measure, tapered gauge, orstepblock gauge. Measure t

34、he cycle length (L) from peak topeak of a full center region with a ruler or tape measure.NOTE 1Tapered gauge for all thicknesses and sizes of cut sheets.FIG. 2 Flatness Tapered GaugeFIG. 3 Wavy EdgeFIG. 4 Ridge Buckle, Quarter Buckle, Center BuckleA1030/A1030M 1136.3.2.2 In the case of a sheet samp

35、le, it is permissible toshear through the centerline of the flatness anomaly andmeasure as an edge wave (see 6.1.2.1) using a ruler, tapemeasure, tapered gauge, or stepblock gauge.6.3.3 Permissible Variations6.3.3.1 The height (H) of the highest peak measured inaccordance with 6.3.2.1 or 6.3.2.2 sha

36、ll comply with applicablelimits, such as found in the tables on flatness tolerances ofSpecifications A568/A568M and A924/A924M. Note that thereferenced tables apply to cut sheet that has received adequateflattening. While the buckle height result from a coil area stillattached to a coil is a reasona

37、ble indication of flatness, it is notbound by the limits of the referenced tables.6.3.3.2 As stated in the section on flatness tolerances ofSpecifications A568/A568M or A924/A924M, I-Unit and %Steepness rejection limits are subject to agreement betweenproducer and purchaser. Using the procedures ofA

38、ppendix X1,and the readings from 6.3.2.1 or 6.3.2.2, determine the I-Unitand % Steepness values, first using the distance between thetwo highest peaks, and second using the distance between twoadjacent peaks. The highest I-Unit and % Steepness valuesobtained from these two situations shall be used t

39、o determineif the specification has been met.6.3.3.3 If the I-Unit and % Steepness values are supplieddirectly using a shape gauge; determine if the results are withinthe maximum specified values.6.4 Coil Set and Reverse Coil Set (see Fig. 6):6.4.1 DefinitionA bow condition in the sheet, parallelwit

40、h the rolling direction, as measured from a recognized flatsurface. Coil set (also known as positive coil set) curvesdownward in the same direction as the upper outside lap of anoverwound coil. Reverse coil set (also known as negative coilset) curves upward, opposite to the curvature of the upperout

41、side lap of an overwound coil.6.4.2 Measuring Methods:6.4.2.1 For coil set, place a sheet sample of approximately 4ft 1.2 m by coil width on a recognized flat surface. Measurethe highest rise (H) of the sheet edges from the flat surface. Usea ruler accurate to116 in. 1 mm.6.4.2.2 For reverse coil se

42、t, place an adequately leveledsheet sample of approximately 4 ft 1.2 m by coil width on arecognized flat surface. Measure the highest rise (H) of the cutend(s) of the sheet from the flat surface. Use a ruler accurate to116 in. 1 mm.6.4.3 Permissible Variations6.4.3.1 The height (H) of the highest de

43、viation measured inaccordance with 6.4.2.1 or 6.4.2.2 shall comply with applicablelimits, such as found in the tables on flatness tolerances ofSpecifications A568/A568M or A924/A924M, or a valueagreed upon between the producer and purchaser.6.5 Crossbow and Reverse Crossbow (see Fig. 7):6.5.1 Defini

44、tionA bow condition in the sheet, perpendicu-lar to the rolling direction as measured from a recognized flatsurface. Crossbow (also known as positive crossbow) curvesdownward, with the center portion of the sheet raised ameasurable amount (H) above the sheet edges. Reverse cross-bow (also known as n

45、egative crossbow) curves upward, withthe edges of the sheet raised a measurable amount (H) abovethe center portion of the sheet. The degree of cross bow isdetermined in a horizontal position on a recognized flatsurface.6.5.2 Measuring Methods:6.5.2.1 For crossbow, place a sheet sample, or coil area,

46、 ofapproximately 4 ft 1.2 m by coil width on a recognized flatsurface. Measure the highest rise (H) of the center of the sheetfrom the flat surface. Use a ruler accurate to116 in. 1 mm.6.5.2.2 For reverse crossbow, place an adequately leveledsheet sample, or coil area, of approximately 4 ft 1.2 m by

47、 coilwidth on a recognized flat surface. Measure the highest rise (H)of the edges of the sheet from the flat surface. Use a ruleraccurate to116 in. 1 mm or a lightweight straightedge asrequired.6.5.3 Permissible Variations6.5.3.1 The height (H) of the highest deviation measured inaccordance with 6.5

48、.2.1 or 6.5.2.2 shall comply with applicablelimits, such as found in the tables on flatness tolerances ofSpecifications A568/A568M or A924/A924M, or a valueagreed upon between the producer and purchaser.6.6 Camber (see Fig. 8):6.6.1 DefinitionThe greatest deviation of a coil edge froma straight line

49、. The measurement is taken on the concave sideFIG. 5 Full CenterA1030/A1030M 114and is the perpendicular distance from a straight line to thepoint of maximum deviation (A).6.6.2 Measuring Methods:6.6.2.1 Lay a sample of at least 20 ft 6 m next torecognized straightedge. The perpendicular distance (A) ismeasured using a ruler accurate to116 in. 1 mm.6.6.2.2 Cut two 20 ft 6 m consecutive sections from themaster coil. Butt together the sections lengthwise with thesame edges together. At a 10 ft 3 m distance from the end,measure the d