API TR 938-B-2008 Use of 9Cr-1Mo-V (Grade 91) Steel in the Oil Refining Industry (First Edition)《炼油工业中使用9Cr-1Mo-V(91级)钢.第1版》.pdf

《API TR 938-B-2008 Use of 9Cr-1Mo-V (Grade 91) Steel in the Oil Refining Industry (First Edition)《炼油工业中使用9Cr-1Mo-V(91级)钢.第1版》.pdf》由会员分享，可在线阅读，更多相关《API TR 938-B-2008 Use of 9Cr-1Mo-V (Grade 91) Steel in the Oil Refining Industry (First Edition)《炼油工业中使用9Cr-1Mo-V(91级)钢.第1版》.pdf（57页珍藏版）》请在麦多课文档分享上搜索。

1、Use of 9Cr-1Mo-V (Grade 91) Steel in the Oil Refining IndustryAPI TECHNICAL REPORT 938-B FIRST EDITION, JUNE 2008Use of 9Cr-1Mo-V (Grade 91) Steel in the Oil Refining IndustryDownstream SegmentAPI T ECHNICAL REPORT 938-B FIRST EDITION, JUNE 2008Special NotesAPI publications necessarily address probl

2、ems of a general nature. With respect to particular circumstances, local, state, and federal laws and regulations should be reviewed.Neither API nor any of APIs employees, subcontractors, consultants, committees, or other assignees make any war-ranty or representation, either express or implied, wit

3、h respect to the accuracy, completeness, or usefulness of the information contained herein, or assume any liability or responsibility for any use, or the results of such use, of any information or process disclosed in this publication. Neither API nor any of APIs employees, subcontractors, consult-a

4、nts, or other assignees represent that use of this publication would not infringe upon privately owned rights.API publications may be used by anyone desiring to do so. Every effort has been made by the Institute to assure the accuracy and reliability of the data contained in them; however, the Insti

5、tute makes no representation, warranty, or guarantee in connection with this publication and hereby expressly disclaims any liability or responsibility for loss or damage resulting from its use or for the violation of any authorities having jurisdiction with which this publication may conflict.API p

6、ublications are published to facilitate the broad availability of proven, sound engineering and operating practices. These publications are not intended to obviate the need for applying sound engineering judgment regarding when and where these publications should be utilized. The formulation and pub

7、lication of API publications is not intended in any way to inhibit anyone from using any other practices.Any manufacturer marking equipment or materials in conformance with the marking requirements of an API standard is solely responsible for complying with all the applicable requirements of that st

8、andard. API does not represent, war-rant, or guarantee that such products do in fact conform to the applicable API standard.All rights reserved. No part of this work may be reproduced, stored in a retrieval system, or transmitted by any means, electronic, mechanical, photocopying, recording, or othe

9、rwise, without prior written permission from the publisher. Contact the Publisher, API Publishing Services, 1220 L Street, N.W., Washington, D.C. 20005.Copyright 2008 American Petroleum InstituteForewordThis recommended practice is under the jurisdiction of the API Subcommittee on Fiberglass and Pla

10、stic Tubulars.For the purposes of this recommended practice the following definitions are applicable:Shall: as used in a standard, “shall” denotes a minimum requirement in order to conform to the specification. Should: as used in a standard, “should” denotes a recommendation or that which is advised

11、 but not required in order to conform to the specification. May: as used in a standard, “may” denotes that a recommendation is optional.Nothing contained in any API publication is to be construed as granting any right, by implication or otherwise, for the manufacture, sale, or use of any method, app

12、aratus, or product covered by letters patent. Neither should anything contained in the publication be construed as insuring anyone against liability for infringement of letters patent.This document was produced under API standardization procedures that ensure appropriate notification and participati

13、on in the developmental process and is designated as an API standard. Questions concerning the interpretation of the content of this publication or comments and questions concerning the procedures under which this publication was developed should be directed in writing to the Director of Standards,

14、American Petroleum Institute, 1220 L Street, N.W., Washington, D.C. 20005. Requests for permission to reproduce or translate all or any part of the material published herein should also be addressed to the director.Generally, API standards are reviewed and revised, reaffirmed, or withdrawn at least

15、every five years. A one-time extension of up to two years may be added to this review cycle. Status of the publication can be ascertained from the API Standards Department, telephone (202) 682-8000. A catalog of API publications and materials is published annually and updated quarterly by API, 1220

16、L Street, N.W., Washington, D.C. 20005.Suggested revisions are invited and should be submitted to the Standards Department, API, 1220 L Street, NW, Washington, D.C. 20005, standardsapi.org.iiiContentsPage1 Scope . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

17、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .12 Terms, Definitions, Acronyms, and Symbols . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .12.1 Terms and Definitions . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

18、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .12.2 Acronyms . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .12.3 Symbols. . . . . . . . . . . . . . . . . . . . . . . .

19、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .33 Base Metal Chemical, Physical, Mechanical and Metallurgical Properties . . . . . . . . . . . . . . . . . . . . . . . .33.1 General. . . . . . . . . . . . . . . . . . . . . . . . . . . . .

20、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .33.2 Chemical Composition . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .33.3 Physical Properties . . . . . . . . .

21、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .33.4 Metallurgical Properties. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .73.5 Mechanical Prop

22、erties . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .144 Metallurgy and Environmental Related Failure Mechanisms . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .214.1 Oxidation and Sulfidation Res

23、istance . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .214.2 Wet Hydrogen Sulfide Cracking . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .214.3 Hydrogen Attack Resistance. .

24、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .224.4 Hydrogen Embrittlement, Hydrogen Diffusivity and Trapping . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .224.5 Temper Embrittlement . . . . . . . . . . . . . .

25、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .224.6 Type IV Cracking. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .225 Material Requirements. . . .

26、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .235.1 Base Metal . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .235.2 Wel

27、ding Consumables. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .236 Fabrication and Welding Requirements . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .276.1 Gener

28、al Concerns. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .276.2 Cold Bending . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

29、 . . . . . . .276.3 Hot Bending . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .286.4 Welding . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

30、 . . . . . . . . . . . . . . . . . . . . . . . .287 Examples of 9Cr-1Mo-V Applications and Refinery Experiences. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .367.1 Experiences. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

31、 . . . . . . . . . . . . . . . . . . .367.2 Applications . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .36Bibliography. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

32、. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 40Figures1 Thermal Conductivity. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .42 Mean Coefficient of Linear Expansion. . . . . . . . . . .

33、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .63 Modulus of Elasticity vs. Temperature. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .74 Deep Hardening Behavior of Grade 91 Steel. . . . . . . . . . . .

34、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .85 Effect of Ni + Mn on AC1. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .96 CCT Diagram of Grade 91 Steel . . . . . . . . . . . . . . . . . . .

35、 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .97 Typical Microstructure of T/P91 After Normalizing and Tempering . . . . . . . . . . . . . . . . . . . . . . . . . . . . .108 Grain Coarsening Behavior. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

36、 . . . . . . . . . . . . . . . . . . . . . . . . . . . .139 Typical Plot of Hardness vs. Tempering Temperature for Heat Rolled and Normalized Grade 91 Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .1410 Yield (0.2 %) and Ult

37、imate Tensile Strengths vs. Temperature for Grade 91 Alloy Steel . . . . . . . . . . . .1511 Charpy Impact Energy vs. Temperature of Grade 91 Alloy Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .1712 Stress Rupture Strength of Commercial Heats of N + T Grade 91 Alloy Steel at 593

38、 C (1100 F) . . . .2013 Comparison of Creep Rupture Strength of Grade 91 Steel Weldments to Base Metal . . . . . . . . . . . . .21vPage14 Hardness Profile of Grade 91 Weldment with Type IV Soft Zone . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .2315 Effect of Oxygen Content on Toughne

39、ss for Selected Grade 91 Weldments . . . . . . . . . . . . . . . . . . . . .2616 Influence of PWHT Temperature on Toughness of Grade 91 Filler Metal . . . . . . . . . . . . . . . . . . . . . . . .3317 Influence of PWHT Temperature and Holding Time on Hardness of Grade 91 SMAW Weld Metal. . . .34Tabl

40、es1 Specifications and Code Cases for 9Cr-1Mo-V Steels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .42 Chemical Composition (Heat Analysis) of 9Cr-1Mo-V and 9Cr-1Mo Steels. . . . . . . . . . . . . . . . . . . . . . . .53 Physical Properties of T/P91 Alloy vs. Temp

41、erature . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .64 Heat Treatment and Mechanical Properties of 9Cr-1Mo-V Steel and 9Cr-1Mo Steel . . . . . . . . . . . . . . .115 Temperature Limits for 9Cr-1Mo-V Steel per ASME Section VIII, Division 1 (Section II, Part D) .

42、 . . . . .166 Temperature Limits of 9Cr-1Mo-V Steel per Section VIII, Division 2 (Section II, Part D) . . . . . . . . . . . .167 Maximum Allowable Stress Values “S” in ASME Section VIII, Division 1, for 9Cr-1Mo-V Steel in Comparison with 2 1/4 Cr-1Mo-V, 2 1/4 Cr-1Mo 9Cr-1Mo Alloy Steels and 316H Sta

43、inless Steel . . . .188 Design Stress Intensity Values “Sm” in ASME Section III, Division 2, for 9Cr-1Mo-V Steel in Comparison with 2 1/4 Cr-1Mo, 2 1/4 Cr-1Mo-V, 9Cr-1Mo Steels and 316 H Stainless Steel . . . . . . . . 199 Creep Rupture of ASTM A213 Grade T91 Steel. . . . . . . . . . . . . . . . . .

44、 . . . . . . . . . . . . . . . . . . . . . . . . . . . .2010 Compositional Specifications of 9Cr-1Mo-V Steels Weld Consumables. . . . . . . . . . . . . . . . . . . . . . . . .2411 Dissimilar Welding Filler Metal Selection for 9Cr-1Mo-V Steels . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

45、 . . .3512 Guideline for PWHT Temperature for Dissimilar Metal Welds. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .3513 Case Histories of Grade 91 Refinery Uses Reported in NACE REFIN-COR . . . . . . . . . . . . . . . . . . . . . .3714 Additional Case History for Using Grade P91/

46、T91 Steel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .38IntroductionAlloy steel 9Cr-1Mo-V was initially developed in the 1950s by the ORNL for the Clinch River Breeder Reactor. In 1974, a task force was initiated by the U.S. Department of Energy (DOE) to select materia

47、ls for the Liquid Metal Fast Breeder Reactor Program (LMFBR). ORNL assisted by Combustion Engineering, initiated a program to develop a 9Cr-1Mo steel for 512 C (970 F) service temperature and with toughness of 54 J (40 ft-lbs) at room temperature 36, 37. This was achieved through the controlled addi

48、tions of vanadium (V), Nb and nitrogen (N) to become Grade 91. Later, the carbon content in Grade 91 was lowered to the range of 0.08 % to 0.12 % from 0.15 % maximum specified for the standard 9Cr-1Mo steel.In the 1980s, it was recognized that the elevated temperature mechanical properties of Grade

49、91 made it a viable candidate for utility boiler applications. Code Case 1943 20 approved on July 20, 1983, permitted the use of Grade 91 for Section I construction. The 9Cr-1Mo-V alloy steels are now included in Section II, Part D for ASME Section VIII, Division 1 2, applications up to 649 C (1200 F) but their use is not permitted in ASME Section VIII, Division 2 4, except as allowed by Code Case 1973-2 22. This alloy also has allowable stresses about 50 % higher than standard 9Cr-1Mo alloy steel for temperatures up to 510 C (950 F) and the difference is significantly m