《ASTM A789A789M-17a Standard Specification for Seamless and Welded FerriticAustenitic Stainless Steel Tubing for General Service.pdf》由会员分享，可在线阅读，更多相关《ASTM A789A789M-17a Standard Specification for Seamless and Welded FerriticAustenitic Stainless Steel Tubing for General Service.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A789/A789M 17aStandard Specification forSeamless and Welded Ferritic/Austenitic Stainless SteelTubing for General Service1This standard is issued under the fixed designation A789/A789M; the number immediately following the designation indicates the yearof original adoption or, in the ca

2、se of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification2covers grades of average wallthickness, or, if specified on the order,

3、 minimum wallthickness, of stainless steel tubing for services requiringgeneral corrosion resistance, with particular emphasis onresistance to stress corrosion cracking. These steels are suscep-tible to embrittlement if used for prolonged periods at elevatedtemperatures.1.2 The values stated in eith

4、er SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard. Within the text

5、, the SI units are shown inbrackets. The inch-pound units shall apply unless the Mdesignation of this specification is specified in the order.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Pri

6、nciples for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3A480/A480M Specification for General Requirements forFlat-Rolled Stainless and Heat-Resistin

7、g Steel Plate,Sheet, and StripA1016/A1016M Specification for General Requirements forFerritic Alloy Steel, Austenitic Alloy Steel, and StainlessSteel TubesE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)2.2 SAE Standard:4SAE J 1086 Practice for Numbering Metals and

8、Alloys(UNS)3. Ordering Information3.1 Orders for product under this specification should in-clude the following, as required, to describe the desiredmaterial adequately:3.1.1 Quantity (feet, metres, or number of lengths),3.1.2 Name of product (seamless or welded tubes),3.1.3 Grade (see Table 1),3.1.

9、4 Size (outside diameter and average wall thickness,unless minimum wall thickness is specified),3.1.5 Length (specific or random),3.1.6 Optional requirements (for product analysis, see Sec-tion 8; for hydrostatic or nondestructive electric test, seeSection 10),3.1.7 Test report required (see the Ins

10、pection section ofSpecification A1016/A1016M),3.1.8 Specification designation, and3.1.9 Special requirements.4. General Requirements4.1 Product furnished under this specification shall conformto the applicable requirements of Specification A1016/A1016M, unless otherwise provided herein.5. Manufactur

11、e5.1 The tubes shall be made by the seamless or weldedprocess with no filler metal added.6. Heat Treatment6.1 All tubes shall be furnished in the heat-treated conditionin accordance with the procedures shown in Table 2. Forseamless tubes, as an alternate to final heat treatment in acontinuous furnac

12、e or batch-type furnace, immediately follow-ing hot forming while the temperature of the tubes is not less1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.10 on Stainless and Alloy Stee

13、l Tubular Products.Current edition approved Sept. 1, 2017. Published October 2017. Originallyapproved in 1981. Last previous edition approved in 2017 as A789/A789M 17.DOI: 10.1520/A0789_A0789M-17A.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SA789 in Section II

14、of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from Society of Automotive Engineers

15、(SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in acco

16、rdance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1than the specified minimum solu

17、tion treatment temperature,tubes may be individually quenched in water or rapidly cooledby other means.7. Chemical Composition7.1 The steel shall conform to the chemical requirementsprescribed in Table 1.8. Product Analysis8.1 An analysis of either one billet or one length offlat-rolled stock or one

18、 tube shall be made from each heat. Thechemical composition thus determined shall conform to therequirements specified.8.2 A product analysis tolerance (see the annex table onChemical Requirements (Product Analysis Tolerances) inSpecification A480/A480M) shall apply. The product analysistolerance is

19、 not applicable to the carbon content for materialwith a specified maximum carbon of 0.04 % or less.8.3 If the original test for product analysis fails, retests oftwo additional billets, lengths of flat-rolled stock, or tubes shallbe made. Both retests for the elements in question shall meetthe requ

20、irements of this specification; otherwise, all remainingmaterial in the heat shall be rejected or, at the option of theproducer, each billet or tube may be individually tested foracceptance. Billets, lengths of flat-rolled stock, or tubes that donot meet the requirements of this specification shall

21、be re-jected.NOTE 1For flange and flaring requirements, the term lot applies to alltubes prior to cutting of the same nominal size and wall thickness that areproduced from the same heat of steel. When final heat treatment is in abatch-type furnace, a lot shall include only those tubes of the same si

22、zeand from the same heat that are heat treated in the same furnace charge.When the final heat treatment is in a continuous furnace, or when heattreated condition is obtained directly by quenching after hot forming, thenumber of tubes of the same size and from the same heat in a lot shall bedetermine

23、d from the size of the tubes as prescribed in Table 3.NOTE 2For tension and hardness test requirements, the term lotapplies to all tubes prior to cutting, of the same nominal diameter and wallthickness that are produced from the same heat of steel. When final heattreatment is in a batch-type furnace

24、, a lot shall include only those tubes ofthe same size and the same heat that are heat treated in the same furnacecharge. When the final heat treatment is in a continuous furnace, or whenheat treated condition is obtained directly by quenching after hot forming,a lot shall include all tubes of the s

25、ame size and heat, heat treated in thesame furnace at the same temperature, time at heat, and furnace speed, orall tubes of the same size and heat, hot formed and quenched in the sameproduction run.9. Mechanical Tests Required9.1 Tension TestsOne tension test shall be made on aspecimen for lots of n

26、ot more than 50 tubes. Tension tests shallbe made on specimens from two tubes for lots of more than 50tubes (see Note 2).9.2 Flaring Test (for Seamless Tubes)One test shall bemade on specimens from one end of one tube from each lot(see Note 1) of finished tubes. The minimum expansion of theinside di

27、ameter shall be 10 %.9.3 Flange Test (for Welded Tubes)One test shall be madeon specimens from one end of one tube from each lot (see Note1) of finished tubes.TABLE 1 Chemical RequirementsAUNSDesignationBC Mn P S Si Ni Cr Mo N Cu OthersS31200 0.030 2.00 0.045 0.030 1.00 5.56.5 24.026.0 1.202.00 0.14

28、0.20 . . . . . .S31260 0.030 1.00 0.030 0.030 0.75 5.57.5 24.026.0 2.53.5 0.100.30 0.200.80 W 0.100.50S31500 0.030 1.202.00 0.030 0.030 1.402.00 4.35.2 18.019.0 2.503.00 0.050.1 . . . . . .S31803 0.030 2.00 0.030 0.020 1.00 4.56.5 21.023.0 2.53.5 0.080.20 . . . . . .S32001 0.030 4.006.00 0.040 0.030

29、 1.00 1.03.0 19.521.5 0.60 0.050.17 1.00 . . .S32003 0.030 2.00 0.030 0.020 1.00 3.0-4.0 19.5-22.5 1.50-2.00 0.14-0.20 . . . . . .S32101 0.040 4.0-6.0 0.040 0.030 1.00 1.35-1.70 21.0-22.0 0.10-0.80 0.20-0.25 0.10-0.80 . . .S32202 0.030 2.00 0.040 0.010 1.00 1.002.80 21.524.0 0.45 0.180.26 . . . . .

30、.S32205 0.030 2.00 0.030 0.020 1.00 4.56.5 22.023.0 3.03.5 0.140.20 . . . . . .S32304 0.030 2.50 0.040 0.040 1.00 3.05.5 21.524.5 0.050.60 0.050.20 0.050.60 . . .S32506 0.030 1.00 0.040 0.015 0.90 5.57.2 24.026.0 3.03.5 0.080.20 . . . W 0.050.30S32520 0.030 1.50 0.035 0.020 0.80 5.58.0 23.025.0 3.5.

31、 0.200.35 0.503.00 . . .S32550 0.04 1.50 0.040 0.030 1.00 4.56.5 24.027.0 2.93.9 0.100.25 1.502.50 . . .S32707 0.030 1.50 0.035 0.010 0.50 5.59.5 26.029.0 4.05.0 0.300.50 1.0 max Co 0.52.0S32750C0.030 1.20 0.035 0.020 0.80 6.08.0 24.026.0 3.05.0 0.240.32 0.50 . . .S32760D0.030 1.00 0.030 0.010 1.00

32、6.08.0 24.026.0 3.04.0 0.200.30 0.501.00 W 0.501.00S32808 0.030 1.10 0.030 0.010 0.50 7.08.2 27.027.9 0.801.20 0.300.40 . . . W 2.102.50S32900 0.08 1.00 0.040 0.030 0.75 2.55.0 23.028.0 1.002.00 . . . . . . . . .S32906 0.030 0.801.50 0.030 0.030 0.80 5.87.5 28.0 30.0 1.502.60 0.300.40 0.80 . . .S329

33、50 0.030 2.00 0.035 0.010 0.60 3.55.2 26.029.0 1.002.50 0.150.35 . . . . . .S33207 0.030 1.50 0.035 0.010 0.80 6.09.0 29.033.0 3.05.0 0.400.60 1.0 . . .S39274 0.030 1.00 0.030 0.020 0.80 6.08.0 24.026.0 2.53.5 0.240.32 0.200.80 W 1.502.50S39277 0.025 0.80 0.025 0.002 0.80 6.58.0 24.026.0 3.004.00 0.

34、230.33 1.202.00 W 0.801.21S82011 0.030 2.03.0 0.040 0.020 1.00 1.002.00 20.523.5 0.101.00 0.150.27 0.50 . . .S82441 0.030 2.504.00 0.035 0.005 0.70 3.04.5 23.025.0 1.002.00 0.200.30 0.100.80 . . .S83071 0.030 0.501.50 0.030 0.020 0.50 6.08.0 29.031.0 3.04.0 0.280.40 0.80 . . .AMaximum, unless a rang

35、e or minimum is indicated. Where ellipses (.) appear in this table, there is no minimum and analysis for the element need not be determinedor reported.BDesignation established in accordance with Practice E527 and SAE J1086.C%Cr+3.3%Mo+16%N$ 41.D%Cr+3.3%Mo+16%N$ 40.A789/A789M 17a29.4 Hardness TestBri

36、nell or Rockwell hardness tests shallbe made on specimens from two tubes from each lot (see Note2).9.5 When more than one heat is involved, the tension,flaring, flanging, and hardness test requirements shall apply toeach heat.9.6 Reverse Flattening TestFor welded tubes, one reverseflattening test sh

37、all be made on a specimen from each 1500 ft450 m of finished tubing.10. Hydrostatic or Nondestructive Electric Test10.1 Each tube shall be subjected to the nondestructiveelectric test or the hydrostatic test. The type of test to be usedshall be at the option of the manufacturer, unless otherwisespec

38、ified in the purchase order.10.2 The hydrostatic test shall be in accordance with Speci-fication A1016/A1016M, except that in the calculation of thehydrostatic test pressure 64000(441.2) shall be substituted for32000(220.6).11. Tensile and Hardness Properties11.1 The material shall conform to the te

39、nsile and hardnessproperties prescribed in Table 4.12. Permissible Variations in Dimensions12.1 Variations in outside diameter, wall thickness, andlength from those specified shall not exceed the amountsprescribed in Table 5.12.2 The permissible variations in outside diameter given inTable 5 are not

40、 sufficient to provide for ovality in thin-walledtubes, as defined in the table. In such tubes, the maximum andminimum diameters at any cross section shall deviate from thenominal diameter by no more than twice the permissiblevariation in outside diameter given in Table 5; however, themean diameter

41、at that cross section must still be within thegiven permissible variation.13. Surface Condition13.1 All tubes shall be free of excessive mill scale, suitablefor inspection. A slight amount of oxidation will not beconsidered as scale. Any special finish requirements shall besubject to agreement betwe

42、en the manufacturer and the pur-chaser.14. Product Marking14.1 In addition to the marking prescribed in SpecificationA1016/A1016M, the marking shall indicate whether the tubingis seamless or welded and the wall designation (average wall orminimum wall).15. Keywords15.1 duplex stainless steel; ferrit

43、ic/austenitic stainless steel;seamless steel tube; stainless steel tube; steel tube; welded steeltubeTABLE 2 Heat TreatmentUNS Designation Temperature F C QuenchS31200 1920201010501100rapid cooling in waterS31260 1870201010201100rapid cooling in air or waterS31500 180019009801040rapid cooling in air

44、 or waterS31803 1870201010201100rapid cooling in air or waterS32001 180019509821066rapid cooling in air or waterS32003 1850205010101120rapid cooling in air or waterS32101 1870 1020 min quenched in water or rapidlycooled by other meansS32202 1870197510201080rapid cooling in air or waterS32205 1870201

45、010201100rapid cooling in air or waterS32304 170019209251050rapid cooling in air or waterS32506 1870205010201120rapid cooling in air or waterS32520 1975205010801120rapid cooling in air or waterS32550 19001040 minrapid cooling in air or waterS32707 1975205010801120rapid cooling in air or waterS32750

46、1880206010251125rapid cooling in air or waterS32760 1960208510701140rapid cooling in air or waterS32808 1920210010501150rapid cooling in air or waterS32900 17001750925955rapid cooling in air or waterS32906 1870210010201150rapid cooling in air or waterS32950 182018809901025air coolS33207 190520851040

47、1140rapid cooling in wateror by other meansS39274 1920206010251125rapid cooling in air or waterS39277 1975215510801180rapid cooling in air or waterS82011 1850205010101120rapid cooling in air or waterS82441 1830 1000 min rapid cooling in air or waterS83071 1830210010001150rapid cooling in wateror by

48、other meansTABLE 3 Number of Tubes in a Lot Heat Treated by theContinuous Process or by Direct Quench after Hot FormingSize of Tube Size of Lot2 in. 50.8 mm and over in outside diameterand 0.200 in. 5.1 mm and overin wall thicknessnot more than 50 tubesLess than 2 in. 50.8 mm but over 1 in. 25.4mm i

49、n outside diameter or over 1 in.25.4 mm in outside diameter and under0.200 in. 5.1 mm in wall thicknessnot more than 75 tubes1 in. 25.4 mm or less in outside diameter not more than 125 tubesA789/A789M 17a3TABLE 4 Tensile and Hardness RequirementsAUNS DesignationTensileStrength,min, ksiMPaYieldStrength,min, ksiMPaElonga