ASTM B709-17 Standard Specification for Iron-Nickel-Chromium-Molybdenum Alloy (UNS N08028) Plate, Sheet, and Strip.pdf

《ASTM B709-17 Standard Specification for Iron-Nickel-Chromium-Molybdenum Alloy (UNS N08028) Plate, Sheet, and Strip.pdf》由会员分享，可在线阅读，更多相关《ASTM B709-17 Standard Specification for Iron-Nickel-Chromium-Molybdenum Alloy (UNS N08028) Plate, Sheet, and Strip.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B709 17Standard Specification forIron-Nickel-Chromium-Molybdenum Alloy (UNS N08028)Plate, Sheet, and Strip1This standard is issued under the fixed designation B709; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the y

2、ear of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers iron-nickel-chromium-molybdenum alloy (UNS N08028)2plate, sheet, and strip inthe solu

3、tion-annealed condition.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafet

4、y concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateSafety Data Sheet (SDS) for this product/material as providedby the manufacturer, to establish appropriate safety and heal

5、thpractices, and determine the applicability of regulatory limi-tations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Gu

6、ides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3B880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys andCobalt AlloysB906 Specification for Genera

7、l Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and StripE8/E8M Test Methods for Tension Testing of Metallic Ma-terials3. Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification

8、. Examples of such requirements include, but arenot limited to those specified in Ordering Information Sectionin Specification B906.4. General Requirements4.1 Material furnished under this specification shall con-form to the applicable requirements of the current edition ofSpecification B906, unless

9、 otherwise specified herein.5. Materials and Manufacture5.1 Heat TreatmentThe final heat treatment shall be asolution-anneal. Minor cold working such as flattening ortemper rolling may be performed after the final solutionannealing treatment.NOTE 1This recommended solution-anneal consists of heating

10、 to aminimum temperature of 1975F (1080C) and cooling rapidly to roomtemperature.6. Chemical Composition6.1 The material sampled in accordance with 10.2 shallconform to the composition limits prescribed in Table 1.6.2 If a product analysis is subsequently made, the materialshall conform to the compo

11、sition limits with the productanalysis variation prescribed Specification B880.7. Mechanical Properties7.1 The material shall conform to the requirements as to themechanical property prescribed in Table 2.8. Dimensions and Permissible Variations8.1 SheetMaterial furnished under this specification sh

12、allconform to the applicable requirements of the current edition ofSpecification B906, except as specified in Table 3 and Table 4.8.2 Cold-Rolled StripMaterial furnished under this speci-fication shall conform to the applicable requirements of thecurrent edition of Specification B906, except as spec

13、ified inTables 5-7.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved April 1, 2017. Published April 2017. Originallyapproved

14、in 1982. Last previous edition approved in 2014 as B709 04 (2014).DOI: 10.1520/B0709-17.2New designation in accordance with ASTM E527 and SAE J1086, Practice forNumbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at

15、serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordan

16、ce with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.18.3 PlateMaterial furnished under t

17、his specification shallconform to the applicable requirements of the current edition ofSpecification B906.9. Sampling9.1 Sampling for Chemical Analysis, Mechanical Testing,and Corrosion Testing shall be performed in accordance withSpecification B906, except as specified herein:9.1.1 PlateA lot of pl

18、ate for testing and inspection pur-poses shall consist of the products resulting from the rolling ofone heat of material in the same condition and specifiedthickness, solution annealed by the same practice, but in nocase more than 25 000 lb (11 340 kg).9.1.2 Sheet and StripA lot of sheet or strip fo

19、r testing andinspection purposes shall consist of material from one heat inthe same form (sheet or strip), condition, finish, and specifiedthickness, solution-annealed by the same practice but in nocase more than 25 000 lb (11 340 kg).9.2 Sampling for Mechanical Tests:9.2.1 When samples are to be ta

20、ken after delivery, thepurchaser of material ordered to cut lengths may request on thepurchase order additional material of adequate size to providesample coupons for inspection purposes.10. Number of Tests and Retests10.1 In the case of sheet or strip supplied in coil form, twoor more tension tests

21、 (one from each end of each coil), and oneor more hardness tests shall be made on specimens taken fromeach end of the coil. When material is supplied in flatsheet, flatstrip, or plate, one tension and one or more hardness tests shallbe made on each 100 or less sheets, strips, or plates of the samelo

22、t. When specified, one corrosion test shall be conducted foreach lot.10.2 If any specimens selected to represent any lot fail tomeet any of the test requirements, the material represented bysuch specimens may be retested. If there is valid reason tobelieve the result is not representative, the mater

23、ial may bere-reannealed and retested.11. Specimen Preparation11.1 Tension test specimens from material under12 in. (12.7mm) in thickness shall be of the full thickness of the materialand machined to the form and dimensions shown for thesheet-type specimen in Test Methods E8/E8M. Tension testspecimen

24、s from material12 in. (12.7 mm) and over shall be ofthe full thickness of the material, machined to the form anddimensions shown for the plate-type specimen in Test MethodsE8/E8M. Tension test specimens shall be taken from materialafter final heat treatment and shall be selected in the transversedir

25、ection unless prohibited by width.12. Keywords12.1 N08028; plate; sheetstripTABLE 1 Chemical RequirementsElement Composition, %Ni 30.0 to 34.0Fe remainderACr 26.0 to 28.0Mo 3.0 to 4.0C, max 0.030Si, max 1.00Mn, max 2.50P, max 0.030S, max 0.030Cu 0.6 to 1.4ADetermined arithmetically by difference.B70

26、9 172TABLE 2 Mechanical Property RequirementsFormTensileStrength,min, ksi(MPa)YieldStrength(0.2 % off-set),min,ksi (MPa)Elongationin2in.or50 mm,or4D, min,%RockwellHardness(or equivalent)ASheet 73 (500) 31 (214) 40 7090 HRBStrip 73 (500) 31 (214) 40 7090 HRBPlate 73 (500) 31 (214) 40 7090 HRBAHardnes

27、s values are shown for information only and shall not constitute a basis for acceptance or rejection as long as the other mechanical properties are met.TABLE 3 Flatness Tolerances for Hot-Rolled and Cold-Rolled SheetsSheets not Specified to Stretcher Leveled Standard of FlatnessSpecified Thickness,

28、in. (mm) Width, in. (mm)Flatness Tolerance (maxDeviation from a HorizontalFlat Surface), in. (mm)0.062 (1.57) and over to 60 (1524), inclover 60 to 72 (1524 to 1829), incl12 (12.7)34 (19.1)over 72 (1829) 1 (25.4)Under 0.062 (1.57) to 36 (914), inclover 36 to 60 (914 to 1524), incl12 (12.7)34 (19.1)o

29、ver 60 (1524) 1 (25.4)TABLE 4 Weight Tolerances for Hot-Rolled and Cold-Rolled SheetsIt is not practicable to produce hot-rolled and cold-rolled sheets to exact theoretical weight. Sheets of any one item of a specified thicknessand size in any finish may be overweight to the following extent:(1) An

30、item of five sheets or less, or an item estimated to weigh 200 lb (90.7 kg) or less, may actually weigh as much as 10 % over thetheoretical weight.(2) An item of more than five sheets and estimated to weigh more than 200 lb (90.7 kg) may actually weigh as much as 712 % over thetheoretical weight.(3)

31、 The underweight variations for sheets are limited by the under thickness tolerances shown in Table 3 of Specification B906.For determining theoretical weight, the factor 42 lb/ft2in. (0.0008 kg/cm2mm) thickness may be used.B709 173TABLE 5 Thickness ToleranceA,B,Cfor Cold-Rolled Strip for the Thickn

32、esses and Widths Given, Over and UnderSpecified ThicknessWidth, in.0.187 to 1,inclOver 1 to3, inclOver 3 to6, inclOver 6 to9, inclOver 9 to12, inclOver 12 to16, inclOver 16 to20, inclOver 20 to24, inclThickness Tolerance, in.Over 0.160 to less than 0.002 0.003 0.004 0.004 0.004 0.005 0.006 0.0060.18

33、7Over 0.099 to 0.160, incl 0.002 0.002 0.003 0.003 0.004 0.004 0.005 0.005Over 0.068 to 0.099, incl 0.002 0.002 0.003 0.003 0.003 0.004 0.004 0.004Over 0.049 to 0.068, incl 0.002 0.002 0.003 0.003 0.003 0.003 0.004 0.004Over 0.039 to 0.049, incl 0.002 0.002 0.0025 0.003 0.003 0.003 0.004 0.004Over 0

34、.034 to 0.039, incl 0.002 0.002 0.0025 0.0025 0.003 0.003 0.003 0.003Over 0.028 to 0.034, incl 0.0015 0.0015 0.002 0.002 0.0025 0.0025 0.003 0.003Over 0.025 to 0.028, incl 0.001 0.0015 0.0015 0.002 0.002 0.002 0.0025 0.003Over 0.019 to 0.025, incl 0.001 0.001 0.0015 0.0015 0.002 0.002 0.0025 0.0025O

35、ver 0.016 to 0.019, incl 0.001 0.001 0.001 0.0015 0.0015 0.002 0.002 0.002Over 0.012 to 0.016, incl 0.001 0.001 0.001 0.001 0.0015 0.0015 0.002 0.002Over 0.011 to 0.012, incl 0.001 0.001 0.001 0.001 0.0015 0.0015 0.0015 0.0015Over 0.010 to 0.011, incl 0.001 0.001 0.001 0.001 0.001 0.0015 0.0015 0.00

36、150.010 0.001 0.001 0.001 0.001 0.001 0.001 0.0015 0.0015Specified Thickness, mmWidth, mm4.76 to25.4, inclOver25.4to 76.2,inclOver 76.2to 152.4,inclOver152.4 to228.6,inclOver228.6 to304.8, inclOver304.8 to406.4,inclOver406.4 to508, inclOver 508to 609.6,inclThickness Tolerance, mmOver 4.06 to less th

37、an 0.05 0.08 0.10 0.10 0.10 0.13 0.15 0.154.76Over 2.51 to 4.06, incl 0.05 0.05 0.08 0.08 0.10 0.10 0.13 0.13Over 1.73 to 2.51, incl 0.05 0.05 0.08 0.08 0.08 0.10 0.10 0.10Over 1.25 to 1.73, incl 0.05 0.05 0.08 0.08 0.08 0.08 0.10 0.10Over 0.99 to 1.24, incl 0.05 0.05 0.06 0.08 0.08 0.08 0.10 0.10Ov

38、er 0.86 to 0.99, incl 0.05 0.05 0.06 0.06 0.08 0.08 0.08 0.08Over 0.71 to 0.86, incl 0.04 0.04 0.05 0.05 0.06 0.06 0.08 0.08Over 0.64 to 0.71, incl 0.02 0.04 0.04 0.05 0.05 0.05 0.06 0.08Over 0.48 to 0.64, incl 0.02 0.02 0.04 0.04 0.05 0.05 0.06 0.06Over 0.41 to 0.48, incl 0.02 0.02 0.02 0.04 0.04 0

39、.05 0.05 0.05Over 0.38 to 0.41, incl 0.02 0.02 0.02 0.02 0.04 0.04 0.05 0.05Over 0.28 to 0.30, incl 0.02 0.02 0.02 0.02 0.04 0.04 0.04 0.04Over 0.25 to 0.28, incl 0.02 0.02 0.02 0.02 0.02 0.04 0.04 0.040.25 0.02 0.02 0.02 0.02 0.02 0.02 0.04 0.04AFor thickness under 0.010 to 0.005 in. (0.254 to 0.12

40、7 mm), inclusive, in widths up to and including 16 in. (406 mm), a tolerance of 10 % of the thickness applies. Forthicknesses under 0.010 to 0.005 in. (0.254 to 0.127 mm), inclusive, in widths over 16 to 24 in. (406 to 610 mm), exclusive, a tolerance of 15 % of the thickness applies.For thickness to

41、lerances on thicknesses under 0.005 in. (0.127 mm) in widths up to 24 in. (610 mm), exclusive, the producer should be consulted.BThickness measurements are taken38 in. (9.5 mm) in from the edge of the strip, except that on widths less than 1 in. (25.4 mm) the tolerances are applicable formeasurement

42、s at all locations.CThe tolerances in this table do not include crown tolerances.TABLE 6 Crown Tolerances for Cold-Rolled StripSpecified Thickness, in. (mm)Additional Thickness, at Middle of Strip over That Shown in Table 5 forEdge Measurement, for Widths and Thicknesses Given, in. (mm)Width, in. (m

43、m)To 5 (127), inclOver 5 to 12 (127 to305), inclOver 12 to 24 (305 to610), excl0.005 to 0.010 (0.127 to 0.254), incl 0.0075 (0.19) 0.001 (0.02) 0.0015 (0.04)Over 0.010 to 0.025 (0.254 to 0.635), incl 0.001 (0.02) 0.0015 (0.04) 0.002 (0.05)Over 0.025 to 0.065 (0.635 to 1.65), incl 0.0015 (0.04) 0.002

44、 (0.05) 0.0025 (0.06)Over 0.065 to 0.187 (1.65 to 4.76), excl 0.002 (0.05) 0.0025 (0.06) 0.003 (0.08)B709 174ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised

45、that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reap

46、proved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you

47、 feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual

48、reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from th

49、e Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 7 Length and Camber Tolerances for Cold-Rolled StripLength TolerancesSpecified Length, ft (mm)Tolerance OverSpecifiedLength (No UnderTolerance), in. (mm)To 5 (1524), incl38 (9.5)Over 5 to 10 (1520 to 3050), incl12 (12.7)Over 10 to 20 (3050 to 6100), incl58 (15.9)B709 175