ASTM D2943 - 02(2012) Standard Test Method for Aluminum Scratch of 1,1,1-Trichloroethane to Determine Stability (Withdrawn 2017).pdf

《ASTM D2943 - 02(2012) Standard Test Method for Aluminum Scratch of 1,1,1-Trichloroethane to Determine Stability (Withdrawn 2017).pdf》由会员分享，可在线阅读，更多相关《ASTM D2943 - 02(2012) Standard Test Method for Aluminum Scratch of 1,1,1-Trichloroethane to Determine Stability (Withdrawn 2017).pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D2943 02 (Reapproved 2012)Standard Test Method forAluminum Scratch of 1,1,1-Trichloroethane to DetermineStability1This standard is issued under the fixed designation D2943; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revisio

2、n, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This is a screening test method to determine if sufficientinhibitors are present in 1,1,1-trichloroetha

3、ne to provide atleast minimal stability in the presence of aluminum.1.2 Solvent passing this test method may not be stable forall applications.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standar

4、d to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. A specific hazardstatement is given in Section 6.2. Summary of Test Method2.1 A cleaned, degreased, dry metal coupon of aluminumalloy is immersed in inhibited 1,1,1-trichl

5、oroethane andscratched while in the solvent. After sufficient time has elapsedto allow any reaction to occur, the presence or absence ofbubbling, solvent discoloration, or dark resinous material isnoted. The 1,1,1-trichloroethane is sufficiently inhibited only ifnone of these conditions is observed.

6、3. Significance and Use3.1 The degradation of insufficiently stabilized 1,1,1-trichloroethane, in the presence of aluminum, results in theformation of hydrochloric acid and polymeric residue. Thus, ifsuch degradation is allowed to continue, the aluminum will becorroded and the 1,1,1-trichloroethane

7、rendered unusable. Thepresence of free water invalidates this test method.3.2 This test method can be used to determine if 1,1,1-trichloroethane is sufficiently stabilized to inhibit reaction withaluminum or aluminum alloys. Solvent passing this testmethod still may not be stable for all application

8、s. Consult aproducer for use applications.3.3 Aluminum should not be used as a material of construc-tion for pumps, tanks, pipelines, valves, spray equipment, orother handling equipment used for chlorinated solvents. Prop-erly stabilized halogenated solvents are, however, commonlyused in cleaning al

9、uminum and other sensitive metals.4. Apparatus4.1 Aluminum Sheet Metal, designated ASTM Alloy 1100(UNS No. A91100),20.016 to 0.040 in. (0.4 to 1 mm) thick.4.2 Mild Steel Metal Object, such as an ice pick sharpenedto lead pencil-sized point.5. Preparation of Aluminum Coupon5.1 Degrease an aluminum co

10、upon, 1 by 1 in., (2.5 by 2.5cm) by rinsing in a commercial grade of solvent such asperchloroethylene, trichloroethylene, or 1,1,1-trichloroethane.Hand-sand both sides of the aluminum coupon lightly with afine emery cloth, and rinse the coupon again. The surfaceshould be bright and free of haze.6. H

11、azards6.1 This test method should be performed in a fume hood.Insufficiently inhibited solvent can react with aluminum toform hydrogen and hydrogen chloride gases. Solvent vaporsare also present. Their release to the atmosphere must beminimized.7. Procedure7.1 Conduct this test method at room temper

12、ature. Measure50 mL of inhibited 1,1,1-trichloroethane into a clean solvent-rinsed glass beaker. Place a freshly prepared aluminum couponin the solvent sample in a horizontal position on the bottom ofthe beaker. Scratch (Note 1) the top surface of the submergedaluminum coupon with a sharply pointed

13、mild steel instrument.Make three scratches approximately equally spaced and 0.005in. (0.1 mm) deep in one direction. Then make three additionalscratches at right angles to the original three (Note 2). Observethe aluminum coupon after 10 min and again after1hhaselapsed. In the event that continued de

14、composition occurs after1This test method is under the jurisdiction of ASTM Committee D26 onHalogenated Organic Solvents and Fire Extinguishing Agents and is the directresponsibility of Subcommittee D26.04 on Test Methods.Current edition approved March 1, 2012. Published May 2012. Originallyapproved

15、 in 1971 as D294371 T. Last previous edition approved in 2007 as D294302 (2007). DOI: 10.1520/D2943-02R12.2Annual Book of ASTM Standards, Vol 02.02.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesNOTICE: This standard has either been s

16、uperseded and replaced by a new version or withdrawn.Contact ASTM International (www.astm.org) for the latest information11 h, add water to stop the reaction, remove the aluminumcoupon, and discard the solvent in a solvent container toprevent evaporation.NOTE 1The scratch should be a lateral scrape

17、rather than a verticalperforation.NOTE 2Scratches are to appear as follows:8. Report8.1 For each test method, report observations as follows:8.1.1 Passes/no reaction.8.1.2 Fails/the appearance of gas bubbles, color formation,or metal corrosion at the edge of the scratch marks are evidenceof failure

18、to pass the test method.8.2 The solvent should be considered sufficiently stabilizedfor many uses in the presence of aluminum or aluminum alloysonly if no reaction occurs. The absence of reactivity in this testmethod may not indicate stability for all applications.9. Precision and Bias9.1 Only visua

19、l observations are reported. No precision andbias statements can be made.10. Keywords10.1 aluminum; aluminum scratch test; inhibitors; stabilitytest; 1,1,1-trichloroethaneASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedi

20、n this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and mu

21、st be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of th

22、eresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C70

23、0, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D2943 02 (2012)2