SAE AMS 4337A-2006 Aluminum Alloy Extruded Profiles (7055-T77511) 8 0Zn - 2 3Cu - 2 0Mg - 0 16Zr Solution Heat Treated Stress Relieved and Overaged (UNS A97055)《通过拉直和覆盖释放应力的(7055-T.pdf

《SAE AMS 4337A-2006 Aluminum Alloy Extruded Profiles (7055-T77511) 8 0Zn - 2 3Cu - 2 0Mg - 0 16Zr Solution Heat Treated Stress Relieved and Overaged (UNS A97055)《通过拉直和覆盖释放应力的(7055-T.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4337A-2006 Aluminum Alloy Extruded Profiles (7055-T77511) 8 0Zn - 2 3Cu - 2 0Mg - 0 16Zr Solution Heat Treated Stress Relieved and Overaged (UNS A97055)《通过拉直和覆盖释放应力的(7055-T.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2011 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4337A AEROSPACE MATERIAL SPECIFICATION AMS 4337 REV. A Issued 1998-11 Revised

5、2006-09 Reaffirmed 2011-11 Superseding AMS 4337 Aluminum Alloy, Extruded Profiles (7055-T77511) 8.0Zn - 2.3Cu - 2.0Mg - 0.16Zr Solution Heat Treated, Stress Relieved, and Overaged (Composition similar to UNS A97055) RATIONALE This document has been reaffirmed to comply with the SAE five-year review

6、policy. 1. SCOPE 1.1 Form This specification covers an aluminum alloy in the form of extruded profiles (shapes). 1.2 Application This product has been used typically for structural applications requiring a combination of high mechanical properties and good resistance to exfoliation corrosion, but us

7、age is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document

8、 issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (ins

9、ide USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS 2355 Quality Assurance Sampling and Testing, Aluminum Alloys and Magnesium Alloys, Wrought Products, Except Forging Stock, and Rolled, Forged, or Flash Welded Rings AMS 2772 Heat Treatment of Aluminum Alloy Raw Materials Provided by

10、 IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS 4337A Page 2 of 6 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 594 Ultrasonic Ins

11、pection of Aluminum-Alloy Wrought Products for Aerospace Applications ASTM B 660 Packaging/Packing of Aluminum and Magnesium Products ASTM G 34 Exfoliation Corrosion Susceptibility in 2xxx and 7xxx Series Aluminum Alloys (EXCO Test) ASTM B 666/B666M Identification Marking of Aluminum Products 2.3 AN

12、SI Publications Available from American National Standards Institute, 25 West 43rd Street, New York, NY 10036, Tel: 212-642-4900, www.ansi.org. ANSI H35.2 Dimensional Tolerances for Aluminum Mill Products ANSI H35.2M Dimensional Tolerances for Aluminum Mill Products (Metric) 3. TECHNICAL REQUIREMENT

13、S 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined in accordance with AMS 2355. TABLE 1 - COMPOSITION Element min maxSilicon - 0.10Iron - 0.15Copper 2.0 2.6 Manganese - 0.05Magnesium 1.8 2.3 Chromium - 0.04Zinc 7.6 8.4 Titanium - 0.06Zirconium 0.08 0.25Other El

14、ements, each - 0.05Other Elements, total - 0.15Aluminum remainder 3.2 Condition Solution heat treated, stress-relieved by stretching to produce a nominal permanent set of 1.5%, but not less than 1% or more than 3%, and overaged. 3.2.1 Product shall be supplied with an as-extruded surface finish; lig

15、ht polishing to remove minor surface imperfections is permissible provided such imperfections can be removed within the dimensional tolerances. 3.2.2 Product may receive minor straightening, after stretching, of an amount necessary to meet the requirements of 3.6. Provided by IHSNot for ResaleNo rep

16、roduction or networking permitted without license from IHS-,-,-SAE AMS 4337A Page 3 of 6 3.3 Heat Treatment Shall be in accordance with AMS 2772 and as follows: 3.3.1 Overaging Heat Treatment Overaging shall be performed at a specific temperature and time, as required to meet the requirements of 3.4

17、 (See 8.2). 3.4 Properties Product shall conform to the following requirements, determined in accordance with AMS 2355 on the mill produced size. 3.4.1 Longitudinal and long transverse tensile properties of extrusions, with a maximum cross-sectional area of 20 square inches (129 cm2) and a maximum c

18、ircle size of 10 inches (254 mm), shall be as specified in Table 2A or 2B. TABLE 2A - Minimum Tensile Properties, Inch/Pound Units Nominal Thickness Inch Specimen Orientation Tensile Strength ksi Yield Strength at 0.2% Offset ksi Elongation in 2 inches or 4D % 0.500 to 1.500, incl Longitudinal Long-

19、Transverse 94.0 88.0 90.0 84.0 9 5 TABLE 2B - MINIMUM TENSILE PROPERTIES, SI UNITS Nominal Thickness Millimeters Specimen Orientation Tensile Strength MPa Yield Strength at 0.2% Offset MPa Elongation in 50.8 mm or 4D % 12.7 to 38.1, incl Longitudinal Long-Transverse 648 607 621 579 9 5 3.4.2 Longitu

20、dinal compressive yield strength, when specified, shall be 92.0 Ksi (634 MPa), minimum. 3.4.3 Electrical Conductivity Shall be not lower than 35.5% IACS (International Annealed Copper Standard) (20.6 MS/m), determined on the surface of the test coupon prior to turning. 3.4.4 Exfoliation Corrosion Re

21、sistance Specimens cut from extrusions and tested per ASTM G 34 shall not exhibit exfoliation corrosion at a T/10 plane greater than that illustrated by Photograph B, Figure 2, of ASTM G 34. 3.4.5 Residual Strength The net area residual strength of the product (with sufficient size to accommodate th

22、e test specimen), when tested in ambient air, shall be not lower than 45 ksi (310 MPa). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS 4337A Page 4 of 6 3.4.5.1 Test Specimen Shall be a 4-inch (102-mm) wide by 0.25 inch (6.4-mm) thick center

23、 cracked panel machined from the mid-thickness of the extruded leg. The length of the specimen shall be such that the central 11.0 inches (279 mm) are exposed between test machine grips. The center notch shall consist of a 0.1875 inch (4.8-mm) drilled central hole, a 0.75 inch (19.0-mm) long center

24、cut 0.062 inch (1.6-mm) wide, and extension cuts on both ends of approximately 0.125 inch (3.2-mm) length and maximum width of 0.012 inch (0.3 mm). The total length of the fabricated center notch should be approximately 1.0 inch (25 mm). 3.4.5.2 Test Procedure Measure panel width, thickness and tota

25、l crack length to the nearest 0.001 inch (0.025 mm); fatigue precrack from a 1.0 to 1.1-inch (25 to 28-mm) long center notch to a total crack length of 1.25 inches (31.8 mm), using constant amplitude cycling (f=5 Hz, R=+0.06) and a maximum gross area stress of 15.3 ksi (106 MPa); ramp load to fractu

26、re at a rate of 1.0 gross ksi per second (6.9 MPa/s); determine the total non-precracked cross-sectional area after fracture; calculate the peak net area stress at fracture (Residual Strength) and record to 0.1 ksi (0.7 MPa). 3.5 Quality Products, as received by purchaser, shall be uniform in qualit

27、y and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the extrusions. 3.5.1 When specified, each extruded profile (shape) shall be subjected to ultrasonic inspection in accordance with ASTM B 594 and shall meet the following requirements: 3.5.1.1 Each

28、 extruded profile (shape) weighing 600 pounds (272 kg) and under and having a maximum width-to-thickness ratio of 10:1 shall meet ultrasonic class B requirements, as described in ASTM B 594. 3.5.1.2 The ultrasonic class for all tubing and for other extruded profiles weighing over 600 pounds (272 kg)

29、, or in excess of 10:1 maximum width-to-thickness ratio shall be as agreed upon by purchaser and vendor. 3.6 Tolerances Shall conform to all applicable requirements of ANSI H35.2 or ANSI H35.2(M). 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the products shall supp

30、ly all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the products conform to the specified requirements. 4.2 Classification of Tests 4.2.1 Ac

31、ceptance Tests Composition (3.1), tensile properties (3.4.1), electrical conductivity (3.4.3), tolerances (3.6), and when specified, ultrasonic soundness (3.5.1) are acceptance tests and, except for composition, shall be performed on each lot. 4.2.2 Periodic Tests Tests for exfoliation-corrosion res

32、istance (3.4.4) and residual strength (3.4.5) are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS 4337A Page 5

33、of 6 4.3 Sampling and Testing Shall be in accordance with AMS 2355. 4.4 Reports The vendor of product shall furnish with each shipment a report stating that the product conforms to the composition, tolerances and ultrasonic inspection (when required); and showing the numerical results of tests on ea

34、ch inspection lot to determine conformance to the other acceptance test requirements and to the periodic tests when performed. This report shall include the purchase order number, inspection lot number(s), AMS 4337A, size and quantity. The report shall also identify the producer, the mill product fo

35、rm, and the mill produced size. 4.5 Resampling and Retesting Shall be in accordance with AMS 2355. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in accordance with ASTM B 666/B666M. 5.2 Packaging Products shall be prepared for shipment in accordance with ASTM B 660. 6. ACKNOWLEDGMENT A ven

36、dor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Products not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located

37、in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of a specification. An (R) symbol to the left of the document title indicates a complete revision of the specification, including technical r

38、evision. Change bars and (R) are not used in original publications, nor in specifications that contain editorial changes only. 8.2 Actual overaging heat treatments are proprietary. 8.3 Extrusions should be visually inspected for the presence of intergranular attack (IGA). If detected, surface machin

39、ing or milling is recommended to remove surface IGA which may occur during fabricating. 8.4 Alloy-temper definitions for aluminum products are presented in AS1990. Designation systems are presented in ANSI H35.1 and ANSI H35.1(M). 8.5 Terms used in AMS are clarified in ARP1917. 8.6 Dimensions and pr

40、operties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. Provided by IHSNot for ResaleNo reproduction or networkin

41、g permitted without license from IHS-,-,-SAE AMS 4337A Page 6 of 6 8.7 Purchase documents should specify not less than the following: AMS 4337A Form and size or section identification number of extrusions desired Quantity of extrusions desired Whether ultrasonic inspection of extruded profiles (shapes) is required (See 3.5.1). PREPARED BY AMS COMMITTEE “D” Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-