GME QK 000746-2014 Phenolic plast with Mineralic Fillers and Glass Fibres (Issue 3 English German This standard may be applied only for current programs It is inactive for all futuro.pdf

《GME QK 000746-2014 Phenolic plast with Mineralic Fillers and Glass Fibres (Issue 3 English German This standard may be applied only for current programs It is inactive for all futuro.pdf》由会员分享，可在线阅读，更多相关《GME QK 000746-2014 Phenolic plast with Mineralic Fillers and Glass Fibres (Issue 3 English German This standard may be applied only for current programs It is inactive for all futuro.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、ADAM OPEL AGTDCCentral LaboratoriesTECHN. LIEFERBEDINGUNGENFR WERKSTOFFEENGINEERINGMATERIAL SPECIFICATIONLIMITED USEQK 000746Phenoplast mit mineralischen Fllstoffen und GlasfasernPhenolic plast with Mineralic Fillers and Glass FibresNote: This standard may be applied only for current programs. It is

2、 inactive for all future projectsand without replacement.If this product should be used for a new project, a Re-Certification according to GMW15702 isrequired.Hinweis: Diese Spezifikation darf nur noch fr laufende Projekte angewendet werden und ist fr allezuknftigen Projekte ohne Ersatz ungltig.Fall

3、s dieses Produkt fr ein neues Projekt zum Einsatz kommen soll, ist eine Neu-Zertifizierung nachGMW15702 erforderlich.Werkstoff: Phenolharz-Formmasse mit 55 Massenanteil in % mineralischen Fllstoffen undGlasfasernMaterial: Phenolic resin moulding compound with 55 % by mass mineralic fillers and glass

4、fibresKurzzeichen: PF-M/GF55 Symbol:Verwendung: Formpre-, Spritzpre- und Spritzgietype zur Herstellung thermisch hochbelastbarer technischer Teile mit hoher Druckfestigkeit und guter Zhigkeit,z.B. Dichtung-KraftstoffpumpeApplication: Compression-, transfer- and injection moulding type for manufactur

5、ingthermically high loaded technical parts requiring high pressure and impactresistance, e.g. sealing-fuel pumpHandelsname: Bakelite PF 2774 PTrade Name: Bakelite PF 2774 SLieferant: Bakelite AG, Postfach 7154, D-58609 Iserlohn-LetmatheSupplier:Lieferform: GranulatForm of Delivery: GranulesAusfertig

6、ungs-Nr.:Issue: 3Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehmigt:Approved: MKSeite vonPage 1 of 4Unbeschadet etwaiger durch den Abnehmer erfolgenden Stichprobenprfungen trgt der Lieferant die Verantwortung dafr, da die gelieferteWare die Opel-Zeichnungsvorschriften erfllt. Ein Prfbericht mit zah

7、lenmigen Ergebnissen aus Prfungen der Lieferung selbst ist bei jederBemusterung, Erstbelieferung und Ausfhrungsnderung mitzugeben.Despite spot checks possibly performed by Opel, it is the suppliers responsibility that the delivered parts are in line with the Opel drawings.Deliveries of samples, firs

8、t off-tool parts and parts, whose performance has been changed, must be accompanied by a test report showing thetest results in terms of figures.LBSP TL WS 1 11/95LIMITED USE QK 000746Ausfertigungs-Nr.:Issue: 3Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehmigt:Approved: MKSeite vonPage 2 of 4Forder

9、ungen / Requirementsa) zu dokumentierende Eigenschaften / values for documentationEigenschaftenPropertiesMittelwertAverageValueStandardab-weichungStandardDeviationEinheitUnitNormStandardDichteDensity 1,75 0,01 g/cm3ISO 1183GlhrckstandAsh 40 0,8Massenanteilin % /% by massISO 3451(bei/at +950C)Bruchsp

10、annungStress at Break 70 1,4 N/mm2ISO 527Charpy-SchlagzhigkeitCharpy Impact Strengthbei/at +23C 8,0 0,3 kJ/m2ISO 179 / 1eUFormbestndigkeitstemperaturTemperature of Deflection under LoadVerfahren/Method A (1,8 N/mm2) 200 2,0 CISO 75-2b) nur zur Information / only for informationEigenschaftenPropertie

11、sMittelwertAverageValueEinheitUnitNormStandardVerarbeitungsschwindungMould Shrinkagelngs / longitudinal 0,25 %ISO 2577 oderISO 294-4ZugmodulTensile Modulus 10000 N/mm2ISO 527BruchdehnungStrain at Break 1,1 %ISO 527Charpy-SchlagzhigkeitCharpy Impact Strengthbei/at -30C 8 kJ/m2ISO 179 / 1eUCharpy-Kerb

12、schlagzhigkeitCharpy Notched Impact Strengthbei/at +23Cbei/at -30C1,81,8kJ/m2kJ/m2ISO 179 / 1eAFormbestndigkeitstemperaturTemperature of Deflection under LoadVerfahren/Method B (0,45 N/mm2)Verfahren/Method C (5,0 N/mm2)250150CCISO 75-2Koeffizient der linearen Wrmeaus-dehnungCoefficient of Linear The

13、rmalExpansionlngs / longitudinal 0,25 x 10-4 1/KDIN 53752LIMITED USE QK 000746Ausfertigungs-Nr.:Issue: 3Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehmigt:Approved: MKSeite vonPage 3 of 4EigenschaftenPropertiesMittelwertAverageValueEinheitUnitNormStandardDielektrizittszahlDielectric Number100 Hz 11

14、DIN IEC 250Dielektrischer VerlustfaktorDielectric Dissapation Factor100 Hz 0,4DIN IEC 250Spez. DurchgangswiderstandVolume Resistivity 1 x 1012:cm DIN IEC 93Spez. OberflchenwiderstandSurface Resistivity 1 x 1011: DIN IEC 93Vergleichszahl der KriechwegbildungComparative Tracking IndexCTI 175DIN IEC 11

15、2Hinweis / ReferenceWeitere Informationen siehe QK 000000. /For further information refer to QK 000000.Bemerkung / NoteAlle Probekrper werden im Spritzgieverfahren hergestellt. /All test pieces shall be manufactured by injection moulding.Abfallbeseitigung / Waste DisposalGruppe D, Opel-Betriebsricht

16、linie Nr. 440 /Group D, Opel-Plant Directive No. 440LIMITED USE QK 000746LBSP TL 3 11/9522.10.2014 Limited Use Status14.05.96 War Ausfertigungs-Nr. 1, Datum 09/87Englische bersetzung zugefgtnach neuesten Lieferantenangaben entsprechend QK 000000berarbeitetWas Issue No. 1, Date 09/87English Translation addedreworked to newest suppliers information according to QK 000000DatumDateBeschreibung / Description GeprftCheckedGenehmigtAppd.nderungen / RevisionsAusfertigungs-Nr.:Issue: 3Datum:Date: 10/14Ausgefertigt:Prepared: JKGenehmigt:Approved: MKSeite vonPage 4 of 4