FORD ESB-M4D251-A-2008 ABS - POLYCARBONATE MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《丙烯腈-丁二烯-苯乙烯共聚物(ABS)-聚碳酸酯成型料 与标准FORD WSS-M99P1111-A一起使用 A[使用 FORD WSS-M4D585-B F.pdf

《FORD ESB-M4D251-A-2008 ABS - POLYCARBONATE MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《丙烯腈-丁二烯-苯乙烯共聚物(ABS)-聚碳酸酯成型料 与标准FORD WSS-M99P1111-A一起使用 A[使用 FORD WSS-M4D585-B F.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M4D251-A-2008 ABS - POLYCARBONATE MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《丙烯腈-丁二烯-苯乙烯共聚物(ABS)-聚碳酸酯成型料 与标准FORD WSS-M99P1111-A一起使用 A[使用 FORD WSS-M4D585-B F.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2008 02 22 N-STATUS Replaced by WSS-M4D585-B G. Kowalski 2007 05 31 Revised Inserted 3.0; Deleted 3.2.1, 3.3 & 4 1967 05 04 Released AW1-970 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 3 ABS - POLYC

2、ARBONATE MOLDING COMPOUND ESB-M4D251-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an acrylonitrile butadiene styrene (ABS) and polycarbonate alloy, blended to achieve exceptional impact and thermal properties. Two types of materials are approved under this s

3、pecification. 2. APPLICATION This specification was released originally for the following materials: Type I Used for interior trim components where high impact strength and heat resistance is required, such as automatic transmission shift console handles. Type II A self-extinguishing grade used in e

4、lectrical applications. In addition to offering high thermal and impact properties, this resin exhibits good resistance to hydrocarbons. 3. REQUIREMENTS ESB-M4D251 specification shown without type designation is understood to be Type I material. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Mat

5、erial suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 MOLDED TEST SPECIMEN Type I Type II 3.1.1 Color Natural Black/gray (Unless otherwise specified on engineering drawing) 3.1.2 Specific Gravity 1.12 - 1.25 1.15 - 1.28 (

6、ASTM D 792) 3.1.3 Tensile Strength, 7,800 (54) 7,500 (52) psi (MPa), min (ASTM D 638) 3.1.4 Flexural Strength, 10,000 (69) 10,000 (69) psi (MPa), min (ASTM D 790) ENGINEERING MATERIAL SPECIFICATION ESB-M4D251-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 3

7、 Type I Type II 3.1.5 Impact Strength, Izod, ft lb/in (J/m), min (ASTM D 256, 1/8 in (3.2 mm) specimen width) 3.1.5.1 Notched Natural 9.0 (481) 8.0 (427) Pigmented 8.0 (427) 7.0 (374) 3.1.5.2 Unnotched 20 (1068) No break 3.1.6 Deflection Temperature, C min (ASTM D 648, 1/2 in (12.7 mm) specimen widt

8、h) At 66 psi (455 kPa) 124 116 At 264 psi (1820 kPa) 113 102 3.1.7 Hardness - Rockwell “R“ 115 121 113 - 123 (ASTM D 785) 3.2 MOLDED PART (Types I and II, unless otherwise stated) 3.2.2 Physical Properties Specific requirements for physical properties of molded parts, when required, shall be specifi

9、ed on engineering drawings. 3.2.3 Resistance to Fade, pigmented material only (FLTM BO 101-01) The material shall fade no more than the master sample approved for production on file in the Quality Control or Test Laboratory after 120 SFH. 3.2.4 Resistance to Heat Finished parts must pass the followi

10、ng test: Test Method: Condition the parts for 3 h at 107 +/- 3 C (or as otherwise specified on engineering drawing). After removal, parts shall show no more than 0.5% shrinkage where the part has been gated, which will interfere with assembly to mating parts or affect its appearance. The part shall

11、not warp to an extent that would affect its use in ultimate assembly. 3.2.5 Chemical Resistance, weight change, max 5% (ASTM D 543, immersion in n-Heptane (90 - 110 C boiling range) for 40 h) 3.2.6 Flammability, Type II only Self-extinguishing (ASTM D 635) ENGINEERING MATERIAL SPECIFICATION ESB-M4D2

12、51-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 3 of 3 3.2.7 Odor The intensity and character of the material odor shall not be objectionable or offensive. 3.2.8 Hydrocarbon Resistance, Type II only Impact and flexural properties shall not decrease by more tha

13、n 25% after having been subjected to the following test. Test Method: Following a 24 h period of total immersion in gasoline, the impact and flexural properties shall be measured after an open time (23 +/- 2 C, 50 +/- 5% relative humidity) of no less than 24 h, but within 48 h. In addition, the imme

14、rsion samples shall not exhibit evidence of delamination. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Type I Type II 5.1 MOLD SHRINKAGE, in/in or mm/mm 0.006 0.006 5.2 COEFFICIENT OF LINEAR 3.5 x 10-5/ F 3.78 x 10-5/ F THERMAL EXPANSION (6.3 x 10-5/ C) (6.8 x 10-5/ C) 5.3 FLEXURAL MODULUS, psi (GPa), min 3.5 x 105 (2.4) 3.3 x 105 (2.3) (ASTM D 790)