FORD ESB-M2G183-A-2014 ADHESIVE VINYL ACETATE - HOT MELT - PRESSURE SENSITIVE TYPE TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD ESB-M2G183-A-2014 ADHESIVE VINYL ACETATE - HOT MELT - PRESSURE SENSITIVE TYPE TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M2G183-A-2014 ADHESIVE VINYL ACETATE - HOT MELT - PRESSURE SENSITIVE TYPE TO BE USED WITH FORD WSS-M99P1111-A .pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2014 12 08 N Status No replacement named L. Sinclair, NA 2003 01 24 Revised Para 3.0 inserted ; Para 3.13, 3.14, 4 deleted 1970 08 07 Released AA1-58 Page 1 of 4 Copyright 2014, Ford Global Technologies, Inc

2、. ADHESIVE, VINYL ACETATE - HOT MELT - PRESSURE SENSITIVE TYPE ESB-M2G183-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a 100% solids, thermoplastic pressure sensitive type, hot melt adhesive of the vinyl acetate class. 2. APPLICATION This specification was r

3、eleased originally for material used to effect a temporary bond for shipping purposes prior to final assembly, between materials such as, polyethylene foam, closed cell sponge neoprene, molded sponge rubber and polyurethane gaskets to stamped sheet metal, zinc die cast, polypropylene, A.B.S., acryli

4、c or fiberglass reinforced polyester resin lamp bodies. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COLOR Amber 3.2 VISCOSITY AT OPERATING TE

5、MPERATURE 4,000 9,000 cP (mPa.s) (Brookfield, #5 Spindle, 10 r.p.m.) The viscosity of the material is recorded at 163 C, 177 C, 191 C. 3.3 SOLIDS, min 95% (ASTM D 2046, except heat at 177 C for 4 h, save sample for next test) 3.4 ASH, max 0.5% (Based on weight of solids) Test Method Place the crucib

6、le containing the solids residue in a cool muffle furnace. Slowly heat to and maintain at 760 +/- 30 C for 1 h. 3.5 SOFTENING POINT 57 - 66 C (ASTM E 28, Ring and Ball Apparatus) ENGINEERING MATERIAL SPECIFICATION ESB-M2G183-A Page 2 of 4 Copyright 2014, Ford Global Technologies, Inc. 3.6 NORMAL SHE

7、AR ADHESION, min (177 C application temperature both tests shall show cohesive failure at 23 +/- 2 C) 3.6.1 1 in (25 mm) overlap - Steel - Steel 7 psi (0.048 MPa) (Clean SAE 1010 steel) 3.6.2 1 in (25 mm) overlap - Polypropylene - 7 psi (0.048 MPa) Polypropylene (ESB-M4D175-A) The above substrates s

8、hall be used for control purposes to establish reproducible shear adhesion values. The use of metal and rigid plastics is necessary due to the low tensile strength of the foam materials and the high shear adhesion values obtainable with this hot melt adhesive. Test Method Apply sufficient material a

9、t the proper application temperature 177 C to a section of the above substrates to provide a bond area of 1 sq in (6.5 cm2) by approximately 0.030 in (0.76 mm) thickness. With hand pressure, apply 1 sq in (6.5 cm2) of a 1 x 3 in (25 x 75 mm) section of the above substrates to the adhesive surface an

10、d allow the composite to cool to room temperature (30 minutes minimum). Pull the bonded assembly in a tensile machine with a jaw separation rate of 1 in (25 mm)/min. (See Fig I). 3.7 ODOR The adhesive shall be free from objectionable or irritating odors, both as received and at application temperatu

11、res. 3.8 QUALITY The adhesive shall be a smooth homogeneous mixture, free from foreign materials and properties detrimental to normal production operations. 3.9 TOXICITY The material shall be non-toxic and shall not cause skin rash or irritation (dermatitis) to exposed handlers in normal production

12、operations. 3.10 OPERATING TEMPERATURE 163 - 191 C The hot melt adhesive shall function at the specified operating temperature range for acceptable production application. ENGINEERING MATERIAL SPECIFICATION ESB-M2G183-A Page 3 of 4 Copyright 2014, Ford Global Technologies, Inc. 3.11 HEAT STABILITY a

13、t 177 C, max 12,000 cP (mPa.s) (Brookfield #5 Spindle, 10 r.p.m. with no skin or gel formation) Test Method Place a 1/2 pt (0.3 1) sample of the material in an open metal can and place in mechanical convection oven for 96 h at 177 +/- 3 C, and examine for a skin or gel formation. Agitate material at

14、 177 C just prior to conducting viscosity of the aged sample with the Brookfield #5 Spindle at 10 r.p.m. 3.12 STORAGE LIFE, when stored at 0 to 49 C Indefinite 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specific

15、ation. 5.1 WEIGHT PER VOLUME 7.8 - 8.8 lb/gal (ASTM D 816) (0.93 - 1.05 kg/l) The weight tolerance for any one supplier shall be +/- 0.2 lb/gal (0.024 kg/l) based on the recorded weight for his original approved production sample. 5.2 DEGRADATION POINT 204 C This adhesive may be used at 191 - 204 C

16、for short periods of time (100 h max). The material must not be used under any circumstances when the temperature exceeds 204 C, since decomposition occurs, with permanent degradation of physical and adhesive properties. 5.3 PRESSURE SENSITIVE TACK When hot melt adhesive has cooled to 23 +/- 2 C, the material shall remain tacky for 90 days, with the surface protected from dirt or dust contamination. ENGINEERING MATERIAL SPECIFICATION ESB-M2G183-A Page 4 of 4 Copyright 2014, Ford Global Technologies, Inc.