FORD ESB-M1L120-A-2003 CABLE PRIMARY LOW TENSION 85 VINYL INSULATED - REDUCED WALL THICKNESS TO BE USED WITH FORD WSS-M99P1111-A 《乙烯基塑料绝缘的（小壁厚度）85℃PRIMARY低压电缆 与标准FORD WSS-M99P11.pdf

《FORD ESB-M1L120-A-2003 CABLE PRIMARY LOW TENSION 85 VINYL INSULATED - REDUCED WALL THICKNESS TO BE USED WITH FORD WSS-M99P1111-A 《乙烯基塑料绝缘的（小壁厚度）85℃PRIMARY低压电缆 与标准FORD WSS-M99P11.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1L120-A-2003 CABLE PRIMARY LOW TENSION 85 VINYL INSULATED - REDUCED WALL THICKNESS TO BE USED WITH FORD WSS-M99P1111-A 《乙烯基塑料绝缘的（小壁厚度）85℃PRIMARY低压电缆 与标准FORD WSS-M99P11.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 06 25 Revised Para 3.0 inserted; Para 3.1, 3.5, & 4 deleted 1986 02 03 CAQ1-DR532891 Released Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 5 CABLE, PRIMARY LOW TENSION, 85 C ESB-M1L120-A VINYL I

2、NSULATED - REDUCED WALL THICKNESS 1. SCOPE The material defined by this specification is a low tension stranded cable, vinyl-insulated with non-coated conductor. The cable is similar to SAE J 1128 Type GPT (General Purpose - Thermoplastic Insulated) but with a reduced insulation wall thickness, and

3、an 85 C classification. 2. APPLICATION This specification was released originally for material used in automotive electrical harnesses. Note: The assemblers of electrical wire harnesses shall use the bulk wire suppliers as shown in the Ford Motor Company Materials Approved Source List. 3. REQUIREMEN

4、TS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CONDUCTOR 3.2.1 The individual strands of the conductor shall be soft or annealed copper conforming to ASTM B

5、3 - 1974, except strand dimensions. These dimensions shall be controlled to yield the cross-sectional area listed for the conductor of the finished cable per Table 1. Conductor area shall be determined by measuring individual strand diameters and calculating the sum of the individual strand areas. A

6、s an alternate method, conductor area may also be determined in accordance with ASTM B 263 - 1958. 3.2.2 The strands shall be bunched per ASTM B 174 - 1971. The maximum lay length shall be as specified in ASTM B 174 - 1971 Table 2, Column A. Conductor strand count shall comply with Table 1. Missing

7、strands are not allowed. 3.3 INSULATION 3.3.1 The color of the vinyl insulation shall be specified on the engineering drawing of the component utilizing this material. Base and stripe color codes shall correspond to SAE J 1128. Where striping is specified, the stripe shall be a minimum of 0.5 mm wid

8、e, but not more than 19% of the circumference of the wire. The stripe shall be of the same material as the vinyl insulation. 3.3.2 The insulating material shall be a polyvinyl chloride (PVC) material, homogeneous in character, and similar to SAE J 1128 Type GPT. The material shall adhere closely to,

9、 but strip readily from the conductors, leaving them free of insulation and in suitable condition for applying terminals. ENGINEERING MATERIAL SPECIFICATIONESB-M1L120-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 5 3.3.3 Insulation thickness shall comply w

10、ith the requirements of Table 2. Insulation thickness shall be measured in accordance with ANSI/UL-1581-1985, Reference Standard for Electrical Wires, Cables, and Flexible Cords, Paragraphs 240. through 250.11. A 0.51 mm diameter pin will be used for determining minimum insulation thickness at any p

11、oint. 3.4 CABLE QUALITY (TESTS) The Physical Properties, High Temperature, Dielectric, and Cold Bend Tests shall all be conducted in accordance with SAE J 1128. Note: The following paragraphs shall be tested in accordance with SAE J 1128, but with exceptions to the requirements as indicated. 3.4.1 O

12、il Absorption Test (SAE J 1128) Except that the outside diameter of the cable shall not increase more than 15% when measured 4 h after removal from the oil. 3.4.2 Pinch Test (SAE J 1128) Values as specified in Table 3 of this document. 3.4.3 Flame Test A 610 mm specimen shall be suspended in a verti

13、cal position within a partial enclosure which allows a flow of sufficient air for complete combustion but is free from drafts. The tip of a 50 mm gas flame with an inner cone one-third its height shall then be applied to the end of the specimen for 15 seconds. After removal of the flame, the specime

14、n shall not continue to burn for more than 30 seconds. ENGINEERING MATERIAL SPECIFICATIONESB-M1L120-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 3 of 5 TABLE 1 AWG Wire Size Conductor Strand No. Stranding Nom Size inches Conductor Minimum Cir Mil Area # Maximu

15、m Cir Mil Nominal* Cond. Dia inches 22 7 0.0100 672 719 0.030 20 7 0.0126 1072 1147 0.038 18 19 0.0092 1537 1645 0.046 18 16 0.0100 1537 1645 0.046 16 19 0.0113 2336 2500 0.057 14 19 0.0142 3702 3961 0.071 12 19 0.0179 5833 6241 0.090 10 19 0.0226 9343 9997 0.113 METRIC Wire Size Conductor Strand No

16、. Stranding Nom Size mm Conductor Minimum mm2Area # Maximum mm2Nominal* Cond. Dia mm 0.35 7 0.25 0.32 0.34 0.76 0.50 7 0.32 0.51 0.55 0.97 0.80 19 0.23 0.76 0.81 1.17 1.00 19 0.28 1.12 1.20 1.45 2.00 19 0.36 1.85 1.98 1.80 3.00 19 0.45 2.91 3.11 2.29 5.00 19 0.57 4.65 4.98 2.87 NOTE: Metric sizes ar

17、e not direct conversions from AWG wire sizes. They are not considered to be equivalent substitutes. * Neither the nominal strand diameter nor normal conductor diameter are intended for checking purposes. However, the individual strands must not vary from nominal by more than plus or minus 10%. # Con

18、ductor areas are based on SAE J 1128 minimums where applicable, with a 7% tolerance. ENGINEERING MATERIAL SPECIFICATIONESB-M1L120-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 4 of 5 TABLE 2 AWG Nominal Wire Size Minimum Insulation Thickness Nominal Insulation

19、Thickness # Finished Cable Diameter inches AWG inches inches Minimum Maximum Nominal 22 0.012 0.0.16 0.059 0.065 0.062 20 0.012 0.016 0.067 0.073 0.070 18 0.012 0.016 0.075 0.081 0.078 16 0.012 0.016 0.086 0.092 0.089 14 0.012 0.016 0.100 0.106 0.103 12 0.015 0.018 0.122 0.130 0.126 10 0.017 0.021 0

20、.151 0.159 0.155 METRIC Nominal Wire Size Minimum Insulation Thickness Nominal Insulation Thickness # Finished Cable Diameter mm Metric Mm Mm Minimum Maximum Nominal 22 0.012 0.0.16 0.059 0.065 0.062 20 0.012 0.016 0.067 0.073 0.070 18 0.012 0.016 0.075 0.081 0.078 16 0.012 0.016 0.086 0.092 0.089 1

21、4 0.012 0.016 0.100 0.106 0.103 12 0.015 0.018 0.122 0.130 0.126 10 0.017 0.021 0.151 0.159 0.155 ENGINEERING MATERIAL SPECIFICATIONESB-M1L120-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 5 of 5 TABLE 3 PINCH TEST Wire Size Min. Pinch Resistance Gauge mm sq LB kf 22 0.35 2.6 1.2 20 0.50 3.3 1.5 18 0.80 3.3 1.5 16 1.00 4.4 2.0 14 2.00 4.4 2.0 12 3.00 5.5 2.5 10 5.00 5.5 2.5