DIN EN 1559-4-2015 Founding - Technical conditions of delivery - Part 4 Additional requirements for aluminium alloy castings German version EN 1559-4 2015《铸造 交货技术条件 第4部分 铝合金铸件的附加要求.pdf

《DIN EN 1559-4-2015 Founding - Technical conditions of delivery - Part 4 Additional requirements for aluminium alloy castings German version EN 1559-4 2015《铸造 交货技术条件 第4部分 铝合金铸件的附加要求.pdf》由会员分享，可在线阅读，更多相关《DIN EN 1559-4-2015 Founding - Technical conditions of delivery - Part 4 Additional requirements for aluminium alloy castings German version EN 1559-4 2015《铸造 交货技术条件 第4部分 铝合金铸件的附加要求.pdf（15页珍藏版）》请在麦多课文档分享上搜索。

1、May 2015 Translation by DIN-Sprachendienst.English price group 10No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77

2、.150.10!%BZz“2315587www.din.deDDIN EN 1559-4Founding Technical conditions of delivery Part 4: Additional requirements for aluminium alloy castings;English version EN 1559-4:2015,English translation of DIN EN 1559-4:2015-05Gieereiwesen Technische Lieferbedingungen Teil 4: Zustzliche Anforderungen an

3、Gussstcke aus Aluminiumlegierungen;Englische Fassung EN 1559-4:2015,Englische bersetzung von DIN EN 1559-4:2015-05Fonderie Conditions techniques de fourniture Partie 4: Spcifications complmentaires pour les pices moules en alliagesdaluminium;Version anglaise EN 1559-4:2015,Traduction anglaise de DIN

4、 EN 1559-4:2015-05SupersedesDIN EN 1559-4:1999-07www.beuth.deIn case of doubt, the German-language original shall be considered authoritative.Document comprises 15 pages 04.15 DIN EN 1559-4:2015-05 2 A comma is used as the decimal marker. National foreword This document (EN 1559-4:2015) has been pre

5、pared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys” (Secretariat: AFNOR, France). The responsible German body involved in its preparation was the DIN-Normenausschuss Gieereiwesen (DIN Standards Committee Foundry Practice), Working Committee NA 036-00-07 AA Aluminiumgusslegierung

6、en. Amendments This standard differs from DIN EN 1559-4:1999-07 as follows: a) the standard has been editorially revised and brought in line with EN 1559-1:2011; b) the definition of 3.1 “excavation” has been modified; c) Figures A.1 and A.2: key and references have been clarified. Previous editions

7、 DIN EN 1559-4: 1999-07 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 1559-4 February 2015 ICS 77.150.10 Supersedes EN 1559-4:1999English Version Founding - Technical conditions of delivery - Part 4: Additional requirements for aluminium alloy castings Fonderie - Conditions techniques de four

8、niture - Partie 4: Spcifications complmentaires pour les pices moules en alliages daluminium Gieereiwesen - Technische Lieferbedingungen - Teil 4: Zustzliche Anforderungen an Gussstcke aus Aluminiumlegierungen This European Standard was approved by CEN on 26 December 2014. CEN members are bound to c

9、omply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENE

10、LEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the

11、 same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembo

12、urg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels

13、 2015 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 1559-4:2015 EEN 1559-4:2015 (E) 2 Contents Page Foreword 3 Introduction . 4 1 Scope 5 2 Normative references 5 3 Terms and definitions . 5 4 Information to be supplied by the pu

14、rchaser 6 4.1 Mandatory information 6 4.2 Optional information 6 4.3 Drawing, patterns and tools 6 4.4 Information on the mass . 6 4.5 Preliminary sample 6 4.6 Initial sample 6 5 Designations . 6 6 Manufacture 6 6.1 Manufacturing process 6 6.2 Welding operations 6 7 Requirements . 7 7.1 General 7 7.

15、2 Material 7 7.3 Casting 7 8 Inspection . 9 8.1 General 9 8.2 Type of inspection documents and type of inspection 9 8.3 Test unit 9 8.4 Samples. 9 8.5 Test procedures . 9 8.6 Invalidation of test results. 9 8.7 Retests 9 8.8 Sorting and reprocessing 9 9 Marking . 9 10 Packaging and surface protectio

16、n . 9 11 Complaints 9 Annex A (informative) Procedure for the classification of excavation for finishing welding 10 Annex B (informative) Significant technical changes between this European Standard and the previous edition . 12 Bibliography 13 DINEN 1559-4:2015-05EN 1559-4:2015(E)3 Foreword This do

17、cument (EN 1559-4:2015) has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the lates

18、t by August 2015 and conflicting national standards shall be withdrawn at the latest by August 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such

19、patent rights. This document supersedes EN 1559-4:1999. Within its programme of work, Technical Committee CEN/TC 132 requested CEN/TC 132/WG 22 “Revision of EN 1559-4:1999“ to revise the following standard: EN 1559-4, Founding Technical conditions of delivery Part 4: Additional requirements for alum

20、inium alloy castings. Annex B provides details of significant technical changes between this European Standard and the previous edition. This European Standard is part of a series of standards which specify technical delivery conditions for castings. The other standards in this series are: EN 1559-1

21、, Founding Technical conditions of delivery Part 1: General; EN 1559-2, Founding Technical conditions of delivery Part 2: Additional requirements for steel castings; EN 1559-3, Founding Technical conditions of delivery Part 3: Additional requirements for iron castings; EN 1559-5, Founding Technical

22、conditions of delivery Part 5: Additional requirements for magnesium alloy castings; EN 1559-6, Founding Technical conditions of delivery Part 6: Additional requirements for zinc alloy castings. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following

23、countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway

24、, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 1559-4:2015-05 EN 1559-4:2015 (E) 4 Introduction In order to assist manufacturers and purchasers to prepare proper contractual arrangements and prevent misunderstandings, CEN/TC 190 “Fo

25、undry Technology“ approved the preparation of a series of standards covering technical delivery conditions. These have been prepared as separate parts. This European Standard covers the additional technical delivery conditions for aluminium alloy casting materials and has the same structure as EN 15

26、59-1 “Founding - Technical conditions of delivery Part 1: General“. This European Standard cannot be used alone for compiling a specification for ordering and supplying aluminium alloy castings, but as a complement to EN 1559-1. The structure of this standard is as follows: clauses and sub clauses p

27、receded by indicate no additional conditions to EN 1559-1; clauses and sub clauses marked with a single dot indicate that conditions shall be agreed at the time of enquiry and order; clauses and sub clauses marked with two dots indicate that conditions can be agreed at the time of enquiry and order

28、(optional); clauses and sub clauses without a symbol are mandatory; clauses and sub clauses preceded by are supplementary to those in EN 1559-1; clauses and sub clauses preceded by completely replace those in EN 1559-1. DIN EN 1559-4:2015-05 EN 1559-4:2015 (E) 5 1 Scope This European Standard specif

29、ies the additional technical delivery conditions for aluminium alloy castings unless other conditions have been agreed at the time of enquiry and order. This European Standard retains the same structure and numbering system as used in EN 1559-1 and repeats the numbering of clauses and sub-clauses ev

30、en if nothing extra or different has been added. It also indicates items specific to aluminium alloy castings under existing or new headings. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. Fo

31、r dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 1371-1, Founding Liquid penetrant testing Part 1: Sand, gravity die and low pressure die castings EN 1559-1, Founding Technical conditions

32、of delivery Part 1: General EN 1706, Aluminium and aluminium alloys Castings Chemical composition and mechanical properties EN 12681, Founding Radiographic examination 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 1559-1, in the applicable material

33、standard and the following apply. 3.1 excavation cavity produced by the removal of cast material prior to subsequent welding (or other finishing methods) DIN EN 1559-4:2015-05 EN 1559-4:2015 (E) 64 Information to be supplied by the purchaser 4.1 Mandatory information 4.2 Optional information 4.3 Dra

34、wing, patterns and tools 4.4 Information on the mass 4.5 Preliminary sample 4.6 Initial sample If required, a minimum of two initial samples shall be supplied to the purchaser for approval. If these initial samples are accepted, one shall be retained by the purchaser and one returned to the manufact

35、urer marked as “approved“. Supplementary initial samples (one for metallurgical and the other for dimensional purposes) should be retained either by the manufacturer or by the purchaser. NOTE Testing of initial samples by the manufacturer can be agreed. 5 Designations 6 Manufacture 6.1 Manufacturing

36、 process 6.2 Welding operations 6.2.1 General 6.2.2 Production welding Production welding is permitted, unless otherwise agreed at the enquiry and order stage. For railway applications, production welding has to be agreed separately (see EN 15085-2). Actions to finish castings or eliminate casting i

37、mperfections may include the use of a filler metal deposited by a suitable welding process or the insertion of a machined piece secured by welding. The manufacturers and purchasers attention is drawn to the need for approved procedures and suitably qualified welders (see EN ISO 15614-4, for finishin

38、g welding). After preparing the casting for finishing welding, the excavation can be classified in accordance with the procedure given in Annex A. 6.2.2.1 6.2.2.2 DIN EN 1559-4:2015-05 EN 1559-4:2015(E)7 6.2.2.3 6.2.2.4 6.2.2.5 6.2.2.6 7 Requirements 7.1 General 7.2 Material 7.2.1 Chemical compositi

39、on NOTE Metal is usually taken for optical emission spectrometry analysis at the time the castings are made, in the form of a chill cast disc (see EN 14361). 7.2.2 Mechanical properties 7.2.3 Other properties 7.2.4 Additional requirements The manufacturer shall examine the results of any treatment o

40、f the melt carried out during the melting process by using appropriate methods. 7.3 Casting 7.3.1 Chemical composition For chemical composition of aluminium alloy castings, refer to the appropriate table in EN 1706. 7.3.2 Mechanical properties 7.3.3 Outer and inner conditions (non-destructive testin

41、g) Liquid penetrant examination shall be carried out in accordance with EN 1371-1. Radiographic inspection shall be carried out in accordance with EN 12681. Where applicable, unacceptable external and internal discontinuities shall be eliminated by production welding (see 6.2.2) or other agreed meth

42、ods. 7.3.3.1 7.3.3.2 7.3.3.3 7.3.3.4 DIN EN 1559-4:2015-05 EN 1559-4:2015 (E) 87.3.4 Conditions of the casting 7.3.4.1 Shape and size 7.3.4.2 Fettling and finishing 7.3.4.3 In order to eliminate leaks in castings, it is possible with the approval of the purchaser, to use impregnation. The impregnati

43、on medium and method, maximum permitted size of discontinuities and retest procedures shall be agreed between purchaser and manufacturer. 7.3.4.4 In the case of as cast castings, it is recommended that the purchaser agrees with the manufacturer on the choice of any non-destructive testing and criter

44、ia to determine the acceptability of a subsequently machined surface. Unless specifically agreed, discontinuities revealed on the machined surface should not be regarded as a cause for rejection. If the porosity on machined surfaces is to be assessed, manufacturer and purchaser should agree on the m

45、ethod to be used. 7.3.5 Mass of the casting 7.3.6 Additional requirements regarding the conditions of the casting 7.3.6.1 Macrostructure Where appropriate, a macroscopic examination of a suitably prepared and etched section shall be used to assess the grain size and/or structural discontinuities of

46、a casting to agreed criteria. Assessment is usually carried out with or without low magnification. 7.3.6.2 Microstructure Where appropriate, a microscopic examination of a suitably polished and etched section shall be used to determine the metallurgical structure of a casting to agreed criteria. Ass

47、essment is usually carried out at a high magnification and includes the nature, shape and distribution of the structural constituents. NOTE A cooling curve/thermal analysis carried out on a sample of liquid alloy before casting, can predict, to a limited extent, the metallurgical structure to be exp

48、ected in the casting. 7.3.6.3 Density evaluation can be used to estimate the soundness of castings by weighting in air and water to agreed criteria. DIN EN 1559-4:2015-05 EN 1559-4:2015(E)9 8 Inspection 8.1 General 8.2 Type of inspection documents and type of inspection 8.3 Test unit 8.3.1 Formation of test units 8.3.2 Size of