BS ISO 3597-3-2003 Textile-glass-reinforced plastics - Determination of mechanical properties on rods made of roving-reinforced resin - Determination of compressive strength《纺织玻璃纤维.pdf

《BS ISO 3597-3-2003 Textile-glass-reinforced plastics - Determination of mechanical properties on rods made of roving-reinforced resin - Determination of compressive strength《纺织玻璃纤维.pdf》由会员分享，可在线阅读，更多相关《BS ISO 3597-3-2003 Textile-glass-reinforced plastics - Determination of mechanical properties on rods made of roving-reinforced resin - Determination of compressive strength《纺织玻璃纤维.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS ISO 3597-3:2003 Textile-glass-reinforced plastics Determination of mechanical properties on rods made of roving-reinforced resin Part 3: Determination of compressive strength ICS 59.100.10; 83.120 BS ISO 3597-3:2003 This British Standard was published under the authority of the S

2、tandards Policy and Strategy Committee on 30 October 2003 BSI 30 October 2003 ISBN 0 580 42833 8 National foreword This British Standard reproduces verbatim ISO 3597-3:2003 and implements it as the UK national standard. It supersedes BS 2782-10 Method 1008C:1996 which is withdrawn. The UK participat

3、ion in its preparation was entrusted to Technical Committee PRI/42, Fibre reinforced thermosetting plastics and prepregs, which has the responsibility to: A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which i

4、mplement international publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not pu

5、rport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. aid enquirers to understand the text; present to the responsible international/European commit

6、tee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. Summary of pages This document comprises a front cover, an inside front cover, the ISO title page, pages ii to

7、iv, pages 1 to 4, an inside back cover and a back cover. The BSI copyright notice displayed in this document indicates when the document was last issued. Amendments issued since publication Amd. No. Date Comments Reference number ISO 3597-3:2003(E)INTERNATIONAL STANDARD ISO 3597-3 Second edition 200

8、3-10-01 Textile-glass-reinforced plastics Determination of mechanical properties on rods made of roving-reinforced resin Part 3: Determination of compressive strength Plastiques renforcs verre textile Dtermination des proprits mcaniques sur joncs de stratifils Partie 3: Dtermination de la rsistance

9、en compression BSISO35973:2003ii IS-7953 O3:(3002E) I SO 3002 All irhgts seredevr iiiContents Page Foreword iv 1 Scope 1 2 Normative references. 1 3 Apparatus. 1 4 Preparation and conditioning of specimens 2 5 Procedure. 2 6 Expression of results 4 7 Precision 4 8 Test report 4 BSISO35973:2003iiiISO

10、 3597-3:2003(E) iv I SO 3002 All irhgts seredevrForeword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each m

11、ember body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International

12、Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards a

13、dopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of p

14、atent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 3597-3 was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 13, Composites and reinforcement fibres. This second edition cancels and replaces the first edition (ISO 3597-3:1993), wh

15、ich has been technically revised. ISO 3597 consists of the following parts, under the general title Textile-glass-reinforced plastics Determination of mechanical properties on rods made of roving-reinforced resin: Part 1: General considerations and preparation of rods Part 2: Determination of flexur

16、al strength Part 3: Determination of compressive strength Part 4: Determination of apparent interlaminar shear strength BSISO35973:2003ivINTENRATIONAL TSANDADR IS-7953 O3:(3002E)I SO 3002 All irhgts seredevr 1Textile-glass-reinforced plastics Determination of mechanical properties on rods made of ro

17、ving-reinforced resin Part 3: Determination of compressive strength 1 Scope This part of ISO 3597 specifies a method for determining the compressive strength of composite rods of circular cross-section made of roving-reinforced resin. The test may be carried out on “as-moulded” rods, or on rods that

18、 have been pretreated by immersion in boiling water (or another medium) for a specified time. The test is intended for inspection and quality control of rovings or for evaluating their suitability for use in a resin system. The results obtained are not intended for the generation of design data. 2 N

19、ormative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 3597-1, Textile-glass-rei

20、nforced plastics Determination of mechanical properties on rods made of roving-reinforced resin Part 1: General considerations and preparation of rods 3 Apparatus 3.1 Compression-testing machine, capable of maintaining a compression speed of 1 mm/min. 3.2 Two test jigs, for example as shown in Figur

21、e 1, each consisting of: a) a baseplate (1); b) an elastic compression pad (2) (made of polyamide, for example); c) a support ring (3). Parts 1 and 3 of the upper jig may be bolted together to prevent them falling (see Figure 2 for an example of how this may be done). The opening in the support ring

22、 shall fit snugly round the specimen in order to ensure consistent results. The maximum permitted opening diameter is 0,1 mm larger than the specimen diameter. If the specimen diameter is more than 0,1 mm smaller than that of the opening in the support ring, a support ring with a smaller opening sha

23、ll be used. Deviations from nominal specimen dimensions can occur due to variations in the inner diameter of the mould or resin shrinkage. BSISO35973:20031ISO 3597-3:2003(E) 2 I SO 3002 All irhgts seredevr3.3 Micrometer or vernier gauge, capable of measuring to the nearest 0,1 mm. Dimensions in mill

24、imetres Key 1 baseplate 2 elastic compression pad 3 support ring Figure 1 Example of jig for testing specimens of diameter 6,0 mm 4 Preparation and conditioning of specimens The procedure specified hereafter is suitable for specimens of diameter 6 mm to be tested “as-moulded” and, if required, pre-t

25、reated. For each type of test (“as-moulded” or pre-treated), the minimum required number of specimens is eight. If specific statistical limits are agreed between interested parties, additional specimens may be tested to permit statistical analysis of the results. Prepare a sufficient number of rods,

26、 using the method specified in ISO 3597-1, and cut them into specimens of length 22,5 mm. Take care to ensure that the cut ends of the specimens are parallel. When rods of diameter other than 6 mm are used, the ratio of the rod length L to the rod diameter d shall satisfy the following equation: L =

27、 0,625d 25 Procedure 5.1 Before carrying out the compressive test, measure the diameter of each test specimen with a micrometer or vernier gauge (3.3) to the nearest 0,1 mm at two points around the circumference located 90 apart at the centre of the specimen. Use the average of these two measurement

28、s in the calculation of the results. BSISO35973:20032ISO 3597-3:2003(E) I SO 3002 All irhgts seredevr 35.2 Conduct the compressive test in the same standard laboratory atmosphere as that used for specimen conditioning. Assemble a test specimen with a test jig (3.2) at each end. Place the assembly ve

29、rtically between the platens of the test machine (3.1) (see also Figure 2). Compress the test specimen at a speed of 1 mm/min until the specimen fails. Record the maximum force, in newtons, that occurred during the test. Key 1 upper plate of test machine 2 test specimen 3 lower plate of test machine

30、 Figure 2 Example of test assembly in test machine with bolted upper jig 5.3 The person requiring the test may require that the mode of failure be recorded (see Figure 3). a) Type K (crushing) b) Type L (splitting) c) Type M (buckling) d) Type N (edge failure) Figure 3 Typical failure modes BSISO359

31、73:20033ISO 3597-3:2003(E) 4 I SO 3002 All irhgts seredevr6 Expression of results For each specimen, calculate the compressive strength C , expressed in megapascals, using the equation: C 2 4 F d = where F is the maximum force, in newtons, that is recorded during the test; d is the diameter, in mill

32、imetres, of the test specimen. For each type of test (“as-moulded” or pretreated), calculate the average of the results obtained on each specimen, discarding those results which are lower than 50 % of this average. Report the resulting value as the compressive strength of the material. If fewer than

33、 five results are available for this calculation, a further set of test specimens shall be prepared and tested. If this second set results in similar difficulties, record this situation in the test report. 7 Precision The precision of this test method is not known because inter-laboratory data are n

34、ot available. When inter- laboratory data are obtained, a precision statement will be added at the following revision. 8 Test report The test report shall include the following information: a) a reference to this part of ISO 3597; b) all information necessary for complete identification of the rovin

35、g tested; c) all information necessary for complete identification of the resin used; d) the diameter of the mould used to prepare the test specimens; e) whether a release agent was used and, if so, details of the agent used; f) the curing and post-curing conditions; g) the test atmosphere; h) the t

36、est results: 1) for “as-moulded” specimens, the glass content, diameter, compressive strength and, if required, mode of failure of each specimen tested and (except for the mode of failure) the average value; 2) if testing was also carried out after pretreatment: the medium used; the length of the pr

37、etreatment; the individual and average values of the compressive strength after pretreatment. BSISO35973:20034blankBS ISO 3597-3:2003 BSI 389 Chiswick High Road London W4 4AL BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presen

38、ts the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI

39、to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 899

40、6 9000. Fax: +44 (0)20 8996 7400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer

41、 Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: ordersbsi-. Standards are also available from the BSI website at http:/www.bsi-. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Sta

42、ndards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details o

43、n all its products and services. Contact the Information Centre. Tel: +44 (0)20 8996 7111. Fax: +44 (0)20 8996 7048. Email: infobsi-. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these

44、and other benefits contact Membership Administration. Tel: +44 (0)20 8996 7002. Fax: +44 (0)20 8996 7001. Email: membershipbsi-. Information regarding online access to British Standards via British Standards Online can be found at http:/www.bsi- Further information about BSI is available on the BSI

45、website at http:/www.bsi-. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a r

46、etrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. Details and advice can be obtained from the Copyright & Licensing Manager. Tel: +44 (0)20 8996 7070. Fax: +44 (0)20 8996 7553. Email: copyrightbsi-.