BS EN 61249-2-9-2003 Materials for interconnection structures - Sectional specification set for reinforced base materials clad and unclad - Reinforced base materials clad and unclam.pdf

《BS EN 61249-2-9-2003 Materials for interconnection structures - Sectional specification set for reinforced base materials clad and unclad - Reinforced base materials clad and unclam.pdf》由会员分享，可在线阅读，更多相关《BS EN 61249-2-9-2003 Materials for interconnection structures - Sectional specification set for reinforced base materials clad and unclad - Reinforced base materials clad and unclam.pdf（26页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS EN 61249-2-9:2003 Materials for printed boards and other interconnecting structures Part 2-9: Reinforced base materials clad and unclad Bismaleimide/triazine, modified epoxide or unmodified, woven E-glass reinforced laminated sheets of defined flammability (vertical burning test)

2、, copper-clad The European Standard EN 61249-2-9:2003 has the status of a British Standard ICS 31.180 BS EN 61249-2-9:2003 This British Standard was published under the authority of the Standards Policy and Strategy Committee on 14 August 2003 BSI 14 August 2003 ISBN 0 580 42390 5 National foreword

3、This British Standard is the official English language version of EN 61249-2-9:2003. It is identical with IEC 61249-2-9:2003. The UK participation in its preparation was entrusted to Technical Committee EPL/501, Electronic assembly technology, which has the responsibility to: A list of organizations

4、 represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence

5、Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself

6、confer immunity from legal obligations. aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and prom

7、ulgate them in the UK. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 23 and a back cover. The BSI copyright date displayed in this document indicates when the document was last issued. Amendments issued since publication Amd. No. Date Co

8、mmentsEUROPEAN STANDARD EN 61249-2-9 NORME EUROPENNE EUROPISCHE NORM May 2003 CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Central Secretariat: rue de Stassart 35, B - 1050 Brussels 20

9、03 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 61249-2-9:2003 E ICS 31.180 English version Materials for printed boards and other interconnecting structures Part 2-9: Reinforced base materials clad and unclad - Bismaleimide/tr

10、iazine, modified epoxide or unmodified, woven E-glass reinforced laminated sheets of defined flammability (vertical burning test), copper-clad (IEC 61249-2-9:2003) Matriaux pour circuits imprims et autres structures dinterconnection Partie 2-9: Matriaux de base renforcs, plaqus et non plaqus Feuille

11、s stratifies renforces en tissu de verre de type E poxyde, modifi ou non, et bismalimide/triazine, dinflammabilit dfinie (essai de combustion verticale), plaques cuivre (CEI 61249-2-9:2003) Materialien fr Leiterplatten und andere Verbindungsstrukturen Teil 2-9: Kaschierte und unkaschierte verstrkte

12、Basismaterialien - Kupferkaschierte mit E-Glasgewebe verstrkte Laminattafeln auf der Basis von modifiziertem oder nicht-modifiziertem Epoxidharz, modifiziert mit Bismaleinimid/Triazin, definierter Brennbarkeit (Brennprfung mit vertikaler Prflingslage) (IEC 61249-2-9:2003) This European Standard was

13、approved by CENELEC on 2003-04-01. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such

14、national standards may be obtained on application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own lan

15、guage and notified to the Central Secretariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, N

16、orway, Portugal, Slovakia, Spain, Sweden, Switzerland and United Kingdom. Foreword The text of document 91/360/FDIS, future edition 1 of IEC 61249-2-9, prepared by IEC TC 91, Electronics assembly technology, was submitted to the IEC-CENELEC parallel vote and was approved by CENELEC as EN 61249-2-9 o

17、n 2003-04-01. The following dates were fixed: latest date by which the EN has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 2004-01-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2006-04

18、-01 Annexes designated “normative“ are part of the body of the standard. Annexes designated “informative“ are given for information only. In this standard, annex ZA is normative and annexes A, B and C are informative. Annex ZA has been added by CENELEC. _ Endorsement notice The text of the Internati

19、onal Standard IEC 61249-2-9:2003 was approved by CENELEC as a European Standard without any modification. _ Page2 EN6124929:200361249-2-9 IEC:2003 3 CONTENTS 1 Scope.5 2 Normative references5 3 Materials and construction 5 3.1 Resin system.5 3.2 Reinforcement.6 3.3 Metal foil .6 4 Internal marking6

20、5 Electrical properties 6 6 Non-electrical properties of the copper-clad laminate 6 6.1 Appearance of the copper-clad sheet.6 6.2 Appearance of the unclad face.8 6.3 Laminate thickness8 6.4 Bow and twist 9 6.5 Properties related to the copper foil bond.9 6.6 Punching and machining10 6.7 Dimensional

21、stability10 6.8 Sheet sizes11 6.9 Cut panels.11 7 Non-electrical properties of the base material after complete removal of the copper foil.12 7.1 Appearance of the dielectric base material.12 7.2 Flexural strength13 7.3 Flammability13 7.4 Water absorption.14 7.5 Measling14 7.6 Glass transition tempe

22、rature and cure factor14 8 Quality assurance.15 8.1 Quality system.15 8.2 Responsibility for inspection.15 8.3 Qualification inspection15 8.4 Quality conformance inspection .15 8.5 Certificate of conformance.15 8.6 Safety data sheet.15 9 Packaging and marking.16 10 Ordering information.16 Annex A (i

23、nformative) Engineering information .17 Annex B (informative) Common laminate constructions.19 Annex C (informative) Guideline for qualification and conformance inspection.21 Annex ZA (normative) Normative references to international publications with their corresponding European publications22 Bibl

24、iography23 Page3 EN6124929:200361249-2-9 IEC:2003 4 Table 1 Electrical properties .6 Table 2 Nominal thickness and tolerance of metal-clad laminate.8 Table 3 Bow and twist 9 Table 4 Pull-off and peel strength.10 Table 5 Dimensional stability11 Table 6 Size tolerance for cut panels12 Table 7 Rectangu

25、larity of cut panels.12 Table 8 Flexural strength13 Table 9 Flammability 13 Table 10 Water absorption .14 Table 11 Measling14 Table 12 Glass transition temperature and cure factor 14 Page4 EN6124929:200361249-2-9 IEC:2003 5 MATERIALS FOR PRINTED BOARDS AND OTHER INTERCONNECTING STRUCTURES Part 2-9:

26、Reinforced base materials, clad and unclad Bismaleimide/triazine modified epoxide or unmodified, woven E-glass reinforced laminated sheets of defined flammability (vertical burning test), copper-clad 1 Scope This part of IEC 61249 gives requirements for properties of bismaleimide/triazine modified e

27、poxide, or unmodified, woven E-glass reinforced laminate sheets of defined flammability (vertical burning test), copper-clad in thicknesses of 0,05 mm to 3,2 mm. The flammability rating is achieved through the use of brominated fire retardants contained as an integral part of the epoxide polymeric s

28、tructure. The glass transition temperature is defined to be 160 C minimum. Some property requirements may have several classes of performance. The class desired needs to be specified on the purchase order, otherwise the default class of material may be supplied. 2 Normative references The following

29、referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. IEC 61189-2:1997, Test methods for electrical materials, interc

30、onnection structures and assemblies Part 2: Test method for interconnection structures IEC 61249-5-1:1995, Materials for interconnection structures Part 5: Sectional specification set for conductive foils and films with and without coatings Section 1: Copper foils (for the manufacture of copper-clad

31、 base materials) ISO 9000:2000, Quality management systems Fundamentals and vocabulary ISO 11014-1:1994, Safety data sheet for chemical products Part 1: Content and order of sections ISO 14001:1996, Environmental management systems Specification with guidance for use 3 Materials and construction The

32、 sheet consists of an insulating base with metal-foil bonded to one side or both. 3.1 Resin system Bismaleimide/triazine modified brominated epoxide resulting in a laminate with a glass transition temperature of 160 C minimum. Contrast agents may be added to enhance processing such as automated opti

33、cal inspection (AOI). Its flame resistance is defined in terms of the flammability requirements of 7.3. Page5 EN6124929:200361249-2-9 IEC:2003 6 3.2 Reinforcement Woven E-glass as specified in IEC 61249-6-3, woven E-glass fabric (for the manufacture of prepreg and copper clad materials). 3.3 Metal f

34、oil Copper as specified in IEC 61249-5-1, copper foil (for the manufacture of copper-clad materials). The preferred foils are electro-deposited of defined ductility. 4 Internal marking Not specified 5 Electrical properties The requirements for the electrical properties are shown in Table 1. Table 1

35、Electrical properties Property Test method (IEC 61189-2) Requirement Resistance of foil 2E12 As specified in IEC 61249-5-1 Surface resistance after damp heat while in the humidity chamber (optional) 2E03 10 000 M Surface resistance after damp heat and recovery 2E03 50 000 M Volume resistivity after

36、damp heat while in the humidity chamber (optional) 2E04 10 000 Mm Volume resistivity after damp heat and recovery 2E04 50 000 Mm Relative permittivity after damp heat and recovery at 1 MHz 2E10 5,0 Dissipation factor after damp heat and recovery at 1 MHz 2E10 0,020 Electric strength (only for materi

37、al thicknesses 0,5 mm) 2E11 30 kV/mm Arc resistance 2E14 60 s Dielectric breakdown (only for material thicknesses 0,5 mm) 2E15 40 kV Surface resistance at 170 C 2E07 50 000 M Volume resistivity at 170 C 2E07 50 000 Mm 6 Non-electrical properties of the copper-clad laminate 6.1 Appearance of the copp

38、er-clad sheet The copper-clad face shall be substantially free from defects that may have an impact on the materials fitness for use for the intended purpose. For the following specific defects, the requirements given shall apply when inspection is made in accordance with IEC 61189-2, Method 2M18. P

39、age6 EN6124929:200361249-2-9 IEC:2003 7 6.1.1 Indentations (pits and dents) The size of an indentation, usually the length, shall be determined and given a point value to be used as measure of the quality. Size mm Point value for each indentation 0,13 0,25 1 0,26 0,50 2 0,51 0,75 4 0,76 1,00 7 Over

40、1,00 30 The total point count for any 300 mm 300 mm area shall be calculated to determine the indentation class. Class A 29 maximum Class B 17 maximum Class C 5 maximum Class D 0 Class X to be agreed upon by user and supplier The desired class of indentations shall be specified in the purchase order

41、. Indentation Class A applies unless otherwise specified. 6.1.2 Wrinkles There shall be no wrinkles on the copper surface. 6.1.3 Scratches Scratches deeper than 10 m or 20 % of the nominal thickness of the foil thickness, whichever is lower, are not permitted. Scratches with a depth less than 5 % of

42、 the nominal thickness of the foil shall not be counted, unless this depth is 10 m or more. Scratches with a depth between 5 % and 20 % of the nominal thickness of the foil are permitted to a total length of 100 mm for a 300 mm 300 mm area. 6.1.4 Raised areas Raised areas are usually impressions cau

43、sed by defects in the press plates used during manufacture but may also be caused by blisters or inclusions of foreign particles under the foil. Raised areas caused by blisters or inclusions are not permitted. Page7 EN6124929:200361249-2-9 IEC:2003 8 Raised areas caused by impressions of defects in

44、the press plates are permitted to the following extent: Class A and X material: maximum height 15 m and maximum length 15 mm; Class B and C material: maximum height 8 m and maximum length 15 mm; Class D material: maximum height 5 m and maximum length 15 mm. 6.1.5 Surface waviness When examined in ac

45、cordance to test method 2M12 of IEC 61189-2, the surface waviness in both the machine and cross-machine direction shall not exceed 7 m. 6.2 Appearance of the unclad face The unclad face of a single-sided clad sheet shall have the natural appearance resulting from the curing process. Small irregulari

46、ties in colour are permitted. The gloss of the unclad face shall be that given by the press plate, release film, or release foil used. Variations of gloss due to the impact of pressure of gases released during the curing are permitted. 6.3 Laminate thickness The laminate thickness may be ordered to

47、include or exclude the copper foil contribution as specified in the purchase order. As a general rule, laminates less than 0,8 mm are measured excluding copper, and laminates greater or equal to 0,8 mm are measured including copper. If the copper-clad laminate is tested in accordance with test metho

48、d 2D01 of IEC 61189-2, the thickness shall not depart from the nominal thickness by more than the appropriate value shown in Table 2. The fine tolerances shall apply unless the other tolerances are ordered. Table 2 Nominal thickness and tolerance of metal-clad laminate Tolerance requirement mm Nomin

49、al thickness excluding metal foil (material intended for multilayer boards) mm Nominal thickness including metal foil (material intended for single or double sided boards) mm Coarse Fine Extra fine 0,05 0,10 0,10 0,15 0,15 0,30 0,30 0,50 0,50 0,80 0,80 1,00 1,00 1,30 0,80 1,00 1,00 1,30 1,30 1,70 1,