1、Designation:F185910 Designation: F1859 12Standard Specification forRubber Sheet Floor Covering Without Backing1This standard is issued under the fixed designation F1859; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of l

2、ast revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for the compound and physical characteristics of rubber sheet floor covering

3、without backing.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1.3 The following precautionary statement pertains only to the test

4、 method portion, Section 10, of this specification: Thisstandard does not purport to address all the safety concerns, if any, associated with its use. It is the responsibility of the user ofthis standard to establish appropriate safety and health practices and determine the applicability of regulato

5、ry limitations priorto use.2. Referenced Documents2.1 The following documents of the issue in effect on the date of the material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:2D412 Test Methods for Vulcanized Rubber and Thermoplastic ElastomersTensionD8

6、83 Terminology Relating to PlasticsD1566 Terminology Relating to RubberD2240 Test Method for Rubber PropertyDurometer HardnessF141 Terminology Relating to Resilient Floor CoveringsF386 Test Method for Thickness of Resilient Flooring Materials Having Flat SurfacesF410 Test Method for Wear Layer Thick

7、ness of Resilient Floor Coverings by Optical MeasurementF710 Practice for Preparing Concrete Floors to Receive Resilient FlooringF925 Test Method for Resistance to Chemicals of Resilient FlooringF970 Test Method for Static Load LimitF1482 Practice for Installation and Preparation of Panel Type Under

8、layments to Receive Resilient FlooringF1514 Test Method for Measuring Heat Stability of Resilient Flooring by Color ChangeF1515 Test Method for Measuring Light Stability of Resilient Flooring by Color Change2.3 ANSI Standard:ANSI/ASQC Z1.4 Sampling Procedures and Tables for Inspection by Attributes3

9、3. Terminology3.1 DefinitionsFor definitions of other terms used in this standard, see Terminology F141.4. Classification4.1 Rubber sheet floor covering covered by this specification shall conform to the following types:4.1.1 Type IHomogeneous rubber sheet floor covering, and4.1.2 Type IILayered rub

10、ber sheet floor covering. Heterogeneous (Layered) rubber sheet floor covering.4.2 The above may have either smooth, embossed, or molded pattern surfaces.1This specification is under the jurisdiction of ASTM Committee F06 on Resilient Floor Coverings and is the direct responsibility of Subcommittee F

11、06.80 onSpecifications.Current edition approved May 1, 2010. Published June 2010. Originally approved in 1998. Last previous edition approved in 2009 as F1859 04(2009)1. DOI:10.1520/F1859-10.Current edition approved May 1, 2012. Published May 2012. Originally approved in 1998. Last previous edition

12、approved in 2010 as F1859-10. DOI: 10.1520/F1859-12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3Availa

13、ble from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit

14、 may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr H

15、arbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.3 These products shall not contain asbestos.5. Ordering Information5.1 Purchasers shall state whether this specification is to be used, select the preferred options permitted herein and include thefollowing information in th

16、e invitation to bid or purchase order:5.1.1 Title, number, and date of this specification,5.1.2 Type, color, and surface (see Section 4 and Section 6),5.1.3 Quantity, in square feet, square yards, or square metres,5.1.4 Thickness required. (see Section 8),5.1.5 Overall thickness, if molded pattern s

17、heet flooring is specified (see 8.1),5.1.6 Width required (see 8.4),5.1.7 Length required (see 8.5),5.1.8 Resistance to chemicals, (see 7.4),5.1.9 Lot information, if other than as specified in ANSI/ASQC Z1.4 (see 10.1 and 11.1),5.1.10 Sampling, if other than as specified in ANSI/ASQC Z1.4 (see 10.1

18、 and 11.1),5.1.11 Statement requesting certification, if certification of compliance is required (see 12.1),5.1.12 Packing requirements, if other than as specified (see 14.1),5.1.13 Palletization, if required,5.1.14 Marking required, if other than specified (see 13.1), and5.1.15 Other requirements.6

19、. Materials and Manufacture6.1 MaterialThe polymeric binder of the rubber sheet floor covering shall satisfy the definition of rubber in TerminologyD1566, and have been vulcanized, as defined in Terminology D1566 (under vulcanization), such that it becomes thermoset asdefined in Terminology D883. Th

20、e rubber sheet flooring made from this compound shall be resistant to neutral pH cleaners.6.2 Color, Pattern, and Wear Layer SurfaceThe color, pattern, and wear layer surface, as applicable, shall be as specified inthe contract or order (see 5.1).NOTE 1The colors and patterns that are available are

21、indicated in individual manufacturers current catalogs. As manufactured, colors may varysomewhat in hue or shade from the catalog.NOTE 2Where color match is a concern, samples from the manufacturer shall be obtained to verify color acceptability.6.3 Homogeneous Rubber Sheet Floor CoveringThe surface

22、 coloring or mottling shall be uniform throughout the entirethickness of the rubber sheet floor covering.6.4 Layered Rubber Sheet Floor CoveringHeterogeneous (Layered) Rubber Sheet Floor CoveringThe surface coloring ormottling need not extend through the entire thickness of the rubber sheet floor co

23、vering, but must extend throughout the entirethickness of the wear layer.6.4.1 The wear layer must have a minimum thickness of 0.040 in. (1.0 mm) when measured in accordance with Test MethodF410.6.4.2 The appearance of the rubber sheet floor covering, after removing 0.020 in. (0.51 mm) of the wear l

24、ayer thickness, shallcompare favorably in appearance with the rubber sheet floorings original appearance. The removal of the wear layer may beaccomplished by any suitable method.7. Performance Requirements7.1 HardnessThe rubber sheet floor covering shall have a durometer hardness of not less than 85

25、 (Shore, TypeA) when testedin accordance with Test Method D2240.7.2 Modulus at 10 % ElongationWhen tested in accordance with Test Method D412 at a rate of 6 in. (152.4 mm)/min, usinga 1 in. (25.4 mm) by 5 in. (127 mm) gage length rectangular specimen, the modulus shall not be less than 300 psi (2.07

26、 MPa).For molded pattern rubber sheet floor covering, the raised pattern shall be removed by any suitable method.7.3 Static Load LimitWhen tested in accordance with Test Method F970, with an applied load of 250 lb (113.4 kg), theresidual indentation shall not be greater than 0.005 in. (0.127 mm).7.4

27、 Resistance to ChemicalsWhen tested in accordance with Test Method F925, the rubber sheet floor covering shall have nomore than a slight change in surface dulling, surface attack, or staining when exposed to the following chemicals:7.4.1 White vinegar (5 % acetic acid),7.4.2 Rubbing alcohol (70 % is

28、opropyl alcohol),7.4.3 Sodium hydroxide solution (5 % NaOH),7.4.4 Hydrochloric acid solution (5 % HCl),7.4.5 Sulfuric acid solution (5 % H2SO4),7.4.6 Household ammonia solution (5 % NH4OH),7.4.7 Household bleach (5.25 % NaOCl),F1859 122NOTE 3These basic chemicals are representative of those likely t

29、o be found in domestic, commercial, and institutional use. Many proprietarycompounds contain one or more of these basic chemicals. Should the flooring for an unusual application need to be resistant to a specific chemical, thisadditional requirement should become part of the procurement document (se

30、e 5.1.8).NOTE 4Since standard SBR rubber flooring is not recommended for installation where the product will be exposed to animal fats, vegetable oils, andpetroleum-based reagents, mineral oil, olive oil, kerosene, and gasoline have been removed from the standard chemical list to eliminate any confu

31、sionregarding product selection.7.5 Resistance to HeatWhen tested in accordance to Test Method F1514, the color change of the rubber sheet floor coveringshall have an average DE not greater than 8.0 after seven days exposure to 158F (70C). The specimen surface shall be wipedwith a clean, white cotto

32、n cloth prior to taking the initial and post test conditioned period color readings to remove any wax bloomor other contaminants which may affect the accuracy of the color readings.7.6 Resistance to LightWhen tested in accordance to Test Method F1515, the color change of the rubber sheet floor cover

33、ingshall have an average DE not greater than to 8.0 after 300 h of exposure to light, simulated by a properly fitted xenon-arc radiantenergy source.8. Dimensions, Mass, and Permissible Variations8.1 Overall ThicknessMolded pattern rubber sheet floor covering shall be measured for overall thickness a

34、t the thickestcross-sectional area of the flooring. The thickness of the molded pattern shall be uniform throughout the flooring.8.2 Base Thickness Molded pattern rubber sheet floor covering base thickness shall be measured at the thinnestcross-sectional area of the flooring. The thinnest cross-sect

35、ional area shall be uniform throughout the flooring.8.3 ThicknessThe thickness of the rubber sheet floor covering shall be as specified in the contract or order (see 5.1.4). Anaverage tolerance, obtained from five individual measurements, of 60.006 in. (60.15 mm) from the specified thickness shall b

36、epermitted in the base thickness alone or in combination with the overall thickness, when measured in accordance with Test MethodF386. The difference between the five individual measurements can not be greater than 0.008 in. (0.2 mm). In the case of moldedpattern rubber sheet floor covering, overall

37、 thickness and base thickness shall be reported.8.4 WidthThe width shall be as specified in the contract or order (see 5.1.6). The net width (gross width less selvages) shallnot be less than as marked on the label or package when measured in accordance with 8.6.8.5 LengthThe length of the roll shall

38、 be as specified in the contract or order (see 5.1.7). The sheet length shall not be lessthan as marked on the label or package when measured in accordance with 8.6. Each roll shall be in one piece, except that lessthan 20 % of the rolls in any one shipment may consist of not more than two pieces, t

39、he shortest length shall not be less than 5linear yards (4.57 m), or as agreed upon by the purchaser and seller. Such rolls shall be clearly marked.8.6 Length and Width MeasurementsMeasurements shall be made with a calibrated 100 ft (30 m) steel tape graduated atintervals of116 in. or 1 mm. The roll

40、 shall be extended to its full length on a flat surface and all creases and buckles removed,insofar as practical, without applying stresses that cause any significant stretching. Measurements of length shall be rounded to thenearest inch or 10 mm. Net width shall be measured to the nearest116 in. or

41、 1 mm at not less than ten locations uniformlydistributed along the length of each roll, and the results averaged.9. Workmanship, Finish and Appearance9.1 The rubber sheet floor covering furnished in accordance with this specification shall be an acceptable match to approvedsamples in color, pattern

42、, and appearance. The product shall be free of defects, which adversely affect performance or appearance.Such defects include: blemishes, spots, lines, indentations, blisters, and delamination.9.2 Unless otherwise specified in the contract or order (see 5.1), the back or bonding surface of the rubbe

43、r sheet floor coveringshall be buffed, roughened, ribbed, grooved, or otherwise modified to improve the adhesive bond of the rubber sheet floor covering,but in no case shall the thickness of the flooring be decreased to the extent that any depression or groove on the bonding surfacebe perceptible, u

44、nder any circumstances, on the exposed surface.TABLE 1 Characteristics and TestsCharacteristic Requirement ASTM Test Method ReferenceComposition of Material Certificate of Compliance 6.1Wear Layer Thickness min 0.040 in. (1.0 mm) F410 6.4.1Hardness min 85 Shore A D2240 7.1Modulus at 10 %Elongationmi

45、n 300 psi (2.07 MPa) D412 7.2Static Load Limit #0.005 in. (0.127 mm) F970 7.3Resistance to Chemicals No more than a slightchange in surface dulling,surface attack, or staining.F925 7.4Resistance to Heat Ave. DE not greater than 8.0 F1514 7.5Resistance to Light Ave. DE not greater than 8.0 F1515 7.6A

46、verage Thickness 60.006 in. (60.15 mm) F386 8.3Width Not less than as specified Section 8 8.4Length Not less than as specified Section 8 8.5F1859 12310. Sampling for Test10.1 Sampling for testing physical characteristics listed in Table 1 shall be done in accordance with the provisions set forth inA

47、NSI/ASQC Z1.4. The inspection level shall be special inspection level S-1, as noted in Table I of ANSI/ASQC Z1.4, and theacceptable quality level (AQL) shall be 6.5 defects per hundred units as noted in Table II-(A) of ANSI/ASQC Z1.4 or as otherwisespecified in 10.2. The lot size shall be expressed

48、in units. A unit represents a single, manufactured, inventoried, finished roll.10.1.1 Samples shall be obtained in the required length from the outside end of the roll and shall encompass the total width ofthe material.10.2 Sampling for testing physical characteristics listed in Table 1 shall be agr

49、eed upon by the purchaser and the manufactureras part of the procurement document.11. Inspection11.1 Sampling for inspection of the rubber sheet floor covering for defects that would adversely affect performance (see 9.1)shall be done in accordance with the provisions set forth in ANSI/ASQC Z1.4. The inspection level shall be Level I as noted inTable I of ANSI/ASQC Z1.4 with an acceptable quality level (AQL) of 6.5 defects per hundred as noted in Table II(A) ofANSI/ASQC Z1.4or as otherwise specified in 11.2. The lot size shall be expressed in unit