SANS 258-2008 Wax stoep polish《蜡质鞋油》.pdf

《SANS 258-2008 Wax stoep polish《蜡质鞋油》.pdf》由会员分享，可在线阅读，更多相关《SANS 258-2008 Wax stoep polish《蜡质鞋油》.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、 Collection of SANS standards in electronic format (PDF) 1. Copyright This standard is available to staff members of companies that have subscribed to the complete collection of SANS standards in accordance with a formal copyright agreement. This document may reside on a CENTRAL FILE SERVER or INTRA

2、NET SYSTEM only. Unless specific permission has been granted, this document MAY NOT be sent or given to staff members from other companies or organizations. Doing so would constitute a VIOLATION of SABS copyright rules. 2. Indemnity The South African Bureau of Standards accepts no liability for any

3、damage whatsoever than may result from the use of this material or the information contain therein, irrespective of the cause and quantum thereof. ISBN 978-0-626-21942-0 SANS 258:2008Edition 2.4 SOUTH AFRICAN NATIONAL STANDARD Wax stoep polish Published by SABS Standards Division 1 Dr Lategan Road G

4、roenkloof Private Bag x191 Pretoria 0001 Tel: +27 12 428 7911 fax: +27 12 344 1568 www.sabs.co.za SABS SANS 258:2008 Edition 2.4 Table of changes Change No. Date Scope Amdt 1 1991 Amended to change the requirements for penetration, performance, non-volatile matter content, softening point of the non

5、-volatile matter and the ash content of the non-volatile matter. Amdt 2 1993 Amended to change the requirement for the ash content of non-volatile matter of the red and green polishes. Amdt 3 2004 Amended to change the designation of SABS standards to SANS standards, to change the definition of acce

6、ptable, and to convert appendices A and B to form part of the requirements of the specification. Amdt 4 2008 Amended to update the applicable standards and to remove reference to national legislation from the text. Foreword This South African standard was approved by National Committee SABS SC 1006A

7、, Detergents, polishes and other chemicals Polishes, in accordance with procedures of SABS Standards Division, in compliance with annex 3 of the WTO/TBT agreement. This document was published in August 2008. This document supersedes SANS 258:2004 (edition 2.3). A vertical line in the margin shows wh

8、ere the text has been technically modified by amendment No.s 1, 2, 3 and 4. In 4.2, reference is made to “relevant national regulations and statutory requirements regarding trade metrology“. In South Africa this is the Trade Metrology Act, 1973 (Act No. 77 of 1973), as amended from time to time. SAN

9、S 258:2008 Edition 2.4 1 Contents Page Foreword 1 Scope . 3 2 Definitions 3 3 Requirements . 3 4 Packing and marking . 5 5 Sampling and compliance with the specification . 5 6 Inspection and methods of test 6 6.1 Inspection . 6 6.2 Conditioning of samples 6 6.3 Heat-cool stability 6 6.4 Penetration

10、. 6 6.5 Performance . 6 6.6 Non-volatile matter content 6 6.7 Softening point of the non-volatile matter 6 6.8 Ash content of the non-volatile matter . 7 6.9 Flash point of solvents . 7 Appendix A Applicable standards 8 Appendix B Notes to purchasers 8 SANS 258:2008 Edition 2.4 2 This page is intent

11、ionally left blank SANS 258:2008 Edition 2.4 3 Wax stoep polish 1 Scope 1.1 This specification covers wax polish suitable for use on surfaces of cement, and available in three colours. NOTE a) The standards referred to in the specification are listed in appendix A. b) Requirements that must be speci

12、fied by the purchaser are listed in appendix B. 2 Definitions 2.1 For the purposes of this specification the following definitions shall apply: acceptable acceptable to the authority administering this standard or to the parties concluding the purchase contract, as relevant Amdt 1; amdt 3 batch the

13、material from a single mix defective stoep polish or its container that fails in one or more respects to comply with the appropriate requirements of the specification lot not less than 10 containers of stoep polish that bear the same batch identification, from one manufacturer, submitted at any one

14、time for inspection and testing 3 Requirements 3.1 General The polish shall consist essentially of a wax or a blend of waxes and pigments in a mixture of water and organic solvents. It shall be a homogeneous smooth paste free from lumps and granules. It shall not be harmful to surfaces of the cement

15、 type. Under normal conditions of use it shall not be irritating to the normal skin and its vapours shall not be toxic to human beings. The odour of the polish shall be acceptable. SANS 258:2008 Edition 2.4 4 3.2 Freedom from grit When approximately 0,1 g of the polish is rubbed between two glass sl

16、ides, there shall be no evidence of grit. 3.3 Colour The colour of the polish shall be an acceptable shade of black, green, or red, as specified by the purchaser. 3.4 Heat-cool stability When tested in accordance with 6.3, the polish shall not show any sign of separation. 3.5 Penetration The penetra

17、tion of the polish, determined in accordance with 6.4, shall be in the range 60-110 units (tenths of a millimetre) at 20 C and not more than 90 units (tenths of a millimetre) at 25 C. Amdt 1 3.6 Performance When tested in accordance with 6.5, the polish shall apply easily and shall dry to a thin fil

18、m within 15 min. On rubbing with a soft cloth, the film shall polish smoothly and the gloss of the panel shall not be reduced. Amdt 1 3.7 Non-volatile matter 3.7.1 Content The non-volatile matter content of the polish, determined in accordance with 6.6, shall be not less than 22 % (m/m) in the cases

19、 of red and green polishes and not less than 20 % (m/m) in the case of a black polish. Amdt 1 3.7.2 Properties The non-volatile matter of the polish shall comply with the requirements given in table 1. Table 1 Properties of the non-volatile matter 1 2 3 4 Requirement Property Red and green polishes

20、Black polishes Test method subsection Softening point, C, min. Ash content, % (m/m), max. min. 70 15,0 70 15,0 0,0 6.7 6.8 Amdt 1; amdt 2 SANS 258:2008 Edition 2.4 5 3.8 Organic solvents The solvents shall have a flash point, determined in accordance with 6.9, of at least 25 C. 3.9 Storage stability

21、 When stored at room temperature for 12 months in its original unopened container, the polish shall still comply with all the other relevant requirements of the specification. 4 Packing and marking 4.1 Packing Unless containers of a plastics material1)are specified by the purchaser, the polish shall

22、 be packed in metal containers. It shall be so packed as to prevent leakage and deterioration of the product and the containers shall be strong enough to withstand normal handling and transportation. Each container shall contain only polish from the same batch. These containers may be packed in bulk

23、 packages, but only containers of the same size and bearing the same batch identification shall be packed together in a bulk package. 4.2 Marking Each container shall bear, in prominent, legible and indelible marking, the information required in terms of the relevant national and statutory requireme

24、nts regarding trade metrology (see foreword), and the following additional information (which shall also appear on each bulk package): Amdt 4 a) The name or trade name or trade mark of the manufacturer, or a combination of these; b) in the case of containers, 1) words indicating that the polish is a

25、 wax polish intended for use on cement surfaces; 2) the colour; 3) the net volume of the contents; 4) if larger than 1 L, the batch identification; c) in the case of bulk packages, 1) a description of the contents (that includes the colour); 2) the batch identification; 3) the number of containers.

26、5 Sampling and compliance with the specification NOTE This section applies to the sampling for inspection and testing before acceptance or rejection of single lots (consignments) in cases where no information about the implementation of quality control or testing during manufacture is available to h

27、elp in assessing the quality of the lot. It is also used as the procedure for adjudicating in cases of dispute. 1) It is not recommended that the container be of polyethylene. SANS 258:2008 Edition 2.4 6 5.1 Sampling The following sampling procedure shall be applied in determining whether a lot comp

28、lies with the appropriate requirements of the specification. The sample so drawn shall be deemed to represent the lot. After checking the lot for compliance with the requirements of section 4, take from it at random at least six containers and mark each container with the date of sampling and, when

29、relevant, the batch number. 5.2 Compliance with the specification The lot shall be deemed to comply with the requirements of the specification if, after inspection of the lot and inspection and testing of the sample taken in accordance with 5.1, no defective is found. 6 Inspection and methods of tes

30、t 6.1 Inspection After conditioning (see 6.2) the containers in the sample taken in accordance with 5.1, check their contents for compliance with those requirements of the specification with which compliance is not assessed by the tests given in 6.36.9 (inclusive). 6.2 Conditioning of samples Condit

31、ion all samples at room temperature for at least 7 d before testing. 6.3 Heat-cool stability Use SANS 5976. 6.4 Penetration Use SANS 5977 but modified as follows: a) Condition one of the two test samples at 20,0 0,5 C for 24 h and the other sample at 25,0 0,5 C for 24 h. b) Determine the penetration

32、 of the polish conditioned at 20,0 0,5 C, using the 60/90 cone, and determine the penetration of the sample conditioned at 25,0 0,5 C, using the 90 cone. c) Report the penetration of the polish at 20 C and at 25 C. Amdt 1 6.5 Performance Use the procedure given in section 3 of SANS 5978:2008, but om

33、it the step given in 3.3. Amdt 1 6.6 Non-volatile matter content Use SANS 5981. Amdt 4 6.7 Softening point of the non-volatile matter Use SANS 5980. SANS 258:2008 Edition 2.4 7 6.8 Ash content of the non-volatile matter Use SANS 5981. 6.9 Flash point of solvents Use ASTM D93. SANS 258:2008 Edition 2

34、.4 8 Appendix2)A Amdt 1 Applicable standards (This appendix does not form part of the requirements of the specification) Amdt 1; amdt 3 Reference is made to the latest issues of the following standards: ASTM D93, Standard test methods for flash point by Pensky-Martens closed cup tester. SANS 5976, H

35、eat-cool stability of wax polishes. SANS 5977, Penetration of wax (paste) polishes. SANS 5978:2008, Performance of wax polishes. SANS 5979 (SABS SM 979), Non-volatile matter content of wax polishes. Amdt 4 SANS 5980, Softening point of the non-volatile matter of wax polishes. SANS 5981 (SABS SM 981)

36、, Wax polishes Ash content of the non-volatile matter. SANS 5981, Wax polishes Non-volatile matter content and the ash content of non-volatile matter. Amdt 4 Appendix B Notes to purchasers (This appendix does not form part of the requirements of the specification) Amdt 1; amdt 3 The following requir

37、ements must be specified in tender invitations and in each order or contract: a) The colour of the polish (see 3.3) b) When relevant, that the container in which the polish is to be packed is to be of a plastics material (see 4.1) SABS 2) The information in the appendices is additional to that in the specification and has been included purely for information and guidance. Amdt 1