NAVY MIL-C-81268 A-1988 CLOTH NYLON《尼龙布料》.pdf

《NAVY MIL-C-81268 A-1988 CLOTH NYLON《尼龙布料》.pdf》由会员分享，可在线阅读，更多相关《NAVY MIL-C-81268 A-1988 CLOTH NYLON《尼龙布料》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、MIL-C-812bBA 3 7779706 0404820 3 /Y- 37-/5 MI L-C-812684(08) 18 Feb ruarv ISS distribution is unlimited. , . THIS DOCUMENT CNTINS -5 PAGES. , Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-L26A 3 777770b 0404ZL 5 MI L-C-81268A(OS) PU B LI CATI

2、 ON S American Society for Testing and Materials ASTM D 1682 ASTM D 1777 ASTM D 3776 Standard Test Method for-Breaking Load and Elongation of Textile Fabrics Method for Measuring Thickness of Textile Material Test Method for Mass Per Unit Area (Weight of Woven Fabrics) (Application for copies should

3、 be addressed to the American Society for Testing and Materials, 1916 Race Street, Philadelphia, Pennsylvania, 19103.) 3. REQUIREMENTS 3.1 First article. When specified in the contract or purchase order, a sample shall be subjected to first article 3.2 Data requirements. No data is required by this

4、specification or by applicable documents referenced in section 3.3 Physical properties. The physical properties shall be as specified in Table I. inspection (see 4.4 and 6.3). 2 unless specified in the contract or order (see 6.2). TABLE I. Physical properties. Requirement Average values Minimum Maxi

5、mum I Thread count, threads per inch Warp Fill 22 24 22 24 Breaking strength, pounds - - Warp Fill Elongation, percent Warp Fill Thickness, inches Weight, ounces per square yard Weave - 35 - 35 O.O6 0.009 1.55 2.00 plain 3.4 Workmanship. The material shall be uniform in weave and composition and sha

6、ll be free of visible damage, foreign material, or other defects that could adversely affect its use. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for inspection. Unless otherwise specified in the contract or purchase order, the supplier is responsible for the performance of all inspection req

7、uirements as specified herein. Except as otherwise specified, the supplier may utilize his own facilities or any commercial laboratory acceptable to the Government. The Government reserves the right to perform any of the inspections set forth in the specification where such inspections are deemed ne

8、cessary to assure supplies and services conform to prescribed requirements. t 4 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-LZbA 83 7977706 CIL104822 7 MI L-C-81268A(OS) 4.1.1 Responsibility for compliance. All items must meet all require

9、ments of sections 3 and 5. The inspection set forth in this specification shall become a part of the contractors overall inspection system or quality program. The absence contractor of the responsibility of assuring that all products or supplies submitted to the Government for acceptance comply with

10、 all requirements of contract. Sampling in quality conformance does not authorize submissionof known defective material, either indicated or actual, nor does it commit the Government to acceptance of defective material. 4.2 Classification of inspections. Inspection of the nylon cloth shall be classi

11、fied as follows: a. First article inspection (see 4.4) b. Quality conformance inspection (see 45) 4.3 Sampling. 4.3.1 First article sample. A first article sample of three test specimens of the nylon cloth, manufactured in accordance with 31 shall be subjected to the first article tests detailed in

12、4.4 at an activity designated by the procuring activity. Further production of the nylon cloth by the supplier, prior to the approval of the first article sample, shall be at the suppliers risk. 4.3.2 Quality conformance inspection sampling. Except as otherwise specified, the sampling plans and proc

13、edures set forth in MIL-STD-105, level II shall be used in the determination of acceptability of the nylon cloth inspected as specified in 4.5. From each end of the roll of material for sampling, select ten specimens, 4 inches in width and 6 inches in length. Two sets of five specimens from each end

14、 shall be taken in the following manner: one set of five for warp breaking strength shall have the longer dimension parallel fo the warp yarns: the other set for fill breaking strength shall have the longer dimension parallel to the fill yarns. No two specimens within a set of five for warp breaking

15、 strength shall contain the same warp yarns or for fill breaking strength shall contain the same fill yarns. Specimens shall be taken no nearer to the selvage than one-tenth the width of the fabric, nor nearer than one foot from the ends of the rolls. 4.3.3 Inspection lot. An inspection lot of nylon

16、 cloth shall be all the material presented for acceptance at one time and produced in a single manufacturing run under homogeneous conditions of manufacture. 4.4 First article inspection. The first article sample shall satisfactorily pass the quality conformance inspections detailed in 4.5. 4.5 Qual

17、ity conformance inspection. 4.5.1 Visual examination. Visually examine all containers or rolls in a lot to determine conformance to 3.4 and Section 5. 4.5.2 Physical tests. 4.5.2.1 Thread count test. The total number of strands for 3 inches in both the warp and fill directions shall be visually dete

18、rmined for each specimen. 4.5.2.2 Breaking strength and elongation tests. All tensile property tests shall be performed using the modified grab test method of ASTM D 1682, and a constant rate of extension of one inch per minute. All test samples shall be conditioned in a desiccator containing anhydr

19、ous magnesium perchlorate or anhydrous calcium sulfate at 75O f 5OF for a minimum of 24 hours immediately prior to testing. A stress-strain curve shall be recorded for each tensile test. Elongation shall be expressed as the percentage increase in length of the sample as determined from the stress-st

20、rain curve. Breaking strength shall be read directly from the test apparatus. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,- MIL-C-L2bA 3 m 9799906 0404823 7 m MI L-C-8126&4(OS) a 4.5.2.3 Thickness test. The thickness of the fabric shall be determi

21、ned with a suitable testing instrument having a presser foot 0.375 inch in diameter at 1.1 f 0.1 pounds per square inch (psi) for 5 seconds, and in accordance with ASTM D 1777. 4.5.2.4 Weight test. The fabric weight shall be determined in accordance with ASTM D 3776. The specimens 4.6 Acceptance cri

22、teria. 4.6.1 First article. Failure of any sample to comply with any requirement of this specification shall be cause for rejection of the sample. 4.6.2 Quality conformance. Failure of any sample to meet any requirement of this specification shall be cause for rejection of the sample. Acceptance of

23、the lot shall be based upon an Acceptable Quality Level (AQL) of 1.0 percent in accordance with MIL-STD-105, level II, normal inspection, single sampling. 5. PACKAGING shall be conditioned and the weight in ounces per square yard calculated as specified therein. 5.1 Packaging and marking. Preservati

24、on, packaging and packing shall be in accordance with MIL-P-116, method III. 5.2 Marking. Marking shall be in accordance with MIL-STD-129. Marking shall include, but not be limited to, the following information: a. Manufacturers name and location b. Material trade name c. Lot number, batch number an

25、d date of manufacture d. Number and revision letter of this specification. 6. NOTES 6.1 Intended use. Material purchased under this specification is intended for use as an inhibitor or the external surface of propellant grain in rocket motors. 6.2 Acquisition requirements. Acquisition documents shou

26、ld specify, but not be limited to, the following information: a. Title, number and revision letter of this specification b. Special preservation, packaging and packing requirements, if applicable c. Length and width of rolls d. Place of inspection e. Place of delivery f. Whether first article sample

27、 is required g. Request for test data 6.3 First article. When a first article inspection is required, the item should be a first article sample. The first article should consist of three test specimens of the nylon cloth. The contracting officer should include specific instructions in acquisition do

28、cuments regarding arrangements for examinations, approval of first article test results and disposition of first articles. Invitations for bids should provide that the Government reserves the right to waive the requirements for samples for first article inspection to those bidders offering a product

29、 which has been previously acquired or tested by the Government, and that bidders offering such products, who wish to rely on such production or test, must furnish evidence with the bid that prior Government approval is presently appropriate for the pending contract. 4 Provided by IHSNot for ResaleN

30、o reproduction or networking permitted without license from IHS-,-,-Custodian: Navy OS NIL-C-L268A 83 W 73O6 0404824 O E MI L-C-81268A(C)S) 6.4 Subject term (key word) listing. Cloth, Nylon Propellant wrapper Propellant inhibitor Rocket motor Preparing activity: Navy OS (Project No. 8305N171) 5 $?US. GOVERNMENT PRIkTING OFFICE: 1988 - 5u5-U33/90Hx9 1, Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-