NAVISTAR MPAPS F-6016-2015 Hose High Temperature with End Fittings.pdf

《NAVISTAR MPAPS F-6016-2015 Hose High Temperature with End Fittings.pdf》由会员分享，可在线阅读，更多相关《NAVISTAR MPAPS F-6016-2015 Hose High Temperature with End Fittings.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、This document is restricted and may not be sent outside Navistar, Inc or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2015 by Navistar, Inc. OCTOBER 2015 Page 1 of 16 NAVISTAR, INC. Material, Parts, and Process Specification

2、s (MPAPS) NUMBER: MPAPS F-6016 Former Designation: TMS-6016 TITLE: Hose, High Temperature, with End Fittings CURRENT REV No.: 1510 DATE: OCT. 2015 WRITTEN/EDITED BY: M. Ghaddar APPROVED BY: R. Goluch SUPERSEDES: 1310 Oct. 2013 PRINTED COPIES OF THIS DOCUMENT MUST BE VERIFIED FOR CURRENT REVISION Thi

3、s specification may involve hazardous materials, equipment, and procedures. This specification does not purport to address all of the safety issues associated with its use. The user is responsible to consult appropriate safety and health practices and to determine the applicability of regulatory lim

4、its prior to use. Change Notice: Updated Table V burst. Released as MPAPS 1.0 APPLICATION This specification covers six types of hose, with end-fittings, used in the air brake, engine oil, diesel fuel, transmission oil cooling, low-pressure power steering, and coolant systems. Types I through IV and

5、 VI may be used in applications operating between -40 and 150C (-40 to 302F) which conform to the pressures and bend radii listed in Table 5. Type V may be used in systems operating between -53 to 232C (-65 to 450F) which conform to the pressures and bend radii listed in Table 2. Type V may also be

6、used in applications requiring extra chemical resistance, such as engine oil recirculation lines. RESTRICTIONS: Hose covered by this specification shall not be used in the following applications: High-pressure power steering, cab-lift, or hydraulic brake systems. Air brake jounce/articulating lines

7、- see TMS-6036. Application in coolant systems is limited to Type VIII and to customer demand option only. 2.0 SCOPE This specification covers general requirements, property and performance requirements, identification, quality, packing and shipping and source approval and quality control requiremen

8、ts. 2.1 Restricted Chemical Substances Effective January 1, 2007, all product supplied to the requirements of this specification must comply with the requirements of the MPAPS B-50 specification. NUMBER: MPAPS F-6016 TITLE: Hose, High Temperature, With End Fittings REVISION: 1510 This document is re

9、stricted and may not be sent outside Navistar, Inc or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2015 by Navistar, Inc. OCTOBER 2015 Page 2 of 16 3.0 REFERENCE DOCUMENTS Unless otherwise specified the latest issue of all r

10、eferenced standards shall apply. The following specifications and standards are referenced in this specification: Quality System Standard ISO 9001 or TS-16949 NAVISTAR Eng. Drw. PT10-53568 ASTM D 792 NAVISTAR Eng. Design Std A-16 NAVISTAR MPAPS A-0, Part II ASTM D 865 NAVISTAR Manufacturing Std MS-D

11、-13 NAVISTAR MPAPS A-37 ASTM D 1457 NAVISTAR Eng. Procedural Standard EPS-143 NAVISTAR MPAPS G-1 MIL-H-8446 CFR Title 29, Part 1910 NAVISTAR MPAPS G-20 MIL-L-7807 NAVISTAR Eng. Drw. AD 1324 NAVISTAR CEMS C-3 MIL-L-2104E NAVISTAR Eng. Drw. AD 6466 TMC Recommended Practice 307 SAE J516 NAVISTAR Eng. D

12、rw. AD 6717 NAVISTAR MPAPS B-50 SAE J517 NAVISTAR Eng. Drw. AD 9290 NAVISTAR TMS-6812 ASTM D 412 FMVSS 106 NAVISTAR TMS-6803 SAE J343 SAE J1405 ASTM D 380 ASTM D 622 NAVISTAR MPAPS DT-9 NAVISTAR MPAPS C-10 ASTM B 117 NAVISTAR MPAPS G-22 ASTM D 610 MPAPS G-9009 ASTM D 4895 NAVISTAR MPAPS A-45 Pt I MP

13、APS P-9543 4.0 GENERAL REQUIREMENTS Hose and hose assemblies shall meet SAE, FMVSS, and NAVISTAR requirements as indicated in Tables 2, 3, and 4. TABLE 1 - DESCRIPTION OF TYPES MPAPS F-6016 SAE J1402 SAE J517 FMVSS 106 ENG. DR Type I Type AI N/A YES AD1324, AD6466, AD6717 Type II Type AI N/A YES AD1

14、324, AD6466, AD6717 Type III Type AII 100R5 YES AD1324, AD6466, AD6717 Type IV Type AII 100R5 YES AD1324, AD6466, AD6717 Type V N/A 100R14 NO AD9290 Type VI N/A 100R6 NO PT10-53568 Type VII 4.1 Construction 4.1.1 Type I - This hose shall consist of a seamless tube of oil resistant rubber, reinforced

15、 with either a single wire braid covered by a textile braid or two textile braids separated by a wire braid. All braids shall be impregnated with a black oil and mildew resistant synthetic rubber compound. 4.1.2 Type II No longer used. Use type I. 4.1.3 Type III - This hose shall consist of a seamle

16、ss tube of oil and hydraulic brake fluid resisting rubber reinforced with two textile braids separated by a wire braid. All braids shall be impregnated with an oil and mildew resistant synthetic rubber compound. 4.1.4 Type IV No longer used. Use Type III. NUMBER: MPAPS F-6016 TITLE: Hose, High Tempe

17、rature, With End Fittings REVISION: 1510 This document is restricted and may not be sent outside Navistar, Inc or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2015 by Navistar, Inc. OCTOBER 2015 Page 3 of 16 4.1.5 Type V - T

18、his hose shall consist of a seamless smooth bore extrusion of Teflon meeting the requirements of Type III resin per ASTM D1457, except suitable additives (up of 2% max) are permissible. The reinforcement shall consist of a 300 series stainless steel wire braid of sufficient strength to insure the ho

19、se will meet requirements of this specification. 4.1.6 Type VI - This hose shall consist of a seamless tube of oil resistant rubber reinforced and covered with textile. 4.1.7 Type VII - This hose shall consist of a seamless tube of virgin PTFE reinforced with 90% electrical grade continuous filament

20、 glass fibers blended with 10% aramid fibers having minimum 9000 yarn denier for 5/16 inch nominal inside diameter, 14000 yarn denier for 3/8 inch, and 14000 for 1/2 inch hose bonded to tube by means of Teflon coating with weaving construction of two over and two under such that a minimum 90% covera

21、ge is achieved. 4.1.8 Type VIII This hose shall have the same construction requirements as Type VII hose but is intended for water and glycol based coolant applications. In addition to the requirements of this specification this hose must also satisfy the requirements of MPAPS F-30 Sections: 6.2.4 F

22、or Oven Aged Burst Strength, 6.2.6 Electrochemical Resistance, Section 6.2.9 Chemical Interaction, and Section 8.6 Immersions. Use the performance criteria for MPAPS F-30 Grade 1 tube material for the Oven Aged Burst Strength and Immersions testing. 4.2 General Requirements for Fittings and Tubing 4

23、.2.1 Fittings 4.2.1.1 Types I, II, III, and IV Hose Fittings Shall comply with requirements of SAE J1402 and SAE J516. Fittings may be permanent (crimped) or reusable as indicated on the Engineering drawing and/or purchase order. Reusable end fittings used in air brake applications shall have a bras

24、s or stainless steel inner, the outer nut and collar may be brass, stainless steel or plated steel (see Section 4.2.1.3 for material requirements). In some cases, the print may require the inner to be phosphate coated. Reusable end fittings used in fluid (non air) applications may use a coated steel

25、 liner. Such applications are not interchangeable with air applications. 4.2.1.2 Type V, VI, VII, Type VIII Hose Fittings Fittings are permanent (crimp). Reusable fittings are not recommended. Material requirements are the same as Types I through IV for air applications except that only stainless st

26、eel or brass are allowed on Type V. Fittings shall comply with SAE J516 except as indicated on the engineering drawing. 4.2.1.3 Fitting Materials NOTE - Fittings are not interchangeable between types; each material has its own type and style of fitting that does not work with other types of hose. Ap

27、plications between Types I and III may be interchanged based on economics or availability, with prior engineering approval. Types I and III may also be used for Type VI with prior approval. As outside diameters change between hose style, care must be taken to ensure that assembly issues do not arise

28、 due to substitutions. NUMBER: MPAPS F-6016 TITLE: Hose, High Temperature, With End Fittings REVISION: 1510 This document is restricted and may not be sent outside Navistar, Inc or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability

29、. 2015 by Navistar, Inc. OCTOBER 2015 Page 4 of 16 Fittings shall meet the following requirements, or as specified on engineering drawing: Brass UNS C36000, C34500, C35000, or C37700 per CEMS C-3 Steel 0-100, 0-115 or 0-201 per MPAPS A-0, Part II Finish for steel fittings Unless otherwise specified:

30、 a) Zinc Plating (trivalent), Class 6A, per MPAPS G-20 b) Zinc-Nickel Plating (trivalent) Class ZNi-C3, per MPAPS G-22 (for use w/oil centrifuge lines) c) For inner when specified: phosphate coating, Class B-2, per MPAPS G-1 Stainless Steel Austenitic (18-8) Stainless Steel per MPAPS A-37; Passivate

31、d per MPAPS A-37, Type 5. Aluminum 6061-T6 aluminum per MPAPS C-10 (for use with aluminum tubing only) 4.2.2 Tubing Material 4.2.2.1 Steel - Steel tubing will be single-wall, electric-resistance welded (ERW) low carbon steel, Grade F, per MPAPS A-45 Part II with flash height controlled to 380 m (0.0

32、15 inch) max. For lower pressure applications, such as transmission oil cooler hose assemblies, single-wall, electric-resistance welded (ERW) low carbon steel, Grade 5, per MPAPS A-45 Part I with flash height controlled to 380 m (0.015 inch) max, is acceptable when designated on the drawing. 4.2.2.1

33、.2 Tubing Finish unless otherwise specified, steel tubing will have one of the following finishes and meet the performance requirements as specified in the applicable specification: a) Zinc plating (trivalent), Class 6A, per MPAPS G-20 b) Paint, Class II, per MPAPS G-9009 c) Hot-dipped zinc-aluminum

34、 coating (95% zinc, 5% aluminum) (Galfan) (Must provide ASTM B117 salt spray performance of 360 hr to red rust, with no more than 1% red rust per ASTM D610, Plate #6) d) Zinc-nickel plating (trivalent), Class ZNi-C3, per MPAPS G-22 (esp. for oil centrifuge lines) 4.2.2.2 Aluminum 3003-H14 per MPAPS

35、C-10. Aluminum tubing will be plain (no finish). 4.3 Dimensions and Tolerances All types shall comply with standards indicated in Table 1 and 3. See Table 6 for common tolerances. Types I thru IV and VI inside diameter and outside diameter shall be concentric within the following limits: 4.3.1 Conce

36、ntricity shall be measured over the finished O.D. The readings shall be taken at 90 intervals around the hose and acceptance shall be based on the total variations of the readings. Size Concentricity - T.I.R. Mm in -3 through -20 0.8 0.030 NUMBER: MPAPS F-6016 TITLE: Hose, High Temperature, With End

37、 Fittings REVISION: 1510 This document is restricted and may not be sent outside Navistar, Inc or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2015 by Navistar, Inc. OCTOBER 2015 Page 5 of 16 Dimensional measurements shall b

38、e made at a minimum distance of 13 mm (0.50 in) from the cut ends of the hose. Type V shall meet the concentricity requirements of SAE 100R14 per SAE J517. 4.4 Performance Requirements 4.4.1 Hose and Hose Assemblies Hose and hose assemblies furnished will meet required tests per SAE J1402, SAE J517

39、and FMVSS-106 and any additional requirements of this specification or TMC Recommended Practice 307. Unless otherwise indicated, all tests shall be performed in accordance with SAE J343, ASTM D 380 or D 622. 4.4.1.1 Burst Pressure (Assemblies) Hose shall not burst or indicate failure at a hydrostati

40、c pressure below the minimum specified burst pressure in Table 5. The assemblies shall be brought to minimum burst pressure at a constant rate within a period of 15-30 seconds and then continue to failure at the same rate. 4.4.1.2 Proof Pressure Hose assemblies shall not leak when proof pressure tes

41、ted at the minimum pressure specified in Table 5. Hose assemblies shall be subjected to the required pressure for a period of 30-60 seconds. 4.4.1.3 Cold Flexibility Hose assemblies shall show no leakage or visible cracking after being exposed to a cold environment, bent over a mandrel, and proof pr

42、essure tested after returning to room temperature. The assemblies shall be subjected to -40C (-40F) for Types I, II, III, IV and VI; and -53 C (-65 F) for Type V and Type VIII for 24 hours in a straight position. While still at the specified temperature, the sample shall be evenly and uniformly bent

43、 over a mandrel having a diameter equal to twice the specified minimum bend radius in Table 5. The mandrel shall be cooled to the specified test temperature. Bending shall be to the indicated angle within 8-12 seconds. I.D. of Hose Angle Less than 2.5 cm (less than 1 in) 180 25 mm and greater (1 in

44、and greater) 90 For Type VI hose, an alternate strip method per ASTM D 380 or SAE J30R7 may be used. 4.4.1.4 Burst Strength, Elevated Temperature 4.4.1.4.1 Method: Similar to room temperature burst, except media shall be an appropriate fluid such as: MIL-H-8446 Oronite Chemical #8200 Dow Chemical F-

45、60 General Electric F-50 MIL-L-7807 ASTM Service Fluid 101 Dexron II 4.4.1.4.2 Procedure: The assembly, filled with the test fluid, shall be heat aged for 1 hour at 150 C (302 F), or at 232 C (450 F) for Type V (1-hour period doesnt include time for oven or assembly NUMBER: MPAPS F-6016 TITLE: Hose,

46、 High Temperature, With End Fittings REVISION: 1510 This document is restricted and may not be sent outside Navistar, Inc or reproduced without permission from Corporate Technical Standards. Suppliers are required to assume all patent liability. 2015 by Navistar, Inc. OCTOBER 2015 Page 6 of 16 to re

47、ach required temperature). After aging, the assembly shall be pressurized to proof pressure for 2 minutes and then burst tested. Hot oil circulation is an acceptable alternative method to oven aging. 4.4.1.4.3 Required: There shall be no leakage, hose burst, or separation from the fittings at 80% of

48、 the minimum proof and burst pressures indicated in Table 5. 4.4.1.5 Vacuum - Types I, II, III, IV, and VI: Hose assemblies shall show no leakage or visible ply separation after bending to the indicated angle from Table 2, over a mandrel with minimum bend radius shown in Table 5. The specimens shoul

49、d be subjected to the indicated vacuum pressure from Table 2 for 5 minutes. TABLE 2 - HOSE ASSEMBLY METRICS TO PREVENT LEAKAGE AND PLY SEPARATION Hose Dash Size Angle of Bend Vacuum Pressure cm-Hg in-Hg -4 180 71.1 28 -5 180 71.1 28 -6 180 71.1 28 -8 180 71.1 28 -10 180 71.1 28 -12 180 50.8 20 -16 180 38.1 15 -20 90 25.4 10 4.4.1.5.1 Assemblies shall be checked during test for maintenance of vacuum and be sectioned longitudinally after t