HOLDEN HN 2424-2003 DEADENER PATCH - PRESSURE SENSITIVE《隔音材料 压敏型》.pdf

《HOLDEN HN 2424-2003 DEADENER PATCH - PRESSURE SENSITIVE《隔音材料 压敏型》.pdf》由会员分享，可在线阅读，更多相关《HOLDEN HN 2424-2003 DEADENER PATCH - PRESSURE SENSITIVE《隔音材料 压敏型》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2424 1 of 4 June, 2003 NAME: DEADENER PATCH - PRESSURE SENSITIVE THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFI

2、RM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 1. SCOPE This specification covers the requirements of a pressure sensitive deadener patch. The deadener patch is supplied with release paper on one side and a suitable constraining la

3、yer (polyethylene, aluminium, fibreglass, stainless steel etc.) on the other. A typical application would include dampening sheet metal closure panels such as decklids, hoods or doors. The deadener must adhere to CRS, zinc anneal, zinc-iron and galvanised panels and be compatible with production pro

4、cessing oils. Material must be supplied to ensure dimensional stability, no blocking and ease of release paper removal under typical production conditions. 2. REFERENCES HN 1000 HN 0013 ASTM D570 HN 0214 GM4465P GM9832P ASTM E502 ASTM D1475 3. MATERIAL REQUIREMENTS 3.1 Solids content (HN 0013) 99% m

5、in 3.2 Odour (GM9832P) Material must not have a noxious or toxic odour when received or after curing. 3.3 Flash Point (ASTM E502) 200 C min 3.4 Specific Gravity (ASTM D1475) 2.0 - 2.5 g/ml 3.5 Formability The patch must not crack or delaminate when folded 180 upon itself at 10C. A.C.N. 006 893 232 H

6、olden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2424 2 of 4 June, 2003 NAME: DEADENER PATCH - PRESSURE SENSITIVE THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSU

7、E DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 3. MATERIAL REQUIREMENTS (continued) 3.3 Adhesion to oily steel Max slide 5mm Apply 3g/m2 of standard production press oil to a 100mm x 300mm CRS panel. Bend the panel at its mid-length point to form a 60

8、 acute angle. Attach a 50mm x 100mm piece of material to one inside face and apply 2kPa pressure for 10 seconds uniformly over the area of the patch. Stand up the test assembly so that the test piece is on the underside of the folded panel and 60 to horizontal per Figure 1. Leave in standard conditi

9、ons (20C, 65% RH) for 3h, then examine for evidence of deformation, slippage or loss of adhesion. Place in same orientation in an oven for 20 minutes (hold) at 190C. Remove and allow to cool to room temperature. There shall be no deformation or loss of adhesion. Max slide 5mm Figure 1- Panel orienta

10、tion for adhesion test 3.7 Water Absorption (Refer ASTM D570) Values shall be less than 1% when laminates are tested according to the specification. 3.8 Phosphate and Elpo Compatibility Test samples exposed to Holden production phosphate and Elpo system shall exhibit no loss of adhesion from the tes

11、t substrate. 60 A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2424 3 of 4 June, 2003 NAME: DEADENER PATCH - PRESSURE SENSITIVE THIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESP

12、ONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 4. PERFORMANCE REQUIREMENTS 4.1 Noise and Vibration test Material will be fitted to production panel and submitted to a Noise and Vibration test engineer for measuremen

13、t of the Decay Rates and Frequency Responses. A minimum of a rating 8 on the N&V rating scale is required. 4.2 Cold impact resistance A 50mm x 200mm patch is applied centrally on a 100mm x 300mm panel. After baking, condition the test piece for 4 hours at 30C. The material shall not crack not lose a

14、dhesion after two 1.69J impacts. The two impacts are made with a 51mm diameter 2” steel ball weighing 535g. 4.3 Corrosion resistance Prepare test panel as per section 3.6 then process through the complete production cleaning, pre-treatment and ELPO lines. Remove after ELPO oven and subject to 20 cyc

15、les scab (HN 0214). When complete, remove the patch and assess. There shall be no evidence of corrosion under patch. 4.4 Humidity resistance (GM4465P) Prepare test panel as per section 3.6 then process through the complete production cleaning, pre-treatment and ELPO lines. Remove after ELPO oven and

16、 subject to 3 weeks at 38C, 100%RH. Upon removal, conduct cold impact test. There shall be no loss of adhesion or delamination. 4.5 Heat resistance Prepare test panel as per section 3.6 then process through the complete production cleaning, pre-treatment and ELPO lines. Remove after ELPO oven and su

17、bject to 14 days at 70C. Upon removal conduct cold impact test. There shall be no loss of adhesion or delamination. A.C.N. 006 893 232 Holden Limited Engineering Department MATERIAL SPECIFICATION NUMBER SHEET RELEASE REVISION : HN 2424 4 of 4 June, 2003 NAME: DEADENER PATCH - PRESSURE SENSITIVE THIS

18、 DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TO THE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TO CONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID. FORM : I:CentralLaboratoryStandardForms MaterialSpecificationMatspec.doc 5. STORAGE STABILITY 5.1 Elevated Temperature Stability As shipped,

19、the laminate shall be capable of withstanding a temperature of 55 C for a period of 72 hours without cold flowing or blocking or laminate separation. 5.2 Low Temperature Stability As shipped, the laminate shall be capable of withstanding a temperature of 10 C for a period of 72 hours without crackin

20、g or laminate delamination. 5.3 Storage Stability As shipped, the shelf life of the material shall be 60 days at a temperature of 35 C. The shelf life of the material shall commence upon receipt of the material from the manufacturer. NOTE: Material conditioned in the above environments (5.1, 5.2 & 5

21、.3) shall meet all requirements of this specification. 6 APPROVAL, INSPECTION AND REJECTION Refer HN 1000, Clauses A, C and G(Line Trial). 7 HAZARDOUS MATERIALS Refer HN 1000, Clause H. 8 RESTRICTED CHEMICALS Refer HN 1000, Clause J. 9. APPROVED SUPPLIERS AND MATERIALS APPROVED SUPPLIER APPROVED MATERIAL Henkel HSTM 203H Prepared by: Mark Franke