GMW GMW15692-2012 Abrasion Resistance for Glass Seals Issue 2 English.pdf

《GMW GMW15692-2012 Abrasion Resistance for Glass Seals Issue 2 English.pdf》由会员分享，可在线阅读，更多相关《GMW GMW15692-2012 Abrasion Resistance for Glass Seals Issue 2 English.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 WORLDWIDE ENGINEERING STANDARDS Test Procedure GMW15692 Abrasion Resistance for Glass Seals Copyright 2012 General Motors Company All Rights Reserved July 2012 Originating Department: North American Engineering Standards Page 1 of 4 1 Scope Note: Nothing in this standard supercedes applicable laws

2、and regulations. Note: In the event of conflict between the English and domestic language, the English language shall take precedence. 1.1 Purpose. This standard describes the method to test and evaluate the durability of weatherstrip coatings, including flocking, spray applied coatings, and co-extr

3、uded low friction materials, and geometric effectiveness of a given profile on glass run sections and areas where constant wear is likely to occur on the vehicle. 1.2 Foreword. Not applicable. 1.3 Applicability. This standard is applicable to all coated glass run channel seals. 2 References Note: On

4、ly the latest approved standards are applicable unless otherwise specified. 2.1 External Standards/Specifications. None 2.2 GM Standards/Specifications. GMW14125 2.3 Additional References Glass Fab Inc., Part No. 44750-0001 or equivalent 3 Resources 3.1 Facilities. Not applicable. 3.2 Equipment. 3.2

5、.1 Wear Resistance Tester. Suitable wear resistance tester (e.g., see Appendix A, Figure A1 or linear abrasion tester to GMW14125). 3.2.2 Appropriate wear resistance mounting fixture for profile to be tested. 3.2.3 Test Glass Abrader. Non- or semi-tempered, acid etched, 4 mm thick, radius on edge sh

6、all be 6 mm. Abrader source: Glass Fab, Inc., 257 Ormond Street, Rochester, NY 14605, (585) 262-4000, part number 44750-0001 or equivalent. 3.3 Test Vehicle/Test Piece. Cut three sections of weatherstrip seal to be tested, each 200 mm 5 mm in length. Lips may be trimmed as necessary for mounting to

7、wear resistance fixture. 3.4 Test Time. Not applicable. 3.5 Test Required Information. Not applicable. 3.6 Personnel/Skills. Not applicable. 4 Procedure 4.1 Preparation. Not applicable. 4.2 Conditions. Copyright General Motors Company Provided by IHS under license with General Motors CompanyNot for

8、ResaleNo reproduction or networking permitted without license from IHS-,-,-GM WORLDWIDE ENGINEERING STANDARDS GMW15692 Copyright 2012 General Motors Company All Rights Reserved July 2012 Page 2 of 4 4.2.1 Environmental Conditions. The minimum time between manufacturing and testing shall be 72 h. The

9、 test pieces shall be maintained at a temperature of 23 C 5 C and 50% 5% relative humidity for at least 24 h prior to test and shall be free from strain during this period. 4.2.2 Test Conditions. Deviations from the requirements of this standard shall have been agreed upon. Such requirements shall b

10、e specified on component drawings, test certificates, reports, etc. 4.3 Instructions. Note: A new abrader shall be used for each test. 4.3.1 Mount seals to wear resistance mounting fixture. 4.3.2 Attach mounting fixture to wear resistance tester. 4.3.3 Center mounting fixture and tighten so that the

11、 mounting fixture remains stationary and straight during test. 4.3.4 Apply weight as defined in performance specification. 4.3.5 Set wear resistance tester to 60 cycles/minute, where the stroke of the abrasion element (glass) is 150 mm 1 mm with one back and forth movement as one cycle. A constant s

12、peed tester may be used. 4.3.6 Load the abrader to the wear resistance tester. 4.3.7 Run the wear resistance test, examining profiles every 1000 cycles. Abrader shall be wiped with methyl ethyl ketone (MEK) at each evaluation interval. Evaluation of the profile may be needed more or less frequently

13、according to initial results. 4.3.8 Record cycles and any observations such as element scratching or pressure points. 5 Data 5.1 Calculations. Not applicable. 5.2 Interpretation of Results. Not applicable. 5.3 Test Documentation. With reference to this test procedure, the results shall be represente

14、d in a test report. The report shall include the following: Complete identification of the specimen. Conditioning of the test specimen. Test conditions. Any deviations to the test method. Observations of the condition of each tested area. Number of cycles. 6 Safety This standard may involve hazardou

15、s materials, operations, and equipment. This standard does not propose to address all the safety problems associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prio

16、r to use. 7 Notes 7.1 Glossary. Not applicable. 7.2 Acronyms, Abbreviations, and Symbols. MEK Methyl ethyl ketone 8 Coding System This standard shall be referenced in other documents, drawings, etc., as follows: Test to GMW15692 Copyright General Motors Company Provided by IHS under license with Gen

17、eral Motors CompanyNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-GM WORLDWIDE ENGINEERING STANDARDS GMW15692 Copyright 2012 General Motors Company All Rights Reserved July 2012 Page 3 of 4 9 Release and Revisions This standard was originated in September 2007. It

18、 was first approved by the Global Elastomers Team in November 2007. It was first published in November 2007. Issue Publication Date Description (Organization) 1 NOV 2007 Initial publication. 2 JUL 2012 Five year refresh of standard. (Elastomers Global Subsystem Leadership Team Copyright General Moto

19、rs Company Provided by IHS under license with General Motors CompanyNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-GM WORLDWIDE ENGINEERING STANDARDS GMW15692 Copyright 2012 General Motors Company All Rights Reserved July 2012 Page 4 of 4 Appendix A Figure A1: Wear Resistance Tester Copyright General Motors Company Provided by IHS under license with General Motors CompanyNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-