FORD WSS-M7C95-A-2004 SUPERFICIAL WAX SOLVENT BASED 35% SOLIDS TO BE USED WITH FORD WSS-M99P1111-A 《35%含固量的溶剂型饰面蜡 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD WSS-M7C95-A-2004 SUPERFICIAL WAX SOLVENT BASED 35% SOLIDS TO BE USED WITH FORD WSS-M99P1111-A 《35%含固量的溶剂型饰面蜡 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M7C95-A-2004 SUPERFICIAL WAX SOLVENT BASED 35% SOLIDS TO BE USED WITH FORD WSS-M99P1111-A 《35%含固量的溶剂型饰面蜡 与标准FORD WSS-M99P1111-A一起使用 》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 09 15 Activated A. Latado Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 1 of 4 SUPERFICIAL WAX, SOLVENT BASED, 35% SOLIDS WSS-M7C95-A 1. SCOPE The materials defined by this specification are solvent ba

2、sed rust preventive compounds. 2. APPLICATION This specification was released originally for materials used as corrosion protective compound for the door hinges. The material is applied to the vehicle after the paint process. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Materia

3、l suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION Solvent based waxes and resins. 3.3 PHYSICAL PROPERTIES 3.3.1 Non Volatile Content 35 +/- 5% (FLTM BI 102-01) 3.3.2 Viscosity See Initial Sample A flow diagram

4、 to identify the characteristic properties of the material shall be added to the Initial Sample Report, together with a list of the relevant test parameter (temperature, shear rate, time, etc.) and equipment details. 3.3.3 Density See Initial Sample (ASTM D 1475) +/- 0.05 g/mL 3.3.4 Creeping Ability

5、, min 20 mm (FLTM BJ 128-02) 3.3.5 Flow Rate See Initial Sample (FLTM BJ 128-01) +/- 5 mm The flow rate shall be determined at 20 C and at 40 C. 3.3.6 Color Transparent ENGINEERING MATERIAL SPECIFICATIONWSS-M7C95-A Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2

6、of 4 3.3.7 Appearance The wax shall dry to a smooth homogeneous film. 3.3.8 Storage Stability, min The storage stability must be adapted to the climate conditions at the individual plant. Min storage conditions for all waxes: 6 months at 32 C and climates: 6 months at 5 C Additionally for tropical 3

7、 months at 40 C After the storage, the material shall not show any insoluble separation or coagulation and must meet all specification requirements. 3.4 PREPARATION OF TEST PANELS The back side of test panels shall be protected to avoid excessive rusting during the following resistance tests. Panel

8、edges, being subject of the investigation, must not be protected by any additional action. 3.4.1 Substrate (FLTM BJ 106-01, solvent wiped) 3.4.1.1 Ford Standard Steel Panels according to SAE J403 Steel or U-MA 18006, if not otherwise specified. 3.4.1.2 Welded test assemblies per para 4.2. 3.4.2 Wax

9、Application Prior to application, the wax must be stirred for 15 minutes. Test Panels: The wax may be sprayed airless or air assisted as recommended by the supplier to provide a homogenous film. Test Assemblies: An excess of wax shall be sprayed to the vertically positioned assemblies to enable the

10、wax creeping into the welded joint. Two minutes after the wax application, the assemblies shall be turned into a horizontal position for drying. 3.4.3 Application Temperature 20 25 C ENGINEERING MATERIAL SPECIFICATIONWSS-M7C95-A Printed copies are uncontrolled Copyright 2004, Ford Global Technologie

11、s, LLC Page 3 of 4 3.4.4 Drying Time 5 minutes (23 +/- 2 C) 3.4.5 Dry Film Thickness on Test Panels 40 - 50 (FLTM BI 156-01 or gravimetrically) micrometer 3.5 REMOVAL The wax film must be removable from automotive topcoats at any time without damaging the painted surface. The supplier must recommend

12、 a suitable solvent/cleaner process in the Initial Sample Report. Relevant topcoat systems are: Body enamel, catalyzed repair enamel, plastic paint, repair paint materials. 3.6 WATER DISPLACING PROPERTIES No rust Panel Preparation: UMA 18001 test panels (may be cut to approximately a 5 x 7 cm size)

13、shall be degreased and cleaned with an a applicable solvent. The panels shall not be touched after cleaning. Test Method: The test panels shall be completely immersed into an aqueous solution of NaCl (3%) for 2 minutes (complete wetting of the steel surface must be checked after the first 30 seconds

14、). After draining in a vertical position for 10 seconds, the samples shall be immersed into the rust preventive under test for 2 minutes and then be dried vertically for 1 hour at room temperature. The test sample and an uncoated control panel shall be exposed to the atmosphere above a saturated sol

15、ution of sodium carbonate with an excess of solid sodium carbonate for 72 hours. Evaluation: No corrosion and no staining. 3.7 COMPATIBILITY The wax must be adaptable for application in accordance with the appropriate Ford Motor Company Process Specification, e.g. U-C 800. The wax must be compatible

16、 with all related materials. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. ENGINEERING MATERIAL SPECIFICATIONWSS-M7C95-A Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC

17、Page 4 of 4 4.1 MATERIAL REFERENCE All related materials used for approval of superficial wax according to this specification, e.g. substrate materials, paint materials, solvents, etc. as well as the application parameter shall be noted in the Initial Sample Report of the wax. 4.2 TEST ASSEMBLIES Test assemblies shall be prepared from U-MA 001-18001/6 Standard Panels according to the following sketch to simulate flanges, edges and joints of a vehicle body.