FORD WSH-M2A112-B3-2009 ALUMINUM SHEET VACUUM BRAZING TO BE USED WITH FORD WSS-M99P1111-A 《真空钎焊用铝片 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSH-M2A112-B1上》.pdf

《FORD WSH-M2A112-B3-2009 ALUMINUM SHEET VACUUM BRAZING TO BE USED WITH FORD WSS-M99P1111-A 《真空钎焊用铝片 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSH-M2A112-B1上》.pdf》由会员分享，可在线阅读，更多相关《FORD WSH-M2A112-B3-2009 ALUMINUM SHEET VACUUM BRAZING TO BE USED WITH FORD WSS-M99P1111-A 《真空钎焊用铝片 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSH-M2A112-B1上》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 07 09 B1/B3 - N-STATUS No Replacement Named B. Curtiss, NA 2005 01 19 Revised Inserted 3.0, Deleted 3.8, 4 1991 08 20 Released CE00E10109215010 C. C. GrayPrinted copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1

2、 of 3 ALUMINUM SHEET, VACUUM BRAZING NOT TO BE USED FOR NEW DESIGN WSH-M2A112-B1 NOT TO BE USED FOR NEW DESIGN WSH-M2A112-B3 WSS-M2A112-B4 1. SCOPE The materials defined by these specifications are aluminum sheet clad with brazing alloy typically on both sides. 2. APPLICATION These materials were re

3、leased originally for fabrication of plates and supports for air conditioning evaporator assemblies joined by vacuum brazing. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Mat

4、erials (WSS-M99P1111-A). 3.2 CHEMICAL COMPOSITION % (ASTM E 34) B1 B3 B4 Core Core Core Silicon 0.60 max 0.50 max 0.50 max Iron 0.70 max 0.70 max 0.70 max Copper 0.10 - 0.30 0.30 max 0.23 - 0.36 Magnesium 0.15 - 0.80 0.40 - 0.60 0.39 - 0.51 Manganese 0.10 - 0.80 1.0 - 1.5 0.60 - 0.80 Chromium 0.10 m

5、ax 0.10 max 0.05 max Nickel 0.05 max - 0.05 max Titanium 0.10 max 0.10 max 0.09 - 0.17 Zinc 0.10 max 0.10 max 0.05 max Zirconium - - 0.05 - 0.15 Each other element 0.05 max 0.05 max 0.05 max Total other elements 0.15 max 0.15 max 0.15 max Aluminum Balance Balance Balance ENGINEERING MATERIAL SPECIFI

6、CATIONWSH-M2A112-B1/B3 WSS-M2A112-B4 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 3 3.3 CHEMICAL COMPOSITION PERCENTAGE - BRAZE CLAD MATERIAL (ASTM E 34) B1 B3/B4 Clad Clad Silicon 9.2 - 10.2 11.5 - 12.5 Iron 0.50 max 0.50 max Copper 0.10 max 0.10 max Magne

7、sium 1.25 - 1.75 0.10 - 0.25 Manganese 0.10 max 0.10 max Zinc 0.10 max 0.10 max Bismuth 0.15 max - Each other element 0.05 max 0.05 max Total other elements 0.15 max 0.15 max Aluminum Balance Balance Specific composition limits to meet performance and manufacturing requirements will form part of an

8、agreed Control Plan for individual component geometries and process routes. See para 5.1. 3.4 BRAZE CLAD THICKNESS Material will be clad on both sides of the sheet (unless otherwise specified) at the percentage (shown below) of the total material thickness specified on the engineering drawing. B1 Cl

9、ad Material B3 Clad Material B4 Clad Material Thickness Thickness Thickness 1.0 mm, 5 - 9% 1.0 mm, 4 - 8% 1.0 mm, 4 - 8% 3.5 MECHANICAL PROPERTIES (Material as supplied) (ASTM B 557M) B1 - Material O-Temper H-120 Temper Ultimate Tensile Strength 93 - 138 MPa 117 - 179 MPa Yield Strength, min 36 MPa

10、83 MPa Elongation, 50 mm, min 19% 6% B3 Material O-Temper H-120 Temper Ultimate Tensile Strength 120 - 155 MPa 117 - 179 MPa Yield Strength, min 45 MPa 83 MPa Elongation, 50 mm, min 20% 6% B4 Material O-Temper H-120 Temper Ultimate Tensile Strength 131 - 159 MPa - Yield Strength, min 45 MPa - Elonga

11、tion, 50 mm, min 19% - ENGINEERING MATERIAL SPECIFICATIONWSH-M2A112-B1/B3 WSS-M2A112-B4 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 3 3.6 CORE MATERIAL GRAIN SIZE (ASTM E 112) B1 Material ASTM #3 - #5 B3 Material ASTM #5 - #8 B4 Material ASTM #5 - #8 3.7 M

12、ATERIAL CONDITION This material shall be free of any visible staining as from oils, solvents, water, etc. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 DESIRED CHEMICAL COMPOSITION, % B1 B3 B4 Core Core Core Silicon, max .15 .30 .30 Magnesium .25 .50 .45 Manganese .20 1.12 .70 Bismuth - - - B1 B3 B4 Clad Clad Clad Silicon 9.80 12.00 12.00 Magnesium 1.50 .17 .17 Manganese - - - Bismuth .08 - -