1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2000 09 25 Revised Updated A. Cockman 1989 10 27 NE01 - E - 10000474 - 059 Revised E. J. Dud a 1987 10 01 NE01 E - 10000474 - 000 Released Printed copies are uncontrolled Page 1 of 4 Copyright 2000, Ford Glo

2、bal Technologies, Inc. DIAPHRAGM CLOTH, FLUOROSILICONE WSE-M99H136-A RUBBER (FVMQ) COATED 1. SCOPE The material defined by this specification is a polyester cloth of good quality and uniform composition coated on both sides with a high temperature, oxygenated and oxidized (“ sour“) fuels, ozone, and

3、 low temperature stiffening resistant fluorosilicone (FVMQ) rubber. It is usually furnished molded to a desired shape, but may be sheet stock. 2. APPLICATION This specification was released originally as the diaphragm application s for the carburetor accelerator pump. 3. REQUIREMENTS Material specif

4、ication requirements are to be used for initial qualification of materials. 3.1 QUALITY SYSTEM REQUIREMENTS Material suppliers and part producers must conform to the Companys Quali ty System Requirements. 3.2 INFRARED SPECTROPHOTOMETRY AND/OR THERMAL ANALYSIS IR spectra and thermograms established f

5、or initial approval shall constitute the reference standard and shall be kept on file at the designated material laboratory. All samp les shall produce IR spectra and thermograms that correspond to the reference standard when tested under the same conditions. 3.3 CONDITIONING AND TEST CONDITIONS All

6、 test values indicated herein are based on material conditioned in a controlled atmosph ere of 23 +/ - 2 C and 50 +/ - 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. 3.4 CONSTRUCTION The overall construction (base fabric

7、 and rubber) must be such as to meet the re quirements of this specification and the requirements of the engineering drawing. 3.5 THICKNESS 0.275 +/ - 0.350 mm (ASTM D 751) ENGINEERING MATERIAL SPECIFICATION WSE-M99H136-A Page 2 of 4 Copyright 2000, Ford Global Technologies, Inc. 3.6 BURSTING STRENG

8、TH, min 0.85 MPa (ASTM D 751) 3.7 STIFFNESS (ASTM D 747, at 30 deg angle, 2.8E - 3 N.m bending m oment, 3.2 mm specimen span) Fil 5 - 15 Warp 8 - 18 3.8 FLEX CRACK RESISTANCE (FLTM BN 102 - 02, except cut 25 x 125 mm specimens) Non - pierced sample No cracks or Flex 2 000 000 cycles rubber separatio

9、n 3.9 ADHESION (ASTM D 751) Attempt to separate coating from the fabric must always result in a cohesive failure. 3.10 OZONE RESISTANCE, max Rating 0 (FLTM BP 101 - 01, Procedure A, 9.5 mm mandrel) 3.11 PERMEATION No bubbles (FLTM BZ 104 - 02) The elapsed time of the first b ubble to break free from

10、 the surface on the specimen shall not be less than 15 min. 3.12 HEAT AGED (ASTM D 573, 168 h at 150 +/ - 2 C) 3.12.1 Bursting Strength Change, max - 6 % (Test acc. to 3.6) 3.12.2 Stiffness (Test acc. to 3.7) Fill 6 - 1 6 Warp 11 - 21 3.12.3 Flex Crack Resistance No cracks or (Test acc. to 3.8, 2 00

11、0 000 cycles) rubber separation 3.13 HEAT AGED (ASTM D 573, 1000 h at 150 +/ - 2 C) 3.13.1 Bursting Strength Change, max - 20 % (Test acc. to 3.6) ENGINEERING MATERIAL SPECIFICATION WSE-M99H136-A Page 3 of 4 Copyright 2000, Ford Global Technologies, Inc. 3.13.2 St iffness (Test acc. to 3.7) Fill 15

12、- 28 Warp 20 - 34 3.13.3 Flex Crack Resistance No cracks or (Test according to 3.8, 2 000 000 cycles) rubber separation 3.14 IMMERSION IN 85 % ASTM FUEL C + 15 % METHANOL (ASTM D 471, 70 h at 23 +/ - 2 C) 3.14.1 Bursting Strength Change, max - 8 % 3.14.2 Stiffness (Test acc. to 3.7, except total tes

13、ting time must not exceed 10 min after removal from fuel) Fill 4 - 14 Warp 6 - 16 3.14.3 Flex Crack Resistance No cracks or (Test ac c. to 3.8, 2 000 000 cycles) rubber separation 3.14.4 Adhesion (Test according to 3.9) Attempt to separate coating from the fabric must always result in a cohesive fai

14、lure. 3.15 IMMERSION IN OXIDIZED GASOLINE (SOUR GAS) (FLTM AZ 5 - 1, 120 h at 60 +/ - 2 C each cycle, PN - 180) Test Method: Using reflux condensing equipment immerse the specimens in 180 PN (Peroxide Number) sour fuel at 60 +/ - 2 C for 48 to 72 h. Dry out in the convection oven for 4 h at 100 +/ -

15、 2 C. Re -immerse the same specimens in t he 180 PN sour fuel at 60 +/ - 2 C for additional 48 to 72 h. The total time of both immersions shall equal 120 h. Dry specimens for 4 h at 100 +/ - 2 C. Repeat above for 2 cycles and determine the following properties. 3.15.1 Bursting Strength Change, max -

16、 5 % (Test acc. to 3.6) 3.15.2 Stiffness (Test acc. to 3.7) Fill 9 - 19 Warp 14 24 3.15.3 Flex Crack Resistance No cracks or (Test according to 3.8, 2 000 000 cycles) rubber separation 3.15.4 Adhesion, min 1.0 kN/m (Te st according to 3.9) ENGINEERING MATERIAL SPECIFICATION WSE-M99H136-A Page 4 of 4

17、 Copyright 2000, Ford Global Technologies, Inc. 3.16 LOW TEMPERATURE RESISTANCE (FLTM BN 102 - 1, Procedure A, 5 h at - 40 C) 3.16.1 As Received No cracks 3.16.2 After Heat Aging No cracks (Para. 3.12 and 3.13) 3.16.3 After Immersion in 85 % ASTM No cracks Fuel C + 15 % Methanol (Para 3.15) 3.17 SOU

18、RCE IDENTIFICATION Each diaphragm shall have the suppliers identification marks permanently affixed. 3.18 SUPPLIERS RESPONSIBILITY All materials supplied to this specification must be equivalent in all characteristic s to the material upon which approval was originally granted. Prior to making any c

19、hanges to the material originally approved under this specification, whether or not such changes affect the materials ability to meet the specification requirements, the S upplier shall notify the affected Purchasing, and Materials Engineering activities (with reasons) of the proposed changes. Upon

20、notification of the Company, further instructions will be provided. Note: Suppliers should be prepared to provide test data a nd samples demonstrating compliance to this specification, if requested. Substance restrictions imposed by regulations or Company direction applies to the materials addressed

21、 by this document. The restrictions are identified in Restricted Substance Mana gement Standard WSS - M99P9999 - A1. 4. APPROVAL OF MATERIALS Materials defined by this specification for direct supply to the Company must have prior approval. Certain materials subcontracted by part suppliers may also

22、require prior approval. These includ e materials critical to the Companys business for regulatory, safety, environmental or compatibility requirements or contractual agreements. Suppliers desiring approval of their materials shall first obtain an expression of interest from Purchasing, Desi gn or Materials Engineering activity. Upon request, the Supplier shall submit a completed copy of their laboratory test reports, signed by a qualified and authorized representative of the test facility, demonstrating full compliance with all the requireme nts of this specification.