FORD WSD-M1A301-A2-2011 GREY IRON - PISTON RINGS (ACICULAR) TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSD-M1A301-A1)《灰铸铁 活塞环(球光体) 与福特WSS-M99P1111-A 一起使用 在福特WSD-M1A301-.pdf

《FORD WSD-M1A301-A2-2011 GREY IRON - PISTON RINGS (ACICULAR) TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSD-M1A301-A1)《灰铸铁 活塞环(球光体) 与福特WSS-M99P1111-A 一起使用 在福特WSD-M1A301-.pdf》由会员分享，可在线阅读，更多相关《FORD WSD-M1A301-A2-2011 GREY IRON - PISTON RINGS (ACICULAR) TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSD-M1A301-A1)《灰铸铁 活塞环(球光体) 与福特WSS-M99P1111-A 一起使用 在福特WSD-M1A301-.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions Rev 02 2011 12 15 N Status A2/A3 No Usage S. Ryzyi, NA 2002 09 30 Revised Updated and renumbered 1988 02 08 SM/ER 2286 TC Released. N.P. Riley. EAO. Controlled document at www.MATS Page 1 of 3 Copyright 2011

2、, Ford Global Technologies, Inc. GREY IRON - PISTON RINGS (PEARLITIC) WSD-M1A301-A1 GREY IRON - PISTON RINGS (ACICULAR) NOT FOR NEW DESIGN WSD-M1A301-A2 GREY IRON - PISTON RINGS (ACICULAR) NOT FOR NEW DESIGN WSD-M1A301-A3 1. SCOPE The materials defined by this specification are flake graphite irons,

3、 with an acicular or pearlitic matrix; cast statically as single/twins, or centrifugally. 2. APPLICATION This specification was released originally for materials used in the production of piston rings. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part pro

4、ducers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CHEMICAL COMPOSITION (weight %, ladle analysis) A1 A2 A3 Carbon (total)* 3.4 - 4.0 3.4 - 4.0 2.5 - 3.5 Silicon* 1.5 - 3.1 1.5 - 3.1 1.5 - 3.1 Phosphorus 0.3 - 0.8 0.3 - 0.8 0.5 max Sulphur 0.15 m

5、ax 0.15 max 0.15 max Chromium 0.6 max 0.5 max 0.2 - 1.0 Copper 1.5 max 0.5 - 2.5 1.5 max Note: The Silicon content shall be adjusted to suit the casting method. Manganese, Nickel and Molybdenum can be added to a maximum of 1.0% each, vanadium 0.6% maximum. Note: Manganese must be present in sufficie

6、nt quantity to balance the sulphur i.e. ( 1.7 x S% ) + 0.2 min. ENGINEERING MATERIAL SPECIFICATION WSD-M1A301-A1/A3 Page 2 of 3 Copyright 2011, Ford Global Technologies, Inc. Carbon equivalent (*) and alloying elements shall be controlled within the above range to accommodate the ring section, size

7、and method of casting (static/centrifugal are acceptable). The anticipated working range for each component shall be restricted to a limited band within the above. 3.3 HARDNESS (ISO 6506 ; ISO 80) A1 A2 A3 HB 190 300 255 350 245 - 360 HRB 94 107 102 114 100 - 117 An average of three results taken (1

8、) adjacent to the gap (2) 90 degrees to the gap and (3) opposite the gap. Any other position will be within 10 HB or 2 Rockwell B points. In the case of dispute the umpire test method will be HB. 3.4 MICROSTRUCTURE Graphite - uniformally distributed flakes ASTM A 247 form VII type A size 5-8 and typ

9、e B (rosette) types D and E to be avoided or kept below 5% (area). Matrix - A1 - fine lamellar pearlite with phosphide constituent present as small isolated particles or a discontinuous network. Ferrite shall not exceed 10% when averaged over a field of 2mm diameter minimum. Matrix - A2 and A3 - Aci

10、cular ie tempered martensites and bainites with complex alloy carbides where appropriate present as small isolated particles below 10% of matrix volume. 3.5 BENDING STRENGTH (unless otherwise stated on drawing) (BS 5341 or equivalent ISO) A1 340 MPa min A2 and A3 450 MPa min 4. GENERAL INFORMATION T

11、he information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 MODULUS OF ELASTICITY (ISO 6621/2) A1 95 GPa nominal A2 100 GPa “ A3 115 GPa “ Note: The actual values of modulus are adjusted to match the individual requirements of each r

12、ing design. ENGINEERING MATERIAL SPECIFICATION WSD-M1A301-A1/A3 Page 3 of 3 Copyright 2011, Ford Global Technologies, Inc. 4.2 BENDING STRENGTH (BS 5341) In the absence of a complete ring a measure of Bending Strength can be obtained by the skin stress test as defined in BS 5341, in which the span may be adjusted to optimize the test for each specific ring geometry. A1 430 MPa min A2 and A3 550 MPa min