FORD WSB-M2G361-A-2015 ADHESIVE MOISTURE CURE URETHANE WARM APPLIED TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSB-M2G361-A-2015 ADHESIVE MOISTURE CURE URETHANE WARM APPLIED TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M2G361-A-2015 ADHESIVE MOISTURE CURE URETHANE WARM APPLIED TO BE USED WITH FORD WSS-M99P1111-A .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2015 02 03 N Status No replacement named L. Sinclair, NA 2003 02 28 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.14, 3.15, 4 deleted 1992 09 17 NB00E10043064092 Revised, renumbered and updated Y. Chen 19

2、91 06 21 NB00I10043054102 Released D. Henrickson, L. Moriarty Page 1 of 2 Copyright 2015, Ford Global Technologies, Inc. ADHESIVE, MOISTURE CURE URETHANE, WARM APPLIED WSB-M2G361-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a one component moisture cure uret

3、hane adhesive. 2. APPLICATION This specification was originally released for materials used to bond urethane armrest pads to ABS, carpet to vinyl and ABS. Materials meeting this specification do not guarantee that the adhesive will function for all potential applications on a vehicle. The specific d

4、esign condition, including high temperature performance, should be evaluated by a plant trial or laboratory simulation prior to release of the material. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requ

5、irements For Production Materials (WSS-M99P1111-A). 3.4 COLOR Yellow to Amber 3.5 SOLIDS, min 99 % (ASTM D 2834, except heat 4 h at 177 +/- 3 C in a mechanical convection oven) 3.6 ASH (based on solids weight), max 4 % (ASTM D 482) Test Method: Place crucible containing the solids residue in a cool

6、muffle furnace. Slowly heat to and maintain at 760 +/- 30 C for 1 h. Cool in a desiccator and weigh. 3.7 WEIGHT PER VOLUME (ASTM D 816) The weight tolerance of any one supplier shall be 0.060 kg/L based on the recorded weight of his originally approved production sample. ENGINEERING MATERIAL SPECIFI

7、CATION WSB-M2G361-A Page 2 of 2 Copyright 2015, Ford Global Technologies, Inc. 3.8 FOGGING, min (SAE J1756, 3h at 100 C heating, 21 C cooling plate, post test conditioning 1 h and 16 h) Fog Number, min 60 Formation of clear film, droplets or crystals is cause for rejection. 3.9 BOND STRENGTH, min (F

8、LTM BN 113-01) 3.9.1 Original 701 N/m 3.9.2 Cycled 526 N/m 3.9.3 Wet 526 N/m 3.9.4 Steamed 526 N/m 3.10 ODOR, max Rating 2 (SAE J1351) 3.11 QUALITY The material shall be smooth homogeneous mixture, free from foreign materials and properties detrimental to normal production use. 3.12 STORAGE STABILIT

9、Y The adhesive shall be stored in its original, unopened containers at temperatures of 25 +/- 2 C, away from all sources of heat, sunlight or moisture. Storage times greater than 90 days shall be avoided. A rapid increase in material viscosity occurs when this time limit is exceeded, particularly wh

10、en the product is exposed to moisture. 3.13 FUNCTIONAL APPROVAL Materials being evaluated for initial approval to this specification shall be subjected to a production trial to demonstrate processability as well as functional performance. Functional trial results should be available to Design and Ma

11、terial Engineering prior to material approval and release. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 VISCOSITY See suppliers acceptable recommendations dependent on assembly plant manufacturing requirements.