FORD FLTM BO 124-04-2001 DETERMINATION OF MOISTURE IN POLYVINYL BUTYRAL BY GRAVIMETRIC DESICCATION (Replaces FLTM BO 024-04)《重力脱水法测定聚乙烯醇缩丁醛中的水分含量 替代FLTM BO 024-04［替代 FORD FLTM BO 0.pdf

《FORD FLTM BO 124-04-2001 DETERMINATION OF MOISTURE IN POLYVINYL BUTYRAL BY GRAVIMETRIC DESICCATION (Replaces FLTM BO 024-04)《重力脱水法测定聚乙烯醇缩丁醛中的水分含量 替代FLTM BO 024-04［替代 FORD FLTM BO 0.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BO 124-04-2001 DETERMINATION OF MOISTURE IN POLYVINYL BUTYRAL BY GRAVIMETRIC DESICCATION (Replaces FLTM BO 024-04)《重力脱水法测定聚乙烯醇缩丁醛中的水分含量 替代FLTM BO 024-04［替代 FORD FLTM BO 0.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BO 124-04 Date Action Revisions 2001 03 28 Revised Editorial no technical change A. Cockman 1994 12 20 Printed copies are uncontrolled Page 1 of 3 Copyright 2001, Ford Global Technologies, Inc. DETERMINATION OF MOISTURE IN POLYVINYL BUTYRAL BY GRAVIMETRIC DESICCATION App

2、lication This procedure describes a method for determining the moisture content of polyvinyl butyral used in laminated glass. Apparatus Required Weighing Bottle A weighing bottle with a 40 mm I.D. and 80 mm high with a Ts 40/12 ground glass stopper or equivalent. Sample Stand Aluminum stand as shown

3、 in Figure 1. Desiccator Desiccator of sufficient size to hold the weighing bottle, sample and stand. Chemicals Required Phosphorous Pentoxide Anhydrous phosphorous pentoxide, 225 - 450 g. (12 mm deep in desiccator.) Conditioning and Test Conditions All test values indicated herein are based on mate

4、rial conditioned in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. FORD LABORATORY TEST METHOD BO 124-04 Page 2 of 3 Copyright 2001, Ford Global Technologies, Inc. Procedu

5、re 1. Tare weighing bottle, stopper and stand. (W1) 2. Cut sample 25 x 150 mm and place on aluminum stand in the weighing bottle. Replace stopper. Polyvinyl butyral changes moisture content rapidly, depending on relative humidity of surrounding air. 3. Weigh the sample, bottle, and stand to the near

6、est tenth milligram. (W2) 4. Open desiccator and examine surface of phosphorous pentoxide desiccant. If this surface is not dry and powdery, scrape off crust to ensure fresh, dry, powdery desiccating surface. 5. Place weighing bottle in desiccator and open bottle. Remove stand with sample and place

7、next to weighing bottle. Tightly seal desiccator and allow sample to remain for 16 hours (for .7 - .8 mm thick vinyl) at atmospheric pressure. 6. Open desiccator and rapidly replace sample and stand in weighing bottle. Seal weighing bottle and transfer to storage desiccator. 7. Weigh sample bottle o

8、n analytical balance to nearest tenth milligram and calculate moisture content. (W3) W1 = tare weight of bottle plus stand W2 = weight of bottle, stand and sample before desiccation W3 = weight of bottle, stand and sample after desiccation Moisture content = W 2 W 3 x 100 W2 W1 Note: 1. All handling

9、 of vinyl, bottles, stands should be done with clean, white gloves to prevent fingerprints from affecting data. 2. All desiccators use phosphorous pentoxide as desiccant and before each usage should be carefully examined to ensure a dry, fresh, powdery desiccating surface. 3. Moisture content can be

10、 determined after 8 hours desiccation with subsequent redesiccation and reweighing to constant weight. Experience has shown that almost all samples will dry to constant weight before 16 hours desiccation. Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities. FORD LABORATORY TEST METHOD BO 124-04 Page 3 of 3 Copyright 2001, Ford Global Technologies, Inc. DETERMINATION OF MOISTURE IN POLYVINYL BUTYRAL BY GRAVIMETRIC DESICCATION Figure 1