FORD FLTM BI 120-15-2001 DETERMINATION OF LOSS OF SOLIDS DUE TO CURING OF ELECTROCOAT PRIMERS (Replaces FLTM BI 020-15)《电涂底漆的固化过程固体物损失的测定 替代FLTM BI 020-15［替代 FORD FLTM BI 020-15］》.pdf

《FORD FLTM BI 120-15-2001 DETERMINATION OF LOSS OF SOLIDS DUE TO CURING OF ELECTROCOAT PRIMERS (Replaces FLTM BI 020-15)《电涂底漆的固化过程固体物损失的测定 替代FLTM BI 020-15［替代 FORD FLTM BI 020-15］》.pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BI 120-15-2001 DETERMINATION OF LOSS OF SOLIDS DUE TO CURING OF ELECTROCOAT PRIMERS (Replaces FLTM BI 020-15)《电涂底漆的固化过程固体物损失的测定 替代FLTM BI 020-15［替代 FORD FLTM BI 020-15］》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 FORD LABORATORY TEST METHOD BI 120-15 Date Action Revisions 2001 03 19 Revised Editorial no technical change A. Cockman 1989 08 07 Printed copies are uncontrolled Page 1 of 2 Copyright 2001, Ford Global Technologies, Inc. DETERMINATION OF LOSS OF SOLIDS DUE TO CURING OF ELECTROCOAT PRIMERS Applicat

2、ion This test method is applicable to anodic and cathodic electrocoat primers to determine the percentage of solids lost during the bake cycle and during the recommended peak metal temperature cure. Apparatus and Materials Required Test Panels Parker Bonderite 40 CRS panels - 75 x 230 mm. Length of

3、panels may be shortened to permit hanging on the analytical balance. Source: Parker Division, O.M.I. Corp. 322 Main Street Morenci, Michigan 48256 U.S.A. Analytical Balance Must have precision of +/- 0.10 mg. Oven Mechanical convection oven capable of reaching peak metal temperatures in less than 10

4、 minutes. Film Thickness Gage Permascope Type ES, or equivalent. Source: Twin Cities Testing Corp. 107-111 Goundry Street North Tonawanda, NY 14120 U.S.A. Distilled or Deionized Water Less than 10 ppm total dissolved solids (per ASTM D 1888). Procedure 1. Prebake three (3) panels for five (5) minute

5、s at 120 +/- 1 C. 2. Cool the panels to approximately 23 +/- 2 C and weigh to the nearest 0.1 mg. (A = weight of panel.) FORD LABORATORY TEST METHOD BI 120-15 Page 2 of 2 Copyright 2001, Ford Global Technologies, Inc. 3. Electrocoat the panels per FLTM BI 120-01 to the film thickness as required by

6、the relevant Material Specification. Note: The electrocoat bath must be under agitation for at least 48 hours prior to electrocoating of the panels. 4. Rinse the panels with distilled or deionized water after coating and allow to drain for 15 to 20 minutes. 5. Place the panels in the oven for three

7、(3) hours at 105 +/- 1 C. 6. Cool the panels to approximately 23 +/- 2 C and weigh to the nearest 0.1 mg. (B = weight of panel and electrocoat film after three (3) hours at 105 C.) 7. Cure the panels in the oven to 10 minutes at the recommended (*) peak metal temperature +/- 1 C. 8. Cool the panels

8、to approximately 23 +/- 2 C and weigh to the nearest 0.1 mg. (C = weight of panel and electrocoat film after 10 minutes at the recommended (*) peak metal temperature). Evaluation Calculate the percent loss of solids using the following formula: P = B - C x 100 B - A where: P = Percent loss of solids

9、 A = Weight of panel B = Weight of panel and electrocoat film after 3 h at 105 C. C = Weight of panel and electrocoat film after 10 minutes at peak temp. This method determines the percent weight of electrocoat solids that will be lost between 105 C and the recommended peak metal temperature. * As s

10、tated in the applicable Engineering Materials Specification, or per the recommendation of the paint supplier if the Engineering Materials Specification does not make reference to the peak metal temperature. Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is responsible for determining proper use and handling in its facilities.