FORD ESF-M4D325-A-2006 NYLON (TYPE 6) COPOLYMER 20% GLASS - MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《20%玻璃增强的尼龙（型号6）共聚物成型料 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ESF-M4D325-A-2006 NYLON (TYPE 6) COPOLYMER 20% GLASS - MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《20%玻璃增强的尼龙（型号6）共聚物成型料 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESF-M4D325-A-2006 NYLON (TYPE 6) COPOLYMER 20% GLASS - MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《20%玻璃增强的尼龙（型号6）共聚物成型料 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 04 N-STATUS Replaced by WSS-M4D665-A5 A. Reaume/M. Masserant 2005 01 28 Revised Inserted 3.0; Deleted 3.4, 3.5 & 4 1970 10 22 Released (Was XF-M4DX92) F6Z-435 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LL

2、C Page 1 of 2 NYLON (TYPE 6) COPOLYMER, 20% GLASS - MOLDING COMPOUND ESF-M4D325-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a heat stabilized type 6 nylon blended with another polymer to provide a heat sealable, decorable, molded plastic part. This material

3、 contains approximately 20% glass fiber. 2. APPLICATION This specification was released originally for material used where decorability and/or heat sealability are required such as the horn projector. NOTICE: This material absorbs and retains moisture. Part design and tolerances must accommodate cha

4、nges in part dimensions and physical properties due to moisture absorption or loss in the service/assembly environment. Information on this material with respect to moisture should be obtained from the responsible PEO Materials Engineering Department. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PR

5、ODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 CERTIFICATION To be run on a continuing basis. This could be on a lot or daily basis. 3.1.1 Conditioning Specimens are to be dry as molded. They

6、are not to be intentionally exposed to any moisture. If specimens will be exposed to air for more than 5 min after molding and before testing, they shall be kept in a sealed, air and moisture proof glass container. They shall be tested within 5 min after removal from the containers. Maximum moisture

7、 content 0.3%. 3.1.2 Melting Point 210 - 225 C (ASTM D 789) 3.1.3 Specific Gravity 1.20 - 1.30 (ASTM D 792) 3.1.4 Moisture Content, max 0.3% (ASTM D 789) 3.1.5 Tensile Strength, min 13,000 psi (90 MPa) (ASTM D 638, Speed “C“) ENGINEERING MATERIAL SPECIFICATIONESF-M4D325-A Printed copies are uncontro

8、lled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.2 MOLDED TEST SPECIMEN To be run at intervals established by Quality Control to confirm above (para. 3.1) values are representative, and for initial approval. 3.2.1 Impact Strength, Izod, min 0.8 ft lb/in (43 J/m) (ASTM D 256, notched)

9、 3.2.2 Deflection Temperature, min (ASTM D 648, as received, 1/4 in (6.4 mm) specimen width) At 66 psi (455 kPa) 199 C At 264 psi (1820 kPa) 177 C 3.2.3 Flexural Modulus, min 900,000 psi (6.2 GPa) (ASTM D 790, 1/4 x 1/2 in (6.4 x 12.7 mm) specimen) 3.3 MOLDED PART 3.3.1 Parts molded of this material shall be free from visible porosity and voids. 3.3.2 Melting Point 210 - 225 C (ASTM D 789) 3.3.3 Ductility The performance test method and part requirement shall be specified on the engineering drawing.