《FORD ESB-M2P68-A-2008 PAINT PERFORMANCE BLACK OUT - EXTERIOR - SINGLE COAT TO BE USED WITH FORD WSS-M99P1111-A 《汽车外部用单层遮蔽油漆的质量 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M2P68-A-2008 PAINT PERFORMANCE BLACK OUT - EXTERIOR - SINGLE COAT TO BE USED WITH FORD WSS-M99P1111-A 《汽车外部用单层遮蔽油漆的质量 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Ver. 4 2008 09 10 N-STATUS No Replacement Named G. Weber, FNA 2003 08 11 Revised Para 3.0 inserted; Para 3.4, 3.5, 3.6, 3.7, 3.8, 4, deleted 1965 02 05 AVI #703 Released Printed copies are uncontrolled Copyright 2008, Ford Global Technologies

2、, Inc. Page 1 of 2 PAINT PERFORMACE, BLACK OUT EXTERIOR SINGLE COAT ESB-M2P68-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines the performance requirements for exterior surfaces which are painted black to reduce visibility. 2. APPLICATION This specification was released originally

3、 for a finish specified on exterior surfaces to minimize visibility, to mask surface irregularities or to cover non-uniform surfaces. It is generally used behind grilles, under fenders, wheelhouse openings and similar areas. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material

4、 suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 SYSTEM COMPONENTS 3.1.1 Substrate ESB-M2P68-A Zinc Phosphate Coated Steel, ESB-M3P1 3.1.2 Color Coat Visual covering coat of black enamel. 3.2 FILM PROPERTIES 3.2.1 Color B

5、lack 3.2.2 Gloss Shall meet gloss requirements shown on drawing, gloss suffix to color code or other applicable Engineering Release. ENGINEERING MATERIAL SPECIFICATION ESB-M2P68-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 2 of 2 3.2.3 Hardness Shall be suffi

6、ciently hard to withstand normal handling operations. 3.2.4 Adhesion (FLTM BI 106-01) No flaking or chipping from substrate as defined in para 3.1.1. 3.2.5 Dry Film Thickness, min 8 m 3.3 SALT SPRAY, min 24 h (FLTM BI 103-01) Unless otherwise specified on engineering drawing, Trim and Sealer Manual, or other engineering authority. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 COLOR COAT Black, 1724 Material ESB-M2J104 ESB-M2J200 ESB-M6J72 ESB-M6J66 ESB-M2J53 ESB-M2J54