FORD ESB-M2F67-B-2003 FABRIC VINYL COATED TO BE USED WITH FORD WSS-M99P1111-A 《乙烯树脂涂层织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ESB-M2F67-B-2003 FABRIC VINYL COATED TO BE USED WITH FORD WSS-M99P1111-A 《乙烯树脂涂层织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M2F67-B-2003 FABRIC VINYL COATED TO BE USED WITH FORD WSS-M99P1111-A 《乙烯树脂涂层织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 08 26 Revised Para 3.0 inserted; Para 3.1, 3.30, 4 deleted 1979 10 12 Activated Metricated and Retyped CAHI-RD572066-255 1971 08 20 Released 4B1-302-16 Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1

2、of 5 FABRIC, VINYL COATED ESB-M2F67-B 1. SCOPE The material defined by this specification is vinyl copolymer or vinyl chloride, coated knit fabric of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used in applications specified on Enginee

3、ring Chart 534. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center

4、 master sample, or shall be as specified on the engineering drawing. 3.3 BACKING ESB-M9H1-A 3.4 WEIGHT, min (FLTM BN 106-01) Coating 9.5 oz/yd2 (0.322 kg/m2) Total 14.0 oz/yd2(0.475 kg/m2) 3.5 WIDTH Specified on Chart 534 3.6 TENSILE STRENGTH, 10% Tolerance (ASTM D 1682, Grab Method) Warp 100 lb (44

5、5 N) Fill 65 lb (289 N) 3.7 STRETCH AND SET (SAE J 855) Stretch Set Warp 1-5% 0-2% Fill 7-13% 0-4% ENGINEERING MATERIAL SPECIFICATION ESB-M2F67-BPrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 5 3.8 STIFFNESS (ASTM D 747, direct reading at 60 angle with 0.1 i

6、n-lb (0.01 N-m) load) Non-metallic Metallic Warp 15 18 Fill 13 13 The test specimen shall be 2 in (50 mm) x 1 in (25 mm) with 1 in (25 mm) of the 2 in (50 mm) dimension clamped in jaw, 1/2 in (13 mm) span from clamp to bending plate, fabric side up. 3.9 TEAR STRENGTH (trapezoid), min (ASTM D 5733) W

7、arp and Fill 3.5 lb (15.6 N) 3.10 SHRINKAGE, max (FLTM BN 105-01) Warp 3.0% Fill 1.5% 3.11 ADHESION OF COATING 4 lb/in (701 N/m) width TO BACKING FABRIC, min (ASTM D 413, Machine Method; the coating of the test specimen shall be separated from the backing fabric, by hand and without the use of solve

8、nts, prior to pulling. The movable jaw of the testing machine shall move at the rate of 12 in (305 mm)/min.) 3.12 SEAM STRENGTH, min (FLTM BN 119-01) Warp 85 lb (378 N) Fill 50 lb (222 N) Note: The above values apply to fabric breaks only. Thread breaks which exceed the above requirements shall be a

9、ccepted. However, results below the above requirements which are due to thread breaks shall be disregarded and the tests repeated. 3.13 COLD FLEXIBILITY No failure (FLTM BN 102-01, -34 C) 3.14 CROCKING Rating 5 (FLTM BN 107-01) 3.15 MIGRATION STAINING (FLTM BN 103-01) The coated surfaces shall show

10、no evidence of injurious exudation, adhesion (tackiness), separation, color transfer, or flattening of embossing, when placed face to face with itself, or materials of the 2F4-9-62-67 etc., series. ENGINEERING MATERIAL SPECIFICATION ESB-M2F67-BPrinted copies are uncontrolled Copyright 2003, Ford Glo

11、bal Technologies, Inc. Page 3 of 5 3.16 H2S STAINING Rating 5 (FLTM AN 102-01) Production materials shall exhibit H2S staining qualities equal to or better than the master sample (as approved for production and filed by the Textile Engineering Section, BEPE Materials Engineering Department.) 3.17 FA

12、DE (SAE J 1885, 120 SFH) The vinyl coating shall not stain, exhibit color tone change or change in hue, in accordance with rating 5 of the AATCC Gray Scale for Measuring Change in Color. Production materials shall exhibit light fastness qualities equal to or better than the master sample (as approve

13、d for production and filed by the Textile Engineering Section, BEPE Materials Engineering Department. 3.18 AGING When the specimens used for the resistance to fade test (Para 3.17) are folded 180 upon themselves (coating side out), the coating shall not crack. 3.19 ABRASION (FLTM BN 108-02) After th

14、e wear test, the materials color and pattern in the wear area shall be compatible in appearance with the adjacent unabraded areas of the wear test specimen. Printed, metallic, and other vinyl surface coatings shall withstand 500 cycles, using CS #10 wheels, and 1000 g load. The color of the base vin

15、yl coating shall be compatible with the metallic surface and shall in no instance be of a lighter color than the metallic surface. 3.20 SOILING, max 15% (FLTM BN 112-01) 3.21 FOGGING (SAE J 1756) Light Transmission Reading 70 - 100 Note: Exudations resulting in running liquid, heavy beads, and/or dr

16、oplets, or a continuous film deposit on the surface of the glass plate are not desired and shall be reported along with the numerical results but shall not be cause for rejection. 3.22 FLEXING (FLTM BN 102-02, 1000 cycles) The vinyl coating shall show no evidence of crazing (milkiness), lifting (pee

17、ling), or cracking when examined after the above tests. The resistance to flexing of approved production material shall be equal to or better than that exhibited by the master sample (as approved for production and filed by the Textile Engineering Section.) ENGINEERING MATERIAL SPECIFICATION ESB-M2F

18、67-BPrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 4 of 5 3.23 ODOR The coating must not have a disagreeable odor. Materials which are considered to have a disagreeable odor according to Quality Control, or the Textile Engineering Section, will be subject to reje

19、ction. 3.24 SAMPLING The acceptance or rejection of these materials shall be based on samples taken from 20% of the rolls in each shipment, except that, in shipments of 1 - 3 rolls, each roll shall be tested; in shipments of 4 - 9 rolls, 3 rolls shall be tested; in shipments of 10 - 19 rolls, 4 roll

20、s shall be tested. 3.25 FLAMMABILITY REQUIREMENT In order to comply with Federal Motor Vehicle Safety Standard No. 302, the materials, portions of components, and composites shall not burn, or transmit a flame across its surface, at a rate of more than 4 in (101 mm) per min. To demonstrate complianc

21、e, the sample size and method of testing shall be in accordance with FLTM BN 024-02. 3.26 PERFORMANCE - ENVIRONMENTAL AGING REQUIREMENT All materials, portions of components, and composites defined by this specification that have not been treated, modified or reformulated and exceed a max burn rate

22、of 3.0 in (76 mm) per min as specified by the Flammability Lot Sampling Plan of FLTM BN 024-02, must be evaluated for permanency of the materials flame retardant properties per ESB-M25P3-A according to the accelerated environmental aging requirements applicable to the basic material category of this

23、 particular specification. Any material, portions of components, and composites defined by this specification that have been treated, modified or reformulated to conform to Flammability Lot Sampling Plan of FLTM BN 024-02, regardless of max burn rate, must be evaluated for both permanency of materia

24、ls flame retardant properties and changes in mechanical, chemical and physical properties per ESB-M25P3-A applicable to the basic materials category of this particular specification. 3.27 FLAMMABILITY TEST PROGRAM Materials, portions of components, and composites governed by this specification must

25、also comply with the requirements of ES-D3AB-11014-AA. 3.28 DEFECTS Any piece, that averages more than one defect per 12 yd (11 m) shall be considered seconds and unless otherwise agreed upon, shall be subject to rejection for full credit or replacement at our option. ENGINEERING MATERIAL SPECIFICAT

26、ION ESB-M2F67-BPrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 5 of 5 3.29 BONDING ASSEMBLY REQUIREMENTS In addition to the requirements listed above, bonding grade materials shall meet the following added requirements. 3.29.1 Material Acceptability The criterion

27、for material acceptability shall be the assemblys job performance. This means that the materials composition and formulation must form a satisfactory bond to itself as an overlay and/or as an underlay when bonded separately and with the remaining approved components in the assembly and when bonded u

28、nder approved production conditions. 3.29.2 Bond Strength These requirements will depend on the assemblys application and design and are controlled by the specifications for the foundation padding materials used in the assembly when tested as described in FLTM BN 113-01 and BN 113-02. 5. GENERAL INF

29、ORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 WEATHER EXPOSURE TEST At any time during an 8 month Florida weather exposure tests, this material shall not fade or crack any more than the master sample approved for production.