FORD ESB-M1C111-B-2003 GREASE LITHIUM SOAP BASE - ZINC OXIDE FILLER - 15% PTFE ADDITIVE - NLGI #1 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI 15%聚四氟乙烯（PTFE）添加剂用氧化锌填料的锂皂基润滑脂》.pdf

《FORD ESB-M1C111-B-2003 GREASE LITHIUM SOAP BASE - ZINC OXIDE FILLER - 15% PTFE ADDITIVE - NLGI #1 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI 15%聚四氟乙烯（PTFE）添加剂用氧化锌填料的锂皂基润滑脂》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M1C111-B-2003 GREASE LITHIUM SOAP BASE - ZINC OXIDE FILLER - 15% PTFE ADDITIVE - NLGI #1 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI 15%聚四氟乙烯（PTFE）添加剂用氧化锌填料的锂皂基润滑脂》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 10 24 Revised Para 3.0 inserted; paras 3.1, 3.7, 3.9 and 4 deleted 1985 10 09 CAR1-RD532208; Was ESB-M1C111-A; Revised to WW format, Retyped 1963 12 27 Released AS1 #813 Printed copies are uncontrolled Copyright 2003, Ford Global Technolo

2、gies, Inc. Page 1 of 2 GREASE, LITHIUM SOAP BASE - ZINC OXIDE ESB-M1C111-B FILLER - 15% PTFE ADDITIVE - NLGI #1 1. SCOPE The material defined by this specification is a teflon filled grease composed of lithium soap and mineral oil. 2. APPLICATION This specification was released originally for grease

3、 used for lubricating seat track transmissions and related body hardware applications. NOTICE: This grease shall be formulated so that it will not stain or soften painted exterior or interior automotive finishes when evaluated according to FLTM BJ 126-01. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FO

4、R PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION 3.2.1 Lithium Soap 6. 0 - 8.0% (ASTM D 128) 3.2.2 Teflon, min 15.0% 3.2.3 Filler, as Zinc Oxide 3.0 - 5.0% (ASTM D 128) 3.2.4 Min

5、eral Oil Remainder (ASTM D 128) 3.3 PENETRATION 310 - 340 (ASTM D 217, worked 60 strokes) 3.4 DROPPING POINT, min 175 C (ASTM D 566 or D 2265) 3.5 WATER RESISTANCE 3.5.1 The material, when applied to metal strips and solvent evaporated, shall withstand 168 h at 38 +/- 1 C in a 98 +/- 2% relative hum

6、idity atmosphere without breaking. 3.5.2 The material, when applied to metal strips and solvent evaporated, shall withstand 16 h immersion in a bath of running cold water without breaking per ASTM D 1264. ENGINEERING MATERIAL SPECIFICATIONESB-M1C111-BPrinted copies are uncontrolled Copyright 2003, F

7、ord Global Technologies, Inc. Page 2 of 2 3.6 LUBRICANT PAINT STAINING No stain or (FLTM BJ 126-01) softening 3.8 QUALITY Material shall be a smooth homogeneous product free from abrasive particles, it shall be consistent in color and texture, and free from objectionable odors during normal storage.

8、 It shall be suitable for the intended application. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 MINERAL OIL PROPERTIES 5.1.1 Viscosity at 40 C 16.7 - 18.7 mm2/s (ASTM D 445) 5.2 The following parameters are recommended for the Quality Certification Requirements: 5.2.1 Infrared Analysis, para 3.7. 5.2.2 Penetration, para 3.3. 5.2.3 Dropping Point, para 3.4.