EN 10111-2008 en Continuously hot rolled low carbon steel sheet and strip for cold forming - Technical delivery conditions《冷成形用连续热轧低碳钢薄板材及带材 交货技术条件》.pdf

《EN 10111-2008 en Continuously hot rolled low carbon steel sheet and strip for cold forming - Technical delivery conditions《冷成形用连续热轧低碳钢薄板材及带材 交货技术条件》.pdf》由会员分享，可在线阅读，更多相关《EN 10111-2008 en Continuously hot rolled low carbon steel sheet and strip for cold forming - Technical delivery conditions《冷成形用连续热轧低碳钢薄板材及带材 交货技术条件》.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARDBS EN 10111:2008Continuously hot rolled low carbon steel sheet and strip for cold forming Technical delivery conditionsICS 77.140.50g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55g55g40g39

2、g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58BS EN 10111:2008This British Standard was published under the authority of the Standards Policy and Strategy Committee on 30 May 2008 BSI 2008ISBN 978 0 580 54793 5National forewordThis British Standard is the UK implementation of EN 10111:2008. It sup

3、ersedes BS EN 10111:1998 which is withdrawn.The UK participation in its preparation was entrusted to Technical Committee ISE/10, Flat rolled steels products.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to include

4、all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunity from legal obligations.Amendments/corrigenda issued since publicationDate CommentsEUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 10111April 2008I

5、CS 77.140.50 Supersedes EN 10111:1998 English VersionContinuously hot rolled low carbon steel sheet and strip for coldforming - Technical delivery conditionsTles et bandes en acier doux lamines chaud en continupour formage froid - Conditions techniques de livraisonKontinuierlich warmgewalztes Band u

6、nd Blech aus weichenSthlen zum Kaltumformen - Technische LieferbindungenThis European Standard was approved by CEN on 29 February 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national st

7、andard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other

8、 language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Fin

9、land,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMIT

10、EE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2008 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 10111:2008: EEN 10111:2008 (E) 2 Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Terms and definiti

11、ons .4 4 Classification and designation.5 4.1 Classification5 4.2 Designation 5 5 Requirements.5 5.1 Steelmaking and manufacturing processes .5 5.2 Deoxidation 5 5.3 Chemical composition 5 5.4 Delivery conditions5 5.5 Mechanical properties.6 5.6 Surface characteristics .6 5.7 Suitability for surface

12、 coating 6 5.8 Weldability7 5.9 Tolerances on dimensions and shape 7 6 Tests9 6.1 General9 6.2 Inspection units .9 6.3 Number of tests9 6.4 Sampling.9 6.5 Test methods10 6.6 Retests 10 6.7 Inspection document.10 7 Marking .10 8 Packing .11 9 Storage and transportation.11 10 Disputes11 11 Information

13、 to be provided by the purchaser at the time of enquiry and order11 11.1 Mandatory information11 11.2 Options .11 Bibliography 12 BS EN 10111:2008EN 10111:2008 (E) 3 Foreword This document (EN 10111:2008) has been prepared by Technical Committee ECISS/TC 13 “Flat products for cold working - Qualitie

14、s, dimensions, tolerances and specific tests”, the secretariat of which is held by NBN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by October 2008, and conflicting national standards shall be wi

15、thdrawn at the latest by October 2008. This document supersedes EN 10111:1998. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. Accordi

16、ng to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,

17、 Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 10111:2008EN 10111:2008 (E) 4 1 Scope This European Standard specifies the grades of continuously hot rolled low carbon steel sheet and strip (i

18、n coils) for cold forming. Depending on its actual width, strip is classified as: hot rolled wide strip if its width is greater than or equal to 600 mm; hot rolled slit wide strip if its width is less than 600 mm. For each grade, it specifies the chemical composition and the mechanical properties. T

19、his European Standard is applicable to products of thickness not less than 1,0 mm and not exceeding 11 mm. This European Standard is not applicable to products covered by other standards, such as: hot rolled products of non-alloy structural steels for general use (see EN 10025 all parts); steel shee

20、t for pressure purposes (see EN 10028 all parts); steel sheet for welded gas cylinders (see EN 10120); quenched and tempered steels (see EN 10083-1 and EN 10083-2). 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references,

21、 only the edition cited applies. For undated references the latest edition of the referenced document (including any amendments) applies. EN 10002-1, Metallic materials Tensile testing Part 1: Method of test at ambient temperature EN 10021, General technical delivery requirements for steel products

22、EN 10027-1, Designation systems for steels - Part 1: Steel names EN 10027-2, Designation systems for steels Part 2: Numerical system EN 10051, Continuously hot-rolled uncoated plate, sheet and strip of non-alloy and alloy steels - Tolerances on dimensions and shape EN 10079, Definition of steel prod

23、ucts EN 10204, Metallic products Types of inspection documents EN ISO 14284, Steel and iron - Sampling and preparation of samples for the determination of chemical composition (ISO 14284:1996) 3 Terms and definitions For the purposes of this European Standard, the terms and definitions of hot rolled

24、 flat products are those given in EN 10079. BS EN 10111:2008EN 10111:2008 (E) 5 4 Classification and designation 4.1 Classification The choice of steel grade and product type is left to the purchaser. For this choice, the purchaser may be advised by the manufacturer, but without any liability on the

25、 part of the latter, unless agreed at the time of enquiry and order. Hot rolled products are classified into four grades DD11, DD12, DD13 and DD14 defined by chemical composition, mechanical and forming characteristics (see Table 1). 4.2 Designation 4.2.1 The steel names are in compliance with EN 10

26、027-1; the steel numbers, with EN 10027-2. 4.2.2 Products conforming to this European Standard shall be designated, in order, in the following way: a) product designation (e.g. “strip”, “sheet” or “slit strip cut longitudinally”) in line with EN 10079; b) number of this European Standard (EN 10111);

27、 c) symbolic or numerical designation of the steel (see Table 1). EXAMPLE Strip EN 10111 DD13 or Strip EN 10111 1.0335 5 Requirements 5.1 Steelmaking and manufacturing processes Unless otherwise agreed at the time of enquiry and order, the steelmaking and manufacturing processes are left to the disc

28、retion of the manufacturer. The purchaser shall be informed of these processes if he specifies it. 5.2 Deoxidation For grade DD11 the method of deoxidation shall be at the manufacturers discretion. Grades DD12, DD13 and DD14 shall be fully killed. 5.3 Chemical composition Table 1 gives the permissib

29、le chemical composition limits in the cast. 5.4 Delivery conditions 5.4.1 The products shall usually be delivered with their surface as rolled. By agreement at the time of enquiry and order, the products may be delivered with descaled surface. When they are delivered as rolled, they are covered with

30、 a thin layer of scale of variable coloration. The products may be supplied with a light skin-pass, either at the manufacturers discretion or by agreement at the time of enquiry and order. BS EN 10111:2008EN 10111:2008 (E) 6 5.4.2 The descaled products are usually delivered oiled. In this case, both

31、 surfaces are preserved by a layer of neutral non-drying oil, free of impurities, and uniformly spread in such a way that under normal conditions of packaging, transportation, handling and storage the products will show no corrosion for up to three months from the date on which the products are made

32、 available. The date of availability shall be notified to the purchaser with reasonable prior notice compatible with the validity of corrosion resistance. The layer of oil shall be capable of being removed by alkaline solutions or usual solvents. The choice of protective oils may be subject to speci

33、al agreement at the time of enquiry and order. If the conditions of transportation or storage are such that special protection against corrosion is required, the purchaser shall inform the manufacturer at the time of enquiry and order. If the purchaser does not require the surfaces to be oiled, this

34、 shall be clearly indicated at the time of enquiry and order. NOTE If the order is for unoiled products, the manufacturer is not responsible for the risk of corrosion. The purchaser is also advised that there is a greater risk of the appearance of light scratches during handling, transportation and

35、putting into application. 5.4.3 Descaled products may be supplied with trimmed edges upon agreement at the time of enquiry and order (designation GK following EN 10051). 5.5 Mechanical properties Table 1 gives the basic mechanical properties valid for the four grades. They correspond to the increasi

36、ng formability in the order DD11 to DD14. The characteristics indicated in Table 1 are valid for the period specified in the same Table 1, from the date on which the products are made available. The date of availability shall be notified to the purchaser with reasonable prior notice compatible with

37、the validity of the mechanical properties. Subject to special agreement, the products may be supplied with special suitability for the production of a specific part. In this case, a maximum rejection percentage may be set by mutual agreement and acceptance on the basis of mechanical properties does

38、not apply. 5.6 Surface characteristics The sheets shall be free of slivers, blow holes, seams, cracks or scratches which would adversely affect their use. Pores, small pits, small marks, small scratches, kinks from pay-off reels and a slight coloration are permitted. The defects shall not be of such

39、 an extent that they might run the risk of causing failure or damage to tooling or welding difficulties when in use. The surface quality of the unwound coil is assessed as for sheets. However, the percentage of surface defects is generally greater than when supplied in sheets. The maximum percentage

40、 of permissible rejections shall be fixed by special agreement at the time of enquiry and order. 5.7 Suitability for surface coating The products may be intended for metallic coating by the hot dipping or electrodeposition and/or organic or other coatings. When such a coating is required, it shall b

41、e specified at the time of enquiry and order. BS EN 10111:2008EN 10111:2008 (E) 7 5.8 Weldability The products are suitable for standard welding processes. However, the welding process and possible specific requirements of the resulting welded component should be specified at the time of enquiry and

42、 order, e.g. gas welding, structural safety requirements. For non-descaled products, the welding process shall take into account the presence of a layer of scale. 5.9 Tolerances on dimensions and shape The tolerances on dimensions and shape are given in EN 10051 BS EN 10111:2008EN 10111:2008 (E) 8 T

43、able 1 Characteristics aMechanical properties cLadle analysis chemical composition b ReLdMinimum elongation after fracture Validity Rm L0= 80 mm L0 = 5,650SSteel name Steel number Method of deoxidation C max.% Mn max.% P max.% S max.% 1,0 mm e e 2 mmMPa 2 mm e e 11 mm MPa max.MPa 1,0 mm e e 1,5 mm %

44、 1,5 mm ee 2 mm% 2 mm ee 3 mm% 3 mm e e 11 mm % months DD11 DD12 DD13 DD14 1.0332 1.0398 1.0335 1.0389 At the discretion of the manufacturer Fully killed Fully killed Fully killed 0,120,10 0,08 0,08 0,600,45 0,40 0,35 0,0450,0350,0300,0250,0450,0350,0300,025170 to 360170 to 340 170 to 330 170 to 310

45、 170 to 340 170 to 320 170 to 310 170 to 290 440 420 400 380 22 24 27 30 23 25 28 31 24 26 29 32 28 30 33 36 6 6 6 NOTE 1 MPa = 1 N/mm2. aThe mechanical characteristics relate only to hot rolled non-descaled or chemically descaled and oiled products, skin-passed or not. bUnless otherwise agreed at t

46、he time of enquiry and order, nitrogen-fixing elements such as titanium and boron may be added at the discretion of the manufacturer. cAs long as the width of the product permits, the test pieces for the tensile tests shall be taken transverse to the direction of rolling. dRp0,2shall be used instead

47、 of ReLif the product does not exhibit any yield phenomenon. eIt is recommended that products in grade DD11 should be formed within 6 weeks from the time of their availability.BS EN 10111:2008EN 10111:2008 (E) 9 6 Tests 6.1 General 6.1.1 The purchaser shall specify at the time of enquiry and order h

48、is requirements for: type of inspection in accordance with EN 10021; type of inspection document for the products in accordance with EN 10204. 6.1.2 Specific inspection and testing shall be carried out in accordance with 6.2 to 6.6. 6.2 Inspection units The inspection units for products of the same

49、grade and nominal thickness are given in Table 2. Table 2 Inspection units Steel name Inspection unitt DD11 DD12 DD13 DD14 150 100 60 40 6.3 Number of tests A series of tests comprises all the tests necessary to verify the specified characteristics: tensile test; by agreement at the time of enquiry and order, a product chemical analysis. 6.4 Sampling For sheets, the selection of the product(s) for testing is left to the discretion of the inspection representative. For wide strips and slit wide strips, the samples sh