《DIN EN 486-2009 Aluminium and aluminium alloys - Extrusion ingots - Specifications English version of DIN EN 486 2009-11《铝和铝合金 挤压铸锭的规格 德文版本EN 486 2009》.pdf》由会员分享，可在线阅读，更多相关《DIN EN 486-2009 Aluminium and aluminium alloys - Extrusion ingots - Specifications English version of DIN EN 486 2009-11《铝和铝合金 挤压铸锭的规格 德文版本EN 486 2009》.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、November 2009DEUTSCHE NORM English price group 8No part of this standard may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77.150.10!$Zn:“1557523

2、www.din.deDDIN EN 486Aluminium and aluminium alloys Extrusion ingots SpecificationsEnglish version of DIN EN 486:2009-11Aluminium und Aluminiumlegierungen Pressbarren SpezifikationenEnglische Fassung DIN EN 486:2009-11SupersedesDIN EN 486:1994-02www.beuth.deDocument comprises pages11DIN EN 486:2009-

3、11 National foreword This standard has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys” (Secretariat: AFNOR, France), Working Group WG 2 “Extrusion billets and rolling ingots” (Secretariat: AFNOR, France). The responsible German body involved in its preparation was th

4、e Normenausschuss Nichteisenmetalle (Nonferrous Metals Standards Committee), Technical Committee NA 066-01-01 AA Unlegiertes und legiertes Aluminium, Masseln und Barren. Amendments This standard differs from DIN EN 486:1994-02 as follows: a) Clause 2 “Normative references” has been updated. b) In cl

5、ause 3 “Terms and definitions” the terms “extrusion ingot” and “cast” have been deleted; reference to EN 12258-1:1998 has been added. c) Subclause 6.1 “Analysis of chemical composition” has been revised. d) Subclause 7.2 “Inspection certificate” has been completely revised. e) The standard has been

6、editorially revised. Previous editions DIN EN 486: 1994-02 2 EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 486August 2009ICS 77.150.10 Supersedes EN 486:1993 English VersionAluminium and aluminium alloys - Extrusion ingots -SpecificationsAluminium et alliages daluminium - Billettes de filage -Sp

7、cificationsAluminium und Aluminiumlegierungen - Pressbarren -SpezifikationenThis European Standard was approved by CEN on 24 July 2009.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national st

8、andard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other

9、 language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Fin

10、land,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMIT

11、EE FR NORMUNGManagement Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 486:2009: EEN 486:2009 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions .44

12、Ordering information .45 Requirements .55.1 Production and manufacturing processes .55.2 Chemical composition 55.3 Surface and internal quality 55.4 Tolerances on dimensions .66 Test procedures .66.1 Analysis of chemical composition .66.2 Homogenizing treatment .76.3 Other tests 77 Inspection docume

13、nts .77.1 Certificate of mass and analysis 77.2 Inspection certificate .78 Marking . 9 Packaging, transport and storage 810 Complaints .8Bibliography 9DIN EN 486:2009-11 8EN 486:2009 (E) 3 Foreword This document (EN 486:2009) has been prepared by Technical Committee CEN/TC 132 “Aluminium and alumini

14、um alloys”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by February 2010, and conflicting national standards shall be withdrawn at the latest by Februar

15、y 2010. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 486:1993. Within its programme of work, Technical

16、Committee CEN/TC 132 entrusted CEN/TC 132/WG 2 “Extrusion billets and rolling ingots“ to revise EN 486:1993. CEN/TC 132 affirms its policy that in the case when a patentee refuses to grant licences on standardised standard products under reasonable and not discriminatory conditions, then this produc

17、t shall be removed from the corresponding standard. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,

18、 Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. DIN EN 486:2009-11 EN 486:2009 (E) 4 1 Scope This European Standard specifies the general r

19、equirements to be met by extrusion ingots of aluminium and aluminium alloys obtained by semi-continuous or continuous casting, from primary or recycled metal, for general engineering applications. 2 Normative references The following referenced documents are indispensable for the application of this

20、 document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 573-1, Aluminium and aluminium alloys Chemical composition and form of wrought products Part 1: Numerical designation system E

21、N 573-2, Aluminium and aluminium alloys Chemical composition and form of wrought products Part 2: Chemical symbol based designation system EN 573-3, Aluminium and aluminium alloys Chemical composition and form of wrought products Part 3: Chemical composition EN 10204, Metallic products Types of insp

22、ection documents EN 12258-1:1998, Aluminium and aluminium alloys Terms and definitions Part 1: General terms EN 14242, Aluminium and aluminium alloys Chemical analysis Inductively coupled plasma optical emission spectral analysis EN 14726, Aluminium and aluminium alloys Chemical analysis Guideline f

23、or spark optical emission spectrometric analysis 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 12258-1:1998 and the following apply. 3.1 heat quantity of liquid metal that has simultaneously undergone the same preparatory treatment in the furnace be

24、fore the casting operation 3.2 bundle set of ingots held together by suitable means for their transport 4 Ordering information The ordering information shall define the product required and shall contain the following: a) the form of the product (extrusion ingot); DIN EN 486:2009-11 EN 486:2009 (E)

25、5 b) the designation of the aluminium or aluminium alloy according to EN 573-1 and EN 573-2 (or the purchaser alloy designation after agreement between supplier and purchaser). Tighter limits than the composition limits stated in EN 573-3 may be specified as required; c) whether as cast or homogeniz

26、ed; the word “homogenized“ can be replaced by the abbreviation “HO“. Other abbreviations shall be agreed between the supplier and the purchaser; d) the number of this European standard; e) the nominal dimensions of the product (i.e. diameter and length) expressed in millimetres. For hollow ingots an

27、d ingots other than round, dimensions and tolerances shall be given with reference to a drawing; f) quantity: 1) mass (in metric tonnes); 2) quantity tolerances if required; g) any requirements for inspection documents (see Clause 7); h) any additional requirements agreed between supplier and purcha

28、ser. 5 Requirements 5.1 Production and manufacturing processes If no special requirement has been agreed between supplier and purchaser, the manufacturing process, including homogenizing, is the manufacturers responsibility. In the case of special requirements, it is recommended that trial quantitie

29、s be produced to confirm that requirements are met. It is also recommended that the purchaser asks the manufacturer to advise of any significant change in the manufacturing processes which may affect the quality of the final product. It is recommended that a quality assurance system be implemented a

30、s described in EN ISO 9000 and EN ISO 9004. 5.2 Chemical composition The chemical composition of the ingots shall conform to the compositions specified in EN 573-3. It should preferably conform to the numerical designation. 5.3 Surface and internal quality Extrusion ingots shall: a) be free of casti

31、ng surface defects, handling marks, oil, dirt and corrosion; b) be free of inclusions, porosity and cracks; c) have a suitable metallurgical structure; to a standard suitable for extrusion and subsequent processing. Unless otherwise agreed between purchaser and supplier, the grain size is not guaran

32、teed. DIN EN 486:2009-11 EN 486:2009 (E) 6 5.4 Tolerances on dimensions 5.4.1 Diameter (round ingots) The measurements shall be taken at the two sawn ends, on two diameters 90 apart. The tolerance on the nominal diameter is: a) 02mm for ingot diameters not larger than 200 mm; b) 03mm for ingot diame

33、ters larger than 200 mm and not larger than 400 mm; c) 04mm for ingot diameters larger than or equal to 400 mm. 5.4.2 Length The length is measured overall after sawing. The tolerance is: a) 3 mm for ingot lengths not longer than 1 200 mm; b) 15 mm for ingot lengths longer than 1 200 mm. 5.4.3 Squar

34、eness Sawn ends of extrusion ingots shall be square to 0,5. 5.4.4 Straightness The deflection, measured as arrow height on the centre of the curvature side, shall be less than 3 mm per metre with a maximum of 15 mm over the full length of the ingot. 5.4.5 Other dimensions For hollow ingots and ingot

35、s other than round, tolerances shall comply with the specifications in the order. 6 Test procedures 6.1 Analysis of chemical composition The analytical samples shall be taken at the discretion of the manufacturer who shall use methods accepted at European level, EN 14242 and EN 14726, or at Internat

36、ional level. The analytical samples shall be taken during the cast, from the metal distribution system, after the grain refiner addition (if any). The analytical samples shall be suitably machined and when analysed by emission spectrometry, shall be subject to at least two determinations. The sample

37、 result is the arithmetic mean of the determinations. DIN EN 486:2009-11 EN 486:2009 (E) 7 The final result is the arithmetic mean of the results of the taken samples. For cast acceptance, each sample shall meet the specified composition limits. The manufacturer shall use analytical methods standard

38、ized at European or International level. The choice of appropriate methods is at the discretion of the manufacturer. 6.2 Homogenizing treatment The homogenizing treatment is generally required. The manufacturer shall take suitable measures to guarantee the quality and reproducibility of homogenizing

39、, especially by: a) periodic inspection and testing of the treated metal; b) periodic checks of the actual temperature of the ingots during treatment; c) adoption of procedures to achieve satisfactory reproducibility of the treatment. The homogenizing treatment shall be closely monitored by the manu

40、facturers quality control system. 6.3 Other tests If required, other tests should be specified in the order after agreement between supplier and purchaser. 7 Inspection documents 7.1 Certificate of mass and analysis The supplier shall provide with each delivery a certificate of mass and analysis, wh

41、ich shall contain the following information: a) the name and address of the supplying company and the name of the manufacturing plant; b) the name and address of the purchaser; c) the description of the product as described in 4a), 4b), 4c) and 4e); d) the cast numbers, the number of extrusion ingot

42、s of each cast and, for each cast, the actual analysis of the elements (silicon, iron, copper, manganese, magnesium, chromium, zinc, titanium and other elements specified in EN 573-3 or required in the order) in the sequence given in EN 573-3; NOTE Horizontal casting of extrusion ingot may comprise

43、several heats per cast. In this case, the above information should be supplied for each heat. e) the total delivered net mass. 7.2 Inspection certificate Unless otherwise indicated in the order, the supplier shall deliver an inspection certificate 3.1 according to EN 10204 with at least the result o

44、f chemical analysis. DIN EN 486:2009-11 EN 486:2009 (E) 8 Each extrusion ingot shall be marked with at least the following: a) cast number; b) designation of the aluminium or the aluminium alloy as per the order; c) manufacturer identification (e.g. logo, brand name); d) HO or any other agreed abbre

45、viation if the ingot is homogenized. Labelling of each bundle shall be undertaken when agreed upon between supplier and purchaser. 9 Packaging, transport and storage Extrusion ingots shall be packaged in bundles suitable for safe forklift truck handling. Specific packaging requirements may be agreed

46、 between the purchaser and the supplier and shall be included in the order. Transport and storage conditions shall maintain the extrusion ingots in a condition suitable for extrusion without the necessity of further operations. 10 Complaints External and internal defects can give rise to complaints

47、if they affect the processing or the end use of the ingot. The purchaser shall allow the supplier to check the grounds for complaint. For example, he shall present him with the following: a) a piece of faulty ingot, with its complete identification, and/or; b) a specimen of the finished product, or

48、in an intermediate state, obtained from the faulty metal, with all the details allowing identification, and/or; c) justification of the defect in the ingot or finished product, and/or; d) details of conditions of processing and inspection in the intermediate stages. The dispute may entail the servic

49、es of a referee laboratory to perform examination and tests. The supplier and purchaser shall agree on the laboratory and the examination and tests methods employed. DIN EN 486:2009-11 8 Marking EN 486:2009 (E) 9 Bibliography 1 EN ISO 9000, Quality management systems Fundamentals and vocabulary (ISO 9000:2005) 2 EN ISO 9004, Quality management systems Guidelines for performance improvements (ISO 9004:2000) DIN EN 486:2009-11