DIN EN 1301-2-2008 Aluminium and aluminium alloys - Drawn wire - Part 2 Mechanical properties English version of DIN EN 1301-2 2008-12《铝和铝合金 拉制钢丝 第2部分 机械性能 英文版本DIN EN 1301-2-2008》.pdf

《DIN EN 1301-2-2008 Aluminium and aluminium alloys - Drawn wire - Part 2 Mechanical properties English version of DIN EN 1301-2 2008-12《铝和铝合金 拉制钢丝 第2部分 机械性能 英文版本DIN EN 1301-2-2008》.pdf》由会员分享，可在线阅读，更多相关《DIN EN 1301-2-2008 Aluminium and aluminium alloys - Drawn wire - Part 2 Mechanical properties English version of DIN EN 1301-2 2008-12《铝和铝合金 拉制钢丝 第2部分 机械性能 英文版本DIN EN 1301-2-2008》.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、December 2008DEUTSCHE NORM English price group 9No part of this standard may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77.150.10!$T#“1498800w

2、ww.din.deDDIN EN 1301-2Aluminium and aluminium alloys Drawn wire Part 2: Mechanical propertiesEnglish version of DIN EN 1301-2:2008-12Aluminium und Aluminiumlegierungen Gezogene Drhte Teil 2: Mechanische EigenschaftenEnglische Fassung DIN EN 1301-2:2008-12SupersedesDIN EN 1301-2:1997-11www.beuth.deD

3、ocument comprises 14 pagesDIN EN 1301-2:2008-12 2 National foreword This standard has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys” (Secretariat: AFNOR, France), Working Group WG 4 “Wires and drawing stock”. The responsible German body involved in its preparation w

4、as the Normenausschuss Nichteisenmetalle (Nonferrous Metals Standards Committee), Technical Committee NA 066-01-03 AA Draht und Vordraht. Amendments This standard differs from DIN EN 1301-2:1997-11 as follows: a) The foreword has been modified. b) Clause 2: EN 573-3 has been deleted and transferred

5、to Bibliography. c) Tables 1 to 6: The footnotes have been modified. d) Table 2: Tempers H13 and H18 have been added for alloy EN AW-2011 and temper H18 has been added for alloys EN AW-2014A, EN AW-2017A, EN AW-2117 and EN AW-2024. e) Table 5: EN AW-6056 has been added and temper H18 has been added

6、for alloys EN AW-6061 and EN AW-6082. f) Table 6: Temper H18 has been added. Previous editions DIN 1747: 1938-09, 1948-03, 1951-12, 1959-06, 1960-07 DIN 1747-1: 1963-06, 1968-12 DIN 1790: 1938-09, 1954-01, 1957-09 DIN 1790-1: 1977-01, 1983-02 DIN EN 1301-2: 1997-11 EUROPEAN STANDARDNORME EUROPENNEEU

7、ROPISCHE NORMEN 1301-2September 2008ICS 77.150.10 Supersedes EN 1301-2:1997 English VersionAluminium and aluminium alloys - Drawn wire - Part 2:Mechanical propertiesAluminium et alliages daluminium - Fil tir - Partie 2:Caractristiques mcaniquesAluminium und Aluminiumlegierungen - Gezogene Drhte -Tei

8、l 2: Mechanische EigenschaftenThis European Standard was approved by CEN on 16 August 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date li

9、sts and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the respo

10、nsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Icela

11、nd, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stass

12、art, 36 B-1050 Brussels 2008 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 1301-2:2008: EEN 1301-2:2008 (E) 2 Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Tensile test .4 Annex A (normative) Rules for rounding11 Bib

13、liography 12 DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 3 Foreword This document (EN 1301-2:2008) has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, ei

14、ther by publication of an identical text or by endorsement, at the latest by March 2009, and conflicting national standards shall be withdrawn at the latest by March 2009. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or

15、 CENELEC shall not be held responsible for identifying any or all such patent rights. CEN/TC 132 affirms it is its policy that in the case when a patentee refuses to grant licenses on standardised standard products under reasonable and not discriminatory conditions, then this product shall be remove

16、d from the corresponding standard. This document supersedes EN 1301-2:1997. Within its programme of work, Technical Committee CEN/TC 132 entrusted CEN/TC 132/WG 4 “Wires and drawing stock“ to revise EN 1301-2:1997. Besides editorial adjustments in the text and update of normative references the foll

17、owing changes have been made: Foreword amended; Clause 2: EN 573-3 deleted and included in Bibliography; Tables 1 to 6: Footnotes modified; Table 2: Tempers H13 and H18 added for alloy EN AW-2011 and temper H18 added for alloys EN AW-2014A, EN AW-2017A, EN AW-2117 and EN AW-2024; Table 5: Alloy EN A

18、W-6056 added and temper H18 added for alloys EN AW-6061 and EN AW-6082; Table 6: Temper H18 added. EN 1301 comprises the following parts under the general title: “Aluminium and aluminium alloys Drawn wire“: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3

19、: Tolerances on dimensions According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary

20、, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 4 1 Scope This document specifies the mechanical properties of aluminium an

21、d aluminium alloy drawn wires for general engineering applications (except aeronautical rivets). It applies to drawn wires, except for electrical or welding purposes. It does not apply to drawing stock. The designation of aluminium and aluminium alloys, their chemical composition and the temper desi

22、gnations used in this standard are in accordance with EN 573- 3 and EN 515 respectively. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition

23、of the referenced document (including any amendments) applies. EN 515:1993, Aluminium and aluminium alloys Wrought products Temper designations EN 1301-1, Aluminium and aluminium alloys Drawn wire Part 1: Technical conditions for inspection and delivery EN 10002-1, Metallic materials Tensile testing

24、 Part 1: Method of test at ambient temperature 3 Tensile test The conditions for the sampling shall be in accordance with EN 1301-1. The testing conditions specified in EN 10002-1 shall apply together with the following additional conditions: full section test pieces shall be used; elongation shall

25、be measured on a reference length of 100 mm. Tensile strength shall conform to Tables 1 to 6. NOTE Typical values for proof stress and elongation,are given for information only. Tensile strength values shall be rounded in accordance with Annex A. For rivet wire in non heat treatable alloys delivered

26、 in H13 temper the mechanical properties shall be determined in the temper of delivery. For rivet wire in heat treatable alloys delivered in H13 temper, the mechanical properties shall be determined: a) in the delivered temper H13; b) and also in tempers: 1) T4 for EN AW-2017A, EN AW-2117 and EN AW-

27、2024 alloys; 2) T6 for EN AW-2014A, EN AW-6061, EN AW-6082 and EN AW-7075 alloys. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 5 Testing may also be made in T42 temper or T62 temper (EN 515:1993, 7.3.2), instead of T4 or T6 respectively. In this case the mechanical properties limits are those given for

28、the corresponding T4 and T6 tempers. Table 1 Series 1 000 (Al) Temper Diameter Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical O 20 - 70 - 25 EN AW-1098 AI 99,98 H14 18 85 - 80 3 H18 10 115 110 2 O 20 - 80 - 3

29、5 EN AW-1080A AI 99,8 (A) H14 18 90 - 85 5 H18 10 120 115 3 O 20 - 85 - 35 EN AW-1070A AI 99,7 H14 18 95 - 90 5 H18 10 125 120 3 O 20 - 95 - 35 EN AW-1050A AI 99,5 H14 18 100 - 95 5 H16 15 120 115 3 18 10 140 - 135 aThe typical proof stress and elongation values are for information only and are infl

30、uenced by the wire diameter and the method of drawing. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 6 Table 2 Series 2 000 (Al Cu) Temper Diameter Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical EN AW-2011 AI Cu6B

31、iPb T3 18 310 - 295 6 T8 370 310 4 H13 18 155 225 - - 18 10 240 - H13 b18 210 280 190 5 EN AW-2014A AI Cu4SiMg (A) T4 18 380 - 255 18 T6 440 415 9 H18 10 295 - - - EN AW-2017A AI Cu4MgSi (A) H13 b18 210 300 190 5 T4 18 380 - 255 18 H18 10 315 - - EN AW-2117 AI Cu2,5Mg H13 b18 170 240 110 5 T4 18 260

32、 - 160 20 H18 10 260 - - EN AW-2024 AI Cu4Mg1 H13 b18 230 300 200 5 T4 18 420 - 315 18 H18 10 320 - - aThe typical proof stress and elongation values are for information only and are influenced by the wire diameter and the method of drawing. bMechanical properties shall also be tested in T4 temper (

33、alloys EN AW-2017A, EN AW-2117 and EN AW-2024) or T6 temper (alloy EN AW-2014A). Testing may also be made in T42 temper or T62 temper (EN 515:1993, 7.3.2), instead of T4 or T6 respectively. In this case the mechanical properties limits are those given for the corresponding T4 and T6 tempers. DIN EN

34、1301-2:2008-12 EN 1301-2:2008 (E) 7 Table 3 Series 3 000 (Al Mn) Temper Diameter Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical O 20 - 130 60 35 EN AW-3003 AI Mn1Cu H14 18 135 180 120 5 H18 10 180 - 175 3 O 2

35、0 - 130 60 35 EN AW-3103 AI Mn1) H14 18 135 180 120 5 H18 10 170 - 165 3 aThe typical proof stress and elongation values are for information only and are influenced by the wire diameter and the method of drawing. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 8 Table 4 Series 5 000 (Al Mg) Temper Diameter

36、 Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical O 20 - 195 85 15 EN AW-5051A AI Mg2 (B) H12 18 170 220 155 6 H14 195 245 200 4 18 10 245 - 3 O 20 - 215 95 15 EN AW-5251 AI Mg2Mn0,3 H14 18 215 265 220 4 H18 10

37、 265 - 270 3 O 20 - 225 100 15 14 18 225 275 225 4 EN AW-5052 AI Mg2,5 H18 10 275 - 275 3 H32 18 190 240 145 11 34 15 215 265 195 8 38 10 260 - 245 5 O 20 - 275 125 16 H14 18 280 330 270 3 18 10 330 - 320 2 EN AW-5154A AI Mg3,5 (A) H32 18 235 285 170 11 H34 15 265 315 230 8 36 10 290 340 250 6 38 31

38、0 - 280 4 O 20 - 250 110 16 H12 18 230 280 200 6 14 255 305 250 3 EN AW-5754 AI Mg3 H18 10 305 - 300 2 H32 18 220 270 160 11 34 15 245 295 210 8 H38 10 290 - 260 4 O 20 - 330 150 17 H12 18 295 355 255 6 14 325 385 315 3 EN AW-5019 AI Mg5 H18 18 370 - 360 2 H32 280 340 205 11 34 15 310 370 265 8 38 1

39、0 360 - 320 4 aThe typical proof stress and elongation values are for information only and are strongly influenced by the wire diameter and the method of drawing. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 9 Table 5 Series 6 000 (Al MgSi) Temper Diameterd Tensile strength RmProof stress Rp0,2 aElongat

40、ionaA100 mmmm MPa MPa %Material designation min. max. typical typical H13b 18 160 240 140 4 H18 10 240 - 210 2 T39 c 6 400 - - - EN AW-6056 AI Si1MgCuMn T39 c 6 360 - - - T4 20 300 380 - 13 T6 20 400 - 360 10 T89 c 6 420 - - - T39 c 6 220 - - - EN AW-6060 AI MgSi T39 c 6 270 - - - T4 20 140 210 90 1

41、3 T6 20 210 - 160 10 T89 c 6 260 - - - H13b 18 150 210 120 4 H18 10 210 - - - EN AW-6061 AI Mg1 SiCu T39 c 6 310 - - - T39 c 6 260 - - - T4 20 205 285 135 13 T6 20 290 - 260 10 T89 c 6 300 - - - T39 c 6 230 - - - T39 c 6 280 - - - EN AW-6063 AI Mg0,7Si T4 20 150 - 100 13 T6 20 220 - 190 10 T89 c 6 2

42、70 - - - H13b 18 165 225 130 4 H18 10 220 - 200 2 T39 c 6 310 - - - EN AW-6082 AI SiMgMn T39 c 6 360 - - - T4 20 205 285 135 13 T6 20 300 - 270 10 T89 c 6 340 - - - aThe typical proof stress and elongation values are for information only and are influenced by the wire diameter and the method of draw

43、ing. bMechanical properties shall also be tested in T6 temper. Testing may also be made in T62 temper (EN 515:1993, 7.3.2), instead of T6. In this case the mechanical properties limits are those given for the corresponding T6 tempers. cFor these tempers the mechanical properties are very dependent o

44、n the amount of cold work and, for T89 temper, on the ageing conditions. It is recommended that these characteristics should be agreed between supplier and purchaser. Consequently, typical values of Rp0,2and elongation are not given. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 10 Table 6 Series 7 000 (

45、Al Zn) Temper Diameter Tensile strength Proof stress Elongation ad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical O 20 - 275 110 13 EN AW-7075 AI Zn5,5MgCu H13 b18 230 310 230 2,5 H18 10 285 - 260 2 T6 20 510 485 10 aThe typical proof stress and elong

46、ation values are for information only and are influenced by the wire diameter and the method of drawing. bMechanical properties shall also be tested in T6 temper. Testing may also be made in T62 temper (EN 515:1993, 7.3.2), instead of T6. In this case the mechanical properties limits are those given

47、 for the corresponding T6 tempers. DIN EN 1301-2:2008-12 EN 1301-2:2008 (E) 11 Annex A (normative) Rules for rounding In recording test results, the number representing the results of a test to determine a given property shall be expressed to the same number of decimal places as the corresponding nu

48、mber in this standard, except for elongation values which shall be recorded with one more decimal place. The following rounding rules shall be used for determination of compliance with this standard: a) when the figure immediately after the last figure to be retained is less than 5, the last figure

49、to be retained remains unchanged; b) when the figure immediately after the last figure to be retained is greater than 5, or equal to 5 and followed by at least one figure other than zero, the last figure to be retained is increased by one; c) when the figure immediately after the last figure to be retained is equal to 5 and followed by zeros only, the last figure to be retained remains unchanged if even and is increased by one if odd. DIN EN